DE1719175C - Plastic mass for the production of felt-like material - Google Patents
Plastic mass for the production of felt-like materialInfo
- Publication number
- DE1719175C DE1719175C DE1719175C DE 1719175 C DE1719175 C DE 1719175C DE 1719175 C DE1719175 C DE 1719175C
- Authority
- DE
- Germany
- Prior art keywords
- mass ratio
- felt
- fibers
- solid
- polyisobutylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
1 21 2
Die Erfindung helrilTl cine plustische Masse auf MassenverhäUnis (α i b): c wie K): 12 bis Kl: 7,The invention helrilTl cine plus mass to mass ratio (α i b): c like K): 12 to Kl: 7,
der Basis von Kunstharz und Faserinaterial zur Her- vorzugsweise K): K),
stellung von ülzartigem Material zur Verwendungthe basis of synthetic resin and fiber material for Her- preferably K): K),
provision of ulcer-like material for use
als Gleit-, Dichtungs-, Isolier- und Dämpfungsniate- d) hochdisperse, stark thixotrop machende Füll-as a sliding, sealing, insulating and damping compound- d) highly dispersed, highly thixotropic filling
rial od. dgl. 5 stoffe, z. B. aktive Kieselsäure,rial od. Like. 5 substances, z. B. active silica,
Filze aus Tierhaaren, Wollfilze und Filze aus syn- Massenverhaltnis (« f /' t
<): d etwa K): I bis thetisehen oder anderen nichtfilzenden Fasern werden [(): i5_ je nach Wirksamkeit,
für Dichtungszwecke, als Isoliermaterial, für Filterzwecke, zum Schleifen und Polieren, zur Schall- und e) Pigmente, Art und Menge nach Bedarf, z. B.
Schwingungsdämpfung, als Verpackungsmaterial, als io Molybdulrot (Bleichromal und Bleisulfat und
Gleiimalerial usw. \erwendet. So wird in technischen Bleimolybdat), Titandioxid oder Eisenoxid-Geräten,
z. B. in Rundfunkempfängern, an verschie- schwarz,
denen Stellen Filz in Form von Schnüren oderFelts of animal hair, wool felts, and the felts of syn- mass ratio ( "f / 't'): d is about K): I to thetisehen or other fibers are nichtfilzenden [(): i5_ e j efficacy,
for sealing purposes, as insulating material, for filter purposes, for grinding and polishing, for sonic and e) pigments, type and amount as required, e.g. B. Vibration dampening, as packaging material, as molybdenum red (lead chromal and lead sulfate and Gleiimalerial etc. \ erwendiert. So in technical lead molybdate), titanium dioxide or iron oxide devices, e.g. B. in radio receivers, on different black,
which places felt in the form of cords or
Streifen als Dämpfungs- und oder Gleitmaterial, Das Mengenverhältnis der FestkörperbestandteileStrips as damping and / or sliding material, the proportion of the solid components
unter Umständen auch als Dichtungsmaterial, ver- 15 zum Benzin ist je nach Anwendungsart v-uiierbuipossibly also as a sealing material, depending on the type of application, it is v-uiierbui
wendet. Auch ist das Benzin durch andere flüchtige Lösungs-turns. The gasoline is also due to other volatile solutions
Es ist auch filzartiges Material bekannt, das aus mittel ersetzbar.It is also known felt-like material that can be replaced from medium.
klebfähigen und nichtklebenden Fasern durch Akti- Je nach Bedarf ist eine weitere Komponente zuvieren der klebfähigen Fasern hergestellt wird. Als zusetzen, deren Aufgabe darin besteht, die Oberfläche nichtkiebende Fasern werden bei der Herstellung 20 des Gegenstandes anzulösen, auf den die Paste aufunter anderem Naturfasern, wie Zellstoffasern, zutragen ist. Für Kunststoffgegenstände ist beispiels-Baumwolle, Leinen, Jute, Kapok, Wolle, Haar und weise ein Zusatz von Chloroform als Anlösemittel Seide, und synthetische Fasern, z. B. aus Cellulose- ziemlich universell verwendbar. Das Massenverhältnis hydrat, Celluloseestern und Celluloseäthern, einge- der Festkörperbestandteile zu Chloroform soll etwa setzt. Die klebfähigen Fasern bestehen aus Kunst- 25 10:2 betragen. Als weitere Anlösemittel sind je nach harzen oder Kunststoffen; sie werden entweder unter Trägermaterial z. B. Aceton oder Methylenchlorid Erhaltung ihrer faserigen Form klebend gemacht verwendbar.Adhesive and non-adhesive fibers due to active components. Another component can be added as required the adhesive fibers is produced. Than clog, whose job is to finish the surface Non-sticky fibers will loosen during the manufacture of the object on which the paste is placed other natural fibers, such as cellulose fibers. For plastic objects, for example, cotton, Linen, jute, kapok, wool, hair and an addition of chloroform as a solvent Silk, and synthetic fibers, e.g. B. made of cellulose- pretty universally usable. The mass ratio hydrate, cellulose esters and cellulose ethers, some of the solid components of chloroform, are said to be puts. The adhesive fibers consist of synthetic 25 10: 2. As further solvents are depending on resins or plastics; they are either under carrier material z. B. acetone or methylene chloride Preservation of their fibrous shape made adhesive usable.
oder aber so flüssig gemacht, daß sie einen Film Die erfindungsgemäße plastische Masse kann aufor made so fluid that it can form a film
bilden, in welchem die nichtklebenden Fasern fest einfache Weise als »Filz aus der Tube« unmittelbarform, in which the non-adhesive fibers firmly and simply as "felt out of the tube" immediately
eingebettet sind (deutsche Patentschriften 867 167 30 auf die betreffenden Flächen aufgetragen werden,are embedded (German patents 867 167 30 are applied to the surfaces concerned,
und 874 666). Sie haftet dort ohne Anwendung von zusätzlichemand 874 666). It adheres there without the use of any additional measures
Die Befestigung der Filze und des filzartigen Klebstoff und weist nach dem Trocknen filzartigeThe attachment of the felts and the felt-like adhesive and has felt-like after drying
Materials auf Oberflächen erfolgt durch Aufnageln, Beschaffenheit auf.Material on surfaces is done by nailing, texture on.
Aufschrauben oder Aufkleben. Dabei ist die Be- Es sind zwar Dichtungsmassen auf der Basis vonScrew on or glue on. It is true that sealing compounds are based on
festigung umso schwieriger und teurer, je kleiner die 35 Polyisobutylen bekannt, die als Füllstoff AsbestfasernThe smaller the 35 polyisobutylene known as the filler asbestos fibers, the more difficult and expensive it is
Filzstücke sind. Besonders problematisch ist bei- enthalten und die sich ohne Klebstoff mit OberflächenPieces of felt are. Particularly problematic is included and which can be used without adhesive with surfaces
spielsweise das Aufkleben von etwa 3 · 4 mm großen verbinden (schweizerische Patentschrift 323 918).for example, the gluing of about 3 x 4 mm connect (Swiss patent 323 918).
Filzstücken auf die Skalenzeiger von Rundfunk- Mit Asbestfasern ist es jedoch nicht möglich, einPieces of felt on the dial pointer of broadcasting With asbestos fibers, however, it is not possible to
geräten, durch die ein sauberes Gleiten längs der Material zu erzielen, dessen Oberfläche filzartigedevices that allow smooth gliding along the material whose surface is felt-like
Skalenplatte und eine einwandfreie Zeigerführung 40 Beschaffenheit aufweist.Scale plate and a flawless pointer guide 40 has quality.
gewährleistet wird. Ein anderes Problem ist die Bc- Die filzartige Beschaffenheit der Oberfläche deris guaranteed. Another problem is the Bc- The felt-like texture of the surface of the
fcsiigung von Dichtungsstreifen längs des Deckel- erfindungsgeniäßen Masse nach dem Trocknen hängtFcsiigung of sealing strips along the lid of the invention hangs after drying
randes solcher Geräte. vorwiegend von der erhöhten viskositätssteigerndenedge of such devices. mainly from the increased viscosity-increasing
Der Erfindung liegt die Aufgabe zugrunde, die Wirkung des festen, kautschukartigen Polyisobuty-The invention is based on the object of the effect of the solid, rubber-like polyisobutyl
Befestigung von Filzstücken oder Filzstreifen zu ver- 45 lens im Lösungsmittel ab. Vergleichsversuche er-Fastening pieces of felt or felt strips should be left in the solvent. Comparative tests
einfachen. gaben, daß die Fasern beispielsweise von Chlor-simple. indicated that the fibers, for example, from chlorine
Diese Aufgabe wird erfindungsgcmäß mittels einer kautschuk völlig umschlossen werden, so daß eineThis task is completely enclosed according to the invention by means of a rubber, so that a
plastischen Masse gelöst, die dadurch gekennzeich- glatte, geschlossene Oberfläche entsteht,plastic mass, which is characterized by a smooth, closed surface,
net ist, daß sie zu 25°/o aus Festko'rperbestandteilen Das Verhältnis der beiden Polyisobutylensorten istWhat is net is that 25% of it consists of solid constituents. The ratio of the two types of polyisobutylene
und zu 75°/o aus Normalbenzin besteht, wobei die 50 so aufeinander abgestimmt, daß damit eine aus-and 75 ° / o consists of regular gasoline, the 50 being coordinated in such a way that an
Feslkörperbestandteile sich folgendermaßen zu- reichende Elastizität der Masse erzielt wird, ohneSufficient elasticity of the mass is achieved without any solid body constituents
sammensctzen: daß die getrocknete Masse nach außen klebrig wird.In summary: that the dried mass is sticky on the outside.
Dieses Ergebnis wird noch durch die Fasern und dieThis result is made even more by the fibers and the
a) Synthetische Kautschukmassen, Faibpigmentteilchen, welche an der Oberfläche bestellend aus festem Polyisobutylen, Mole- 55 stehen, unterstützt.a) Synthetic rubber compounds, color pigment particles, which on the surface Ordered from solid polyisobutylene, mole-55 stand, supports.
kulargewicht 200 000, und klebrig-teigartigem Der hochdisperse Füllstoff läßt durch seine großekular weight 200,000, and sticky, doughy The highly dispersed filler can be due to its large
.„ , _ Charakter sowie ihr Stehvermögen.. ", _ Character and stamina.
vorzugsweise 10:3,5, 6o Das Terpenphenolharz verbessert die Klebwirkungpreferably 10: 3.5, 6o The terpene phenol resin improves the adhesive effect
...... . ,,, . ,. der erfindungsgemäßen Masse auf Oberflächen........ ,,,. ,. the composition according to the invention on surfaces.
b) n.chthdrtcndes Terpenphenolharz, Chloroform oder andere Lösungsmittel werden zu-Schmclzbereieh 63 bis 700C, Massenverhaltnis gesetzt, um das jeweilige Basismaterial etwas aufa:b wie H): 10 bis 10:5. vorzugsweise 10:7, zu.a,uhen und auf diese Weise' die Haftung zub) n.chthdrtcndes terpene phenol resin, chloroform or other solvents, are set to-Schmclzbereieh 63 to 70 0 C, mass ratio to the respective base material something on a: b such as H): 10 to 10:. 5 preferably 10: 7, zu.a, uhen and in this way 'the liability to
65 erleichtern.65 facilitate.
c) synthetische Fasern oder Naturfasern, z. B. Die erfindungsgemäße Masse wird mit Benzin zu Kunstseidenflocken, ejner paste verarbeitet und je nach Verwendung»- Faserlänge 0,5 bis 3 mm, vorzugsweise 1 mm, zweck auf die richtige Konsistenz gebracht.c) synthetic fibers or natural fibers, e.g. B. The composition of the invention is processed with gasoline to rayon floc, e j ner p aste and depending on use "- fiber length 0.5 mm to 3, preferably 1 mm, conveniently brought to the proper consistency.
I 719I 719
50(1 50 7050 (1 50 70
5 205 20
2020th
wurdenbecame
relative messer,relative knife,
28,9 g 10,1 g 461g28.9 g 10.1 g 461 g
synthetische Kautschuklösung, Har/.losung, Kunstseidenllocken. 1 nun Faserlänge, hergestellt aus Celluloseacetat, Titandioxid,synthetic rubber solution, resin solution, Artificial silk curls. 1 now fiber length, made from cellulose acetate, Titanium dioxide,
chemisch reine Kieselsäure in submikroskopisch feiner Verteilung, ml Chloroformchemically pure silica in submicroscopic fine distribution, ml of chloroform
in einem Mischer zusammengeführt.merged in a mixer.
synthetische Kautschuklösung hatte eine Viskosität von 150 Sekunden (6 mm Durch-DIN-Becher). Sie bestand aus Polyisobutylen, Molekulargewicht 200 000, '5 Polyisobutylen, Molekulargewicht 15 000, Normalbenzin.synthetic rubber cement had a viscosity of 150 seconds (6 mm diameter DIN cup). It consisted of polyisobutylene, molecular weight 200,000, '5 Polyisobutylene, molecular weight 15,000, regular gasoline.
Die Harzlösung hatte eine relative Viskosität von Sekunden (4 mm Durchmesser, DIN-Becher). Sie to bestand aus einer 55°/oigert Lösung von Terpenphenolharz in Benzin.The resin solution had a relative viscosity of seconds (4 mm diameter, DIN cup). She insisted to from a 55 ° / oigert solution of terpene phenolic resin in gasoline.
Claims (2)
Family
ID=