DE1093521B - Optisches Glas - Google Patents

Optisches Glas

Info

Publication number
DE1093521B
DE1093521B DEL32164A DEL0032164A DE1093521B DE 1093521 B DE1093521 B DE 1093521B DE L32164 A DEL32164 A DE L32164A DE L0032164 A DEL0032164 A DE L0032164A DE 1093521 B DE1093521 B DE 1093521B
Authority
DE
Germany
Prior art keywords
percent
weight
oxide
optical glass
glasses
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEL32164A
Other languages
English (en)
Inventor
Dipl-Chem Heinz Broemer
Norbert Meinert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ernst Leitz Wetzlar GmbH
Original Assignee
Ernst Leitz Wetzlar GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ernst Leitz Wetzlar GmbH filed Critical Ernst Leitz Wetzlar GmbH
Priority to DEL32164A priority Critical patent/DE1093521B/de
Priority to FR478A priority patent/FR1228382A/fr
Priority to US705A priority patent/US3143432A/en
Publication of DE1093521B publication Critical patent/DE1093521B/de
Pending legal-status Critical Current

Description

JVL,.
DEUTSCHES
PATENTAMT
INTERNAT. KL. C 03 C
AUSLEGE SCHRIFT 1093 521
L 32164 IVc/32 b
ANMELDE TA G: 9. J A N U A R 1959
BEKANNTMACHUNG
DER ANMELDUNG
UND AUSGABE DEB
AUSLEGESCHRIFT: 24. NOVEMBER 1960
Die Erfindung betrifft optische Gläser hoher Brechkraft und kleiner Dispersion, die besonders beständig gegen Chemikalien und Atmosphärilien sind.
Es sind bereits optische Gläser beschrieben worden, die aus einem Grundglas aus Kieselsäure, Borsäure und Lanthanoxyd bestehen, in dem gegebenenfalls weitere in der Glasherstellung verwendete Oxyde gelöst sind. Bei diesen bekannten Gläsern ist der Anteil der Kieselsäure im Verhältnis zur Borsäure verhältnismäßig niedrig.
Es sind ferner Borosilikatgläser bekannt, die größere Mengen an Lanthanoxyd sowie an Bariumoxyd enthalten. Alle diese bekannten Gläser sind jedoch sehr fleckenempfindlich, so daß ihre Verarbeitung und Verwendung insbesondere in tropischen Gebieten erhebliche Schwierigkeiten bereiten.
Die vorliegende Erfindung betrifft Gläser, die außerordentlich beständig sind und optische Werte aufweisen, die von Gläsern verlangt werden, welche in modernen Präzisionsobjektiven Verwendung finden sollen. Die Gläser lassen sich sehr leicht farblos erschmelzen und bereiten bei der Verarbeitung keinerlei Schwierigkeiten. Sie sind dadurch gekennzeichnet, daß sie zwischen 20 und 24 Gewichtsprozent Kieselsäure und Borsäure, davon Kieselsäure allein zwischen 14 und 35 Gewichtsprozent, zwischen 30 und 40 Gewichtsprozent Lanthanoxyd sowie Erdalkalioxyde zwischen 7,5 und 20 Gewichtsprozent und Oxyde von Zirkon und/oder Zink und/oder Cadmium von mindestens 2 Gewichtsprozent enthalten, wobei die Anteile an Zirkonoxyd aHein 10 Gewichtsprozent sowie an Zink- und/oder Cadmiumoxyd ebenfalls 10 Gewichtsprozent nicht überschreiten sollen. Der Anteil an Bariumoxyd soll 5 Gewichtsprozent nicht überschreiten. Zur Einregulierung der optischen Werte können ferner bis zu 10 Gewichtsprozent Oxyde von Tantal, Niob, Blei, Wolfram und Titan verwendet werden.
Optisches Glas
Anmelder:
Ernst Leitz G. m. b. H., Wetzlar/Lahn, Laufdorfer Weg
Dipl.-Chem. Heinz Brömer,
Hermannstein über Wetzlar/Lahn,
und Norbert Meinert, Wetzlar/Lahn,
sind als Erfinder genannt worden
Der Anteil an Bariumoxyd soll so niedrig wie möglich bleiben, da das Bariumoxyd die Gläser weich und empfindlich macht. Vorzugsweise wird von den Erdalkalioxyden das Calciumoxyd verwendet.
In den folgenden Tabellen sind einige Beispiele für derartige Gläser aufgeführt, wobei die einzelnen Glaskomponenten in Gewichtsprozenten angegeben sind.
Tabelle I
Si 2
Si 5
Schmelz-Nr.
Si3
Si 7
SiIO
Si 21
SiO2 .
B2O3 .
La2O3
CaO .
ZrO2 .
BaO .
ne .... ve
16,0
30,0
32,0
17,0
5,0
1,688
54,6
18,5
21,8
39,1
15,2
5,4
1,699
52,9 21,0
21,0
34,8
17,9
5,3
1,692
53,5
25,0
20,0
33,0
17,0
5,0
1,685
53,5
25,0
15,0
36,0
19,0
5,0
1,688
53,4
33,4
5,5 36,7 18,9
5,5
1,697 51,6
22,0 20,0 37,0 11,0
5,0
5,0
1,690 53,4
009 649/199
Tabelle II Si O2
B2O3
La2O3
CaO
ZrO2
BaO
ZnO
WO3
Ta2O5
TiO2 		Si 12 Si 13 Schmelz-Nr.
Si 33		 Si 32 Si 35
ve 23,5
20,1
32,8
14,4
6,2
3,0
1,696
52,3		 21,0
10,5
39,5
15,0
5,0
9,0
1,735
49,0		 21,0
10,5
32,0
15,0
5,0
9,0
7,5
1,737
46,4		 33,4
5,5
30,0
18,9
5,5
6,7
1,701
49,8		 21,0
10,5
32,0
15,0
7,5
9,0
5,0
1,760
42,1
Tabelle III
SiIOO .
Si 103 .
PM 2 .
PM/Tl
PM/T5
Si99 ..
Si98 .,
PM/T9
B2O3 La2O3 CaO BaO Schmelz-Nr. ZnO CdO PbO ne
SiO2 21,6 36,6 11,5 4,8 ZrO2 2,4 1,696
20,7 24,0 38,0 15,0 1,5 2,4 3,5 — — 1,703
17,0 25,23 37,73 11,17 3,76 1,0 4,23 — — 1,696
16,88 21,5 38,0 10,0 5,0 1,00 5,0 — — 1,696
20,0 25,5 38,2 11,5 3,8 0,5 3,2 — — 1,698
17,1 15,0 32,0 20,0 — 0,7 — 7,0 — 1,696
26,0 20,6 33,8 15,0 — — 2,5 — 7,5 1,704
20,6 29,5 36,0 18,0 — — — — — 1,695
14,5 2,0
53,6 53,7 54,0 53,6 54,4 52,6 50,5 54,8
Die Gläser werden vorzugsweise in Platingefäßen bei Temperaturen zwischen 1350 und 1500° C eingeschmolzen. Sie lassen sich bis etwa 1100° C herunterrühren und dann in bekannter Weise abgießen.
Dem Gemenge können in bekannter Weise entfärbende Substanzen, Arsenoxyd oder stabilisierende Substanzen wie Aluminiumoxyd, in kleinen Mengen zugegeben werden.

Claims (2)

Patentansprüche:
1. Optisches Glas mit hoher Brechkraft und kleiner Dispersion, bestehend aus
Gewichtsprozent
Kieselsäure + Borsäure 20 bis 46
davon Kieselsäure 14 bis 35
Lanthanoxyd 30 bis 40
Gewichtsprozent
Erdalkalioxyde 7,5 bis 20
davon Bariumoxyd <C5
Zirkonoxyd 0 bis 10
Zink- und/oder Cadmiumoxyd .. 0 bis 10
wobei die Summe der Anteile von Zirkon-, Zink- und Cadmiumoxyd mindestens 2 Gewichtsprozent beträgt.
2. Optisches Glas nach Anspruch 1, dadurch gekennzeichnet, daß es zusätzlich bis zu 10 Gewichtsprozent an Oxyden von Tantal, Niob, Wolfram, Blei, Titan enthält.
In Betracht gezogene Druckschriften:
»Journal of Research of the National Bureau of Standards«. Research Paper RP 1881, Volume 40, May 1948.
© 009 649/199 11.60
DEL32164A 1959-01-09 1959-01-09 Optisches Glas Pending DE1093521B (de)