DE1945275B2 - DEVICE FOR DESULFURIZING BIG IRON IN THE SCRAP CHANNEL OF A Blast furnace and its use - Google Patents
DEVICE FOR DESULFURIZING BIG IRON IN THE SCRAP CHANNEL OF A Blast furnace and its useInfo
- Publication number
- DE1945275B2 DE1945275B2 DE19691945275 DE1945275A DE1945275B2 DE 1945275 B2 DE1945275 B2 DE 1945275B2 DE 19691945275 DE19691945275 DE 19691945275 DE 1945275 A DE1945275 A DE 1945275A DE 1945275 B2 DE1945275 B2 DE 1945275B2
- Authority
- DE
- Germany
- Prior art keywords
- container
- pig iron
- blast furnace
- inlet
- outlet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Die Erfindung betrifft eine Vorrichtung zur Ent-Schwefelung von Roheisen unter Zusatz eines Entschwefelungsmittels in der Abstichrinne eines Hochofens mit einem feuerfest ausgekleideten Behälter, der eine Zugabeöffnung für das Entschwefelungsmittel aufweist, sowie einen Einlauf und einen Auslauf, deren untere Innenfläche mit stufenlosen Übergängen in der Höhe der inneren in Auslaufrichtung geneigten Bodenfläche des Behälters liegen, und einen mit der Rinne verbundenen Fuchs mit einer Überlaufkante für das Roheisen, die höher liegt als die obere Innenfläche des Einlaufs.The invention relates to a device for desulfurizing pig iron with the addition of a desulfurizing agent in the tapping channel of a blast furnace with a refractory lined container, which has an inlet opening for the desulfurizing agent, as well as an inlet and an outlet, their lower inner surface with stepless transitions at the level of the inner inclined in the outlet direction Bottom surface of the container lie, and a fox connected to the gutter with an overflow edge for the pig iron, which is higher than the upper inner surface of the inlet.
Man hat bereits im Hochofen durch hochbasische Schlackenführung über 90 % des eingesetzten Schwefels in die Schlacke überführt. Diese Entschwefelung ist zwar kostengünstiger als die Entschwefelung im Stahlwerk und in Gießereien; sie weist aber eine Reihe von Nachteilen auf. Zum einen erhöht sich der spezifische Koksverbrauch, und die ErzeugungsJeistung nimmt ab. Zum anderen werden die über den Möller und den Koks eingebrachten Alkalioxyde nur geringfügig von den basischen Schlacken des Hochofens aufgenommen; sie reichern sich somit im Hochofen an und führen zu einer verstärkten Ansatzbildung und Verschleiß des Mauerwerks, was Störungen des Ofengangs verursacht.Already in the blast furnace you have more than 90% of the sulfur used due to the highly basic slag flow transferred to the slag. This desulfurization is cheaper than desulfurization in the Steel mills and foundries; however, it has a number of disadvantages. For one thing, it increases specific coke consumption and production capacity decreases. On the other hand, the alkali oxides introduced via the Möller and the coke are only negligible absorbed by the basic slag of the blast furnace; they accumulate in the blast furnace and lead to increased build-up and wear of the masonry, which disrupts the Oven gear caused.
Um diese Nachteile zu vermeiden, sind mehrere Verfahren zur Entschwefelung des Roheisens außerhalb des Hochofens in Pfannen entwickelt worden, unter anderem auch ein Rührgerät (deutsches Gebrauchsmuster 1 988 244), das gute Entschwefelungsergebnisse bringt; diese Verfahren sind jedoch zumindest insoweit nachteilig, als bei der Anwendung bei einer Pfanne die Entschwefelung als zusätzliche Verfahrensstufe den Stofffluß stört, den Pfannenumlauf verzögert und zusätzliche Rangier- und Kranarbeiten verursacht; besonders störend ist das nach der Entschwefelungsbehandlung erforderliche Abschlakken der Pfannen; ein sauberes Abschlacken mit geringen F.isenverlusten ist bis heute nicht mit maschinellen Vorrichtungen, sondern nur manuell möglich. Dementsprechend sind die ?fannen-Entscbwefelungsverfahren auch nur in einigen Sonderfällen angewendet worden, z. B. bei der Verhüttung von kieselsäurereichen Eisenerzen, um die spezifische Schlackenmenge auf wirtschaftliche Werte herabzusetzen, sowie bei der Herstellung schwefelarmer Sonderstähle oder zur Absenkung überhöhter Schwefelgehalte bei Störungen des Ofenganges.In order to avoid these disadvantages, several methods for desulfurizing the pig iron are outside of the blast furnace in pans has been developed, including a mixer (German utility model 1 988 244), which brings good desulphurisation results; however, these procedures are at least disadvantageous insofar as the desulfurization as an additional when used in a pan Process stage disturbs the flow of material, delays the ladle circulation and additional maneuvering and crane work caused; The liming required after the desulfurization treatment is particularly disturbing the pans; A clean deslagging with low iron losses is still not possible with a machine Devices, but only possible manually. The fannen desulfurization processes are accordingly has only been used in a few special cases, e.g. B. in the smelting of silica rich Iron ores to reduce the specific amount of slag to economic values, as well as in the production of low-sulfur special steels or for lowering excessive sulfur contents in the event of malfunctions in the oven.
Um eine Entschwefelung des Roheisens ohne Beeinträchtigung des Hochofenganges und ohne Störungen des Stoffflusses zu ermöglichen, ist versucht worden, die Entschwefelung des Roheisens in der Abstichrinne vorzunehmen. Dabei kann die Entschwefelungsschlacke in der Rinne durch einen Fuchs oder einen Siphon zurückgehalten werden, so daß das manuelle Abschlacken entfällt. Bei dieser Verfahrensweise ist jedoch, im Unterschied zu der Entschwefelung in der Pfanne, die Reaktionszeit durch die stark schwankende Roheisenabstichgeschwindigkeit des Hochofens vorgegeben. Zur Abschwächung dieses Einflusses hat man die Entschwefelung au.c einer längeren Wegstrecke der Abstichrinne durchgeführt (Stahl und Eisen, 1969, S. 776 bis 780). Die USA.-Patentschrift 1 590 730 beschreibt ein Verfahren zur Entschwefelung von in einem Kupolofen oder üblichem Schmelzofen erschmolzenen Roheisen. Die dabei anfallenden zeitlich geringen Mengen Gußeisen mögen mit der im Gegenstromprinzip arbeitenden Anlage entschwefelt werden können, jedoch nicht die stark schwankenden, großen Roheisenmengen beim Hochofenabstich. Zum Mischen des leichteren Entschwefelungsmittels mit dem Roheisen hat man Vorrichtungen eingesetzt wie Drehtrommeln und Rinnenstücke, durch deren porösen Boden Gas eingeleitet wurde (A d r i a η ο ν, V. F., Slkaovyj rezim domennych pecey, Moskau 1967, S. 295 bis 302 und Wosko Boinikoff, W. G., Stal in Deutsch, 1955, Heft 7). Aber auch diese Verfahren haben sich betrieblich nicht durchsetzen können, da einmal das Problem der Mischung der Entschwefelungsmittel mit dem Roheisen nichtIn order to enable desulfurization of the pig iron without impairing the blast furnace passage and without disturbing the material flow, attempts have been made to desulfurize the pig iron in the tapping channel. The desulphurisation slag can be retained in the channel by a fox or a siphon, so that manual deslagging is not necessary. With this procedure, however, in contrast to the desulfurization in the ladle, the reaction time is predetermined by the strongly fluctuating pig iron tapping speed of the blast furnace. To weaken this influence, desulphurization has also been used. c carried out a longer stretch of the tapping channel (Stahl and Eisen, 1969, pp. 776 to 780). US Pat. No. 1,590,730 describes a process for the desulfurization of pig iron melted in a cupola furnace or conventional melting furnace. The small amounts of cast iron that occur during this process may be able to be desulphurized with the system that works on the countercurrent principle, but not the strongly fluctuating, large amounts of pig iron when tapping off the blast furnace. To mix the lighter desulphurizing agent with the pig iron, devices such as rotating drums and pieces of gutter, through the porous bottom of which gas was introduced (A dria η ο ν, VF, Slkaovyj rezim domennych pecey, Moscow 1967, pp. 295 to 302 and Wosko Boinikoff, WG, Stal in German, 1955, issue 7). But even these processes have not been able to establish themselves operationally, since there is no problem of mixing the desulphurizing agent with the pig iron
3 43 4
sicher beherrschbar war; zum anderen erreichen die bei den bekannten Drehtrommeln werden bei hohen
bekannten kontinuierlichen Entschwefelungsverfah- Abstichgeschwindigkeiten nur unbefriedigende Entren
nur bei geringen Abstic.'igeschwindigkeiten von 1 schwefelungsgrade erreicht Es konnte daher nicht
bis 3 t/min und nur mit flüssigen Entschwefelungs- erwartet werden, daß bei der erfindungsgemäßen
mitteln wie z.B. Soda, ausreichende Entschwefe- 5 Entschwefelung in der Hochofenrinne, bei der eine
lungergebnisse. Der apparative AufwanG bei den be- Roheisenvolumeinheit schon nach wenigen Rührerkannren
Verfahren ist hoch und die Betriebssicher- umurchuugeü aus dem Behälter ausgetragen wird,
heit, wie etwa bei der bekannten Drehtrommel, we- überhaupt die mäßigen Entschwefelungsergebnisse
gen der Schwierigkeit des Auswechselns bei Störun- der bekannten Drehtrommel erreicht, geschweige
gen gering. Der selbst für geringe Entschwefelungs- io denn übertroffen werden können,
grade erforderliche Bedarf an Entschwefelungsmittel Der Erfolg der Entschwefelung basiert auf dem inist
hoch. tensiven Kontakt von Roheisen und Zuschlagstoff,was certainly manageable; on the other hand, with the known rotary drums, at high known continuous desulfurization process tapping speeds, only unsatisfactory entrances are achieved only at low exhaust speeds of 1 degree of sulfurization the agents according to the invention, such as soda, sufficient desulphurisation in the blast furnace channel, in which a treatment results. The outlay in terms of apparatus for the hot metal volume unit after just a few stirrer can processes is high and the operational reliability is discharged from the container, as is the case with the well-known rotating drum, or the moderate desulphurisation results in the difficulty of replacement in the event of malfunctions known rotary drum reached, let alone gene low. Which can be exceeded even for low desulphurisation rates,
required desulphurisation agent requirement The success of desulphurisation is based on the inist high. intensive contact between pig iron and aggregate,
Nach der deutschen Patentschrift 880212 sollen der dadurch sichergestellt wird, daß die Richtung desAccording to German patent 880212, the should be ensured that the direction of the
im Gußeisen durch Rühren leicht flüchtige und ex- Roheiseneinlaufs radial auf die senkrechte Achse desin cast iron by stirring volatile and ex- pig iron inlet radially on the vertical axis of the
plosible Zusatzstoffe eingeführt wurden. Auch diese 15 Behälters zeigt und der Roheisenauslauf vom Einlaufplosible additives were introduced. Also shows this 15 container and the pig iron outlet from the inlet
Vorrichtung ist nicht zum Entschwefeln von Hoch- ausgehend in Drehrichtung des Rührers gezählt imDevice is not counted for desulphurisation of high starting in the direction of rotation of the stirrer
ofenrohreisen beim Abstich geeignet. dritten Quadranten und die Zugabeöffnung für dasOven pipe iron suitable for tapping. third quadrant and the addition opening for the
Ausgehend von diesem Stand der Technik stellt Entschwefelungsmittel im vierten Quadranten liegt, sich die Erfindung die Aufgabe, eine betrieblichere Dies wirkt einem direkten Durchfließen durch För-Vorrichtung zur Entschwefelung von Roheisen in 20 derung der Ausbildung von Kreisströmungen im Beeiner Hochofenabstichrinne unter Zusatz eines Ent- halter entgegen. Dadurch, daß die Zugabeöffnung für Schwefelungsmittels zu entwickeln, die auch bei stark das Entschwefelungsmittel im vierten Quadranten schwankender Abstichgeschwindigkeit des Roheisens liest, wird dieses durch den Rührer zunächst vom durch eine besonders hohe Reaktionsgeschwindigkeit Auslauf hinweggefördert und im Bereich des Eineine gleichmäßige und starke Absenkung des Schwe- 25 laufs durch Turbulenz mit dem einlaufenden Roheifelgehaltes ermöglicht und die auch geeignet ist, die senstrahl durchmischt.Based on this prior art, desulphurizing agent is in the fourth quadrant, The invention aims to provide a more operational This acts a direct flow through conveying device for desulfurization of pig iron in 20 modification of the formation of circular flows in the feeder Blast furnace tapping channel with the addition of a holder. Because the feed opening for Develop sulphurizing agents, even when heavily the desulphurizing agent in the fourth quadrant reads fluctuating tapping speed of the pig iron, this is initially removed by the stirrer through a particularly high reaction speed spout conveyed away and in the area of the one Uniform and strong lowering of the sulfur run through turbulence with the incoming raw Eifel content made possible and which is also suitable for mixing the senstrahl.
gesamte Roheisenproduktion eines Hochofens durch- Es hat sich gezeigt, daß mit der erfindungsgemä-entire pig iron production of a blast furnace through- It has been shown that with the inventive-
zusetzen, und die nicht an die Verwendung von Soda ßen Vorrichtung trotz unterschiedlicher Verweilzei-add, and not the use of soda essen device despite different dwell times
als Entschwefelungsmittel gebunden ist. ten einzelner Volumeinheiten die gute Entschwefe-is bound as a desulfurizing agent. individual volume units ensure good desulphurisation
Erfindungsgemäß wird diese Aufgabe unter Ver- 30 lung der Gesamtschmelze bis auf niedrige Schwefel-According to the invention, this object is achieved by reducing the total melt except for low sulfur
wendung einer Vorrichtung der eingangs beschriebe- gehalte von rund 0, 005% mit Sicherheit erreichbarUsing a device with a content of around 0.005% described at the beginning can be achieved with certainty
nen Art dadurch gelöst, daß der Behälter einen kreis- ist. Darüber hinaus werden diese Ergebnisse nichtNEN type solved in that the container is a circular. In addition, these results will not be
förmigen Querschnitt aufweist, daß die obere Innen- nur mit Soda, sondern auch mit trockenen Entschwe-has a shaped cross-section that the upper inner only with soda, but also with dry deswe-
fläche des Einlaufs tiefer und die des Auslaufs höher felungsmitteln wie Kalk und Kalziumkarbid erzieit.The area of the inlet is lower and that of the outlet is increased by detergents such as lime and calcium carbide.
liegt als die Uberlaufkante des Fuchses, daß sich ein 35 Dies bietet insofern einen wesentlichen technischenlies as the overflow edge of the fox, that is a 35 This offers an essential technical
an sich bekanntes, um seine senkrechte Achse moto- Fortschritt, als Soda als Entschwefelungsmittel we-known per se, around its vertical axis moto- progress, as soda as a desulfurizing agent
risch angetriebenes Rührorgan von oben in den Be- gen der dabei entstehenden Dämpfe, die gesundheits-electrically driven agitator from above in the area of the vapors produced, which are
hälter erstreckt, daß der Roheiseneinlauf radial auf schädlich sind, nur mit großer Vorsicht anzuwendencontainer extends that the pig iron inlet radially are harmful to use only with great caution
die senkrechte Achse des Behälters gerichtet ist und ist; des weiteren sind die bei der Sodaentschwefelungthe vertical axis of the container is directed and is; furthermore are those in the case of soda desulphurisation
daß der Auslauf, vom Einlauf in Drehrichtung des 40 entstehenden Schlacken mit Rücksicht auf die Rein-that the outlet, from the inlet in the direction of rotation of the slag produced with regard to the clean
Rührorgans gezählt im dritten Quadranten und die haltung des Grundwassers nicht ohne aufwendigeStirrer is counted in the third quadrant and the maintenance of the groundwater is not without complex
Zugabeöffnung für das Enischwefelungsmittel im Vorsichtsmaßnahmen lagerbar oder anderweitig ver-Addition opening for the enisulphurizing agent can be stored in the precautionary measures or otherwise
vierten Quadranten liegt. wendbar.fourth quadrant. reversible.
Das Wesentliche der erfindungsgemäßen Vorrich- Die Zuverlässigkeit der erfindungsgemäßen Vor-The essentials of the device according to the invention The reliability of the device according to the invention
tung ist also die Kombination der konstruktiven 45 richtung bei der Erzielung niedriger Endschwefelge-direction is therefore the combination of the constructive 45 direction in achieving low final sulfur levels.
Merkmale der beschriebenen Vorrichtung. halte und der einfache, robuste, störungsunanfälligeFeatures of the device described. hold and the simple, robust, failure-prone
Durch das intensive Mischen des Entschwefelungs- Aufbau ermöglichen es, die gesamte Produktion auch
mittels mit dem durchströmenden Roheisen mittels von Groß-Hochöfen zu entschwefeln. Wesentlich in
des Rührorgans in dem zylinderförmigcn Behälter dieser Beziehung ist femer, daß die Vorrichtung als
wird eine infolge der räumlichen Anordnung von 50 geschlossene Einheit mittels Kran aus der Rinne her-Einiauf,
Auslauf, Rührer und Zugabeort so hohe ausgehoben und ohne weitere Anpassung schnell geReaktionsgeschwindigkeit
erzielt, daß auch bei gen eine Ersatzeinheit ausgetauscht werden kann.
Schwankungen des Roheisendurchlaufs infolge der Eine besonders gute Durchmischung von Roheisen
vielfach schwankenden Abstichgeschwindigkeit die und Entschwefelungsmittel wird mit einem Rühror-Entschwefelung
bis zum gewünschten Grade abge- 55 gan in der Form eines umgedrehten T erreicht; es
schlossen ist. versieht sich von selbst, daß dessen unterer, balken-The intensive mixing of the desulphurisation structure makes it possible to desulphurise the entire production with the hot metal flowing through it by means of large blast furnaces. Another essential feature of the agitator in the cylindrically shaped container is that the device is lifted out of the gutter, outlet, agitator and addition point as if a unit closed due to the spatial arrangement of 50, and that the reaction speed is rapid without further adjustment achieved that a replacement unit can be exchanged even with gen.
Fluctuations in the pig iron flow due to the tapping speed and desulfurizing agent, which fluctuates particularly well, is achieved with a stirrer desulfurization to the desired degree in the form of an inverted T; it is closed. takes care of itself that its lower, bar-
Dieses Ergebnis ist überraschend. Bei anderen kon- förmiger Teil feuerfest ummantelt ist.
linuierlich arbeitenden Entschwefelungsvei fahren, Bei Innendurchmessern des Behälters von mehr
wie z. B. bei Drehtrommeln, wird mit Soda als einem als 1,5 m beträgt die Länge des balkenfönnigen Rüheine
flüssige Schlacke bildenden Entschwefelungsmit- 60 rerteils zweckmäßig das 0,35- bis 0,45fache, von wetel
gearbeitet; es erfolgt durch das Drehen der Trom- niger als 1,5 m das 0,45- bis 0,8üfache des innenmel
eine gründliche Durchmischung zwischen dem durchmesser des Behälters.This result is surprising. The other con-shaped part is encased in a fire-proof manner.
Linear desulphurization vehicles work, with inner diameter of the container of more such. B. with rotating drums, soda is used as a 1.5 m long desulphurisation agent, which forms a liquid slag, is expediently 0.35 to 0.45 times, from wetel; By turning the drum more than 1.5 m, 0.45 to 0.8 times the inner sleeve, thorough mixing takes place between the diameter of the container.
Entschwefelungsmittel und der Roheisenschmelze; Bei dieser Abmessung des Rührorgans wird eine außerdem sind für eine bestimmte Roheisendurch- kräftige und schnelle Mischung des Entschwefelungsflußgeschwindigkeit die Verweilzeiten aller durch die 65 mittels mit dem Roheisen und somit eine hohe Reak-Drehtrommel hindurchtretenden Roheisen- und tionsgeschwindigkeit erzielt. Für Roheisenabstichge-Schlackenvolumeinheiten gleich. Trotz dieser an- schwindigkeiten von 1 t/min haben sich Behälterscheinend optimalen Entschwefelungsbedingungen durchmesser von 1,2 m gut bewährt, für Abstichge-Desulphurising agents and molten pig iron; With this dimension of the agitator a in addition, for a given pig iron, vigorous and rapid mixing of the desulphurisation flow rate the dwell times all through the 65 means with the pig iron and thus a high reac rotary drum achieved through-passing pig iron and ionization speed. For pig iron tapping slag volume units same. Despite these speeds of 1 t / min optimal desulphurisation conditions diameter of 1.2 m well proven, for tapping
5 65 6
schwindigkeiten von 6i/min Behälterdurchmesser triebemotor 10 für eine Drehung um seine senkrechtispeeds of 6i / min container diameter drive motor 10 for a rotation around its perpendiculari
von 2 m. Achse versehen ist und am oberen Teil des Behälof 2 m. axis is provided and on the upper part of the container
Bekanntlich kann durch Absenken des Basizitäts- ters 2 abgestützt ist. Nach F i g. 1 befinden sich dieAs is known, it can be supported by lowering the basicity tester 2. According to FIG. 1 are the
grades der Hochofenschlacke die Hochofenleistung Einlauföffnung 3 und die Auslauföffnung 4 auf gleidegree of the blast furnace slag, the blast furnace power inlet opening 3 and outlet opening 4 on the same
wesentlich erhöht werden. Außerdem wird dadurch 5 eher Höhe und schließen mit ihren unteren Begrencan be increased significantly. In addition, this makes 5 more height and closes with its lower limit
der Hochofengang gleichmäßiger und die Gefahr des zungsflächen mit der inneren Bodenfläche S des Bethe blast furnace corridor more evenly and the danger of the tongue surfaces with the inner bottom surface S of the Be
Hängens stark verringert. Dieser Weg zur Erhöhung hälters 2 ab. Der Behälterboden und der Boden desHanging greatly reduced. This way to increase holder 2 from. The container bottom and the bottom of the
der Hochofenleistung war jedoch bisher nicht gang- Auslaufs sind schwach in Strömungsrichtung geneigtHowever, the blast furnace output has not yet been aisle - the outlets are slightly inclined in the direction of flow
bar, da die sich ergebenden hohen Schwefelgehalte zur Erleichterung des Entleerens des Gefäßes naclbar, as the resulting high sulfur content makes it easier to empty the vessel
durch nachfolgende Entschwefelung in besonderen io Beendigung des Abstichs. Der Auslauf 4 befindeby subsequent desulphurisation in a special io termination of the tapping. The outlet 4 is located
Entschwefelungsgeräten und im Stahlwerk zu auf- sich entsprechend Fig.2 vom Einlauf 3 in DrehrichDesulphurisation devices and in the steelworks towards you according to Fig.2 from the inlet 3 in Drehrich
wendig war. Es hat sich gezeigt, daß man mit der er- tung des Rührorgans 8 gezählt im dritten Quadranterwas agile. It has been shown that with the evaluation of the agitator 8 one counts in the third quadrant
findungsgemäßen Entschwefelungsvorrichtung über- und ist nach außen konisch erweitert, um ein Häninventive desulfurization device over and is flared outwardly to a Hän
raschenderweise auch derartig hohe Ausgangsschwe- genbleiben der Schlacke zu vermeiden. Das Rühror-surprisingly, it is also possible to avoid such high initial stagnation of the slag. The stirrer
felgehalte von 0,070 °/o zuverlässig und betriebssicher 15 gan befinde, sich mit der Unterkante 11 des balkenA ridge content of 0.070% is reliably and operationally safe 15 gan is located with the lower edge 11 of the beam
auf Gehalte von unter 0,010 %> absenken kann. Das förmigen Rührerteils 9 in einer solchen Höhe obercan lower to levels below 0.010%>. The shaped stirrer part 9 at such a height above
ermöglicht auch die Verwendung von bisher nicht halb der BodcnflacheS des Behälters 2, daß eiralso allows the use of previously not half of the bottom surface of the container 2 that eir
brauchbarem Koks mit Schwefelgehalten über 10Zo. Kurzschluß des durchströmenden Roheisens vermieusable coke with sulfur contents above 1 0 zo. Avoid short-circuit of the pig iron flowing through
Die Erfindung schlägt dementsprechend vor die Ver- den wird. Die Richtung des Roheiseneinlaufs 3 zeigtThe invention accordingly proposes the one. The direction of the pig iron inlet 3 shows
wendung der Vorrichtung zur Entschwefelung von 20 radial auf die senkrechte Achse des Behälters 2. Dieapplication of the device for the desulfurization of 20 radially on the vertical axis of the container 2. The
Roheisen in der Abstichrinne eines Hochofens, bei Entschwefelungsmittel 1 können durch eine öffnungPig iron in the tapping channel of a blast furnace, with desulfurizing agent 1 can through an opening
dem der Basengrad CaOVSiO2 der Hochofenschlacke 12 oben am Behälter 2 zugegeben werden. Die öff-to which the base grade CaOVSiO 2 of the blast furnace slag 12 is added at the top of the container 2. The public
auf weniger als 1,2 eingestellt und/oder Koks mit nung 12 befindet sich gemäß Fig.2, vom Einlauset to less than 1.2 and / or coke with voltage 12 is located according to Figure 2, from the inlet
Schwefelgehalten von über 11Vo verwendet wird. ausgehend in Drehrichtung des Rührorgans 8 gezählt,Sulfur contents of over 1 1 Vo is used. counted starting in the direction of rotation of the agitator 8,
Im folgenden wird an Hand der Zeichnung ein 25 im vierten Quadranten. Beide Maßnahmen erhöhenIn the following, a 25 is shown in the fourth quadrant on the basis of the drawing. Increase both measures
Ausführungsbeispiel der Erfindung erläutert. Es zeigt die Aufenthaltsdauer des Entschwefelungsmittels 1Embodiment of the invention explained. It shows the residence time of the desulfurizing agent 1
im einzelnen im Behälter 2. Die Rührerlänge beträgt das 0,5fach'in detail in container 2. The stirrer length is 0.5 times'
Fig. 1 eine Schnittzeichnung der Vorrichtung zur des inneren Behälterdurchmessers; der obere Rand1 shows a sectional drawing of the device for the inner container diameter; the top edge
Entschwefelung von Roheisen mit horizontalem Ein- des Behälters 2 befindet sich so weit oberhalb deDesulfurization of pig iron with a horizontal one of the container 2 is so far above de
lauf in den Behälter, 3° Oberkante des Auslaufs 4, daß ein Herausspritzenrun into the container, 3 ° upper edge of the outlet 4, that a splash out
F i g. 2 einen waagerechten Schnitt durch den Be- von Roheisen beim Rühren vermieden wird. DiF i g. 2 a horizontal section through the loading of pig iron during stirring is avoided. Tuesday
halter nach F i g. 1. Höhe des Roheisens im Entschwefelungsbehälter 2holder according to FIG. 1. Height of the pig iron in the desulfurization tank 2
Die Vorrichtung zur Entschwefelung von Roheisen wird durch die Überlaufkante 7 des mit dem AusThe device for desulfurization of pig iron is through the overflow edge 7 of the with the off
in einer Abstichrinne eines Hochofens unter Zusatz lauf 4 durch eine Rinne verbundenen Fuchses 6, dein a tapping channel of a blast furnace with the addition of 4 run through a channel connected fox 6, de
eines Entschwefelungsmittels 1 besteht aus einem Be- 35 außerdem das verbrauchte Entschwefelungsmitteof a desulfurizing agent 1 consists of a desulfurizing agent
halter 2 mit einem Einlauf 3, einem Auslauf 4 an der und das Roheisen voneinander trennt, festgelegt. Eiiholder 2 with an inlet 3, an outlet 4 on which and separates the pig iron from each other, set. Eii
Bodenfläche 5 desBehälters 2 und aus einem Fuchs 6 Nolabstich 14 ermöglicht die Entleerung des BchälBottom surface 5 of the container 2 and nolab stitching 14 from a fox 6 enables the bowl to be emptied
mit einer Überlaufkante 7 für das Roheisen. Von ters 2 bei Störungen. Nach Beendigung des Hochwith an overflow edge 7 for the pig iron. From ters 2 in the event of malfunctions. After the high ended
oben erstreckt sich in den Behälter 2 ein um seine ofenabstiches wird der Fuchs 6 bei oder kurz voAt the top, the fox 6 extends into the container 2 around its oven tapping at or shortly before
senkrechte Achse drehbares Rührorgan 8 in der 40 dem Abstichende so weit unten durchstoßen, daß di<vertical axis rotatable agitator 8 in the 40 pierce the tapping end so far below that di <
Form eines umgedrehten T, dessen unterer balkenfnr- feste Entschwefelungsschlacke zurückgehalten wireShape of an upside-down T, the lower beam of which was retained by solid desulphurisation slag
miger Teil 9 feuerfest ummantelt ist und der mit Ge- oder durch einen Beipaß umgangen.miger part 9 is refractory coated and bypassed with Ge or by a bypass.
Hierzu 1 Blatt Zeichnungen1 sheet of drawings
Claims (5)