DE102008013020A1 - Adhesive, preferably dispersion-parquet-adhesive, useful as anti-slip coating for smooth steps or floor tiles in both indoor and outdoor applications, comprises binder, heavy fillers, light fillers, resin and/or resin ester, and water - Google Patents

Adhesive, preferably dispersion-parquet-adhesive, useful as anti-slip coating for smooth steps or floor tiles in both indoor and outdoor applications, comprises binder, heavy fillers, light fillers, resin and/or resin ester, and water Download PDF

Info

Publication number
DE102008013020A1
DE102008013020A1 DE102008013020A DE102008013020A DE102008013020A1 DE 102008013020 A1 DE102008013020 A1 DE 102008013020A1 DE 102008013020 A DE102008013020 A DE 102008013020A DE 102008013020 A DE102008013020 A DE 102008013020A DE 102008013020 A1 DE102008013020 A1 DE 102008013020A1
Authority
DE
Germany
Prior art keywords
adhesive
weight
fillers
adhesive according
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102008013020A
Other languages
German (de)
Inventor
Franz Turtenwald
Heidi Dr. Hummel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BTF PRODUKTENTWICKLUNGS und VE
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH
Original Assignee
BTF PRODUKTENTWICKLUNGS und VE
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BTF PRODUKTENTWICKLUNGS und VE, BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH filed Critical BTF PRODUKTENTWICKLUNGS und VE
Priority to DE102008013020A priority Critical patent/DE102008013020A1/en
Publication of DE102008013020A1 publication Critical patent/DE102008013020A1/en
Withdrawn legal-status Critical Current

Abstract

Adhesive, preferably dispersion-parquet-adhesive based on water, comprises binder (10-80 wt.%), heavy fillers (= 30 wt.%), light fillers (= 40 wt.%), resin and/or resin ester (= 30 wt.%), and water (10-60 wt.%), where the adhesive is hardened at normal room temperature.

Description

Die Erfindung betrifft einen Klebstoff, insbesondere Dispersions-Parkettkleber auf Wasser-Basis, der bei normaler Zimmertemperatur aushärtet.The The invention relates to an adhesive, in particular dispersion parquet adhesive Water-based, which cures at normal room temperature.

Handelsübliche Parkettkleber gibt es als lösemittelfreie Klebstoffe in Form von Pulverklebstoffen, die mit Wasser angerührt werden, sowie in Form von Dispersions-Klebstoffen, als lösemittelhaltige Klebstoffe, wie Kunstharz-Klebstoffe, als Reaktionsharz-Klebstoffe in Form von Ein- und Zweikomponentenklebern, als Schmelzkleber oder als Steinkohleteerkleber, sowie als Leime in Form von Kaltleim, Holzleim oder Knochenleim.Commercially available parquet glue is available as solvent-free Adhesives in the form of powder adhesives, which are mixed with water, and in the form of dispersion adhesives, as solvent-borne adhesives, like synthetic resin adhesives, as reactive resin adhesives in the form of one- and two-component adhesives, as a hot melt adhesive or as a coal tar adhesive, as well as glues in the form of cold glue, wood glue or bone glue.

Infolge der besonderen Eigenschaften von Holz sind an Parkettkleber Anforderungen zu stellen, die sich von den Anforderungen, die an normale Kleber gestellt werden, wesentlich unterscheiden. Holz ist kein toter Werkstoff sondern es lebt und arbeitet. Deshalb muß ein Klebstoff, der für das Verkleben von Parkett, d. h. für das Verkleben von Holz verwendet wird, nach dem Aushärten flexibel bleiben. Außerdem soll der Klebstoff quellungsarm und gut verstreichbar sein und schnell abbinden. Der für das Verkleben von Parkett vorgesehene Klebstoff sollte auch gute Haftungseigenschaften besitzen und nach dem Aushärten gegen mechanische Beanspruchungen und Belastungen bzw. Störungen und gegen Benetzung mit Wasser unempfindlich sein.As a result The special properties of wood are due to parquet glue requirements to make that different from the requirements of normal glue be substantially different. Wood is not a dead material but it lives and works. Therefore, an adhesive must be used for bonding of parquet, d. H. For The bonding of wood is used after curing flexible stay. Furthermore the adhesive should be low in swelling and easy to spread and fast to set. The for gluing parquet provided adhesive should also be good Have adhesion properties and after curing against mechanical stress and loads or disturbances and insensitive to wetting with water.

Der Erfindung liegt in Kenntnis dieser Gegebenheiten die Aufgabe zugrunde, einen Klebstoff, insbesondere Dispersions-Parkettkleber, zu schaffen, der Schall dämmende und Schwingungen dämpfende sowie Wärme isolierende Eigenschaften besitzt.Of the In the knowledge of these circumstances, the invention is based on the object to provide an adhesive, in particular dispersion parquet adhesive, the sound-insulating and vibrations dampening as well as heat has insulating properties.

Diese Aufgabe wird erfindungsgemäß durch die Merkmale des Anspruches 1, d. h. dadurch gelöst, dass der Klebstoff die folgende Zusammensetzung aufweist:
10–80 Gew-% Bindemittel,
≤ 30 Gew-% schwere Füllstoffe,
≤ 40 Gew-% leichte Füllstoffe,
≤ 30 Gew-% Harz und/oder Harzester,
10–60 Gew-% Wasser.This object is achieved by the features of claim 1, ie, characterized in that the adhesive has the following composition:
10-80% by weight of binder,
≤ 30% by weight heavy fillers,
≤ 40% by weight light fillers,
≤ 30% by weight of resin and / or rosin ester,
10-60% by weight of water.

Der erfindungsgemäße Klebstoff weist den Vorteil auf, dass er durch die Kombination harter und weicher Dispersionen mit einem geeigneten Harz und/oder Harzester nach dem Aushärten flexibel bleibt. Das wird durch passend ausgewählte Füllstoffe begünstigt. Ein weiterer Vorteil besteht darin, dass der erfindungsgemäße Klebstoff emissionsarm und geruchsneutral ist. Das Abbinden des Klebstoffes erfolgt primär durch Wasserabgabe. Dabei handelt es sich um einen irreversiblen Vorgang.Of the adhesive according to the invention has the advantage of being harder and softer due to the combination Dispersions with a suitable resin and / or rosin ester after Harden remains flexible. This is favored by suitably selected fillers. Another advantage is that the adhesive according to the invention low emission and odorless. The setting of the adhesive is primary by water delivery. This is an irreversible Process.

Der erfindungsgemäße Klebstoff besitzt eine cremige weiche Konsistenz und lässt sich bspw. mit einem Zahnspachtel auf einen Untergrund gut auftragen und verteilen. Der Klebstoff besteht überwiegend aus natürlichen Materialien und ist frei von organischen Lösungsmitteln und Weichmachern. Das ist unter Umweltgesichtspunkten vorteilhaft.Of the adhesive according to the invention has a creamy soft texture and can be, for example, with a toothed spatula Apply well to a substrate and distribute. The adhesive consists predominantly of natural Materials and is free of organic solvents and plasticizers. This is advantageous from an environmental point of view.

Bevorzugte Aus- bzw. Weiterbildungen des erfindungsgemäßen Klebstoffes sind in den Unteransprüchen gekennzeichnet.preferred Training or further developments of the adhesive according to the invention are in the dependent claims characterized.

Im Wesentlichen beruht die Zusammensetzung des erfindungsgemäßen Klebstoffes darauf, dass ein wässriges Bindemittel-System zusammen mit speziellen Füllstoffen verwendet wird, wobei trotz der Verflüchtigung des Wassers das Volumen des Klebstoffes sich nur wenig verkleinert. Die Schwindung liegt bei ca. 10%. Der ausgehärtete Klebstoff geht bei Einwirkung von Wasser nicht wieder in seinen Ausgangszustand über, sondern er bleibt unlöslich und fest; er ist trotzdem flexibel.in the Essentially, the composition of the adhesive according to the invention is based that an aqueous Binder system is used together with special fillers, taking despite the volatilization of water the volume of the adhesive is only slightly reduced. The shrinkage is about 10%. The cured adhesive is exposed not returning to its original state of water, but he remains insoluble and firm; He is still flexible.

Bei dem Bindemittel des erfindungsgemäßen Klebstoffes handelt es sich um Stoffe, welche die Füllstoffe untereinander sowie mit einem Untergrund zu binden vermögen. Bei dem Bindemittel handelt es sich um wässrige Dispersionen von Polymeren und Copolymeren, sowie um Kunstharze und Cellulose- oder Stärke-Derivate. Die Ester klebrig machender Harze dienen zur Erhöhung der Klebrigkeit des erfindungsgemäßen Klebstoffes. Die Harze und/oder Harzester sind mit dem verwendeten Bindemittel und mit den verwendeten Füllstoffen des erfindungsgemäßen Klebstoffes kompatibel.at the binder of the adhesive according to the invention is substances, which are the fillers capable of binding with one another and with a substrate. at The binder is aqueous dispersions of polymers and copolymers, as well as synthetic resins and cellulose or starch derivatives. The esters of tackifying resins serve to increase the tackiness of the adhesive according to the invention. The resins and / or rosin esters are with the binder used and with the fillers used the adhesive of the invention compatible.

Als Füllstoffe werden schwere mineralische Füllstoffe und leichte Füllstoffe eingesetzt. Bei den schweren mineralischen Füllstoffen handelt es sich vorzugsweise um Tonerden, Kreide, Silikate, Sande, Eisenoxide. Bei den leichten Füllstoffen kann es sich um Hohlkugeln aus Glas, Keramik oder Kunststoff, um Fasern aus Cellulose oder Kunststoff, um Pulver aus Kunststoff und Gummimehl, um Bims, Diatomeenerde, Perlite und/oder Korkmehl und Treibgas-gefüllte, expandierte Hohlkugeln (z. B. Expancel) handeln.When fillers become heavy mineral fillers and light fillers used. The heavy mineral fillers are preferably Clays, chalk, silicates, sands, iron oxides. At the light fillers may be hollow spheres of glass, ceramic or plastic, around Fibers of cellulose or plastic, powder of plastic and Rubber dust, around pumice, diatomaceous earth, perlite and / or cork powder and LPG-filled, expanded hollow spheres (eg Expancel) act.

Bei dem erfindungsgemäßen Klebstoff werden die Füllstoffe derartig gewählt, dass sowohl zerklüftete und unregelmäßige als auch glatte, runde Partikel in einem solchen Verhältnis verwendet werden, dass die verschiedenen Partikel ineinander verhaken.at the adhesive according to the invention become the fillers so chosen that both jagged and irregular as also uses smooth, round particles in such a ratio be that the different particles interlock.

Entsprechend dem jeweiligen Gehalt an leichten Füllstoffen kann die Dichte des erfindungsgemäßen Klebstoffes zwischen 0,1 und 1,3 g/cm3 betragen.Depending on the respective content of light fillers, the density of the adhesive according to the invention may be between 0.1 and 1.3 g / cm 3 .

Zweckmäßig kann es sein, wenn der erfindungsgemäße Klebstoff Zusatzstoffe enthält. Bei dem Zusatzstoff kann es sich um ein Konservierungsmittel handeln, das zum Unterdrücken einer Schimmelbildung vorgesehen ist. Bei dem besagten Konservierungsmittel kann es sich bspw. um Chloracetamid, Thiazolinon- und Isothiazolinon-Derivate sowie Bronopol und Mischungen hieraus handeln.Appropriately it may be when the adhesive according to the invention Contains additives. The additive may be a preservative, that to suppress a mildew is provided. For the said preservative it may, for example, to chloroacetamide, thiazolinone and isothiazolinone derivatives and Bronopol and mixtures of these act.

Desgleichen ist es möglich, dass der Klebstoff außerdem Farbmittel enthält. Hierbei kann es sich z. B. um wässrige Pigmentdispersionen oder Pulverpigmente und/oder um Präparationen aus Eisenoxid handeln. Auf das besagte Farbmittel kann selbstverständlich auch verzichtet werden; es dient lediglich einer gewünschten Farbgebung des erfindungsgemäßen Klebstoffes.Similarly Is it possible, that the glue as well Contains colorant. This may be z. B. aqueous Pigment dispersions or powder pigments and / or preparations made of iron oxide. On the said colorant can of course also be waived; it merely serves for a desired coloring of the adhesive according to the invention.

Um ein unerwünschtes Kleben an Händen und an Werkzeugen sowie eine oberflächliche Hautbildung zu vermeiden bzw. zumindest zu verringern und die Offen-Zeit des Klebstoffes zu verlängern, kann der Klebstoff Wachsemulsionen und/oder Öle enthalten.Around an undesirable Sticking to hands and on tools as well as a superficial Skin formation to avoid or at least reduce and the open-time of the adhesive can extend the adhesive contains wax emulsions and / or oils.

Die Herstellung des erfindungsgemäßen Klebstoffes erfolgt durch Rühren der erfindungsgemäßen Zusammensetzung bspw. in einem Schaufelmischer oder in einem Dissolver. Um ein unerwünschtes Eindicken zu verhindern, wird der hergestellte Klebstoff zweckmäßigerweise in ein Behältnis abgefüllt, das dann luftdicht verschlossen wird. Bei dem Behältnis handelt es sich z. B. um einen Plastikbeutel.The Production of the adhesive according to the invention is done by stirring the composition of the invention for example in a paddle mixer or in a dissolver. To an undesirable Preventing thickening, the adhesive produced is expediently bottled in a container that then sealed airtight. The container is z. B. around a plastic bag.

Nachfolgend wird der erfindungsgemäße Klebstoff an Hand einiger Rezepturbeispiele verdeutlicht, wobei es sich jedoch versteht, dass die Erfindung nicht auf die angegebenen Rezepturbeispiele beschränkt sondern durch die nachfolgenden Ansprüche bestimmt ist.following becomes the adhesive according to the invention illustrated by some recipe examples, but it is understands that the invention is not limited to the formulation examples given but by the following claims is determined.

Rezepturbeispiel 1:Formulation Example 1

  • 10 Gew-% Polyvinylalkohol10% by weight of polyvinyl alcohol
  • 10 Gew-% Kaolin10% by weight of kaolin
  • 8 Gew-% Korkmehl8% by weight cork flour
  • 2 Gew-% Expancel2% by weight of Expancel
  • 5 Gew-% Cellulosefasern5% by weight of cellulose fibers
  • 50 Gew-% Styrol-Acrylat Dispersion50% by weight of styrene-acrylate dispersion
  • 0,2 Gew-% Konservierungsmittel0.2% by weight preservative
  • 14,8 Gew-% Wasser.14.8% by weight of water.

Rezepturbeispiel 2:Formulation example 2:

  • 22 Gew-% Acrylatdispersion22% by weight of acrylate dispersion
  • 5 Gew-% Kaolinerde5% by weight kaolin earth
  • 1 Gew-% Cellulosefasern1% by weight of cellulose fibers
  • 5 Gew-% Korkmehl5% by weight cork flour
  • 5,5 Gew-% Perlite5.5% by weight perlite
  • 3 Gew-% Expancel3% by weight of Expancel
  • 15 Gew-% Harzester15% by weight of rosin ester
  • 5 Gew-% Vinylacatat Dispersion5% by weight of vinyl acetate dispersion
  • 0,2 Gew-% Konservierungsmittel0.2% by weight preservative
  • 38,3 Gew-% Wasser38.3% by weight of water

Rezepturbeispiel 3:Formulation example 3:

  • 15 Gew-% feinkörniger Sand15% by weight finer grain sand
  • 8 Gew-% Perlite8% by weight of perlite
  • 2 Gew-% Korkmehl2% by weight cork flour
  • 7 Gew-% Cellulosefasern7% by weight of cellulose fibers
  • 4,5 Gew-% Mikrohohlkugeln4.5% by weight hollow microspheres
  • 0,5 Gew-% Expancel0.5% by weight of Expancel
  • 8 Gew-% Harzester8% by weight of rosin ester
  • 22 Gew-% Acrylatdispersion22% by weight of acrylate dispersion
  • 0,2 Gew-% Konservierungsmittel0.2% by weight preservative
  • 32,8 Gew-% Wasser.32.8% by weight of water.

Rezepturbeispiel 4:Formulation Example 4

  • 15 Gew-% Tonerde15% by weight alumina
  • 5 Gew-% Perlite5% by weight of perlite
  • 2 Gew-% Korkmehl2% by weight cork flour
  • 2,5 Gew-% Cellulosefasern2.5% by weight of cellulose fibers
  • 4,5 Gew-% Mikrohohlkugeln4.5% by weight hollow microspheres
  • 0,5 Gew-% Expancel0.5% by weight of Expancel
  • 0,5 Gew-% Carboxymethylcellulose (CMC)0.5% by weight of carboxymethylcellulose (CMC)
  • 8 Gew-% Harzester8% by weight of rosin ester
  • 9 Gew-% PE-Wachsemulsion9% by weight PE wax emulsion
  • 3 Gew-% Weißöl3% by weight of white oil
  • 9 Gew-% Polyvinylalkohol9% by weight of polyvinyl alcohol
  • 18 Gew-% Acrylatdispersion18% by weight of acrylate dispersion
  • 0,2 Gew-% Konservierungsmittel0.2% by weight preservative
  • 22,8 Gew-% Wasser.22.8% by weight of water.

Der erfindungsgemäße Klebstoff härtet bei normaler Zimmertemperatur aus und besitzt durch die Kombination von schweren und leichten Füllstoffen, insbesondere durch die Kombination mit den leichten Füllstoffen Perlite, Korkmehl und Cellulosefasern Wärme dämmende und Schall schluckende Eigenschaften bei geringem Schwund. Der Klebstoff bleibt durch die Kombination verschiedener Dispersionen und Cellulosederivate mit entsprechend ausgewählten Füllstoffen nach dem Aushärten flexibel.Of the adhesive according to the invention cures at normal room temperature and owns by the combination heavy and light fillers, in particular by the combination with the light fillers Perlite, cork powder and cellulose fibers heat-insulating and sound-absorbing properties at low shrinkage. The glue stays through the combination various dispersions and cellulose derivatives with corresponding chosen fillers after curing flexible.

Der erfindungsgemäße Klebstoff kann auch als Antirutsch-Belag bspw. für glatte Stufen oder auf Bodenfliesen sowohl im Innen- als auch im Außenbereich verwendet werden.Of the adhesive according to the invention can also be used as anti-slip coating eg for smooth steps or on floor tiles both indoors and outdoors be used.

Es hat sich gezeigt, dass der erfindungsgemäße Klebstoff bspw. auch als Montagehilfe für Kork- und Holzfaser-Dämmplatten sowohl im Innen- als auch im Außenbereich von Gebäuden als Korkfassaden-Kleber, insbesondere im Holzhausbereich verwendet werden kann. Er wird z. B. mittels einer 2 mm Zahnspachtel auf den Untergrund aufgetragen, wonach dann unverzüglich bspw. Fassaden-Dämmplatten montiert werden können. Nach kurzer Zeit sind die Dämmplatten dann nicht mehr vom Untergrund lösbar. Dämmplatten können auch in mehreren Lagen miteinander verklebt werden, um bspw. Possen und Stuckelemente zu realisieren. Bei Dämmplatten mit Verzahnungen kann der erfindungsgemäße Klebstoff auf die Verzahnungen aufgetragen werden, um eine ausgezeichnete Flankenhaften zu bewirken. Bei Versuchen, die Dämmplatten vom Untergrund zu lösen, wurde der Bruch immer in den Dämmplatten und nicht im Kleber oder am Untergrund festgestellt.It has been found that the adhesive according to the invention can also be used, for example, as an assembly aid for cork and wood-fiber insulation panels in the interior and exterior of buildings as cork facade adhesives, in particular in the field of wooden houses. He will z. B. applied by means of a 2 mm notched trowel on the ground, after which then immediately, for example. Facade Dämmplat can be mounted. After a short time the insulation boards are then no longer solvable from the ground. Insulating boards can also be glued together in several layers to realize, for example, antics and stucco elements. In the case of insulation boards with toothing, the adhesive according to the invention can be applied to the toothings in order to produce an excellent flanking effect. In attempts to loosen the insulation boards from the substrate, the break was always found in the insulation boards and not in the adhesive or on the substrate.

Claims (14)

Klebstoff, insbesondere Dispersions-Parkettkleber auf Wasser-Basis, der bei normaler Zimmertemperatur aushärtet, dadurch gekennzeichnet, dass der Klebstoff die folgende Zusammensetzung aufweist: 10–80 Gew-% Bindemittel, ≤ 30 Gew-% schwere Füllstoffe, ≤ 40 Gew-% leichte Füllstoffe, ≤ 30 Gew-% Harz und/oder Harzester, 10–60 Gew-% Wasser.Adhesive, in particular water-based dispersion parquet adhesive, which cures at normal room temperature, characterized in that the adhesive has the following composition: 10-80% by weight of binder, ≤ 30% by weight heavy fillers, ≤ 40% by weight light Fillers, ≤ 30% by weight of resin and / or rosin ester, 10-60% by weight of water. Klebstoff nach Anspruch 1, dadurch gekennzeichnet, dass das Bindemittel eine wässrige Dispersion von Polymeren und Copolymeren ist.Adhesive according to claim 1, characterized in that that the binder is an aqueous Dispersion of polymers and copolymers. Klebstoff nach Anspruch 2, dadurch gekennzeichnet, dass die wässrige Dispersion außerdem Kunstharze und Cellulose- oder Stärke-Derivate enthält.Adhesive according to Claim 2, characterized that the watery Dispersion also synthetic resins and cellulose or starch derivatives contains. Klebstoff nach Anspruch 1, dadurch gekennzeichnet, dass die schweren Füllstoffe mineralische Füllstoffe sind.Adhesive according to claim 1, characterized in that that the heavy fillers mineral fillers are. Klebstoff nach Anspruch 4, dadurch gekennzeichnet, dass die mineralischen Füllstoffe von Tonerde und/oder Kreide und/oder Silikaten und/oder Sanden und/oder Eisenoxiden gebildet sind.Adhesive according to claim 4, characterized in that that the mineral fillers of alumina and / or chalk and / or silicates and / or sands and / or Iron oxides are formed. Klebstoff nach Anspruch 1, dadurch gekennzeichnet, dass die leichten Füllstoffe von Pulver aus Kunststoff und/oder Gummimehl und/oder Bims und/oder Diatomeenerde und/oder Perlite und/oder Korkmehl und/oder Treibgas-gefüllten, expandierten Hohlkugeln (Expancel) gebildet sind.Adhesive according to claim 1, characterized in that that the light fillers of powder of plastic and / or rubber powder and / or pumice and / or Diatomaceous earth and / or perlite and / or cork powder and / or propellant gas filled, expanded hollow spheres (Expancel) are formed. Klebstoff nach Anspruch 1, dadurch gekennzeichnet, dass die leichten Füllstoffe in einer solchen Quantität enthalten sind, dass die Dichte des Klebstoffes zwischen 0,1 und 1,3 g/cm3 beträgt.Adhesive according to claim 1, characterized in that the light fillers are contained in such a quantity that the density of the adhesive is between 0.1 and 1.3 g / cm 3 . Klebstoff nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass der Klebstoff außerdem ≤ 1 Gew-% eines Zusatzstoffes enthält.Adhesive according to one of Claims 1 to 7, characterized that the adhesive also ≤ 1% by weight of a Additive contains. Klebstoff nach Anspruch 8, dadurch gekennzeichnet, dass der Zusatzstoff von einem eine Schimmelbildung unterdrückenden Konservierungsmittel gebildet ist.Adhesive according to claim 8, characterized in that that the additive of a mold suppressing Preservative is formed. Klebstoff nach Anspruch 9, dadurch gekennzeichnet, dass das Konservierungsmittel von Chloracetamid- und/oder Thiazolinon- und Isothiazolinon-Derivaten und/oder Bronopol gebildet ist.Adhesive according to Claim 9, characterized that the preservative of chloroacetamide and / or thiazolinone and isothiazolinone derivatives and / or bronopol is formed. Klebstoff nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass der Klebstoff außerdem ≤ 10 Gew-% eines Farbmittels enthält.Adhesive according to one of claims 1 to 10, characterized in that the adhesive also ≤ 10% by weight of a colorant. Klebstoff nach Anspruch 11, dadurch gekennzeichnet, dass das Farbmittel eine wässrige Pigmentdispersion und/oder Pulverpigmente und/oder eine Eisenoxid-Präparation enthält.Adhesive according to claim 11, characterized in that that the colorant is an aqueous Pigment dispersion and / or powder pigments and / or an iron oxide preparation contains. Klebstoff nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass der Klebstoff außerdem ≤ 15 Gew-% Öl und/oder Wachsemulsion enthält.Adhesive according to one of Claims 1 to 12, characterized that the adhesive also ≤ 15% by weight of oil and / or Contains wax emulsion. Klebstoff nach einem der Ansprüche 1 bis 13, dadurch gekennzeichnet, dass der Klebstoff in einem luftdicht verschlossenen Behältnis vorgesehen ist.Adhesive according to one of Claims 1 to 13, characterized that the adhesive provided in an airtight container is.
DE102008013020A 2008-03-07 2008-03-07 Adhesive, preferably dispersion-parquet-adhesive, useful as anti-slip coating for smooth steps or floor tiles in both indoor and outdoor applications, comprises binder, heavy fillers, light fillers, resin and/or resin ester, and water Withdrawn DE102008013020A1 (en)