DE2744905A1 - Armour plate capable of resisting piercing projectiles - is weldable steel plate covered with carbide forming alloy deposit - Google Patents

Armour plate capable of resisting piercing projectiles - is weldable steel plate covered with carbide forming alloy deposit

Info

Publication number
DE2744905A1
DE2744905A1 DE19772744905 DE2744905A DE2744905A1 DE 2744905 A1 DE2744905 A1 DE 2744905A1 DE 19772744905 DE19772744905 DE 19772744905 DE 2744905 A DE2744905 A DE 2744905A DE 2744905 A1 DE2744905 A1 DE 2744905A1
Authority
DE
Germany
Prior art keywords
armor plate
plate according
application layer
bulletproof
application
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19772744905
Other languages
German (de)
Inventor
Richard Nagel
Hans Dr Ing Wahl
Wolfgang Dr Ing Wahl
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wahl Verschleiss Tech
Original Assignee
Wahl Verschleiss Tech
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wahl Verschleiss Tech filed Critical Wahl Verschleiss Tech
Priority to DE19772744905 priority Critical patent/DE2744905A1/en
Priority to FR7826680A priority patent/FR2405455A1/en
Priority to GB7838704A priority patent/GB2007256A/en
Priority to IT28534/78A priority patent/IT1159924B/en
Publication of DE2744905A1 publication Critical patent/DE2744905A1/en
Withdrawn legal-status Critical Current

Abstract

The projectile resistant armour plate has low weight, and is used in armoured fighting vehicle, aircraft and assault boats. On a thick, tough plate is deposited a layer of higher hardness. The plate is made from weldable rolled steel. The hard deposit consists of a carbide forming steel alloy. The latter can contain 3-5%C and 20-35% Cr, balance Fe. This steel alloy may contain also W, Nb and Mo.

Description

Beschußfeste Panzerplatte Bulletproof armor plate

und Verfahren zu ihrer Herstellung Beschußfeste Panzerplatten werden in erster Linie für den Schutz militärischer Einrichtungen benötigt. Als bevorzugte Anwendungsgebiete sind zum Beispiel zu nennen: Schützenpanzer, Flugzeugpanzerungen, Geschützschutzschilde und Landungsbcote. and processes for their manufacture are bulletproof armor plates primarily needed for the protection of military facilities. As preferred Areas of application are, for example: armored personnel carriers, aircraft armor, Gun shields and landing boats.

Aber auch für andere militärische Einrichtungen werden Panzerplatteu der hier in Rede stehenden Art benötigt.But Panzerplatteu of the type in question here.

Es ist bekannt, Panzerplatten für die genannten Zwecke aus hochwertigen Panzerstahllegierungen herzustellen.It is known that armor plates are made of high quality for the purposes mentioned Manufacture armor steel alloys.

Hiermit ist ein hoher technischer Aufwand verbunden, der naturgemäß entsprechend hohe Unkosten nach sich zieht.This is associated with a high level of technical effort, which of course entails correspondingly high costs.

Außerdem müssen die bekannten Stahlplatten, um die erwünschte Beschußfestigkeit zu gewährleisten, sehr dick dimensioniert sein, was wiederum zu E.cstensteigerungen und darüber hinaus zu einer nachteiligen Gewichtserhöhung der gepanzerten Einrichtung, zum Beispiel eines Fahrzeuges, führt.In addition, the known steel plates must have the desired bullet resistance to ensure that it is dimensioned very thick, which in turn leads to increases in costs and, moreover, to a disadvantageous increase in the weight of the armored equipment, for example a vehicle.

Aufgabe der vorliegenden Erfindung ist es, eine Panzerpiatte zu schaffen, die sich durch ein verhältnismäßig geringes Gewicht bei zugleich hoher Besenuß;estigkeit auszeichnet.The object of the present invention is to create an armor plate, which is characterized by a relatively low weight with high broom-resistance at the same time excels.

Nach dem Grundgedanken der Erfindung ist eine Panzerplatte, die die gestellte Aufgabe löst, gekennzeichnet durch mindestens eine zähfeste dickere Grundplatte und mindestens eine darübergelegete Auftragschicht größerer Härte. Die Grundplatte besteht hierbei zweckmäßig aus einem schweißbaren Walzstahl, während die Auftragschicht aus einem karbidbildengen Werkstoff mit einer Makrohärte Uber 550 Vickerseinheiten, vorzugsweise über 600 Vickerseinheiten, besteht.According to the basic idea of the invention is an armor plate that the Problem solves, characterized by at least one tough, thick base plate and at least one overlaid application layer of greater hardness. The base plate consists here expediently of a weldable rolled steel, while the application layer made of a carbide-forming material with a macro hardness of over 550 Vickers units, preferably over 600 Vickers units.

Bei der erfindungsgemäßen Panzerplatte wird die Beschußfestigkeit im wesentlichen durch die harte Auftragschicht gewährleistet, wohingegen die Grundplatte nur als Tragelement für die Auftragschicht dient. Für die Grundplatte ist keinerlei hochwertiges Legierungsmaterial erforderlich, was erheblich zu einer Kostensenkung bei der gesamten Panzerplatte beiträgt.In the armor plate according to the invention, the bullet resistance essentially guaranteed by the hard application layer, whereas the base plate serves only as a support element for the application layer. There is nothing for the base plate high quality alloy material is required, which greatly reduces costs contributes to the entire armor plate.

Da schon relativ dünne Aufträge aus hartem Material eine große Wieåerstandskraft gegen Durchschüsse erbringen, kann das Gesamtgewicht der Panzerplatte niedrig gehalten werden. Die Beschußfestigkeit kann im übrigen nahezu beliebig dadurch erhöht werden, daß auf der, Grundplatte mehrere Auftragschichten, die gegebenenfalls 7erschiedene Härten besitzen können, aufgebracht sind.Since relatively thin applications made of hard material have a great resilience against bullets, the total weight of the armor plate can be kept low will. The bullet resistance can be increased almost at will by that there are several layers of application on the base plate, which may be different May have hardnesses are applied.

Nach einer anderen Ausführungsform der Erfindung ist es auch möglich, die beschußfeste Panzerplatte aus mehreren lese, mit Zwischenraum übereinandergelegten Einzelplatten zusammenzusetzen, wobei Jede Einzelplatte aus einer zähfesten Grundplatte mit einem darauf befindlichen Auftrag größerer Härte besteht.According to another embodiment of the invention, it is also possible the bulletproof armor plate made of several read, one on top of the other with space in between Assemble individual panels, each individual panel from a tough base plate with an order of greater hardness thereon.

Während die bekannten Panzerplatten aufgrund ihrer Legierungszusammensetzung, die einseitig auf Beschußfestigkeit ausgerichtet ist, wenig für tragende Funktionen geeignet ist, ist es bei der erfindungsgemäßen Panzerplatte ohne weiteres möglich, durch entsprechende Auswahl des Werkstoffes der Grundp'atte und geeignete Dimensionierang derselben zu erreichen, daß die gesamte Panzerplatte selbsttragend ist. Hierdurch können die sonst erforderlichen Tragkonstruktionen eingespart werden, was zu einer erheblichen Gewichtsverminderung der gesamten zu panzernden Einrichtung vorteilhaft beiträgt.While the well-known armor plates due to their alloy composition, which is unilaterally geared towards bullet resistance, little for load-bearing functions is suitable, it is easily possible with the armor plate according to the invention, by appropriate selection of the material of the base plate and suitable dimensions the same to achieve that the entire armor plate is self-supporting. Through this the otherwise necessary supporting structures can be saved, resulting in a considerable weight reduction of the entire equipment to be armored advantageous contributes.

Ein weiterer wesentlicher Vorteil der erfindungsgemäßen Panzerplatte ist darin zu sehen, daß die Beschußfestigkeit derselben in einfacher Weise örtlich variiert werden kann, wobei lediglich die Auftragschicht an den betreffenden Stellen dicker oder dünner zu wählen ist.Another major advantage of the armor plate according to the invention can be seen in the fact that the bullet resistance of the same in a simple manner locally can be varied, with only the application layer on the to choose thicker or thinner areas.

Nach einem weiteren wesentlichen Merkmal der Erfindung ist ein besonders vorteilhaftes Verfahren zur Herstlelung der erfindungsgemäßen Panzerplatte dadurch gekennzeichnet, daß die Autragschicht bzw -schichten in an sich bekannter Weise durch automatische Auftragschweißung pendelnd aufgebracht wird (werden), wobei die Auftragschweißung - wie ebenfalls an sich bekannt - vorzugsweise mit gefülltem Röhrchendraht erfolgen soll.According to a further essential feature of the invention is a special advantageous method for producing the armor plate according to the invention thereby characterized in that the application layer or layers in a manner known per se is (are) applied in a pendulous manner by automatic build-up welding, whereby the Overlay welding - as is also known per se - preferably with filled tubular wire should take place.

In weiterer Ausgestaltung des vorerwähnten erfindungsgemäßen Verfahrens wird vorgeschlagen, daß in an sich bekannter Weise über der Grundplatte ein unlegierter oder legierter, stromführender Draht in parallelen Bahnen pendelnd und vorwärtsbewegt geführt und daß laufend eine in Abhängigkeit vom Drahtvorschub regulierte Menge pulverförmigen, legierten Schweißzusatzwerkstoffes in den Wirkungsbereich des Lichtbogens eingeführt wird.In a further embodiment of the aforementioned method according to the invention it is proposed that in a known manner over the base plate an unalloyed or alloyed, current-carrying wire oscillating and moving forward in parallel tracks out and that continuously a regulated amount depending on the wire feed powdered, alloyed welding filler material in the area of action of the arc is introduced.

Auf diese Weise ergibt sich vorteilhaft eine Auftragschicht, die aus mehreren nebeneinanderliegenden, zeitlich nacheinander aufgebracnten bandförmigen Aufträgen zusammengesetzt ist.In this way, an application layer is advantageously obtained from several juxtaposed, timed one after the other band-shaped Orders is composed.

Weitere Einzelheiten und Vorteile der Erfindung können den Unternsprüchen sowie - anhand von Ausführungsbeispielen - der Zeichnung und der nachstehenden Zeichnungsbeschreibung entnommen werden. Es zeigt: Fig. 1 eine Ausführungsform einer Panzerplatte nach der Erfindung in Draufsicht (schematisch), Fig. 2 eine Panzerplatte, wie zum Beispiel aus Fig. 1 ersichtlich, im Querschnitt, Fig. 3 eine weitere Ausführungsform einer Panzerplatte nach der Erfindung, ebenfalls im Querschnitt, Fig. 4 eine andere Ausführungsform einer Panzerplatte nach der Erfindung, ebenfalls im Querschnitt, Fig. 5 eine Panzerplatte entsprechend Fig. 2 in montierter Steilen und Fig. 6 ein weiteres Mvntagebeispiel für Panzerplatten nach der Erfindung.Further details and advantages of the invention can be found in the subclaims as well as - on the basis of exemplary embodiments - the drawing and the following description of the drawings can be removed. It shows: FIG. 1 an embodiment of an armor plate according to FIG of the invention in plan view (schematic), Fig. 2 an armor plate, such as can be seen from Fig. 1, in cross section, 3 shows a further embodiment an armor plate according to the invention, also in cross section, Fig. 4 another Embodiment of an armor plate according to the invention, also in cross section, FIG. 5 shows an armor plate corresponding to FIG. 2 in the assembled position and FIG. 6 a Another monthly example for armor plates according to the invention.

Nach den Fig. 1 bis 3, 5 und 6 weist die erfindungsgemäße Panzerplatte jeweils eine einzelne Grundplatte aus einem zähfesten Material, vorzugsweise aus einem schweißbaren Walzstahl, auf, die jeweils mit 10 bezeichnet ist. Auf der Grundplatte 10 und fest verbunden mit dieser befindet sich ein Auftrag aus einem Material großer Härte, das bei den Ausführungsformen nach Fig. 1, 2, 5 und 6 einschichtig ausgebildet und mit li beziffert ist. Wie insbesondere aus Fig. 2, 5 und 6 hervorgeht; besteht das Auftragsmaterial 11 nicht aus einer zusammenhängenden durchgehenden Beschichtung, sondern vielmehr aus einzelnen Bahnen 12, die nebenelnandergeleg sind. Die jeweilige Fugenbreite zwischen zwei benachbarten Auftragsbahnen 12 kann hierbei von Null bis zu einem bestimmten Abstand - je nach Verwendungszweck - variieren.According to FIGS. 1 to 3, 5 and 6, the armor plate according to the invention each a single base plate made of a tough material, preferably made of a weldable rolled steel, each designated by 10. On the baseplate 10 and firmly connected to this is an order made of a material of large size Hardness, which in the embodiments according to FIGS. 1, 2, 5 and 6 is formed in one layer and is numbered with li. As can be seen in particular from FIGS. 2, 5 and 6; consists the application material 11 does not consist of a coherent, continuous coating, but rather from individual tracks 12, which are laid next to each other. The respective Joint width between two adjacent application lines 12 can range from zero to at a certain distance - depending on the intended use - vary.

Die bahnenförmige Aufbringung des harten Auftragsmaterials erfolgt - wie Fig. 1 erkennen läßt - durch automatische Auftragschweißung, wobei Draktzuführungsvorrichtung und Lichtbogen - wie in Fig. 1 durch Schlangenlinien angedeutet - in bekannter Weise eine Pendelbewegung ausführen. Die Amplitude dieser Pendelbewegung entspricht hierbei der Breite einer utragsbahn 12.The hard application material is applied in web form - As shown in FIG. 1 shows - by automatic build-up welding, with a Draktzuführungsvorrichtung and arc - as indicated in Fig. 1 by serpentine lines - in a known manner perform a pendulum motion. The amplitude of this pendulum motion corresponds here the width of a railway track 12.

Der Schweißauftrag großer Härte auf der Grundplatte 10 braucht sich Jedoch keineswegs auf eine einlagige Auftragsschicht beschränken. So ist zum Beispiel in Fig. 3 eine Ausführungsform gezeigt, bei der zwei Ubereinanderliegende harte Auftragschichten iia und lib vorgesehen sind. Die obere Auftragschicht lib ist hierbei so aufgebracht, daß die sich zwischen zwei Puftragsbahnen 12a der unteren buftragschicht ila erstrect;ende Trennfuge 13a jeweils von einer Auftr-agsbahn 12b der oberen Auftragschicht lib überdeckt ist. Hierdurch ist eine optimale Beschußfestigkeit gewährleistet.The welding job of great hardness on the base plate 10 is needed However, by no means limit it to a single layer of application. So is for example in Fig. 3 shows an embodiment in which two superposed hard Application layers iia and lib are provided. The upper coating layer is here lib applied in such a way that the between two application webs 12a of the lower application layer Each parting line 13a extends from an application web 12b of the upper application layer lib is covered. This ensures optimal bullet resistance.

Über der zweiten Auftragschicht lib kann - wie in Fig. 3 gestrichelt angedeutet - noch eine dritte Auftragschicht 11c vorgesehen sein. Diese Sußerste Auftragschicht 11c besteht zweckmäsigerweise aus einem relativ weichen Werkstoff mit einer Makrohärte kleiner 300 Vickers, zum Beispiel Chrom-Nickel-Stahl. Hierdurch wird bereits der Aufprall des Geschosses auf die darunterliegenden harten Auftragsschichten gedämpft. Darüber hinaus wirkt sich die äußerste Auftragschicht 11c in vorteilhafter Weise als Korrosionsschutz aus.Above the second application layer lib can - as in Fig. 3 by dashed lines indicated - a third application layer 11c may also be provided. This cutest thing Application layer 11c expediently consists of a relatively soft material with a macro hardness of less than 300 Vickers, for example chrome-nickel steel. Through this the impact of the bullet on the hard layers underneath is already achieved muffled. In addition, the outermost application layer 11c has a more advantageous effect Point out as corrosion protection.

Eine weitere Ausführungsform einer beschußfesten Panzerplatte nach der Erfindung zeigt Fig. 4. Hier sind zwei übereinanderliegende Grundplatten 10a und 10b vorgesehen, die Jweiis mit einem harten Auftragsmaterial 14a bzw. 14b beschichtet sind. Die beiden jeweils aus Grundplatte und Auftragschicht bestehenden Einzelplatten sind hierbei ohne festen Verbund los aufeinandergelegt. Durch diese Doppelausführung der erfindungsgemäßen Panzerplatte ergibt sich ein besonders guter Dämpfunqseffekt beim Auftreffen der Geschosse.Another embodiment of a bulletproof armor plate according to of the invention is shown in FIG. 4. Here are two base plates 10a lying one above the other and 10b are provided which coats the paper with a hard coating material 14a and 14b, respectively are. The two individual plates, each consisting of a base plate and an application layer are laid loose on top of each other without a fixed connection. Through this double execution the armor plate according to the invention results in a particularly good damping effect when the projectiles hit.

In der Regel wird eine einzelne Panzerplatte der in der Zeichnung gezeigten Art flächermäßig nicht ausreichen, um den zu schützenden Gegenstand, zum Beispiel ein Fahrzeug, ausreichend zu panzern. Es müssen daher mehrere Panzerplatten aneinandergefugt werden.Usually a single armor plate is the one in the drawing The type shown in terms of area is not sufficient to encompass the object to be protected Example a vehicle, adequate armor. It must therefore several armor plates are joined together.

In Fig. 2 ist zum Beispiel eine Möglichkeit gezeigt, bei der die einzelnen Panzerplatten im stumpfen Stoß aneinandergelegt und an der Unterseite der Grundplatte 10 jeweils miteinander verschweißt werden. Die betreffenden Schweißstellen sind in Fi. 2 gestrichelt angedeutet und mit 15 bezeichnet.In Fig. 2, for example, a possibility is shown in which the individual Armor plates placed in butt joint and on the underside of the base plate 10 are each welded together. The welds in question are in Fi. 2 indicated by dashed lines and denoted by 15.

Auf der Oberseite der sich zwischen zwei aneinander angrenzenden Panzerplatten ergebenden Trennfuge 16 ist eine diese überdeckende AuftragschweiRung 17 aufgebracht, um dic Verbindungsstelle zwischen zwei Panzerplatten auch von oben her abzusichern.On top of the between two adjacent armor plates The resulting parting line 16 is covered by build-up welding 17, to secure the junction between two armor plates from above.

Die Auftragschweißungen 17 bestehen zweckmäßigerweise aus dem gleichen harten Auftragsmaterial wie die bahnenförmigen Aufträge 12.The build-up welds 17 expediently consist of the same hard application material such as the web-shaped applications 12.

In Fig. 5 ist eine Möglichkeit verdeutlicht, wie die erfindungsgemäßen Panzerplatten an den zu schützenden Teilen, zum Beispiel den Außenwänden eines Fahrzeuges, befestigt werden können. Zu diesem Zweck weisen die von Auftragsenweißungen freien Ränder der Panzerplatte nach Fig. 5 Durchgangsbohrungen 18 auf, die von Schrauben 19 durchsetzt sind. Das darunterliegende durchgehenae abstützende Tragwerk ist mit 20 bezeichnet.In FIG. 5, one possibility is illustrated, such as the one according to the invention Armor plates on the parts to be protected, for example the outer walls of a vehicle, can be attached. For this purpose, those free from build-up whitening show Edges of the armor plate according to FIG. 5 through holes 18, which are screwed 19 are interspersed. The supporting structure underneath is supported by 20 designated.

Um auch die Verbindungsstelle 18, 19 der Panzerplatte mit dem Tragwerk 20 vor Beschuß zu schützen, ist auch der außenseitige Kopf der Schraube 19 mit einer Auftragschweißung 21 aus hartem Auftragsmaterial versehen. Die bei der Ausführungsform nach Fig., 5 verwendete Panzerplatte braucht nicht selbsttragend zu sein, da die Tragefunktionen von dem darunterliegenden Tragwerk übernommen werden.Around the connection point 18, 19 of the armor plate with the supporting structure 20 to protect against bombardment, the outside head of the screw 19 with a Overlay weld 21 made of hard application material is provided. The one in the embodiment According to Fig., 5 armor plate used does not need to be self-supporting, since the Support functions are taken over by the underlying structure.

Bei der aus Fig. 6 ersichtlichen Ausfuhrungsform werden dagegen selbsttragend ausgebildete Panzerplatten verwendet.In the embodiment shown in FIG. 6, however, they are self-supporting trained armor plates used.

Diese stützen sich nur jeweils an ihren Rändern auf im Querschnitt I-förmig ausgebildeten Trägern 22 ab, die in verhältnismäßig weiten Abständen voneinander angeordnet sind und somit ein gitterartiges Traggerippe bilden. Auch hier kann die Befestigung der Panzerplatten an den Trägern 22 - ähnlich wie bei der Ausführungsform nach Fig. 5 -durch Schrauben erfolgen, die in Fig. 6 durch strichpunktierte Linien 23 angedeutet sind.These are only supported at their edges in cross section I-shaped beams 22 from the in relatively wide Are spaced from each other and thus form a grid-like support structure. Here, too, the attachment of the armor plates to the supports 22 - similar to in the embodiment according to FIG. 5 -done by screws, which in FIG Dashed lines 23 are indicated.

Selbstverständlieh ist es aber auch denkbar, die Befestigung der Panzerplatten auf dem darunterliegenden Tragwerk durch Schweißen oder andersartige Verbindung zu bewerkstelligen.Of course, it is also conceivable to attach the armor plates on the underlying structure by welding or other type of connection to accomplish.

Claims (27)

Ansprüche '1.) Beschußfeste Panzerplatte, gekennzeichnet durch mindestens eine zähfeste, dickere Grundplatte (10,10a,10b) und mindestens eine darübergelegte Auftragschicht (11,11a,11b,14a,14b) größerer Härte. Claims' 1.) Bulletproof armor plate, characterized by at least a tough, thicker base plate (10, 10a, 10b) and at least one overlying it Application layer (11, 11a, 11b, 14a, 14b) of greater hardness. 2. Beschußfeste Panzerplatta nach Anspruch 1, dadurch gekennzeichnet, daß die Grundplatte (10,10a,10b) aus einem schweißbaren Walzstahl besteht. 2. Bulletproof Panzerplatta according to claim 1, characterized in that that the base plate (10,10a, 10b) consists of a weldable rolled steel. 3. Beschußfeste Panzerplatte nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Auftragschicht (11,11a, 11b,14a,14b) aus einem karbidbildenden Werkstoff mit einer Makrohärte über 550 Vickerseinheiten, vorzugsweise über 600 Vickerseinheiten, besteht. 3. Bullet-proof armor plate according to claim 1 or 2, characterized in that that the application layer (11, 11a, 11b, 14a, 14b) is made of a carbide-forming material with a macro hardness of more than 550 Vickers units, preferably more than 600 Vickers units, consists. 4. Beschußfeste Panzerplatte nh Anspruch 3, dadurch gekennzeichnet, daß die Auftragschicht (11,11a, 11b,14a,14b) aus eines Werkstoff mit 3 bis 5 Prozent C, 20 bis 35 Prozent Cr, Rest Eisen, besteht. 4. Bulletproof armor plate nh claim 3, characterized in that that the application layer (11, 11a, 11b, 14a, 14b) made of a material with 3 to 5 percent C, 20 to 35 percent Cr, the balance iron. 5. Beachußfeste Panzerplatte nach Anspruch 3, dadurch gekennzeichnet, daß die Auftragschicht (11,11a 11b,14a,14b) aus einem Werkstoff der Zusammensetzung 4 bis 6 Prozent C 20 bis 30 Prozent Cr 5 bis 8 Prozent Nb auch 5 bis 8 Prozent Mo 1 bis 3 Prozent W Rest Eisen und Begleitstoffe besteht.5. Beachuss-proof armor plate according to claim 3, characterized in that that the application layer (11, 11a, 11b, 14a, 14b) consists of a material of the composition 4 to 6 percent C 20 to 30 percent Cr 5 to 8 percent Nb also 5 to 8 percent Mo 1 to 3 percent W the remainder consists of iron and accompanying substances. 6. Beschußfeste Panzerplatte nach einem oder mehreren der Ansprüche 1 bis 5, dadurch gekennzeiehnet, daß auf der Grundplatte (10) mehrere Auftragschichten (11a,11b,11c) aufgebracht sind (Fig. 3).6. Bulletproof armor plate according to one or more of the claims 1 to 5, characterized in that several application layers on the base plate (10) (11a, 11b, 11c) are applied (Fig. 3). 7. Beschußfeste Panzerplatte nach Anspruch 6, dadurch gekennzeichnet, daß die auf der Grundplatte (10) aufgebrachten verschiedenen Auftragschichten (11a,11b,11c) verschiedene Härte besitzen.7. Bulletproof armor plate according to claim 6, characterized in that that the different application layers (11a, 11b, 11c) applied to the base plate (10) have different hardness. 8. Beschußfeste Panzerplatte nach aspruch 6 oder 7, dadurch gekennzeichnet, daß die äußerste (11e) der verschiedenen Auftragschichten auf einem relativ weichen Werkstoff mit einer Makrohärte kleiner 300 Vickers, z.B. Chrom-Nickel-Stahl, besteht (Fig. 3).8. Bulletproof armor plate according to claim 6 or 7, characterized in that that the outermost (11e) of the various application layers on a relatively soft Material with a macro hardness of less than 300 Vickers, e.g. chrome-nickel steel (Fig. 3). 9. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß dieselbe sich aus mehreren lose, mit Zwischenraum Ubereinandergelegten Einzelplatten zusammensetzt, wobei Jede Einzelplatte aus einer zähfesten Grundplatte (10a,10b) mit einem darauf befindlichen Auftrag (14'a,14b) gröBerer Hrte besteht (Fig. 4).9. Bulletproof armor plate according to one or more of the preceding Claims, characterized in that the same is made up of several loose, with space in between Stacked individual plates composed, each individual plate from one tough base plate (10a, 10b) with an order (14'a, 14b) on it there is greater hardness (Fig. 4). 10. Bescnußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß der äußere Rand derselben nur teilweise mit einer Auftragschicht versehen ist.10. Beef-resistant armor plate according to one or more of the preceding Claims, characterized in that the outer edge of the same only partially is provided with an application layer. 11. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß dieselbe gewölbt ist.11. Bullet-proof armor plate according to one or more of the preceding Claims, characterized in that the same is curved. 12. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß dÄs verhältnis von Grundplattenstärke zu Auftragschichtstärke bei einer Auftragschicht mindestens 3 zu 1, bei zwei Auftragschichten mindestens 3 zu 2 ist.12. Bulletproof armor plate according to one or more of the preceding Claims, characterized in that the ratio of the base plate thickness to Application layer thickness for one application layer at least 3 to 1, with two application layers is at least 3 to 2. 13. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß jede einzelne Auftragschicht eine Stärke von 4 bis 6 mm besitzt.13. Bulletproof armor plate according to one or more of the preceding Claims, characterized in that each individual application layer has a thickness from 4 to 6 mm. 14. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß jede Auftragschicht aus mehreren nebeneinanderliegenden bandförmigen Aufträgen (12,12a,12b) zusammengesetzt ist.14. Bulletproof armor plate according to one or more of the preceding Claims, characterized in that each application layer consists of several juxtaposed band-shaped orders (12,12a, 12b) is composed. 15. Beschußfeste Panzerplatte nach Anspruch 14, dadurch gekennzeichnet, daß bei mehreren ubereinanderliegenden Auftragschichten (11a, lib, 11 c) die Trennfuge (13a) zwischen Je zwei benachbarten AuftragsbSndern (12a) der unteren Auftragschicht (via) von einem Auftragsband (12b) der darüberliegenden Auftragschicht (11b) überdeckt ist (Fig. 3).15. Bulletproof armor plate according to claim 14, characterized in that that with several superimposed application layers (11a, lib, 11c) the parting line (13a) between two adjacent application strips (12a) of the lower application layer (via) covered by an application band (12b) of the overlying application layer (11b) is (Fig. 3). 16. Beschußfeste Panzerplatte nach Anspruch 14 oder 15, dadurch gekennzeichnet, daß bei mehreren übereinanderliegenden Auftragschichten (I1a,iib,11c) die die untere Auftragschicht (11a) bildenden Auftragsbänder (12a) gegenüber den die darüberliegende Auftragschicht (alb) bildenden Auftragsbändern (12b) geneigt angeordnet sind.16. Bullet-proof armor plate according to claim 14 or 15, characterized in that that with several superimposed application layers (I1a, iib, 11c) the lower one Application layer (11a) forming application tapes (12a) compared to the overlying Application tapes (12b) forming the application layer (alb) are arranged at an incline. 17. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß die Auftragschicht bzw.17. Bulletproof armor plate according to one or more of the preceding Claims, characterized in that the application layer or -schichten (1 i,1fl) an Stellen, die einer besonders starken Beschußbeanspruchung ausgesetzt sind, dicker ausgebildet ist (sind) als an anderen Stellen der Panzerplatte. -layers (1 i, 1fl) in places that are exposed to particularly heavy bombardment are exposed, is (are) made thicker than at other points of the armor plate. 18. Beschußfeste Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß das Material für die zähfeste Grundplatte (10) derart ausgewählt und dimensioniert ist, daß die gesamte Panzerplatte selbsttragend ist.18. Bullet-proof armor plate according to one or more of the preceding Claims, characterized in that the material for the tough base plate (10) is selected and dimensioned in such a way that the entire armor plate is self-supporting is. 19. Beschußfeste Panzerolatte nach einem oder mehreren der vorstehenen Ansprüche, dadurch gekennzeichnet, daß dieselbe, vorzugsweise an ihren Rändern, Mittel (18,19,23) zur Befestigung auf einem ac3tützenden Tragwerk (20,22) aufweist (Fig. 5 und 6).19. Bulletproof Panzerolatte according to one or more of the above Claims, characterized in that the same, preferably at its edges, Has means (18,19,23) for fastening on a supporting structure (20,22) (Figures 5 and 6). 20. Beschußfeste Fanzerplatte nach Anspruch 19, dadurch gekennzeichnet, daß dieselbe auf ein abstützendes Tragwerk (20,22) aufschraubbar oder -schweißbar ist.20. Bulletproof fan plate according to claim 19, characterized in that that the same can be screwed or welded onto a supporting structure (20, 22) is. 21. Beschußfeste Panzerplatte nach Anspruch 19 oder 20, dadurch gekennzeichnet, daß die Verbindungsstellen (z.B. Verbindungsschweißstellen 15) zwischen der bzw. den beschußfesten Panzerplatten und dem abstützenden Tragwerk (20,22) durch Auftragschweißung (17,21) mit einem der übrigen harten Auftragschicht (11;14) entsprechenden Werkstoff geschützt sind.21. Bullet-proof armor plate according to claim 19 or 20, characterized in that that the joints (e.g. joint welds 15) between the the bulletproof armor plates and the supporting structure (20,22) by surfacing (17,21) with a material corresponding to the rest of the hard application layer (11; 14) are protected. 22. Gesamtanordnung unter Verwendung von mehreren einzelnen beschußfesten Panzerplatten nach einem oder mehreren der vorstrhenden Ansprüche, dadurch gekennzeichnet, daß die im Stumpfstoß (16) nebeneinander angeordneten Einzelplatten mäßiger Größe sich auf ein Tragwerk (20,22) abstützen, auf dem sie z.B. durch Schweißen oder Schrauben beestigt sind.22. Overall arrangement using several individual bulletproof Armor plate according to one or more of the preceding claims, characterized in that that the individual plates of moderate size arranged side by side in the butt joint (16) support themselves on a supporting structure (20,22), on which they can e.g. be welded or screwed are attached. 23. Gesamtanordnung unter Verwendung von mehreren einzelnen beschußfesten Panzerplatten nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß de Einzelplatten sicn nur an ihrem Rand auf ein Traggerippe (22) mit Zwischenräumen abstützen.23. Overall arrangement using several individual bulletproof Armor plate according to one or more of the preceding claims, characterized in that that de individual plates sicn only at their edge on a supporting frame (22) with gaps prop up. 24. Verfahren zur Herstellung einer Panzerplatte nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, daß die Auftragschicht bz.24. A method for producing an armor plate according to one or more of the preceding claims, characterized in that the application layer or. -schichten in an sich bekannter Weise durch automatische Auftragschweißung pendelnd aufgebracht wird (werden). layers in a manner known per se by means of automatic build-up welding is (are) applied in a reciprocating manner. 25. Verfahren nach Anspruch 24, dadurch gekennzeichnet, daß die automatische Auftragschwei.25. The method according to claim 24, characterized in that the automatic Cladding ßung in an sich bekannter Weise mit gefülltem Röhrchendraht erfolgt. ßung takes place in a known manner with filled tubular wire. 26. Verfahren nach Anspruch 24 oder 25, dadurch gekennzeichnet, daß in an sich bekannter Weise über der Grundplatte ein unlegierter oder legierter, stromführender Draht in parallelen Bahnen pendelnd und vorwärtsbewegt geführt und daß laufend eine in Abhängigkeit vom Drahtvorschub regulierte Menge pulverförmigen, legierte Schweißzusatzwerkstoffes in den Wirkungsbereich des L chtbogens eingeführt wird.26. The method according to claim 24 or 25, characterized in that in a manner known per se, an unalloyed or alloyed, Live wire pendulating and moving forward in parallel tracks and that an amount of powdery, Alloyed filler metal introduced into the arc's area of action will. 27. Verfahren nach Anspruch 24, 25 oder 26, dadurch gekennzeichnet, daß die Auftragschweißung derart auFgefiíhrt wird, daß nebeneinanderliegende bandförmige Aufträge nacheinander aufgebracht werden.27. The method according to claim 24, 25 or 26, characterized in that that the build-up welding is carried out in such a way that adjacent strips are in the form of strips Orders are applied one after the other.
DE19772744905 1977-10-06 1977-10-06 Armour plate capable of resisting piercing projectiles - is weldable steel plate covered with carbide forming alloy deposit Withdrawn DE2744905A1 (en)