DE3306780C2 - Process for the surface treatment of cement-bound products in the form of semi-finished products - Google Patents

Process for the surface treatment of cement-bound products in the form of semi-finished products

Info

Publication number
DE3306780C2
DE3306780C2 DE19833306780 DE3306780A DE3306780C2 DE 3306780 C2 DE3306780 C2 DE 3306780C2 DE 19833306780 DE19833306780 DE 19833306780 DE 3306780 A DE3306780 A DE 3306780A DE 3306780 C2 DE3306780 C2 DE 3306780C2
Authority
DE
Germany
Prior art keywords
semi
products
cement
finished products
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19833306780
Other languages
German (de)
Other versions
DE3306780A1 (en
Inventor
Egon Ing.(Grad.) Komarow
Wolfgang Dipl.-Chem. Dr. 1000 Berlin Ortlepp
Karl-Heinrich 8851 Buttenwiesen Paa
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Eternit AG
Original Assignee
Eternit AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Eternit AG filed Critical Eternit AG
Priority to DE19833306780 priority Critical patent/DE3306780C2/en
Publication of DE3306780A1 publication Critical patent/DE3306780A1/en
Application granted granted Critical
Publication of DE3306780C2 publication Critical patent/DE3306780C2/en
Expired legal-status Critical Current

Abstract

Die Erfindung betrifft ein Verfahren zur Oberflächenbehandlung insbesondere Kaschierung und Beschichtung zementgebundener Produkte in Form von Halbfabrikaten wie Holz- und/oder Faserzementplatten. Um dekorative und auch witterungsbeständige Oberflächen zu schaffen, wird erfindungsgemäß vorgeschlagen, daß die gereinigten und getrockneten Halbfabrikate mit einer sauren Kunstharzdispersion und/oder einer wässerigen Säurelösung, pH-Wert kleiner 7, allseitig grundiert und auf der noch nicht vollständig getrockneten Grundierung unter Verwendung von säurehärtenden Dispersionsklebern kaschiert bzw. mit säurehärtenden Dispersionen beschichtet werden.The invention relates to a method for surface treatment, in particular lamination and coating of cement-bound products in the form of semi-finished products such as wood and / or fiber cement panels. In order to create decorative and weather-resistant surfaces, the invention proposes that the cleaned and dried semi-finished products be primed on all sides with an acidic synthetic resin dispersion and / or an aqueous acid solution, pH value less than 7, and on the not yet completely dried primer using acid-hardening Dispersion adhesives are laminated or coated with acid-hardening dispersions.

Description

Die Erfindung betrifft ein Verfahren zur Oberflächenbehandlung, insbesondere Kaschierung und Beschichtung, zementgebundener Produkte in Form von Halbfabrikaten bei dem auf die Halbfabrikate nach einer Säurebehandlung mindestens eine Kunstharzschicht aufgebracht wird.The invention relates to a method for surface treatment, in particular lamination and coating, cement-bound products in the form of semi-finished products in which on the semi-finished products after acid treatment at least one synthetic resin layer is applied.

Aus der DE-OS 25 04 035 ist ein Verfahren zur Herstellung duroplastbeschichteter Baustoffplatten bekannt. Es handelt sich dabei im einzelnen darum, Baustoffplatten, die eine alkalisch reagierende Oberfläche haben, insbesondere Asbestzementplatten, mit amino- und/oder phenolharzhaltigen Trägermaterialien mittels Heißpressung nach vorheriger Säurebehandlung der unbeschichteten Plattenoberfläche zu beschichten, wobei die zu beschichtende Plattenoberfläche mit solchen Säuren behandelt wird, die leicht wasserlösliche Kalziumsalze bilden, worauf die Plattenoberfläche mit Wasser bis zur neutralen Reaktion gewaschen, getrocknet und anschließend die trägermaterialhaltige Amino- und/oder Phenolplastikschicht aufgebracht wird.From DE-OS 25 04 035 a method for producing thermoset-coated building material panels is known. In detail, it is a question of building material panels that have an alkaline reacting surface have, in particular asbestos cement panels, with carrier materials containing amino and / or phenolic resin by means of Hot pressing to coat the uncoated board surface after previous acid treatment, whereby the board surface to be coated is treated with acids that are easily water-soluble calcium salts form, whereupon the plate surface washed with water until neutral, dried and then the carrier material-containing amino and / or phenolic plastic layer is applied.

Das bekannte Verfahren ist also darauf abgestellt, die stark alkalisch reagierende Oberfläche zu neutralisieren, um die sonst durch OH-Ionen verursachten Schwierigkeiten bei der Aushärtung von Duroplastbeschichtungen zu vermeiden.The known method is therefore geared towards neutralizing the strongly alkaline reacting surface, about the difficulties in curing thermoset coatings that are otherwise caused by OH ions to avoid.

Neben Verfahren wie dem oben geschilderten sind aus der Praxis andere Verfahren bekannt, mittels derer dekorative, zum Teil auch witterungsbeständige Produkte durch Kaschieren, Laminieren und Beschichten hergestellt werden. Diese Verfahren sind vor allem im Zusammenhang mit der Oberflächenbehandlung von Holzwerkstücken, wie kunstharzgebundenen Preßspanplatten und stäbchenverleimten Tischlerplatten bekannt. In addition to methods such as those described above, other methods are known from practice by means of which decorative, partly also weather-resistant products through lamination, lamination and coating getting produced. These processes are mainly related to the surface treatment of Wood workpieces, such as resin-bonded chipboard and stick-glued blockboard are known.

Je nach Feuchtegehalt der Halbfabrikate werden die Holzwerkstücke zumeist vorgetrocknet, anschließend mit einer Leimfuge sowie der Folie bzw. einem Laminat versehen und hinterher heißverpreßt. Die Produkte sind nach dem Abkühlen sofort — evtl. auch für weitere Bearbeitungsschritte — gebrauchsfähig.Depending on the moisture content of the semi-finished products, the wooden workpieces are mostly pre-dried, then provided with a glue joint and the film or a laminate and then hot-pressed. The products are Can be used immediately after cooling down - possibly also for further processing steps.

Die von den Holzwerkstücken her bekannten Techniken lassen sich auf zementgebundene Werkstücke wie Holz- und/oder Faserzementplatten nicht ohne weiteres übertragen. Ursachen hierfür sind die hohe Alkalität, die poröse Oberflächenstruktur und die — verglichen mit Holzwerkstücken — deutlich höhere Rohdichte von deren Werkstoffen.The techniques known from wood workpieces can be applied to cement-bound workpieces such as Wood and / or fiber cement panels are not easily transferred. The reasons for this are the high alkalinity, the porous surface structure and - compared to wooden workpieces - the significantly higher bulk density of their materials.

Infolge des alkalischen Untergrundes werden die gebräuchlichen Dispersionskleber verseift bzwn sofern es sich um säurekatalysierte Systeme handelt, inhibiert; der Kleber härtet nicht durch, so daß eine ausreichende Haftfestigkeit von Folien bzw. Laminaten auf diesen Werkstoffen nicht erreicht werden kann.As a result of the alkaline substrate, the conventional dispersion adhesives are saponified or n is provided by acid-catalysed systems is inhibited; the adhesive does not harden through, so that sufficient adhesive strength of foils or laminates on these materials cannot be achieved.

Dieser Effekt wird dadurch verstärkt, daß der bei Verwendung von wässerigen Dispersionsklebern im Zuge des Heißpressens entstehende Wasserdampf wegen der elativ hohen Rohdichte nicht innerhalb der Werkstückoberfläche aufgenommen wird und infolgedessen die gewöhnlich wenig wasserdampfdurchlässigen Folien bzw. Laminate durch den Wasserdampfdruck von der Werkstückoberfläche wieder gelöst werden.This effect is reinforced by the fact that when using aqueous dispersion adhesives in the course The water vapor produced by hot pressing is not within the workpiece surface due to the relatively high bulk density is taken up and consequently the usually little water vapor permeable foils or laminates can be detached from the workpiece surface again by the water vapor pressure.

Diese chemisch und physikalisch bedingten Verbundstörungen, die in entsprechender Weise auch generell bei bzw. nach dem Oberflächenbeschichten mit Dispersionsanstrichmitteln auftreten können, werden durch die Oberflächenporosität von Holz- bzw. Faserzementwerkstücken verstärkt.These chemically and physically caused interconnection disorders, which in a corresponding manner also in general can occur during or after surface coating with dispersion paints reinforced by the surface porosity of wood or fiber cement workpieces.

Die zur Lösung dieser Probleme durchaus mögliche Verwendung lösemittelhaltiger oder zweikomponentiger Kleber und Anstrichmittel ist wegen der damit verbundenen Emissionen und des höheren Verfahrens- und Anlagenaufwandes nicht vorteilhaft.The use of solvent-based or two-component ones, which is entirely possible to solve these problems Glue and paint is because of the emissions involved and the higher process and Investment expense is not advantageous.

Aufgabe der vorliegenden Erfindung ist das Kaschieren, Laminieren sowie Beschichten zementgebundener Holz- und Faserwerkstücke, wie Holzzement- und Faserzementplatten, mit dem Ziel, dekorative und auch — im Fall der Anwendung als Fassadenverkleidungsplatten — witterungsbeständige Oberflächen zu erzeugen.The object of the present invention is the lamination, lamination and coating of cement-bound Wood and fiber workpieces, such as wood cement and fiber cement boards, with the aim of making decorative and also - in the case of application as facade cladding panels - to produce weather-resistant surfaces.

Diese Aufgabe wird erfindungsgemäß durch die im Hauptanspruch angegebenen Verfahrensmerkmale gelöst. Es hat sich überraschenderweise gezeigt, daß — mit bei der Oberflächenveredlung von Holzwerkstücken bekannten, üblichen Methoden und Anlagen — Kaschierungen, Laminierungen und Beschichtungen auf Holz- bzw. Faserzementwerkstücken mit gutem Erfolg durchführbar sind. Als Verdickungs- und/oder Thixotropierungsmittel zur Verbesserung der Theologischen Eigenschaften können der wässerigen Essigsäure-Lösung z. B. Methylcellulose oder Bentonite zugesetzt werden.
Der Vorteil der Erfindung liegt vor allem darin, daß der Säuregehalt der Zementoberfläche die Aushärtung der säurehärtenden Beschichtung katalysiert und zudem, da die Zementoberfläche durch die einwirkende Säure geringfügig aufgerauht wird, ein wesentlich besserer Haftgrund für die Beschichtung geschaffen wird.According to the invention, this object is achieved by the method features specified in the main claim. Surprisingly, it has been shown that - with conventional methods and systems known for the surface finishing of wooden workpieces - lamination, lamination and coatings on wood or fiber cement workpieces can be carried out with good success. As a thickening and / or thixotropic agent to improve the theological properties, the aqueous acetic acid solution z. B. methyl cellulose or bentonite can be added.
The main advantage of the invention is that the acid content of the cement surface catalyzes the hardening of the acid-hardening coating and, in addition, since the cement surface is slightly roughened by the acting acid, a much better primer for the coating is created.

AusführungsbeispielEmbodiment

a) Handelsübliche Holzzementtafeln werden auf ca. 8% Wassergehalt vorgetrocknet.a) Commercially available wood cement boards are pre-dried to a water content of approx. 8%.

b) Die Tafeln werden allseitig — zumindest aber oberflächenseitig — mit einer wässerigen Essigsäurelösung mit einem pH-Wert von 3, die mittels Methylcellulosezusatz auf eine im Fordbecher 4 mm gemessene Auslaufviskosität von ca. 15 DIN-Sekünden eingestellt worden ist, im Spritz-, Gießoder Walzverfahren grundiert, wobei die Auftragsmenge je nach Saugvermögen der Substrate 60 bis 150 g/m2 Oberfläche beträgt.b) The boards are sprayed, poured or poured into an aqueous acetic acid solution with a pH value of 3 on all sides - but at least on the surface, which has been adjusted to an outlet viscosity of approx. 15 DIN seconds measured in a Ford cup 4 mm by means of methyl cellulose Rolling process primed, the application amount depending on the absorbency of the substrates being 60 to 150 g / m 2 surface.

c) Auf die abgedunstete, aber noch säurefeuchte Oberfläche wird ein säurehärtender Kleber, z. B. Melamin-Formaldehyd-Dispersionskleber, aufgetragen. c) An acid-hardening adhesive, e.g. B. Melamine-formaldehyde dispersion adhesive applied.

d) Sofort anschließend oder in einem Arbeitsgang mit dem Leimauftrag wird kaschiert bzw. laminiert und hinterher heißverpreßt.d) Immediately afterwards or in one operation with the application of glue, it is laminated or laminated and afterwards hot-pressed.

Anstelle des säurehärtenden Klebers kann, wenn lediglich die Beschichtung des Substrates vorgesehen ist, mit einem säureversetzbaren Anstrichmittel, beispielsweise einer Melamin-Formaldehyd-haltigen Acrylatdispersion, beschicht werden. In diesem Fall wird nach dem Beschichten getrocknet und bis zum Erreichen der Block- bzw. Einstapeltemperatur gekühlt.Instead of the acid-curing adhesive, if only the coating of the substrate is provided, with an acid-relocatable paint, for example an acrylate dispersion containing melamine-formaldehyde, be coated. In this case it is dried after the coating and until the Block or stacking temperature cooled.

2020th

3535

4040

4545

5050

5555

6060

Claims (3)

Patentansprüche:Patent claims: 1. Verfahren zur Oberflächenbehandlung, insbesondere Kaschierung und Beschichtung, zementgebundener Produkte in Form von Halbfabrikaten, bei dem auf die Halbfabrikate nach einer Säurebehandlung mindestens eine Kunstharzschicht aufgebracht wird, dadurch gekennzeichnet, daß die gereinigten und getrockneten Halbfabrikate mit einer sauren Kunstharzdispersion und/oder einer wässerigen Säurelösung, pH-Wert kleiner 7, allseitig grundiert und auf der noch nicht vollständig getrockneten Grundierung unter Verwendung von säurehärtenden Dispersionsklebern kaschiert bzw. mit säurehärtenden Dispersionen beschichtet werden.1. Process for surface treatment, in particular lamination and coating, cement-bound Products in the form of semi-finished products, in which on the semi-finished products after acid treatment at least one synthetic resin layer is applied, characterized in that the cleaned and dried semi-finished products with an acidic synthetic resin dispersion and / or an aqueous one Acid solution, pH value less than 7, primed on all sides and on the not yet completely dried Primer laminated with acid-hardening dispersion adhesives or with acid-hardening ones Dispersions are coated. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als wässerige Säurelösung eine wässerige Essigsäure-Lösung mit einem pH-Wert von 3 verwendet wird.2. The method according to claim 1, characterized in that an aqueous acid solution is used as the aqueous acid solution Acetic acid solution with a pH of 3 is used. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß der Essigsäure-Lösung Verdickungs- und/oder Thixotropierungsmittel zugesetzt wird.3. The method according to claim 2, characterized in that the acetic acid solution thickening and / or thixotropic agent is added.
DE19833306780 1983-02-23 1983-02-23 Process for the surface treatment of cement-bound products in the form of semi-finished products Expired DE3306780C2 (en)