DE102021101160A1 - Mineral wallpaper and process for their production - Google Patents

Mineral wallpaper and process for their production Download PDF

Info

Publication number
DE102021101160A1
DE102021101160A1 DE102021101160.4A DE102021101160A DE102021101160A1 DE 102021101160 A1 DE102021101160 A1 DE 102021101160A1 DE 102021101160 A DE102021101160 A DE 102021101160A DE 102021101160 A1 DE102021101160 A1 DE 102021101160A1
Authority
DE
Germany
Prior art keywords
aggregate
mineral
wallpaper
paste
percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE102021101160.4A
Other languages
German (de)
Inventor
Michael Zimmermann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wall Rapture Germany GmbH
Original Assignee
Wall Rapture Germany GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wall Rapture Germany GmbH filed Critical Wall Rapture Germany GmbH
Publication of DE102021101160A1 publication Critical patent/DE102021101160A1/en
Pending legal-status Critical Current

Abstract

Die Erfindung betrifft eine Mineralstofftapete, die eine zu Natur- oder Kunststein identische Oberflächenoptik und -haptik besitzt und mittels herkömmlicher Tapeziertechniken verarbeitbar ist; sie betrifft zudem ein Verfahren zur Herstellung der Mineralstofftapete. Die Mineralstofftapete, die eine Dicke von bis zu 1,5 mm aufweist, umfasst eine auf einem flexiblen textilen Trägermaterial (2) aufgebrachte, makroporenfrei ausgebildete Gesteinskörnungsschicht (1). Diese besitzt einen Masseanteil von 71 bis 90 Prozent Gesteinsmehl aus Carbonatgestein; die Gesteinskörner sind in der Gesteinskörnungsschicht (1) mittels eines homogen verteilten Bindemittels verbunden. Die Mineralstofftapete eignet sich zum Aufbringen auf verschiedenste Untergründe; sie kann zum Beispiel zur Verkleidung von Wänden, Decken, Böden oder von Möbelstücken eingesetzt werden.The invention relates to a mineral wallpaper which has a surface look and feel that is identical to natural or artificial stone and can be processed using conventional wallpapering techniques; it also relates to a method for producing the mineral wallpaper. The mineral wallpaper, which is up to 1.5 mm thick, comprises a macropore-free aggregate layer (1) applied to a flexible textile carrier material (2). This has a mass fraction of 71 to 90 percent rock powder made from carbonate rock; the aggregates are connected in the aggregate layer (1) by means of a homogeneously distributed binding agent. The mineral wallpaper is suitable for application on a wide variety of substrates; it can be used, for example, to cover walls, ceilings, floors or pieces of furniture.

Description

Die Erfindung betrifft eine Mineralstofftapete auf Basis einer Gesteinskörnung sowie ein Verfahren zu deren Herstellung. Die Mineralstofftapete eignet sich zum Aufbringen auf verschiedenste Untergründe; sie kann zum Beispiel zur Verkleidung von Wänden, Decken, Böden oder auch von Möbelstücken eingesetzt werden.The invention relates to a mineral wallpaper based on aggregate and a method for its production. The mineral wallpaper is suitable for application on a wide variety of substrates; it can be used, for example, to cover walls, ceilings, floors or furniture.

Neben dem Verkleiden von Decken- und Wänden mit Fließen und Platten haben sich kunststoffbasierte Steinimitatbeläge im Innenausbau und für Fassadenverkleidungen etabliert. Solche kunststoffbasierten Steinimitatbeläge können in nahezu beliebiger Optik hergestellt werden; sie sind u. a. auch im Dickenbereich von ca. 1 mm erhältlich und können hierdurch wie klassische Papiertapeten verarbeitet werden.In addition to cladding ceilings and walls with tiles and slabs, plastic-based imitation stone coverings have established themselves in interior construction and for facade cladding. Such plastic-based imitation stone coverings can be produced in almost any optics; they are inter alia Also available in a thickness range of approx. 1 mm and can therefore be processed like classic paper wallpapers.

Gegenüber Natur- oder Kunststein unterscheiden sich diese Kunststoffbeläge jedoch nicht nur durch ihre Haptik, sondern vielfach auch in ihrer Optik, da sie als Imitate anhand bestimmter Kennzeichen, wie zum Beispiel ihrem Glanz, erkennbar sind. Das Raumklima in echtsteinverkleideten Räumen wird zudem häufig angenehmer empfunden als bei Verwendung von Kunststoffverkleidungen.Compared to natural or artificial stone, however, these plastic coverings differ not only in their feel, but also in many cases in their appearance, as they can be recognized as imitations based on certain characteristics, such as their gloss. The room climate in real stone-clad rooms is also often perceived as more pleasant than when using plastic cladding.

Mineralstoffbasierte Beläge, die die Vorteile der Kunststoffbeläge, insbesondere ihre einfache Verarbeitung, und die natürliche Steinoptik und -haptik vereinen, sind bekannt in Form starrer Platten oder dünner Steinfurniere. Bekannt sind zudem Mineralstofflaminate mit Dicken im Bereich von ca. 1 bis 4 mm, zum Beispiel aus DE 10 2008 032 204 A1 ; die in Form einer Gesteinskörnung aufgebrachten Mineralstoffe sind demgemäß in einem kunststoffbasiertem Bindemittel fixiert, wobei der Anteil der mineralischen Füllstoffe im Bereich von 15 bis 70 Prozent liegt, was einen relativ hohen Bindemittelgehalt bedingt.Mineral-based coverings, which combine the advantages of plastic coverings, especially their ease of processing, and the natural stone look and feel, are known in the form of rigid panels or thin stone veneers. Mineral laminates are also known with thicknesses in the range from approx. 1 to 4 mm, for example from DE 10 2008 032 204 A1 ; the minerals applied in the form of aggregates are accordingly fixed in a plastic-based binder, the proportion of mineral fillers being in the range from 15 to 70 percent, which requires a relatively high binder content.

DE 10 2010 061 869 A1 offenbart eine schäumbare Zusammensetzung, die zur Herstellung von Fußbodenbeläge oder Wandtapeten einsetzbar sind. In der Zusammensetzung können mineralische Zusatzstoffe zu max. 60 % bezogen auf die Gesamtmasse von Bindemittel und Füllstoff enthalten sein. DE 10 2010 061 869 A1 discloses a foamable composition useful for making floor coverings or wall paper. The composition can contain mineral additives up to a maximum of 60% based on the total mass of binder and filler.

Weiterhin beschreibt GB 1 162 991 A einen Mineralstoffbelag, der aus einem einen Mineralstoff enthaltenden Kunstschlicker hergestellt und auf eine starre Platte appliziert wird; ähnliches ist aus EP 0 131 064 A1 bekannt. EP 2 360 025 A2 offenbart einen mineralstoffbasierten Belag, dessen Oberflächenschicht aus feingranuliertem, mit Schmelzkleber vermischtem Naturstein besteht; diese Schicht wird thermisch auf einer Trägerbahn fixiert. Ein Verfahren auf Basis einer Spachtelmasse zur Herstellung einer Platte mit Mineralstoffbelag ist in DE 103 40 238 A1 beschrieben.Further describes GB 1 162 991 A a mineral covering made from an artificial slip containing a mineral and applied to a rigid plate; something similar is over EP 0 131 064 A1 famous. EP 2 360 025 A2 discloses a mineral-based covering, the surface layer of which consists of finely granulated natural stone mixed with hot-melt adhesive; this layer is thermally fixed on a carrier web. A method on the basis of a filler for the production of a plate with a mineral surface is shown in DE 103 40 238 A1 described.

Die bekannten gesteinskörnungsbasierten Mineralstoffbeläge für Wand- und Deckenverkleidungen besitzen zur Sicherstellung der Flexibilität entweder einen hohen Kunststoffbindemittelanteil (z. B. DE 10 2008 032 204 A1 , GB 1 162 991 A ) oder eine definierte Porosität (z. B. DE 10 2017 119 048 A1 ). Mineralstoffbeläge, die wie klassische Papiertapeten auf Wände, Decken oder Böden appliziert werden können, und dennoch einen hohen Gesteinskörnungsanteil aufweisen, sind dagegen bislang wirtschaftlich nur schwierig realisierbar.The well-known aggregate-based mineral coverings for wall and ceiling cladding either have a high proportion of plastic binder (e.g. DE 10 2008 032 204 A1 , GB 1 162 991 A ) or a defined porosity (e.g. DE 10 2017 119 048 A1 ). Mineral coverings, on the other hand, which can be applied to walls, ceilings or floors like classic paper wallpaper, but still have a high proportion of aggregates, have so far been economically difficult to implement.

Aufgabe der Erfindung ist es daher, eine Mineralstofftapete auf Basis einer Gesteinskörnung mit geringer Dicken bereitzustellen, die eine zu Natur- oder Kunststein identische Oberflächenoptik und -haptik besitzt und mittels herkömmlicher Tapeziertechniken verarbeitbar ist.The object of the invention is therefore to provide a mineral wallpaper based on aggregate with low thicknesses, which has a surface look and feel that is identical to natural or artificial stone and can be processed by means of conventional wallpapering techniques.

Diese Aufgabe wird durch eine Mineralstofftapete auf Basis einer Gesteinskörnung mit den kennzeichnenden Merkmalen nach dem Anspruch 1 sowie das Verfahren zur Herstellung einer Mineralstofftapete nach Anspruch 7 gelöst; zweckmäßige Weiterbildungen der Erfindung sind in den Ansprüchen 2 bis 6 sowie 8 bis 10 aufgeführt.This object is achieved by a mineral wallpaper based on a rock grain with the characterizing features according to claim 1 and the method for producing a mineral wallpaper according to claim 7; Expedient developments of the invention are set out in the claims 2 up to 6 and 8 to 10.

Nach Maßgabe der Erfindung umfasst die Mineralstofftapete eine auf einem flexiblen textilen Trägermaterial aufgebrachte Gesteinskörnungsschicht; die Mineralstofftapete weist eine Dicke von bis zu 1,5 mm auf. Die Gesteinskörnungsschicht ist makroporenfrei ausgebildet und besitzt einen Masseanteil von 71 bis 90 Prozent Gesteinsmehl aus Carbonatgestein (vorzugsweise 80 bis 90 Prozent Gesteinsmehl aus Carbonatgestein), zum Beispiel Marmormehl, in der Gesteinskörnungsschicht. Die Gesteinskörner sind in der Gesteinskörnungsschicht mittels eines homogen verteilten Bindemittels verbunden.According to the invention, the mineral wallpaper comprises an aggregate layer applied to a flexible textile carrier material; the mineral wallpaper has a thickness of up to 1.5 mm. The aggregate layer is macropore-free and has a mass fraction of 71 to 90 percent rock powder from carbonate rock (preferably 80 to 90 percent rock powder from carbonate rock), for example marble powder, in the aggregate layer. The aggregates are connected in the aggregate layer by means of a homogeneously distributed binding agent.

Gesteinsmehl im Sinne dieser Erfindung ist eine Gesteinskörnung, deren einzelne Gesteinskörner Korngrößen von bis zu 180 µm Korndurchmesser, insbesondere von Korngrößen von bis zu 63 µm Korndurchmesser, aufweisen.Rock powder in the context of this invention is an aggregate whose individual aggregates have grain sizes of up to 180 μm grain diameter, in particular grain sizes of up to 63 μm grain diameter.

Das erfindungsgemäße Verfahren zur Herstellung der Mineralstofftapete wird gemäß der folgend beschriebenen Verfahrensschritte durchgeführt.The method according to the invention for producing the mineral wallpaper is carried out according to the method steps described below.

Zunächst wird eine Gesteinskörnung mit einer wässrigen Bindemitteldispersion und Wasser zu einer klumpen- und porenfreien, homogenen Gesteinskörnungspaste vermengt bzw. gemischt. Die Gesteinskörnungspaste enthält als Gesteinskörnung einen Masseanteil von 51 bis 70 Prozent Gesteinsmehl aus Carbonatgestein, insbesondere einen Masseanteil von 60 bis 70 Prozent Gesteinsmehl aus Carbonatgestein. Vorzugsweise wird Marmormehl als Gesteinskörnung verwendet.First, an aggregate is mixed or mixed with an aqueous binder dispersion and water to form a lump-free and pore-free, homogeneous aggregate paste. The aggregate paste as aggregate contains a mass fraction of 51 to 70 percent Rock powder made from carbonate rock, in particular a mass fraction of 60 to 70 percent rock powder made from carbonate rock. Marble powder is preferably used as the aggregate.

Anschließend erfolgt das Aufstreichen der Gesteinskörnungspaste auf eine Fertigungsunterlage. Die aufgestrichene Gesteinskörnungspaste wird auf eine homogene Dicke abgezogen. Das flexible textile Trägermaterial wird danach auf die Pastenschicht aufgelegt und in diese eingearbeitet, zum Beispiel indem ein zusätzlicher dünner Film Gesteinskörnungspaste aufgestrichen und abgezogen wird. Nach diesen Schritten liegt ein Tapetengrünling mit homogener Dicke vor, der im Anschluss getrocknet wird, wobei sich die Mineralstofftapete ausgebildet. Diese wird schließlich von der Fertigungsunterlage - zum Beispiel durch Abziehen oder Abrollen - abgenommen.The aggregate paste is then spread onto a manufacturing base. The applied aggregate paste is peeled off to a homogeneous thickness. The flexible textile carrier material is then placed on the paste layer and incorporated into it, for example by applying and removing an additional thin film of aggregate paste. After these steps, there is a green wallpaper with a homogeneous thickness, which is then dried, whereby the mineral wallpaper is formed. This is finally removed from the production document - for example by peeling off or unrolling.

Die erfindungsgemäße Mineralstofftapete zeichnet sich durch eine hohe Flexibilität aus und kann - trotz des hohen Gesteinskörnungsgehaltes - in der von Papiertapeten bekannten Art und Weise gerollt werden. Das Tapezieren unter Verwendung der Mineralstofftapete erfolgt gewohnt schnell und unkompliziert. Zudem ist die Mineralstofftapete flexibel auf verschiedenen Oberflächen bzw. Untergründen einsetzbar, zum Beispiel auch auf Rundungen und an Kanten. Bei Untergrundspannungen treten keine Risse in den Sichtoberflächen auf.The mineral wallpaper according to the invention is characterized by high flexibility and can - despite the high aggregate content - be rolled in the manner known from paper wallpapers. Wallpapering using the mineral wallpaper is quick and uncomplicated as usual. In addition, the mineral wallpaper can be used flexibly on different surfaces or substrates, for example also on curves and on edges. No cracks appear in the visible surfaces when there is tension in the substrate.

Die Verarbeitungszeit beim Aufbringen der vorgeschlagene Mineralstofftapete ist deutlich geringer als beim Applizieren mineralischer Beläge in klassischer Spachteltechnik; Baustaub und -lärm werden insofern vermieden. Zudem ist die Mineralstofftapete im Vergleich zu gespachtelten mineralischen Belägen mit deutlich geringerem Zeit- und Arbeitsaufwand entfernbar.The processing time when applying the proposed mineral wallpaper is significantly shorter than when applying mineral coverings using the classic spatula technique; Construction dust and noise are thus avoided. In addition, the mineral wallpaper can be removed with significantly less time and effort compared to leveled mineral coverings.

Der Anteil des Bindemittels in der Gesteinskörnungsschicht beträgt vorzugsweise 6 bis 14 Prozent der Masse der Gesteinskörnungsschicht. Das Bindemittel kann beispielsweise ein Acrylat sein.The proportion of the binder in the aggregate layer is preferably 6 to 14 percent of the mass of the aggregate layer. The binder can for example be an acrylate.

Als textiles Trägermaterial ist u. a. Glasfaservlies geeignet.The textile carrier material is, inter alia. Glass fiber fleece suitable.

Gemäß einer Ausgestaltung der Mineralstofftapete enthält die Gesteinskörnungsschicht ein feinkörniges Phyllo- oder Schichtsilikat, wobei der Anteil des Phyllosilikates 7 bis 13 Prozent der Masse der Gesteinskörnungsschicht beträgt. Besonders geeignet hat sich das Aluminium-Eisen-Magnesium-Schichtsilikat Vermiculit erwiesen. Vorzugsweise liegt die Korngröße des Phyllosilikates im Korngrößenbereich von 200 µm bis 800 µm. Der Zuschlag des Schichtsilikates verbesserte insbesondere den Glanz und die steinoptische Erscheinung der Mineralstofftapete.According to one embodiment of the mineral wallpaper, the aggregate layer contains a fine-grain phyllo- or sheet silicate, the proportion of phyllosilicate being 7 to 13 percent of the mass of the aggregate layer. The aluminum-iron-magnesium layered silicate vermiculite has proven to be particularly suitable. The particle size of the phyllosilicate is preferably in the particle size range from 200 μm to 800 μm. The addition of the layered silicate improved the gloss and the stone-look appearance of the mineral wallpaper in particular.

Des Weiteren kann die Gesteinskörnungsschicht einen Pigmentzusatz von bis zu fünf Prozent der Masse der Gesteinskörnungsschicht aufweisen. Durch die Pigmentzusätze können verschiedene Farbtönungen eingestellt werden.Furthermore, the aggregate layer can have a pigment addition of up to five percent of the mass of the aggregate layer. Different color tones can be set by adding pigments.

Die Farbe der Mineralstofftapete ist zudem durch Aufbringen von Lasuren modifizierbar.The color of the mineral wallpaper can also be modified by applying glazes.

In einer bevorzugten Ausführung der Mineralstofftapete besitzt die dem Trägermaterial abgewandte Sichtoberfläche der Mineralstofftapete eine vorgegebene Oberflächenstruktur mit regelmäßigen und/oder unregelmäßigen Ausnehmungen. Diese Ausnehmungen können zum Beispiel bekannte Oberflächenstrukturmerkmale, wie die Blasen in Betonoberflächen, die Risse in Wänden älterer Bauwerke oder die Wischstrukturen gespachtelter Wände, imitieren.In a preferred embodiment of the mineral wallpaper, the visible surface of the mineral wallpaper facing away from the carrier material has a predetermined surface structure with regular and / or irregular recesses. These recesses can imitate, for example, known surface structure features such as the bubbles in concrete surfaces, the cracks in the walls of older buildings or the wiping structures of plastered walls.

Bei Herstellung einer Mineralstofftapete mit Phyllosilikatzusatz wird im Rahmen des Verfahrens das feinkörnige Phyllosilikat zunächst mit dem Carbonatgesteinsmehl durchmengt, bevor dieses Gemenge mit dem Bindemittel vermischt wird. Die Masse des Phyllosilikats beträgt 5 bis 10 Prozent der Masse der Gesteinskörnungspaste.When producing mineral wallpaper with the addition of phyllosilicate, the fine-grained phyllosilicate is first mixed with the carbonate rock powder before this mixture is mixed with the binding agent. The mass of the phyllosilicate is 5 to 10 percent of the mass of the aggregate paste.

Gemäß einer Ausgestaltung des vorgeschlagenen Verfahrens beträgt der Anteil der Bindemitteldispersion in der Gesteinskörnungspaste 23 bis 33 Prozent der Masse der Gesteinskörnungspaste.According to one embodiment of the proposed method, the proportion of the binder dispersion in the aggregate paste is 23 to 33 percent of the mass of the aggregate paste.

Beim Mischen der Gesteinskörnung mit der Bindemitteldispersion und dem Wasser können zusätzlich die Pigmente zugegeben werden; der Masseanteil der Pigmente beträgt hierbei bis zu drei Prozent der Masse der Gesteinskörnungspaste.When mixing the aggregate with the binder dispersion and the water, the pigments can also be added; the mass fraction of the pigments is up to three percent of the mass of the aggregate paste.

Der Unterschied der Masseanteile in der Gesteinskörnungspaste und der Gesteinskörnungsschicht ist durch den Trocknungsprozess bedingt. Durch die Trocknung verliert die Gesteinskörnungspaste Wasser. In der Gesteinskörnungsschicht sind - bezogen auf die Gesamtmasse - folglich höhere Anteile der jeweiligen Gesteinskörnung enthalten, als in der Gesteinskörnungspaste aus der die Gesteinskörnungsschicht hergestellt wurde. Die erfindungsgemäße Gesteinskörnungsschicht ergibt sich mithin als Endprodukt bei Verarbeitung der erfindungsgemäßen Gesteinskörnungspaste.The difference in mass proportions in the aggregate paste and the aggregate layer is due to the drying process. The aggregate paste loses water as it dries. The aggregate layer - based on the total mass - consequently contains higher proportions of the respective aggregate than in the aggregate paste from which the aggregate layer was produced. The aggregate layer according to the invention thus results as the end product when processing the aggregate paste according to the invention.

Die im Rahmen des erfindungsgemäßen Verfahrens verwendete Fertigungsunterlage kann eine Negativform mit einer vorgegebenen Oberflächenstruktur sein. Die Formoberfläche der Negativform weist (als Negativ zu der herzustellenden Sichtoberfläche der Mineralstofftapete) regelmäßige und/oder unregelmäßige Erhebungen auf. Die Negativform kann durch Abformen realer Oberflächen, wie zum Beispiel Betonelementen oder gespachtelten Wänden, hergestellt werden.The manufacturing base used in the context of the method according to the invention can be a negative form with a predetermined surface structure. The mold surface of the negative mold shows (as a negative to the Visible surface of the mineral wallpaper) has regular and / or irregular elevations. The negative form can be produced by molding real surfaces, such as concrete elements or plastered walls.

Die Erfindung ist nachfolgend anhand eines Ausführungsbeispiels und mit Bezug auf die schematische Zeichnung erläutert. Hierzu zeigt die einzige Figur die Mineralstofftapete beim Aufbringen an eine Wand. Das in die Figur eingefügte Detail verdeutlicht den Aufbau der Mineralstofftapete.The invention is explained below using an exemplary embodiment and with reference to the schematic drawing. The only figure shows the mineral wallpaper being applied to a wall. The detail inserted into the figure illustrates the structure of the mineral wallpaper.

Die Mineralstofftapete gemäß dem Ausführungsbeispiel in der Figur besteht aus dem Trägermaterial 2 und der auf dem Trägermaterial 1 aufgebrachten Gesteinskörnungsschicht 1. Das Trägermaterial 2 ist ein Glasfaservlies. Die Gesteinskörnungsschicht 1 enthält 87 Masseprozent Marmormehl und 3 Masseprozent Farbpigmente; die Marmormehlkörner sind innerhalb der Gesteinskörnungsschicht 1 mit einem Acrylatbindemittel verbunden.The mineral wallpaper according to the embodiment in the figure consists of the carrier material 2 and the one on the substrate 1 applied aggregate layer 1 . The carrier material 2 is a glass fiber fleece. The aggregate layer 1 contains 87 percent by mass of marble powder and 3 percent by mass of color pigments; the marble powder grains are within the aggregate layer 1 connected with an acrylate binder.

Die Sichtoberfläche der Mineralstofftapete besitzt die unregelmäßigen Ausnehmungen 3. Zur Herstellung dieser Ausnehmungen 3 dient die als Negativform ausgebildet Fertigungsunterlage, die die durch Abformen an einem realen Betonelement erzeugt wurde. Die so hergestellte Mineralstofftapete weist folglich die Optik des abgeformten Betonelements auf.The visible surface of the mineral wallpaper has the irregular recesses 3 . To make these recesses 3 The production base, designed as a negative form, is used, which was created by molding on a real concrete element. The mineral wallpaper produced in this way consequently has the appearance of the molded concrete element.

BezugszeichenlisteList of reference symbols

11
GesteinskörnungsschichtAggregate layer
22
TrägermaterialCarrier material
33
AusnehmungRecess

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDED IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant was generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturPatent literature cited

  • DE 102008032204 A1 [0004, 0007]DE 102008032204 A1 [0004, 0007]
  • DE 102010061869 A1 [0005]DE 102010061869 A1 [0005]
  • GB 1162991 A [0006, 0007]GB 1162991 A [0006, 0007]
  • EP 0131064 A1 [0006]EP 0131064 A1 [0006]
  • EP 2360025 A2 [0006]EP 2360025 A2 [0006]
  • DE 10340238 A1 [0006]DE 10340238 A1 [0006]
  • DE 102017119048 A1 [0007]DE 102017119048 A1 [0007]

Claims (12)

Mineralstofftapete, umfassend eine auf einem flexiblen textilen Trägermaterial (2) aufgebrachte Gesteinskörnungsschicht (1), wobei die Mineralstofftapete eine Dicke von bis zu 1,5 mm aufweist, dadurch gekennzeichnet, dass die makroporenfrei ausgebildete Gesteinskörnungsschicht (1) einen Masseanteil von 71 bis 90 Prozent Gesteinsmehl aus Carbonatgestein aufweist, wobei die Gesteinskörner in der Gesteinskörnungsschicht (1) mittels eines homogen verteilten Bindemittels verbunden sind.Mineral wallpaper, comprising an aggregate layer (1) applied to a flexible textile carrier material (2), the mineral wallpaper having a thickness of up to 1.5 mm, characterized in that the macropore-free aggregate layer (1) has a mass fraction of 71 to 90 percent Has rock powder made of carbonate rock, the rock grains being connected in the rock grain layer (1) by means of a homogeneously distributed binder. Mineralstofftapete nach Anspruch 1, dadurch gekennzeichnet, dass der Anteil des Bindemittels in der Gesteinskörnungsschicht (1) 6 bis 14 Prozent der Masse der Gesteinskörnungsschicht (1) beträgt.Mineral wallpaper after Claim 1 , characterized in that the proportion of the binder in the aggregate layer (1) is 6 to 14 percent of the mass of the aggregate layer (1). Mineralstofftapete nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Gesteinskörnungsschicht (1) ein feinkörniges Phyllosilikat mit einem Anteil von 7 bis 13 Prozent der Masse der Gesteinskörnungsschicht (1) enthält.Mineral wallpaper after Claim 1 or 2 , characterized in that the aggregate layer (1) contains a fine-grain phyllosilicate with a proportion of 7 to 13 percent of the mass of the aggregate layer (1). Mineralstofftapete nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die Gesteinskörnungsschicht (1) einen Pigmentzusatz von bis zu fünf Prozent der Masse der Gesteinskörnungsschicht (1) aufweist.Mineral wallpaper according to one of the Claims 1 until 3 , characterized in that the aggregate layer (1) has a pigment addition of up to five percent of the mass of the aggregate layer (1). Mineralstofftapete nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass das Bindemittel ein Acrylat ist.Mineral wallpaper according to one of the Claims 1 until 4th , characterized in that the binder is an acrylate. Mineralstofftapete nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das textile Trägermaterial (2) ein Glasfaservlies ist.Mineral wallpaper according to one of the Claims 1 until 5 , characterized in that the textile carrier material (2) is a glass fiber fleece. Mineralstofftapete nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die dem Trägermaterial (2) abgewandte Sichtoberfläche der Mineralstofftapete eine vorgegebene Oberflächenstruktur mit regelmäßigen und/oder unregelmäßigen Ausnehmungen (3) aufweist.Mineral wallpaper according to one of the Claims 1 until 6th , characterized in that the visible surface of the mineral wallpaper facing away from the carrier material (2) has a predetermined surface structure with regular and / or irregular recesses (3). Verfahren zur Herstellung einer Mineralstofftapete nach einem Ansprüche 1 bis 7, gekennzeichnet durch die Verfahrensschritte: a) Mischen einer Gesteinskörnung mit einer wässrigen Bindemitteldispersion und Wasser zu einer klumpen- und porenfreien, homogenen Gesteinskörnungspaste, wobei die Gesteinskörnung Gesteinsmehl aus Carbonatgestein ist und der Anteil der Gesteinskörnung in der Gesteinskörnungspaste 51 bis 70 Prozent der Masse der Gesteinskörnungspaste beträgt, b) Aufstreichen der Gesteinskörnungspaste auf eine Fertigungsunterlage, c) Abziehen der Gesteinskörungspaste auf eine homogene Dicke, c) Aufbringen des flexiblen textilen Trägermaterials (2) auf die Gesteinskörnungspaste, d) Einarbeiten des Trägermaterials (2) in die Gesteinskörnungspaste unter Ausbildung eines Tapetengrünlings mit homogener Dicke, e) Trocknen des Tapetengrünlings unter Ausbildung der Mineralstofftapete, und f) Abnehmen der Mineralstofftapete von der Fertigungsunterlage.Process for the production of a mineral wallpaper according to a Claims 1 until 7th , characterized by the process steps: a) Mixing an aggregate with an aqueous binder dispersion and water to form a lump-free and pore-free, homogeneous aggregate paste, the aggregate being rock powder from carbonate rock and the proportion of aggregate in the aggregate paste being 51 to 70 percent of the mass of the aggregate paste b) spreading the aggregate paste onto a production base, c) peeling off the aggregate paste to a homogeneous thickness, c) applying the flexible textile carrier material (2) to the aggregate paste, d) incorporating the carrier material (2) into the aggregate paste to form a green wallpaper with a homogeneous thickness, e) drying the green wallpaper to form the mineral wallpaper, and f) removing the mineral wallpaper from the production base. Verfahren nach Anspruch 8, dadurch gekennzeichnet, dass der Gesteinskörnung vor dem Mischen mit der wässrigen Bindemitteldispersion ein Zuschlag von feinkörnigen Phyllosilikat beigemengt wird, wobei der Anteil des Phyllosilikatzuschlags nach Herstellung der Gesteinskörnungspaste 5 bis 10 Prozent der Masse der Gesteinskörnungspaste beträgt.Procedure according to Claim 8 , characterized in that an aggregate of fine-grain phyllosilicate is added to the aggregate prior to mixing with the aqueous binder dispersion, the proportion of the phyllosilicate aggregate being 5 to 10 percent of the mass of the aggregate paste after the aggregate paste has been produced. Verfahren nach Anspruch 8 oder 9, dadurch gekennzeichnet, dass der Anteil der Bindemitteldispersion in der Gesteinskörnungspaste 23 bis 33 Prozent der Masse der Gesteinskörnungspaste beträgt.Procedure according to Claim 8 or 9 , characterized in that the proportion of the binder dispersion in the aggregate paste is 23 to 33 percent of the mass of the aggregate paste. Verfahren nach einem der Ansprüche 8 bis 10, dadurch gekennzeichnet, dass beim Mischen der Gesteinskörnung mit der Bindemitteldispersion und dem Wasser zusätzlich Pigmente zugegeben werden, wobei der Masseanteil der Pigmente bis zu drei Prozent der Masse der Gesteinskörnungspaste beträgt.Method according to one of the Claims 8 until 10 , characterized in that when the aggregate is mixed with the binder dispersion and the water, additional pigments are added, the mass fraction of the pigments being up to three percent of the mass of the aggregate paste. Verfahren nach einem der Ansprüche 8 bis 11, dadurch gekennzeichnet, dass die Fertigungsunterlage eine Negativform mit einer vorgegebenen Oberflächenstruktur ist, wobei die Formoberfläche der Negativform regelmäßige und/oder unregelmäßige Erhebungen aufweist.Method according to one of the Claims 8 until 11 , characterized in that the production base is a negative mold with a predetermined surface structure, the mold surface of the negative mold having regular and / or irregular elevations.
DE102021101160.4A 2020-01-21 2021-01-20 Mineral wallpaper and process for their production Pending DE102021101160A1 (en)