DE3229288A1 - Application of a composite and composite for the decoration of surfaces - Google Patents

Application of a composite and composite for the decoration of surfaces

Info

Publication number
DE3229288A1
DE3229288A1 DE19823229288 DE3229288A DE3229288A1 DE 3229288 A1 DE3229288 A1 DE 3229288A1 DE 19823229288 DE19823229288 DE 19823229288 DE 3229288 A DE3229288 A DE 3229288A DE 3229288 A1 DE3229288 A1 DE 3229288A1
Authority
DE
Germany
Prior art keywords
intermediate carrier
use according
layer
carrier
composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19823229288
Other languages
German (de)
Other versions
DE3229288C2 (en
Inventor
Elmar Dr. 8000 München Messerschmitt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siebdruck und Plastic Seri - Plastica 8000 M GmbH
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19823229288 priority Critical patent/DE3229288A1/en
Publication of DE3229288A1 publication Critical patent/DE3229288A1/en
Application granted granted Critical
Publication of DE3229288C2 publication Critical patent/DE3229288C2/de
Granted legal-status Critical Current

Abstract

Composite and use of a composite, in which a sublimable ink is printed on a flexible transfer medium that cannot permanently bond to the plastic surface of a substrate and which is released from a base carrier providing stability for printing, applied without bubbles and wrinkles to a possibly highly uneven substrate surface and transferred by heat, especially without the effect of pressure, during or after which the transfer medium is released again if necessary.

Description

Anwendung eines Composites undApplication of a composite and

Composit zur Dekoration von Oberflächen Die Dekoration von uneben geformten Gegenständen mittels Farbdrucken, wieche durch eine flexible Trägerhaut zusammengehalten werden, die beim Einbrennvorgang verschwindet, ist vom-keramischen Abziehbilderdruck bekannt.- Die Dekoration von ebenen Gegenständen, deren Oberfläche sublimierende Farbstoffe mittels sog. Transferbilder, die mittels Druck heiß aufgepreßt werden, annimmt, ist [auch bekannt.Composite for decoration of surfaces The decoration of uneven molded objects by means of color printing, such as through a flexible carrier skin are held together, which disappears during the baking process, is from the ceramic Known decal printing .-- The decoration of flat objects, their surface subliming dyes by means of so-called transfer images, which are hot-pressed by means of pressure to be, assumes, is [also known.

Letzteres Verfahren kann aber nicht unregelmäßig geformte Oberflächen dekorieren.However, the latter method cannot produce irregularly shaped surfaces decorate.

Es scheint vielleicht naheliegend, daß die Vereinigung beider Verfahren die Dekoration uneben geformter Gegenstände durch Sublimierbilder ermöglicht. Obwohl beide Verfahren seit vielen Jahren bekannt sind, ist diese Vereinigung aber nie vorgenommen worden, genauso wie eine Übertragung von Sublimationsbildern auf ebene Flächen ohne Pressendruck nicht bekannt ist. Ursache für diesen offensichtlichen Mangel, der durch besonders geformte Heizstempel in der Praxis umgangen wird, ist offensichtlich ein Vorurteil, basierend auf den Erfahrungen, daß nur ein vollständigerKontakt randscharfe sublimationsübetragung ermöglicht, so daß eine Zwischenschicht, sei es ein temporäres Haftmittel, ein Kleber oder ein durch Athäsion haftender Träger, die Sublimation behindert oder unscharf macht, oder daß das Verbleiben der Zwischenschicht auf dem dekorierten Gegenstand hinderlich wäre, auch dass Erfahrungen mit "verlorenem" Zwischenträger nur bei hohen Temperaturen (über 400 °C) bestehen.It may seem obvious that the combination of both procedures enables the decoration of unevenly shaped objects by means of sublimation images. Even though Both procedures have been known for many years, but this association never is was carried out, as well as a transfer of sublimation images on flat Areas without press pressure is not known. Cause of this obvious Deficiency that is circumvented in practice by specially shaped heating dies obviously a prejudice based on experience that only complete contact sharp-edged sublimation transfer enables, so that an intermediate layer is it is a temporary adhesive, an adhesive or a backing adhered by athesion, the sublimation hinders or blurs, or that the remaining of the intermediate layer on the decorated object would be a hindrance, also that experiences with "lost" Intermediate carriers only exist at high temperatures (over 400 ° C).

Überraschenderweise aber hat sich gezeigt, daß solche Vorurteile nicht haltbar sind, besonders wenn die Farbschichten genügend kräftig, z. . im Siedruck, gedruckt sind und die zwischen Bedruckstoff und Farbschicht befindliche Haftschicht nicht zu dick ist.Surprisingly, however, it has been shown that such prejudices are not are durable, especially if the layers of paint are strong enough, e.g. . in screen print, are printed and the adhesive layer located between the substrate and the ink layer is not too fat.

Erfindungsgemäß werden also auf einfache Weise uneben geformte Gegenstände mit Sublimationsbildern, die sich auf einem dünnen, flexiblen Träger befinden, dekoriert, wobei außer Heizpressen erfindungsgemäß auch HeißluSt, Strahlungswärme und andere bekannte Heizquellen benutzt werden. Die Erfindung eröffnet damit für solche Gegenstände ein neues Verfahren der Dekoration, die wegen ihrer unebenen Oberfläche bisher nicht ohne große Kosten einzeln oder in kleinen Mengen je nach Bedarf dekoriert werden konnten.According to the invention, objects that are unevenly shaped are thus obtained in a simple manner decorated with sublimation images on a thin, flexible support, In addition to heating presses, according to the invention, hot air, radiant heat and others are also used known heating sources are used. The invention thus opens up for such objects a new method of decoration that has not yet been used because of its uneven surface can be decorated individually or in small quantities as required at no great expense could.

Die Dekoration von ebenen und unebenen Einwegverpackungen, Souveniers, Spielaerrulen, Haushaltsgegenstnden, die IErkierung technischer Artikel hat damit eine neue Dimension gewonnen, die zum Teil vollautomatisch kontinuierlich in den Fertigungsprozeß selbst eingebaut werden kann (z. B.The decoration of flat and uneven one-way packaging, souvenirs, Game games, household items, the promotion of technical articles with it gained a new dimension, some of which are automatically and continuously in the Manufacturing process itself can be built in (e.g.

Tiefziehprozeß, Extruderverfahren, Temperverfahren).Deep drawing process, extruder process, tempering process).

Bevorzugte Anwendung findet das Verfahren zur Dekoration unregelmäßig geformter Gebrauchs-, Kunst- und Souverniercheramik, zum Signieren von technischer Cheramik, von Glas, zur Dekoration und Signierung von Kunststoffgegenständen, z. B. aus Polyester, Polyamid, Polyaethylen, auch von Gummi, von polyesterlakierten Gegenständen, z. B. auch Spielzeug, Haushalta- und technischen Gegenständen aus Holz und Metall, aber auch oxydierten Aluminiumoberflächen wobei die nachträgliche Dekorierung fertiger Gegenstände mit örtlicher Erwärmung ohne sehr aufwendige Vorrichtungen besondere wirtschaftliche Vorteile bietet, Das Verfahren ermöglicht es, an in mehreren Dimensionen gleichzeitig gewölbten Gegenständen Sublimationsbilder anzubringen, was mit den bisher bekannten Methoden nicht oder nur bei Wölbungen in einer Dimension und mit 6ehr geringen Abweichungen aus einer weiteren Dimension möglich war.The method for decoration is preferably used irregularly Shaped utility, art and sovereignty ceramics, for signing technical Cheramik, made of glass, for the decoration and signing of plastic objects, e.g. B. made of polyester, polyamide, polyethylene, also of rubber, of polyester lacquered Objects, e.g. B. also toys, household and technical items Wood and metal, but also oxidized aluminum surfaces, with the subsequent Decoration of finished objects with local heating without very expensive devices offers particular economic advantages, the process enables it to be carried out in several Dimensions to attach sublimation images to curved objects at the same time, what with the previously known methods not or only with bulges in one dimension and was possible with very small deviations from another dimension.

Dieses neue Verfahren ist gekennzeichnet dadurch, daß Gegenstände, deren Oberfläche Farbstoffe durch Sublimieren annimmt, mit einem ggf. temporär haftenden Transferbild versehen werden, welches sich auf einer flexiblen bzw.This new method is characterized in that objects, the surface of which accepts dyes through sublimation, with a possibly temporary adhesive Transfer image can be provided, which is on a flexible or

elastischen Haut befindet, aut welches mittels einer Presse, Heißluft oder Strahlungswärme ausreichend Hitze einwirkt, wodurch die Sublimation je nach Farbe bei Temperaturen von 160 bis 180 ° und ggf. bis 220 0C in die Oberfläche stattfindet. Die Zwischenschicht kann sich bei diesem Vorgang auflösen, einbrennen, abwaschen, zersetzen oder nach diesem Vorgang mechanisch oder durch Auflösen wieder abgetrennt worden. Das auf der flexiblen Haut befindliche Transferbild ist in der Weise hergestellt, daß auf eine Basis-Trägerfolie oder ein Basisträgerpapier Sublimierfarben und die flexible Lackschicht aufgebracht bzw.elastic skin is located, aut which by means of a press, hot air or radiant heat acts sufficiently heat, thereby reducing the sublimation depending on Color takes place in the surface at temperatures of 160 to 180 ° and possibly up to 220 0C. During this process, the intermediate layer can dissolve, burn in, wash off, decompose or after this process separated again mechanically or by dissolving been. The transfer image on the flexible skin is produced in such a way that that on a base carrier film or a base carrier paper sublimation dyes and the flexible lacquer layer applied or

aufgedruckt sind, welche vor dem übertragen auf den zu dekorierenden Gegenstand abgezogen wird, wobei ggf. der Basisträger eine Trennschicht besitzt, welche ggf. durch Wärme oder Feuchtigkeit oder Lösemittel löslich gemacht wird, so daß der Druckträger abgehoben bzw. abgeschoben werden ka . Die Trennschicht kann dabei- ganz oder teilweise an den flexiblen Zwischenträger kleben bleiben, sie kann ggf. die Verklebung -am zu dekorierenden Gegenstand befördern. Das Transferbild kann aber auch aus einer sublimierende Farbstoffe enthaltenden Trägerschicht bestehen, welche mit einer die Sublimation abdeckende Maske bedruckt ist, die nur an den offenen Stellen eine Farbübertragung die die zu dekorierende Oberfläche zuläßt. Wird die Sublimation durch Heißdampf bewirkt, kann dieser gleichzeitig den Zwischenträger ablösen. Beflammen oder Strahlungswärme kann ihn verrotten oder verbrennen. In diesem Fall sind Filme, Gewebe oder Vlies aus Zellulose geeignet, besonders wenn sie chemisch in bekannter Weise dafür aufgeschlossen sind.are printed on which is to be decorated before being transferred The object is peeled off, the base support possibly having a separating layer, which may be made soluble by heat or moisture or solvents, so that the print carrier can be lifted or pushed off. The separating layer can while sticking completely or partially to the flexible intermediate carrier, it can if necessary, move the adhesive to the object to be decorated. The transfer image but can also consist of a carrier layer containing subliming dyes, which is printed with a mask covering the sublimation, which only applies to the open Provide a color transfer that allows the surface to be decorated. Will the Sublimation caused by superheated steam, this can also act as an intermediate carrier peel off. Flame or radiant heat can rot or burn it. In this In this case, cellulose films, fabrics or fleece are suitable, especially if they are chemical are open to it in a known way.

Für die nachträgliche Ablösung empfiehlt sich bei einem wasserlöslichen Zwischenträgerfilm warmes Wasser, mit oder ohne chemische Zusätze, z. B. für PVA-Filme, Natrium oder Calciumperjodat. Durch Absaugen kann die Ablösung erleichtert werden, ebenso durch Abbürsten, Absprühen oder andere, mechanische Einwirkung. So können selbst mit Wärmeeinfluß ausgehärtete Filme abgelöst werden.A water-soluble one is recommended for subsequent removal Intermediate film warm water, with or without chemical additives, e.g. B. for PVA films, Sodium or calcium periodate. Removal can be facilitated by suction, also by brushing, spraying or other mechanical action. So can even films cured under the influence of heat can be peeled off.

Die Aufbringung des flexiblen Zwischenträgers auf stark verformte Substrate wird wesentlich erleichtert durch Löcher oder Schlitze, durch möglichst geringe Dicke (10 - 30 µ), wobei dieser aber noch genügend Stabilität zum 6 ertragen haben muß.The application of the flexible intermediate carrier to severely deformed Substrate is made much easier by holes or slits, by as much as possible small thickness (10 - 30 µ), but still enough stability to endure 6 must have.

Die blasenfreie Anbringung auf dem Substrat erfordert eine Glätte und Anschmiegsamkeit an die Substratqberfläche, die eine kleberfreie Adhäsion bewirkt oder die Fähigkeit die temperäre Klebung befördernde Lösemittel oder Wasser diffundieren zu lassen, so daß keine 3lähungen unter Wärme entstehen oder einen Kleber, dep ggf. durch Wärme oder Lösemittel aktivierbar ist, unter der Sublimiererhitzung nicht bläht, aber nach den Erkalten keine erhebliche Klebefähigkeit mehr besitzt, so daß er leicht zu beseitigen ist.The bubble-free application on the substrate requires smoothness and conformability to the substrate surface, which causes glue-free adhesion or the ability to diffuse solvents or water that promote the temperature of the bond to leave, so that no paralysis occurs under heat or an adhesive, dep if necessary can be activated by heat or solvents, but not when heated by the sublimator swells, but no longer has significant adhesive properties after cooling, so that it is easy to remove.

Sehr flexible, zur Klebung neigende Zwischenträgermaterialien, wie thermoplatische Lackschichten, können durch Metallauftrag (z. B. Aufdampfung), Silikon, Wachs oder andere geeignete Trennmittel gegen dauerhaftes Verkleben geschützt sein, wobei die Farbe vorzugsweise auf der Trennschicht liegt.Very flexible intermediate carrier materials that tend to stick, such as thermoplastic lacquer layers, can be achieved by applying metal (e.g. vapor deposition), silicone, Wax or other suitable release agents must be protected against permanent sticking, the color preferably being on the separating layer.

Als Basisträger sind bes. sog. Abziehbild- und Trennpapiere (Silikon-Papier) geeignet. Aber auch Folien aus Kunststoff (Polyester) oder Metall z. B. Aluminium sind für die Anbringung ablösbarer bzw. abziehbarer Zwischenträger geeignet. Sie haben die Aufgabe, falls der Zwischenträger nicht genügend Eigenstabilität für den Druckvorgang, den Transport und die Lagerung besitzt, diese temporär bis zur Übertragung des Zwischenträgers auf das Substrat zu bieten.So-called decal and release papers (silicone paper) are used as the base carrier. suitable. But also films made of plastic (polyester) or metal z. B. aluminum are suitable for attaching removable or removable intermediate supports. she have the task, if the intermediate carrier does not have enough inherent stability for the Printing process, transport and storage, this temporarily until the transfer to offer the intermediate carrier to the substrate.

Figur 1 zeigt den Basisträger 1 z. B. eine Kunststoffolie mit Zwischenträger 2 und sublimierbarer Farbe 3.Figure 1 shows the base support 1 z. B. a plastic film with an intermediate carrier 2 and sublimable color 3.

Figur 2 zeigt Basis 1, z. B. ein Vlies mit einem Trennmittel 6, auf welchem die sublimierbare Farbe 3 aufgedruckt ist und darüber der Zwischenträger 2 Figur 3 zeigt die sublimierbare Farbe 3 eingeschlossen zwischen 2 Zwischenträgerschichten 2 a und 2 b auf dem Basisträger 1, z. B. eine Metallfolie, wobei 2 a eine Haftschicht sein kann.Figure 2 shows base 1, e.g. B. a fleece with a release agent 6 on which the sublimable color 3 is printed and above the intermediate carrier FIG. 3 shows the sublimable paint 3 enclosed between 2 intermediate carrier layers 2 a and 2 b on the base support 1, z. B. a metal foil, where 2a is an adhesive layer can be.

Figur 4 zeigt auf einer Basis, z. B. Papier mit einer Trennschicht @, z. B. Silicon den Zwischenträger 2 und darauf die Farbe 3.Figure 4 shows on a base, e.g. B. Paper with a release liner @, e.g. B. silicone the intermediate carrier 2 and then the color 3.

Figur 5 zeigt den Vorgang der Übertragung. Als erste Stufe in Figur 5 z. B. die sublimierbare Farbe 3 eingeschlossen zwischen Basis 1 und Zwischenträger 2, der gerade sich abhebt, wobei auf der Basis ein Trennmittel @ sichtbar ist, das ggf. auch teilweise am Zwischenträger verbleibt oder in Figur 5 b den Zwischenträger 2 mit der sublimierbaren Farbe 5, der gerade von der Basis 1 abgeschoben bzw. abgehoben wird.Figure 5 shows the transfer process. As the first stage in figure 5 z. B. the sublimable color 3 enclosed between base 1 and intermediate carrier 2, which is just taking off, whereby a release agent @ is visible on the base, which possibly also partially remains on the intermediate carrier or in Figure 5b the intermediate carrier 2 with the sublimable color 5, which has just been pushed off or lifted off the base 1 will.

Als nächste Stufe (5 c) das Substrat 4 (eine cheramische Vase mit Polyesterlacküberzug 4') auf dem der Zwischenträger nach Figur 5 a mit der mit einer der beiden Seiten, je nach Art des Zwischenträgers, und nach Figur 5 b mit der Farbseite in einschlußfreien Kontakt mit dem Substrat gebracht und in letzter Stufe (5 d) von der Wärmequelle 7 mit 180 °C 30 sec. beaufschalgt wird.As the next step (5 c) the substrate 4 (a ceramic vase with Polyester lacquer coating 4 ') on which the intermediate carrier according to Figure 5 a with the one the two sides, depending on the type of intermediate carrier, and according to Figure 5b with the color side brought into inclusion-free contact with the substrate and in the last stage (5 d) is acted upon by the heat source 7 at 180 ° C. for 30 seconds.

Claims (30)

P a t e n t a n s p r ü c h e 1. Verwendung eines Composites aus einer sublimierbaren Farbschicht, die durch einen Druckvorgang aufgebracht ist auf einen Zwischenträger, der flexibel ist und sich unter Übertragungsbedingungen vom Substrat ablöst oder zersetzt und vom einem Basisträger mit ausreichender Stabilität für die Durchführung des oder der Druckvorgange ablösbar ist zur Übertragung von Bildern aufunebene Substrate mittels Wärme im Subliniationsverfahren. P a t e n t a n s p r ü c h e 1. Use of a composite from a sublimable color layer which is applied by a printing process an intermediate carrier that is flexible and can move from the Substrate peeling off or decomposed and from a base support with sufficient stability for the implementation of the printing process (s) is detachable for the transfer of Images on uneven substrates using heat in the sublination process. 2. Verwendung nach 1, wobei die Wärme ohne gleichzeitigen mechanischen'Druck, z. B. durch Flammen, durch Heißluft, Strahlungswärme, Induktion oder ein flüssiges Medium zugeführt wird.2. Use according to 1, wherein the heat without simultaneous mechanical pressure, z. B. by flames, by hot air, radiant heat, induction or a liquid Medium is fed. 3. Verwendung nach 1 - 2, wobei der Zwischenträger transparent ist und als Schutzschicht aut dem. Substrat verbleibt.3. Use according to 1-2, wherein the intermediate carrier is transparent and as a protective layer on top. Substrate remains. 4. Verwendung nach 1 - 2, wobeder Zwischenträger eine Schichtdicke zwischen 10 und 30 /u besitzt.4. Use according to 1-2, where the intermediate carrier is one layer thickness between 10 and 30 / u. 5. Verwendung nach 1 - 2, wo der Zwischenträger ein z. B. im Siebdruck gedruckter Film ist, der unter Übertragungsbedingungen keine dauerhafte Verbindung mit dem Substrat bzw. dessen Oberfläche eingeht.5. Use according to 1 - 2, where the intermediate carrier is a z. B. in screen printing printed film is not permanently bonded under transfer conditions enters into with the substrate or its surface. 6. Verwendung nach 1 - 5, wobei der 3asisträger eine trennschicht, z. 3. Silicon bzw. eine mittels Wasser, Lösemittel und oder Wärme aktivierbare Trennschicht, z. 3. PVA besitzt.6. Use according to 1 - 5, where the base carrier has a separating layer, z. 3.Silicon or a separating layer that can be activated by means of water, solvents and / or heat, z. 3. PVA owns. 7. Verwendung nach 1 - 6, wobei der Zwischenträger ein Vlies oder Gewebe ist.7. Use according to 1-6, wherein the intermediate carrier is a fleece or Tissue is. 8. Verwendung nach 1 - 6, wobei der Zwischenträger ein Film aus Zellulose Collodium (Nitrocellulose), Kunststoff, Kautschuk bzw. Latex oder Siliconkautschuk ist.8. Use according to 1-6, wherein the intermediate carrier is a film made of cellulose Collodion (nitrocellulose), plastic, rubber or latex or silicone rubber is. 9. Verwendung nach 1 - 5, wobei der Zwischenträger cheramisches Material ist.9. Use according to 1-5, wherein the intermediate carrier is ceramic material is. 10. Verwendung nach 1 - 8, wobei der Zwischenträger durch Wasser, ggf. mit Zusätzen, chemischem Lösemittel oder Wasserdampf ablösbaar bzw. auflösbar ist.10. Use according to 1 - 8, wherein the intermediate carrier by water, If necessary, removable or dissolvable with additives, chemical solvents or water vapor is. 11. Verwendung nach 1 - 6, wobei der Zwischenträger so repariert ist, daß er bei Übertragungstemperatur verdampft oder sich nicht verklebbar zersetzt oder verbrennt.11. Use according to 1 - 6, the intermediate carrier being repaired in such a way that that it evaporates at the transfer temperature or does not decompose in such a way that it can be bonded or burns. 12. Verwendung nach 1 - 11, wobei der Zwischenträger oder die Trennschicht durchlässig iiir die Sublimationsfarbe ist.12. Use according to 1-11, wherein the intermediate carrier or the separating layer is permeable to the sublimation color. 13. Verwendung nach 12, wonach beiderseits der Farbe sich eine Zwischensohicht befindet.13. Use after 12, after which there is an intermediate layer on both sides of the color is located. 14. Verwendung nach 1 - 12, wonach die Farbe zwischen Basisträger und Zwischenträger liegt.14. Use after 1 - 12, after which the color between the base carrier and intermediate carrier lies. 15. Verwendung nach 6, wobei Teile der Trennschicht nach dem Ablösen auf dem Zwischenträger verbleiben.15. Use according to 6, wherein parts of the release layer after detachment remain on the intermediate carrier. 16. Verwendung nach 4, wobei ein ansich zur Verbindung mit dem Substrat unter Wärme geeigneter Zwischenträger durch eine Trennschicht, z. B. Silicon, Metall, an der Verbindung behindert ist.16. Use according to 4, wherein a self for connection to the substrate with heat suitable intermediate carrier through a separating layer, e.g. B. silicone, metal, is hindered in the connection. 17. Verwendung nach 1 - 16, wobei der Zwischenträger zur Herstellung eines einwandfreien Kontaktes mit dem Substrat einen Haftmittelauftrag besitzt, der unter Übertragungsbedingungen nicht bläht.17. Use according to 1-16, wherein the intermediate carrier for production a perfect contact with the substrate has an adhesive application, which does not expand under transfer conditions. 18. Verwendung nach 1 - 17, wonach der Zwischenträger während oder nach dem Übertragungsvorgang abgewaschen, abgesaugt oder abgezogen wird.18. Use according to 1 - 17, after which the intermediate carrier during or is washed off, vacuumed or peeled off after the transfer process. 19. Verwendung nach 1 - 18, wobei die terme in zeitlichen Stufen mit Zwischenkühlung zugeführt wird.19. Use after 1 - 18, with the terms in time steps with Intermediate cooling is supplied. 20. Verwendung nach 1 - 19 ,- wobei das Substrat vorgewärmt ist und damit die Ver£ormung des Zwischenträgers auc das Sublimienen begünstigt.20. Use according to 1-19, - wherein the substrate is preheated and so that the deformation of the intermediate carrier also favors sublimation. 21. Verwendung nach 1 - 20, wobei der Basisträger aus einem stark saugfähigen Papier besteht, das Wasser oder Lösemittel aufnehmen kann.21. Use according to 1 - 20, wherein the base support consists of a strong absorbent paper that can absorb water or solvents. 22. Verwendung nach 1 - 21, wobei der Basisträger eine Metallfolie, z. B. aus Aluminium ist.22. Use according to 1 - 21, wherein the base support is a metal foil, z. B. is made of aluminum. 23. Verwendung nach 1 - 27, wobei der Zwischenträger eine durch feinste Punkte oder linienförmig durchbrochene Filmfläche ist.23. Use according to 1 - 27, wherein the intermediate carrier is a through finest Is points or linearly perforated film surface. 24. Verwendung nach 1 - 23, wobei die Trennschicht auf dem Basisträger eine für gleiches Lösemittel höhere oder bez. des Lösemittels unterschiedliche Löslichkeit als die Trennschicht auf dem Zwischenträger hat.24. Use according to 1 - 23, wherein the separating layer on the base support a higher solubility for the same solvent or a different solubility in relation to the solvent than the separating layer on the intermediate carrier. 25. Verwendung nach 1 - 24, wobei die Zwischenträgerschicht in bekannter Weise, z. B. durch Licht und/oder Wärme, aushärtet und durch Chemikalienlösungen auflösbar bleibt.25. Use according to 1-24, the intermediate carrier layer in known Way, e.g. B. by light and / or heat, cures and by chemical solutions remains resolvable. 26. Composit aus einem sublimierbaren Farbdruck auf einem flexiblen Zwischenträger, der ablösbar auf einem Basisträger angebracht ist, welcher dem Zwischenträger die für einen Druckvorgang nötige Stabilität gibt.26. Composite of a sublimable color print on a flexible one Intermediate carrier which is detachably attached to a base carrier, which is the intermediate carrier gives the stability necessary for a printing process. 27. Composit nach 26, das eine Trennschicht zwischen Basisträger und Zwischenträger besitzt.27. Composite according to 26, which is a separating layer between the base support and Has intermediate carrier. 28. Composit nach 26 und 27, das eine mit der bestimmten Kunststoffoberfläche bei Sublimations-Temperatur der Farbe nicht verklebbare Zwischenschicht besitzt.28. Composite according to 26 and 27, the one with the specific plastic surface Has an intermediate layer that cannot be glued at the dye's sublimation temperature. 29. Composit nach 26 und 27, das mindestens auf einer Seite des Zwischenträgers eine Trennschicht besitzt die mit Sublimationstemperatur der Farbe eine Verkleibung mit der bestimmten Kunststoffoberfläche verhindert.29. Composite according to 26 and 27, the at least one side of the intermediate carrier a separating layer has a bonding with the sublimation temperature of the color with the specific plastic surface prevented. 30. Composit aus einer sublimierbaren Farbstoff enthaltenden, elastischen Filmschicht, auf welche eine das Sublimieren und das Verkleben mit dem Substrat verhindernde Trennschicht aufgedruckt ist, wobei ggf. für den Druckvorgang eine ablösbare Basisschicht vorhanden ist.30. Composite of a sublimable dye containing, elastic Film layer on which one sublimates and glues with the substrate preventing separating layer is printed, where appropriate for the printing process a removable base layer is present.
DE19823229288 1982-08-05 1982-08-05 Application of a composite and composite for the decoration of surfaces Granted DE3229288A1 (en)