DE2904747A1 - Imitation wood furniture parts etc. - by casting polyurethane foam into a mould lined with a pigmented reversal coating - Google Patents

Imitation wood furniture parts etc. - by casting polyurethane foam into a mould lined with a pigmented reversal coating

Info

Publication number
DE2904747A1
DE2904747A1 DE19792904747 DE2904747A DE2904747A1 DE 2904747 A1 DE2904747 A1 DE 2904747A1 DE 19792904747 DE19792904747 DE 19792904747 DE 2904747 A DE2904747 A DE 2904747A DE 2904747 A1 DE2904747 A1 DE 2904747A1
Authority
DE
Germany
Prior art keywords
furniture
parts
mold
wood
organic polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19792904747
Other languages
German (de)
Inventor
Geb Freitag Marianne Lohoff
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19792904747 priority Critical patent/DE2904747A1/en
Publication of DE2904747A1 publication Critical patent/DE2904747A1/en
Withdrawn legal-status Critical Current

Abstract

Imitation wood parts for furniture and panelling are made by casting a polyurethane foam compsn. into a mould lined with a thin layer of a reversal coating and allowing the moulding to cure. Mould lining is such that on removal from the mould, the moulding has an integral surface layer having the colour and structure of wood. Mould is e.g. of metal, or a silicone rubber casting made from a piece of wood. Reversal coating is comprised e.g. of colour pigments, an organic polymer or precursor (esp. with active H atoms to react with the hardening polyurethane) and an organic solvent. Process allows excellent imitations of natural wood parts to be made. In contrast to previous processes in which a sepn. wax was applied to moulds before making the moulding, no sepn. wax is used in the present process, so that this does not have to be removed before further processing of the parts (e.g. by lacquering). Imitation wood parts are esp. useful for interior fittings in caravans.

Description

"Verfahren zur Herstellung von holzimitierenden"Process for the production of imitating wood

Möbel- und Verkleidungsteilen" Die Erfindung bezieht sich auf ein Verfahren zur Herstellung von holzimitierenden Möbel- und Verkleidungsteilen aus Polyurethanschaumstoff, insbesondere für Wohnwagen, bei dem eine Form mit dem Ausgangsmaterial gefüllt wird und nach einer geeigneten Aushärtezeit die Teile ausgeformt werden, und auf nach dem Verfahren hergestellte Möbel- und Verkleidungsteile.Furniture and cladding parts " The invention relates focuses on a process for the production of furniture and cladding parts that imitate wood Made of polyurethane foam, especially for caravans, in which a shape with the Starting material is filled and, after a suitable curing time, the parts are molded and on furniture and paneling parts produced by the process.

Es ist bekannt, holzimitierende Möbel- und Verkleidungsteile aus Polyurethanschaumstoff nach dem eingangs genannten Verfahren herzustellen. Dieses Verfahren weist jedoch einige Nachteile auf. So ist es einmal sehr aufwendig dadurch, daß die Form vor dem Befüllen mit einem Trennwachs beschichtet werden muß und daß dieses Trennwachs vor einer Weiterbehandlung der Teile entfernt werden muß. Nachteilig sind die Polyurethanschaumteile empfindlich gegenüber W-Strahlung. Weiterhin ist es erforderlich, die Teile mit einer pigmentierten Grundierung zu versehen, bevor man sie beizen und lackieren kann. Ferner war bisher wegen der relativ grobkörnigen Oberfläche von Polyurethanteilen eine Nachbildung feinster Strukturen, z.B. von Holzoberflächen, nicht möglich.It is known, wood-imitating furniture and paneling parts made of polyurethane foam to produce according to the method mentioned at the beginning. However, this procedure points some disadvantages. So it is once very complex in that the shape is in front the filling must be coated with a release wax and that this release wax must be removed before further treatment of the parts. The polyurethane foam parts are disadvantageous sensitive to UV radiation. It is also necessary to use the parts a pigmented primer before they are stained and varnished can. Furthermore, it was previously because of the relatively coarse-grained surface of polyurethane parts A reproduction of the finest structures, e.g. of wooden surfaces, is not possible.

Dadurch, daß sowohl die Poren als auch die Leimfugen von zusammengesetzten Holzteilen nicht nachgebildet werden konnten, konnten die bisher hergestellten Teile ihren Kunststoffcharakter nicht verbergen und die Imitation von Holzteilen gelang nur in wenig zufriedenstellender Weise.Because both the pores and the glue joints from composite wooden parts could not be reproduced, so far could manufactured parts do not hide their plastic character and imitation of wooden parts was only unsatisfactory.

Es ist Aufgabe der Erfindung, diese Nachteile des Standes der Technik zu vermeiden und ein Verfahren zu schaffen, daß die Nachbildung von Holzoberflächen in vollkommener Weise ermöglicht. Das Verfahren soll insbesondere dadurch, daß die Verwendung eines Trennwachses, die Entfernung desselben und die Aufbringung einer Grundierung entfallen, die Herstellung der genannten Teile wesentlich vereinfachen und wirtschaftlicher machen. Dabei sollen die Teile besonders stabil sein und den Einsatz insbesondere in Wohnwagen, in denen sie starken Erschütterungen ausgesetzt sind, gestatten. Durch das Verfahren soll auch eine erhöhte UV-Beständigkeit der Möbel- und Verkleidungsteile erzielt werden.It is the object of the invention to address these disadvantages of the prior art to avoid and create a process that replicates wooden surfaces made possible in a perfect way. The method is intended in particular that the Using a release wax, removing it and applying a There is no need for a primer, which significantly simplifies the manufacture of the parts mentioned and make it more economical. The parts should be particularly stable and the Use in particular in caravans where they are exposed to strong vibrations are, allow. The method is also intended to increase the UV resistance of the Furniture and cladding parts can be achieved.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß die Form vor dem Befüllen mit einer dünnen Schicht eines Umkehr-coatings beschichtet wird, derart, daß die Möbel- und Verkleidungsteile nach dem Ausformen eine holzgetönte und wie Holz strukturierte Beschichtung der sich ausbildenden, durchgehenden integralen Teiloberfläche aufweisen.This object is achieved according to the invention in that the form is in front of the filling is coated with a thin layer of a reverse coating, in such a way that that the furniture and cladding parts after molding a wood-tinted one and like wood structured coating of the developing, continuous integral Have partial surface.

Das Umkehr-coating besteht vorteilhaft aus Farbpigmenten, einem organischen Polymer oder einem Ausgangsstoff für ein solches und einem Lösungsmittel.The reverse coating advantageously consists of color pigments, an organic one Polymer or a starting material for such and a solvent.

Eine besonders feste Verbindung zwischen der Beschichtung und dem Polyurethanschaumstoff wird dadurch erreicht, daß das organische Polymer oder der Ausgangsstoff für ein solches mit dem aushärtenden Polyurethan reagiert.A particularly strong connection between the coating and the Polyurethane foam is achieved in that the organic polymer or the The starting material for such reacts with the hardening polyurethane.

Um mit der Isocyanat-Komponente der Polyurethan-Ausgangsmischung reagieren zu können, enthält das organische Polymer oder der Ausgangsstoff für ein solches vorteilhaft aktive H-Atome.To react with the isocyanate component of the polyurethane starting mixture to be able to contain the organic polymer or the starting material for such advantageously active H atoms.

Das organische Polymer oder der Ausgangsstoff für ein solches kann Hydroxyl--, Amino- oder Carbonsäure-Gruppen enthalten.The organic polymer or the starting material for such can Contain hydroxyl, amino or carboxylic acid groups.

Um mit der Hydroxyl-Komponente des Polyurethan-Ausgangsgemisches reagieren zu können, enthält das organische Polymer oder der Ausgangsstoff für ein solches vorteilhaft Isocyanat-Gruppen.To react with the hydroxyl component of the starting polyurethane mixture to be able to contain the organic Polymer or the starting material for such advantageous isocyanate groups.

Die Farbpigmente werden vorteilhaft in die Beschichtung eingelagert. Sie können auch durch das organische Polymer oder den Ausgangsstoff für ein solches chemisch gebunden werden.The color pigments are advantageously incorporated into the coating. You can also use the organic polymer or the starting material for one are chemically bound.

Die Beschichtung der Form erfolgt vorteilhaft r:tit einer Schichtdicke von 20 - 30 p.The form is advantageously coated with one layer thickness from 20 - 30 p.

Um ein besonders gefälliges Aussehen zu erzielen, können die Möbel- und Verkleidungsteile nach dem Ausformen gebeizt und lackiert werden.In order to achieve a particularly pleasing appearance, the furniture and trim parts are stained and painted after they have been molded.

Zur Vereinfachung der Herstellung können Scharniere und andere Befestigungselemente vor dem Befüllen der Form in diese eingelegt werden und von dem aushärtenden Polyurethanschaum teilweise umschlossen werden.To simplify manufacture, hinges and other fasteners can be used Before the mold is filled, the mold is placed in it and the hardening polyurethane foam be partially enclosed.

Um das Eindrehen von Schrauben zu vereinfachen und den eingedrehten Schrauben durch eine verdichtete Oberflächenschicht einen besonders festen Halt zu geben, werden vorteilhaft durch in der Form angeordnete Kerne Vertiefungen in den Möbel- und Verkleidungsteilen erzeugt. Zu demselben Zweck könnten vor dem Befüllen der Form Holzdübel in diese eingelegt werden, in die Befestigungsschrauben eingedreht werden können.To simplify the screwing in of screws and the screwed in Screws have a particularly firm hold thanks to a compacted surface layer to give are advantageous through cores arranged in the mold, indentations in the furniture and cladding parts generated. For the same purpose wooden dowels could be inserted into the fastening screws before the mold is filled can be screwed in.

Eine hohe Standzeit der Form wird dadurch erreicht, daß die Form aus Metall besteht.A long service life of the form is achieved by the fact that the form Made of metal.

Die nach dem erfindungsgemäßen Verfahren hergestellten Möbel- und Verkleidungsteile sind durch eine verdichtete, mit Pigmenten versehene und Holzstruktur aufweisende Oberflächenschicht gekennzeichnet.The furniture and manufactured by the process of the invention Cladding parts are made of a compacted, pigmented and wood structure having surface layer marked.

Die Oberflächenschicht kann aus einem anderen Polymer als Polyurethan bestehen.The surface layer can be made from a polymer other than polyurethane exist.

In einer vorteilhaften Ausgestaltung weisen die Möbel-und Verkleidungsteile eine Beiz- und Lackschicht auf der verdichteten Oberflächenschicht auf.In an advantageous embodiment, the furniture and cladding parts a stain and varnish layer on the compacted surface layer.

Es hat sich für den Fachmann überraschend gezeigt, daß durch den Einsatz des Umkehr-coatings in Verbindung mit einer von einem Original-Holzgegenstand abgenommenen Silikon-Kautschukform einerseits die Herstellung von holzimitierenden Möbel. und Verkleidungsteilen wesentlich vereinfacht und damit wirtschaftlicher gemacht wird, weil die Verwendung eines Trennwachses, die Entfernung desselben und die Aufbringung einer Grundierung entfallen, und daß andererseits eine Güte der Nachbildung von Holzoberflächen erzielt wird, die bisher nicht erreichbar war. Dadurch, daß selbst feinste Poren der Holzoberfläche und Leimfugen von zusammengesetzten Holzgegenständen nachgebildet werden, weisen die nach dem erfindungsgemäßen Verfahren hergestellten Teile keinerlei Kunststoffcharakter mehr auf. Ein weiterer Vorteil liegt darin, daß die Oberfläche der Gegenstände besonders hart ist und eine zuverlässige Funktion auch unter erschwerten Bedingungen, z.B. in Wohnwagen, ergibt. Ein weiterer Vorteil liegt in der hohen UV-Beständigkeit der Teile.It has been shown, surprisingly, for the person skilled in the art that through the use the reverse coating in conjunction with one removed from an original wooden article Silicone rubber mold on the one hand the production of wood-imitating furniture. and Fairing is essential simplified and therefore more economical is made because the use of a release wax, the removal of the same and the application of a primer is omitted, and that on the other hand a quality of Replication of wooden surfaces is achieved, which was previously unattainable. Through this, that even the finest pores of the wood surface and glue joints of composite Wooden objects are reproduced, have the method according to the invention manufactured parts no longer have any plastic character. Another advantage lies in the fact that the surface of the objects is particularly hard and reliable Function even under difficult conditions, e.g. in caravans. Another The advantage is the high UV resistance of the parts.

Im folgenden wird die Erfindung anhand eines Ausführungsbeispiels näher erläutert.In the following the invention is based on an exemplary embodiment explained in more detail.

Beispiel: Ein aus Silikon-Kautschuk mit einer Shore-Härte von etwa 60 bestehender, von einem Original-Holzgegenstand abgenommener Abguß wird als Form in einen Rahmen gelegt. Die Form und der zugehörige Deckel werden mittels eines Drucksprühgerätes mit einem aus Farbpigmenten, einem organischen Polymer und einem Lösungsmittel bestehenden Umkehr-coating in einer Schichtdicke von 20 bis 30 ij beschichtet. Nach dem Verdampfen des Lösungsmittels wird die Form geschlossen und in bekannter Weise mittels eines Zwei-Komponenten-Dosiersystems mit den Ausgangsstoffen des Polyurethanschaums gefüllt. Bei einer Temperatur der Form von etwa 400 C kann der Schaumstoffkörper nach etwa 5 Minuten entformt werden. Er wird anschließend gebeizt und lackiert und weist dann eine Oberfläche auf, die von der eines Holzgegenstandes praktisch nicht mehr zu unterscheiden ist.Example: One made of silicone rubber with a Shore hardness of approx 60 existing cast, taken from an original wooden object, is used as a form placed in a frame. The shape and the associated lid are made by means of a Pressure sprayer with one of color pigments, an organic one Polymer and a solvent consisting of reverse coating in one layer thickness coated from 20 to 30 ij. After evaporation of the solvent, the shape closed and in a known manner by means of a two-component metering system filled with the raw materials of the polyurethane foam. At a temperature of The foam body can be removed from the mold after about 5 minutes at a temperature of about 400 ° C. It is then stained and varnished and then has a surface that is practically indistinguishable from that of a wooden object.

Selbstverständlich können durch geeignete Auswahl der Original-Holzvorlage und der Pigmentierung alle Holzarten nachgebildet werden.Of course, you can choose the original wooden template and the pigmentation of all types of wood can be reproduced.

Aufgrund der vereinfachten Herstellung und der bisher nicht erreichbaren Qualität der holzimitierenden M öbel-und Verkleidungsteile aus Polyurethanschaum kann on einer hervorragenden Lösung der anstehenden Probleme gesprochen werden; In der Figur ist teilweise geschnitten ein erfindungsgemäßes Möbelteil in Form ener Leiste dargestellt. Die Schnittfläche zeigt den Kern 1 aus Polyurethanschaum und die mit Pigmenten versehene, verdichtete Oberflächenschicht 4. Die Seiten 2 und 3 weisen Holzstruktur auf.Due to the simplified production and the previously unattainable Quality of the wood-imitating furniture and cladding parts made of polyurethane foam one can speak of an excellent solution to the problems at hand; In the figure is a partially sectioned furniture part according to the invention in the form of ener Bar shown. The cut surface shows the core 1 made of polyurethane foam and the pigmented, compacted surface layer 4. Pages 2 and 3 have a wood structure.

LeerseiteBlank page

Claims (18)

Patentansprüche: 1J Verfahren zur Herstellung von holzimitierenden Möbel- und Verkleidungsteilen aus Polyurethanschaumstoff, insbesondere für Wohnwagen, bei dem eine Form mit dem Ausgangsmaterial gefüllt wird und nach einer geeigneten Aushärtezeit die Teile ausgeformt werden, dadurch gekennzeichnet, daß die Form vor dem Befüllen mit einer dünnen Schicht eines Umkehr-coatings beschichtet wird, derart, daß die Möbel- und Verkleidungsteile nach dem Ausformen eine holzgetönte und wie Holz strukturierte Beschichtung der sich ausbildenden, durchgehenden integralen Teiloberfläche aufweisen.Claims: 1J process for the production of wood-imitating Furniture and cladding parts made of polyurethane foam, especially for caravans, in which a mold is filled with the starting material and after a suitable one Curing time the parts are molded, characterized in that the shape is before the filling is coated with a thin layer of a reverse coating, in such a way that that the furniture and cladding parts after molding a wood-tinted and how Wood structured coating of the developing, continuous integral Have partial surface. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß ein Original-Holzgegenstand mit Silikonkautschuk umgossen wird und dieser Abguß als Form verwendet wird.2. The method according to claim 1, characterized in that an original wooden object is encased with silicone rubber and this cast is used as a mold. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das Umkehr-coating aus Farbpigmenten, einem organischen Polymer oder einem Ausgangsstoff für ein solches und einem Lösungsmittel besteht.3. The method according to claim 1 or 2, characterized in that the Reverse coating from color pigments, an organic polymer or a raw material for such and a solvent. 4. Verfahren nach Anspruch 3, dadurch gekennzeichnet, daß das organische Polymer oder der Ausgangsstoff für ein solches mit dem aushärtenden Polyurethan reagiert.4. The method according to claim 3, characterized in that the organic Polymer or the starting material for one with the hardening polyurethane reacted. 5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, daß das organische Polymer oder der Ausgangsstoff für ein solches aktive H-Atome enthält.5. The method according to claim 4, characterized in that the organic Polymer or the starting material for such an active H-atom. 6. Verfahren nach Anspruch 5, dadurch gekennzeichnet, daß das organische Polymer oder der Ausgangsstoff für ein solches Hydroxyl-, Amino- oder Carbonsäure-Gruppen enthält.6. The method according to claim 5, characterized in that the organic Polymer or the starting material for such a hydroxyl, amino or carboxylic acid group contains. 7. Verfahren nach Anspruch 4, dadurch gekennzeichnet, daß das organische Polymer oder der AUsgangsstoff für ein solches Isocyanatgruppen enthält.7. The method according to claim 4, characterized in that the organic Polymer or the starting material for such isocyanate groups. 8. Verfahren nach Anspruch 1 bis 7, dadurch gekennzeichnet, daß die Farbpigmente in die Beschichtung eingelagert werden.8. The method according to claim 1 to 7, characterized in that the Color pigments are incorporated into the coating. 9. Verfahren nach Anspruch 1 bis 8, dadurch gekennzeichnet, daß die Farbpigmente durch das organische Polymer oder den Ausgangsstoff für ein solches chemisch gebunden werden. 9. The method according to claim 1 to 8, characterized in that the Color pigments through the organic polymer or the starting material for such are chemically bound. 10. Verfahren nach Anspruch 1 bis 9, dadurch gekennzeichnet, daß die Beschichtung der Form mit einer Schichtdicke von 20 - 30 t erfolgt.10. The method according to claim 1 to 9, characterized in that the The mold is coated with a layer thickness of 20-30 t. 11. Verfahren nach Anspruch 1 bis 10, dadurch gekennzeichnet, daß die Möbel- und Verkleidungsteile nach dem Ausformen gebeizt und lackiert werden.11. The method according to claim 1 to 10, characterized in that the furniture and cladding parts are stained and varnished after they have been molded. 12. Verfahren nach Anspruch 1 bis 11, dadurch gekennzeichnet, daß Scharniere und andere Befestigungselemente vor dem Befüllen der Form in diese eingelegt werden und von dem aushärtenden- Polyurethanschaum teilweise umschlossen werden.12. The method according to claim 1 to 11, characterized in that Hinges and other fastening elements are inserted into the mold before it is filled and are partially enclosed by the hardening polyurethane foam. 13. Verfahren nach Anspruch 1 bis 11, dadurch gekennzeichnet, daß durch in der Form angeordnete Kerne Vertiefungen in den Möbel- und Verkleidungsteilen erzeugt werden, die das Eindrehen von Schrauben vereinfachen und den eingedrehten Schrauben einen besonders festen Halt geben.13. The method according to claim 1 to 11, characterized in that through cores arranged in the mold, indentations in the furniture and paneling parts which simplify the screwing in of screws and the screwed in Give screws a particularly firm hold. 14. Verfahren nach Anspruch 1 bis 11, dadurch gekennzeichnet, daß vor dem Befüllen der Form Holzdübel in diese eingelegt werden, die das Eindrehen. von Schrauben vereinfachen und den eingedrehten Schrauben einen besonders festen Halt geben.14. The method according to claim 1 to 11, characterized in that before the mold is filled, wooden dowels are inserted into the mold to allow it to be screwed in. of screws and the screwed-in screws a particularly strong one Give hold. 15. Verfahren nach Anspruch 1 und 3 bis 14, dadurch gekennzeichnet, daß die Form aus Metall besteht.15. The method according to claim 1 and 3 to 14, characterized in that that the mold is made of metal. 16. Möb.el- und Verkleidungsteile aus Polyurethanschaumstoff insbesondere für Wohnwagen, gekennzeichnet durch eine verdichtete, mit Pigmenten versehene und Holzstruktur aufweisende Oberflächenschicht.16. Furniture and cladding parts made of polyurethane foam in particular for caravans, characterized by a compacted, pigmented and Surface layer with wood structure. 17. Möbel- und Verkleidungsteile nach Anspruch 16, dadurch gekennzeichnet, daß die Oberflächenschicht aus einem anderen Polymer als Polyurethan besteht.17. Furniture and trim parts according to claim 16, characterized in that that the surface layer consists of a polymer other than polyurethane. 18. Möbel- und Verkleidungsteile nach Anspruch 16 oder 17, gekennzeichnet durch eine Beiz- und Lackschicht auf der verdichteten Oberflächenschicht.18. Furniture and trim parts according to claim 16 or 17, characterized through a stain and varnish layer on the compacted surface layer.
DE19792904747 1979-02-08 1979-02-08 Imitation wood furniture parts etc. - by casting polyurethane foam into a mould lined with a pigmented reversal coating Withdrawn DE2904747A1 (en)