DE878086C - Process for improving the properties of glues - Google Patents
Process for improving the properties of gluesInfo
- Publication number
- DE878086C DE878086C DEP45128A DEP0045128A DE878086C DE 878086 C DE878086 C DE 878086C DE P45128 A DEP45128 A DE P45128A DE P0045128 A DEP0045128 A DE P0045128A DE 878086 C DE878086 C DE 878086C
- Authority
- DE
- Germany
- Prior art keywords
- water glass
- glue
- glues
- fiber
- properties
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Verbesserung der Eigenschaften von Leimen Zusatz zum Patent 3&5 391 Gegenstand des Patents 765 ggi ist ein Verfahren zur Verbesserung der Eigenschaften von Leimen. Dies ist im wesentlichen dadurch gekennzeichnet, daß Leimen tierischen oder synthetischen Ursprungs Faserstoffe zugefügt werden, die durch Naßvermahlung in einen schleimartigen Zustand übergeführt wurden. Ein Zusatz von derartigem Faserschleim, der aus nahezu bis zur Strukturlosigkeit zermahlenen Fasern besteht, erhöht die Bindekraft der betreffenden Leime und verbessert die wertvollen Eigenschaften der Kerbzähigkeit, Schlagbiegfestigkeit usw.Process for improving the properties of glue additive to Patents 3 & 5,391 The 765 ggi patent relates to a method of improvement the properties of glues. This is essentially characterized in that Glues of animal or synthetic origin fiber materials are added to the were converted into a slime-like state by wet milling. An addition of such fiber slime, which is ground from almost to a lack of structure Fibers, increases the binding force of the glue in question and improves the valuable properties of notch toughness, impact resistance, etc.
Es wurde nun gefunden, daß das Verfahren gemäß dem Patent 765 ggi sich besonders gut anwenden läßt auf Wasserglas. Durch den Zusatz von Faserschleim zu Wasserglas erhält man hierbei Leime von besonders guten Eigenschaften. Insbesondere wird die Festigkeit der Wasserglasmasse durch den Schleimzusatz erhöht. Dieses erklärt sich dadurch, daß die unelastische und leicht brüchige Wasserglasmasse durch den Zusatz an Faserschleim eine Struktur erhält. Ferner wird durch den F.aserschleimzusatz die Viskosität des flüssigen Wasserglases erhöht, so daß eine sämige Leimbrühe entsteht, die ein sehr gutes Haftvermögen besitzt.It has now been found that the process according to patent 765 ggi can be used particularly well on water glass. By adding fiber slime Glues with particularly good properties are obtained in addition to water glass. In particular the strength of the water glass mass is increased by the addition of slime. This explains the fact that the inelastic and easily brittle water glass mass through the Addition of fiber slime is given a structure. Furthermore, the addition of fiber mucilage the viscosity of the liquid water glass increases, so that a creamy glue broth is created, which has very good adhesion.
Es ist zwar bekannt, Leime aus fasrigem Material und Wasserglas herzustellen, indem man Papier in Wasserglas auflöst. Hierbei wird jedoch die Faser durch das Aufweichen in Wasserglas bei Siedetemperatur und durch das Kochen unterDruck zerstört.Although it is known to produce glues from fibrous material and water glass, by dissolving paper in a glass of water. Here, however, the fiber is affected by the Softening in water glass at boiling temperature and destroyed by boiling under pressure.
Das Verfahren gemäß der Erfindung sieht im Gegensatz hierzu vor, daß bei der Naßvermahlung eine gewisse Struktur der Faser in Form von Fäserchen oder Faserresten erhalten bleibt. Außerdem werden bei dieser Arbeitsweise gegenüber der bekannten Energiekosten eingespart, da keine Zufuhr von Energie zum Zerkochen der Faser unter Druck erforderlich ist.In contrast, the method according to the invention provides that a certain structure of the fiber in the form of Fuzz or fiber remains. In addition, this way of working is opposite the known energy costs saved, since no energy is supplied for cooking the fiber under pressure is required.
In Ausübung der Erfindung wurde ferner gefunden, -daß=man bei Wasserglas mit geringeren Faserzusätzen auskommt, als bei anderen Leimen; ein Zusatz von 2 bis 3 Teilen Cellulose zu 97 bis 98 Teilen Wasserglas ergibt einen sehr guten Leim. Die Eigenschaften dieses Leimes entsprechen denen der bisher erhaltenen Leime aus Faserschleim und Leimen tierischen oder synthetischen Ursprungs.In the practice of the invention it was also found that one is with water glass uses less fiber than other glues; an addition of 2 Up to 3 parts of cellulose to 97 to 98 parts of water glass results in a very good glue. The properties of this glue correspond to those of the glues obtained so far Fiber slime and glues of animal or synthetic origin.
Die erfindungsgemäß hergestellte Leimlösung, bestehend aus Wasserglas und wäßrigem Faserschleim, ist infolge ihres Wassergehalts für viele Zwecke zu dünn und muß bis zur erforderlichen Konsistenz durch Kochen, zweckmäßig im Vakuum, eingedickt werden. Um die hierbei anfallenden Verdampfungskosten möglichst niedrig zu halten, ist es zweckmäßig, von Wasserglas höherer Konzentration, beispielsweise von Wasserglas von 4.3 bis 45° Be an Stelle von Wasserglas der üblichen Konzentration von 37 bis 4.o° Be, auszugehen. Ferner ist es zweckmäßig,. den wäßrigen Faserschleim in einer Zentrifuge vor dem Vermischen mit Wasserglas abzuschleudern, wobei man ebenfalls eine konzentrierte Leimlösung erhält. Beispiel Zur Herstellung .des Faserschleims aus Wasserglas wurden 3 bis q.kg lufttrockene Sulfitcellulose mit einem ursprünglichen Trockengehalt von 35'/o im 14o-Liter-Steinzeugholländer in 12 bis 15 Stunden schleimig gemahlen. Der Schleim wird auf ein Filtertuch gebracht und zwar einen Jutesack, so daß ein Teil des überschüssigen Wassers abläuft. Der Trockengehalt des so abfiltrierten Faserbreis beträgt etwa io°/o Cellulose, nachdem ein weiterer Teil des Wassers sich .durch Synärese noch abgeschieden hat.The glue solution produced according to the invention, consisting of water glass and aqueous fiber slime, is too thin for many purposes due to its water content and must be thickened to the required consistency by boiling, expediently in a vacuum. In order to keep the evaporation costs as low as possible, it is advisable to use water glass of higher concentration, for example water glass of 4.3 to 45 ° Be, instead of water glass of the usual concentration of 37 to 40 ° Be. It is also useful. spinning off the aqueous fiber slime in a centrifuge before mixing with water glass, a concentrated glue solution also being obtained. Example To produce the fiber slime from water glass, 3 to q.kg air-dry sulfite cellulose with an original dry matter content of 35% was ground slimy in a 14o-liter stoneware Dutchman in 12 to 15 hours. The slime is placed on a filter cloth, namely a jute sack, so that some of the excess water runs off. The dry content of the pulp filtered off in this way is about 10% cellulose, after a further part of the water has separated out by syneresis.
Der etwa 8 bis io%ige Faserbrei wird nun mit Wasserglas von 37 bis q.o° Be vermischt, wobei die intensive Mischung in einer Mischmaschine erfolgt. Die so hergestellte Mischung enthält für die Verleimung zuviel Wasser. Daher wird diese Mischung in einem Kochbehälter, zweckmäßig einem Vakuumverdampfer mit Rührwerk, auf etwa zwei Drittel eingedickt, wodurch ein sehr bindekräftiger Lehn entsteht.The approximately 8 to 10% pulp is now with water glass from 37 to q.o ° Be mixed, whereby the intensive mixing takes place in a mixer. The mixture produced in this way contains too much water for gluing. Hence will this mixture in a cooking container, expediently a vacuum evaporator with agitator, thickened to about two thirds, creating a very strong backrest.
Der zähflüssige, gemäß der Erfindung hergestellte Wasserglasfaserleim läßt sich beispielsweise zum Verkleben von Holz auf Holz, Papier auf Blech, Holz auf Metall und Holz auf Stein verwenden. SeineVerwendung kann noch auf vieleGegenstände ausgedehnt werden, insbesondere auf die Verleimung von Hartfaserplatten auf Stein, Beton und Metall.The viscous waterglass fiber glue produced according to the invention can be used, for example, to glue wood to wood, paper to sheet metal, wood use on metal and wood on stone. Its use can still be applied to many objects be extended, in particular to the gluing of hardboard on stone, Concrete and metal.
Die praktische Anwendung hat erwiesen, daß bei der Verleimung von Baustoffen mit Beton und Metall .der Wasserglasfaserleim wesentlich höhere Leimfestigkeiten ergibt, als .die meisten bisher dafür angewendeten Leime.Practical application has shown that when gluing Building materials with concrete and metal. The water glass fiber glue has significantly higher glue strengths than most of the glues used for this purpose up to now.
Infolge des billigen Preises der Ausgangsstoffe Cellulose und Wasserglas ist es möglich, einen guten und billigen, flüssigen Kaltleim herzustellen, der ohne weiteres einen Wettbewerb mit flüssigen synthetischen Leimen zuläßt. Der Preis für den flüssigen Wasserglasfaserleim dürfte etwa um 50% niedriger liegen als für das zu vergleichende synthetische Produkt.As a result of the cheap price of the raw materials cellulose and water glass it is possible to make a good and cheap, liquid cold glue that without further allows competition with liquid synthetic glues. The price for the liquid waterglass fiber glue should be around 50% lower than for that synthetic product to be compared.
Claims (1)