DE102004048427B3 - Wooden material panel for wall coverings, has upper surface and lower surface of cover layer made of chippings and binders whereby filterable, silicate containing material is bound by binders to upper surface of wooden material panel - Google Patents

Wooden material panel for wall coverings, has upper surface and lower surface of cover layer made of chippings and binders whereby filterable, silicate containing material is bound by binders to upper surface of wooden material panel Download PDF

Info

Publication number
DE102004048427B3
DE102004048427B3 DE200410048427 DE102004048427A DE102004048427B3 DE 102004048427 B3 DE102004048427 B3 DE 102004048427B3 DE 200410048427 DE200410048427 DE 200410048427 DE 102004048427 A DE102004048427 A DE 102004048427A DE 102004048427 B3 DE102004048427 B3 DE 102004048427B3
Authority
DE
Germany
Prior art keywords
wood
silicate
containing material
binders
cover layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE200410048427
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Swiss Krono Tec AG
Original Assignee
Kronotec AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kronotec AG filed Critical Kronotec AG
Priority to DE200410048427 priority Critical patent/DE102004048427B3/en
Application granted granted Critical
Publication of DE102004048427B3 publication Critical patent/DE102004048427B3/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The wooden material panel e.g. oriented strand board panel, has an upper surface (1) and a lower surface of a cover layer made of chippings and binders. A filterable, silicate containing material (2) is bound by binders to the upper surface of wooden panel. The silicate containing material is used for the formation of a rough, skid-proof surface at the upper surface of the wooden panel. Independent claims are also included for the following: (A) Device for the production of the wooden material panel; and (B) Method of production of the wooden material panel.

Description

Die Erfindung betrifft eine Holzwerkstoffplatte, sowie eine Vorrichtung und ein Verfahren zur Herstellung einer Holzwerkstoffplatte, insbesondere OSB-Platte, mit einer Oberseite und einer Unterseite aus einer Deckschicht aus Spänen und Bindemittel, bei der auf der Oberseite ein siebbares, silikathaltiges Material in die Deckschicht eingepresst ist.The The invention relates to a wood-based panel, and a device and a method for producing a wood-based panel, in particular OSB board, with a top and a bottom of a cover layer shavings and binder, wherein on the top of a sieve, silicate-containing Material is pressed into the cover layer.

Eine solche Holzwerkstoffplatte ist beispielsweise aus der deutschen Patentschrift DE 861 923 B bekannt. Sowohl das silikathaltige Material als auch das zerkleinerte Holz wird mit Kunstharzlösungen beladen und ggf. getrocknet. In eine Pressform wird eine dünne Schicht des mit Kunstharz beladenen Silikates eingestreut und darauf das zerkleinerte Holz geschichtet. Anschließend wird die Platte gepresst. Solche Platten eignen sich als Wandbeläge oder Tischplatten, da sie durch die Silikate gegen das Eindringen von Wasser und beispielsweise gegen Zigarettenbrand unempfindlich sind.Such a wood-based panel is for example from the German patent DE 861 923 B known. Both the silicate-containing material and the shredded wood are loaded with synthetic resin solutions and dried if necessary. In a mold, a thin layer of the loaded with resin silicate is scattered and layered on the crushed wood. Then the plate is pressed. Such plates are suitable as wall coverings or table tops, since they are insensitive by the silicates against the ingress of water and, for example, against cigarette burn.

Holzwerkstoffplatten werden beispielsweise auch zur Beplankung und Aussteifung des Dachstuhls eines Wohnhauses nach außen verwendet. Dazu werden die Platten beispielsweise mit Schrauben, Nägeln oder Klammern an den Sparren des Dach stuhls befestigt. Anschließend erfolgt die Eindeckung des Daches mit Schindeln oder dergleichen, die auf den Holzwerkstoffplatten aufgebracht werden. Bei der Verlegung der Holzwerkstoffplatten auf den Sparren ist es notwendig, dass bereits mit den Sparren verbundene Platten von den ausführenden Handwerkern begangen werden müssen. Damit die Handwerker die Holzwerkstoffplatten, trotz der Neigung des Dachstuhles ohne abzurutschen begehen können, muss die Oberfläche der Platten rutschfest ausgebildet sein.Wood-based panels For example, the planking and stiffening of the roof truss of a residential building to the outside used. For this purpose, the plates are, for example, with screws, nails or clips attached to the rafters of the roof chair. Then done Covering the roof with shingles or the like on top the wood-based panels are applied. When laying the Wood-based panels on the rafters it is necessary that already Plates associated with the rafters committed by the exporting craftsmen Need to become. So that the craftsmen the wood-based panels, despite the inclination the roof truss can do without slipping, the surface of the Non-slip plates are formed.

Die Herstellung von Holzwerkstoffplatten, insbesondere OSB-Platten, verläuft heutzutage häufig auf kontinuierlichen Produktionsanlagen. Diese Anlagen enthalten zumeist eine Zerspanungseinrichtung, um aus Rohholz geeignete Späne für die Holzwerkstoffherstellung zu erzeugen. Die waldfrischen Späne werden in einer separaten Trocknungsvorrichtung auf die gewünschte Holzfeuchte getrocknet. Die getrockneten Späne werden anschließend in einer Sichtungsvorrichtung nach Spänen für die Deck- und Mittelschicht sortiert. Deck- und Mittelschichtspäne gelangen nach dem Durchgang durch eine Beleimvorrichtung in die Streuvorrichtung. Die Streuvorrichtung orientiert, insbesondere bei der Herstellung von OSB-Platten, die Späne und streut die beleimten Späne zu einem Formling auf das Formband. Das Formband transportiert den Holzwerkstoffformling in Richtung der Pressvorrichtung, in der die Verpressung des Holzwerkstoffformlings zu einer Holzwerkstoffplatte erfolgt.The Production of wood-based panels, especially OSB panels, extends nowadays often on continuous production lines. These plants contain usually a cutting device to chips suitable for raw wood from the wood material production to create. The fresh wood chips be in a separate drying device to the desired wood moisture dried. The dried chips will be afterwards in a sighting device after chips for the top and middle layers sorted. Cover and middle-layer chips arrive after the passage by a gluing device in the spreader. The spreader oriented, especially in the production of OSB boards, the Chips and sprinkle the glued chips to a molding on the form band. The forming belt transports the Wood material molding in the direction of the pressing device in which the Pressing of the wood material molding to a wood-based material board he follows.

Eine OSB-(Oriented Strands Board) Platte wird durch Verpressen eines mindestens dreischichtig (Deckschicht, Mittelschicht, Deckschicht) aus Holzspänen oder -partikeln (Strands) gestreuten Formlings gebildet. Dabei werden die Strands der äußeren Schichten (Deckschichten) in Produktionsrichtung ausgerichtet (Oriented). In der Mittelschicht werden die Strands quer zur Produktionsrichtung ausgerichtet. Mit Kunstharzen als Bindemittel werden die Strands unter Druck und Temperatur zu Platten verpresst. Durch das Verpressen des Formlings bildet sich zwischen Pressblech und Formling auf der Oberfläche ein dünner Film aus Kunstharz und Holzharz. Die OSB-Platte erhält dadurch eine glatte Oberfläche. Eine besonders glatte Oberfläche ergibt sich bei OSB-Platten, die auf Pressen mit Contiroll-Technologie hergestellt werden.A OSB (Oriented Strands Board) plate is made by crimping a at least three layers (top layer, middle layer, top layer) from wood chips or particles (strands) of scattered molding. It will be the strands of the outer layers (Cover layers) oriented in the direction of production (Oriented). In the middle class, the beaches become transversal to the production direction aligned. With synthetic resins as binders the beaches become pressed under pressure and temperature to plates. By pressing of the molding is formed between pressed sheet and molding on the surface a thinner one Film made of synthetic resin and wood resin. The OSB board receives thereby a smooth surface. A particularly smooth surface results in OSB boards that are based on presses with Contiroll technology getting produced.

Um rutschfeste Oberflächen bei OSB-Platten zu erzielen, kann in einer weiteren Einrichtung im Anschluss des Pressvorgangs beispielsweise ein Pottasche-Farbegemisch aufgebürstet werden oder in einer weiteren Presseinrichtung eine Struktur in die Oberfläche der Platte eingeprägt werden.Around non-slip surfaces Achieving OSB panels can be done in another facility After the pressing process, for example, a potash color mixture can be brushed or in another pressing device, a structure in the surface of Plate stamped become.

Aus der DE 101 39 864 C1 ist es bekannt, zur Erzielung einer rutschfesten Oberfläche bei OSB-Platten im Anschluss an den Pressvorgang auf der Oberseite der Platten vollflächig Raupen aus einem Kunstharz oder einem Kunststoffkleber aufzutragen. Der Auftrag des Kunstharzes oder des Kunststoffklebers erfolgt hierbei vorzugsweise in einer speziellen Sprüheinrichtung mit einer Sprühdüse.From the DE 101 39 864 C1 It is known, in order to achieve a non-slip surface in OSB boards following the pressing process on the top of the plates over the entire surface beads of a synthetic resin or a plastic adhesive to apply. The order of the synthetic resin or the plastic adhesive is preferably carried out in a special spraying with a spray nozzle.

Nachteilig an den beschriebenen Möglichkeiten, eine Platte mit rutschfesten Oberflächen auszustatten ist, dass ein zusätzlicher Arbeitsschritt mit einer zusätzlichen maschinellen Einrichtung und hohem Fertigungsaufwand erforderlich ist.adversely at the described possibilities, to equip a slab with non-slip surfaces is that an additional one Work step with an additional Machinery and high production costs required is.

Zusätzliche Maschinen, wie zum Beispiel eine Strukturpresse oder eine Sprüheinrichtung, sind sowohl in der Anschaffung als auch im Betrieb und in der Wartung kostenintensiv, so dass die Fertigungskosten für eine Platte mit rutschfester Oberfläche immer höher sein müssen, als die für eine Platte ohne rutschfeste Beschichtung.additional Machines, such as a structure press or a sprayer, are in purchase as well as in operation and maintenance costly, so the production cost of a slab with non-slip surface higher and higher have to be as the for a plate without non-slip coating.

Ausgehend von dieser Problemstellung soll eine Holzwerkstoffplatte sowie eine Vorrichtung und ein Verfahren zur Herstellung der Holzwerkstoffplatte bereitgestellt werden, die eine einfache und kostengünstige Erzeugung einer rutschfesten Oberfläche auf Holzwerkstoffplatten ermöglicht.outgoing from this problem is a wood-based panel and a Device and a method for producing the wood-based panel provided Be a simple and inexpensive generation of a non-slip Surface on Wood-based panels allows.

Zur Problemlösung zeichnet sich eine gattungsgemäße Holzwerkstoffplatte dadurch aus, dass das siebbare, silikathaltige Material durch das vorhandene Bindemittel der Holzwerkstoffplatte zur Aufrauung und Ausbildung einer rutschfesten Oberfläche an die Deckschicht der Platte gebunden ist.to Troubleshooting is a generic wood-based panel characterized in that the sieve, silicate-containing material through the existing binder of the wood-based panel for roughening and Formation of a non-slip surface on the cover layer of Plate is tied.

Die Verpressung des siebbaren, silikathaltigen Materials in die Deckschicht der Holzwerkstoffplatte erfolgt gemeinsam mit der Verpressung des Formlings.The Pressing the sieve, silicate-containing material in the top layer the wood-based panel is done together with the compression of the molding.

Vorteilhaft hieran ist, dass die Zugabe eines zusätzlichen Bindemittels für die Bindung des silikathaltigen Materials an die Plattenoberfläche nicht notwendig ist, da die Bindung durch den Pressvorgang und durch die vorhandenen Bindemittel der Holzwerkstoffplatte erfolgt.Advantageous this is because the addition of an additional binding agent for binding of the silicate-containing material to the plate surface is not is necessary because the binding by the pressing process and by the existing binder of the wood-based panel is done.

Durch diese Ausbildung können weitere Maschinen nach der Presse entfallen.By this training can no further machines are required after the press.

Da kein zusätzliches Bindemittel notwendig ist, kann die rutschfeste Oberfläche sehr kostengünstig erzeugt werden. Durch das gemeinsame Verpressen von Holzwerkstoffplatte und silikathaltigem Material können die Fertigungszeiten und die Fertigungskosten für Platten mit rutschfester Oberfläche erheblich verringert werden.There no additional Binder is necessary, the non-slip surface can be very economical be generated. By the common pressing of wood-based panel and silicate-containing material the production times and the production costs for non-slip plates surface be significantly reduced.

Damit eine ausreichende Rutschfestigkeit der Plattenoberfläche sichergestellt werden kann, ist das silikathaltige Material vorzugsweise vollflächig auf der Oberseite des Formlings aufgestreut.In order to ensured sufficient slip resistance of the disk surface can be, the silicate-containing material is preferably on the entire surface the top of the molding sprinkled.

Als silikathaltiges Material kann beispielsweise Quarzsand verwendet werden.When Silicate-containing material can be used, for example, quartz sand become.

Der Auftrag des silikathaltigen Materials auf den Formling der Holzwerkstoffplatte erfolgt vor dem Einlauf des Formlings in die Presseinrichtung, durch eine vor der Presse vorzugsweise quer zur Produktionsvorrichtung angeordneten Auftragsvorrichtung.Of the Application of the silicate-containing material to the molding of the wood-based panel takes place before the inlet of the molding in the pressing device, by a preferably arranged transversely to the production device in front of the press Applicator.

Als Auftragsvorrichtung für die silikathaltigen Materialien kann vorzugsweise ein Rüttelsieb eingesetzt werden. Die Steuerung der Auftragsvorrichtung erfolgt durch die Regelung der Press- und Formbandgeschwindigkeit. Wird die Geschwindigkeit der Presse und des Formbandes verringert, erhöht sich die Auftragsmenge des silikathaltigen Materials pro Flächeneinheit.When Application device for the silicate-containing materials may preferably be a vibrating screen be used. The control of the application device takes place by the regulation of the pressing and forming belt speed. Becomes the speed of the press and the forming belt decreases, increases the application rate of the silicate-containing material per unit area.

Eine weitere Möglichkeit zur Veränderung der Auftragsmenge besteht in der Regelung der Frequenz der Rüttelsieb, die als Auftragsvorrichtung eingesetzt werden kann.A another possibility to change the Order quantity consists in the regulation of the frequency of the vibrating screen, which can be used as an application device.

Das erfindungsgemäße Verfahren lässt sich auf alle im Flachpressverfahren hergestellte Holzwerkstoffplatten ohne Eingrenzung des Dickenbereichs anwenden.The inventive method lets up All panels made by flat pressing without Use the limitation of the thickness range.

Mit Hilfe einer Zeichnung soll ein Ausführungsbeispiel der Erfindung nachfolgend näher erläutert werden. Es zeigt:With Help a drawing to an embodiment of the invention below explained become. It shows:

1 Eine schematische Draufsicht auf die rutschfeste Oberfläche der Holzwerkstoff platte; 1 A schematic plan view of the non-slip surface of the wood-based panel;

2 einen schematischen Querschnitt der Holzwerkstoffplatte mit rutschfester Oberfläche; 2 a schematic cross section of the wood-based panel with non-slip surface;

3 eine Vorrichtung zur Herstellung der Holzwerkstoffplatte mit rutschfester Oberfläche. 3 a device for producing the wood-based panel with non-slip surface.

Auf den Formling 3 einer herkömmlichen OSB-Platte wird auf der Oberseite 1 zur Aufrauung der Oberfläche Quarzsand 2 aufgebracht. Der Quarzsand 2 wird durch ein Rüttelsieb 4 vollflächig auf der gesamten Plattenoberfläche verteilt und zusammen mit dem Formling der OSB-Platte 3 in einer Pressvorrichtung 5 unter Temperatureinfluss verpresst.On the molding 3 a conventional OSB board will be on top 1 for roughening the surface of quartz sand 2 applied. The quartz sand 2 gets through a vibrating screen 4 distributed over the entire surface of the plate and together with the molding of the OSB plate 3 in a pressing device 5 Pressed under the influence of temperature.

Die Streuung der beleimten Späne zu einem Formling 3 auf das Formband 6 ist vorab durch die Streuvorrichtung 7 erfolgt. In der Streuvorrichtung 7 erfolgt außerdem die Orientierung der Späne.The scattering of the glued chips to a molding 3 on the form band 6 is in advance through the spreader 7 he follows. In the spreader 7 In addition, the orientation of the chips takes place.

Während des Pressvorgangs wird der Quarzsand 2 durch die Pressbleche 8, 8a, 8b in die Deckschicht der Oberseite 1 des OSB-Formlings 3 eingepresst und gleichzeitig durch das vorhandene Bindemittel an die Oberfläche des OSB-Formlings 3 gebunden.During the pressing process the quartz sand becomes 2 through the press plates 8th . 8a . 8b in the top layer of the top 1 of the OSB molding 3 pressed and at the same time by the existing binder to the surface of the OSB molding 3 bound.

Die fertig gepresste OSB-Platte weist aufgrund des auf der Oberseite 1 der Platte in die Deckschichtoberfläche eingepressten und -gebunden Quarzsandes 2 eine rutschfeste Oberfläche auf.The finished pressed OSB plate has due to the top 1 the plate pressed into the top layer surface and bound quartz sand 2 a non-slip surface.

Diese OSB-Platten können zur Beplankung und Aussteifung von Dachkonstruktionen aber auch für andere Einsatzbereiche, z. B. für Paletten, Verpackungen, Regale und Industriefußböden, eingesetzt werden.These OSB boards can for planking and stiffening of roof structures but also for others Applications, eg. For example Pallets, packaging, shelves and industrial floors.

11
Oberseitetop
22
silikathaltiges Material (Quarzsand)containing silicate Material (quartz sand)
33
Formlingmolding
44
Rüttelsiebvibrating screen
55
Pressvorrichtungpressing device
66
Formbandforming belt
77
Streuvorrichtungspreader
88th
Pressblechpress plate
8a8a
Pressblechpress plate
8b8b
Pressblechpress plate

Claims (7)

Holzwerkstoffplatte, insbesondere OSB-Platte, mit einer Oberseite (1) und einer Unterseite aus einer Deckschicht aus Spänen und Bindemittel, bei der auf der Oberseite (1) ein siebbares, silikathaltiges Material (2) in die Deckschicht eingepresst ist, dadurch gekennzeichnet, dass das siebbare, silikathaltige Material (2) durch das vorhandene Bindemittel der Holzwerkstoffplatte zur Aufrauung und Ausbildung einer rutschfesten Oberfläche an die Deckschicht der Platte gebunden ist.Wood material board, in particular OSB board, with a top side ( 1 ) and a underside of a cover layer of chips and binder, in which on the top ( 1 ) a sieve, silicate-containing material ( 2 ) is pressed into the cover layer, characterized in that the sieve, silicate-containing material ( 2 ) is bonded by the existing binder of the wood-based panel for roughening and forming a non-slip surface to the cover layer of the plate. Holzwerkstoffplatte nach Anspruch 1, dadurch gekennzeichnet, dass das siebbare, silikathaltige Material (2) vollflächig über die Deckschicht der Platte verteilt ist.Wood material board according to claim 1, characterized in that the sieve, silicate-containing material ( 2 ) is distributed over the entire surface of the cover layer of the plate. Holzwerkstoffplatte nach Anspruch 1, dadurch gekennzeichnet, dass das siebbare, silikathaltige Material (2) Quarzsand ist.Wood material board according to claim 1, characterized in that the sieve, silicate-containing material ( 2 ) Is quartz sand. Vorrichtung zur Herstellung einer Holzwerkstoffplatte, insbesondere OSB-Platte nach einem oder mehreren der Ansprüche 1 bis 3, mindestens bestehend aus einer Streuvorrichtung (7), einem Formband (6) und einer Pressvorrichtung (5), dadurch gekennzeichnet, dass vor der Pressvorrichtung (5) über dem Formband (6) als Auftragsvorrichtung für silikathaltiges Material (2) quer zur Transportrichtung des Formbandes (6) ein Rüttelsieb (4) angeordnet ist.Apparatus for producing a wood-based panel, in particular OSB panel according to one or more of claims 1 to 3, at least consisting of a spreading device ( 7 ), a forming belt ( 6 ) and a pressing device ( 5 ), characterized in that before the pressing device ( 5 ) above the forming belt ( 6 ) as an applicator for siliceous material ( 2 ) transversely to the transport direction of the forming belt ( 6 ) a vibrating screen ( 4 ) is arranged. Verfahren zur Herstellung einer Holzwerkstoffplatte nach einem oder mehreren der Ansprüche 1 bis 3 aus beleimten Spänen, die in einer Streueinrichtung (7) orientiert und zu einem mehrschichtigen Formling (3) auf ein umlaufendes Formband (6) gestreut und in einer Pressvorrichtung (5) verpresst werden, dadurch gekennzeichnet, dass silikathaltiges Material (2) mit einem quer zur Transportrichtung des Formbandes (6) angeordneten Rüttelsieb (4) vor dem Verpressen auf den Formling (3) aufgestreut wird.Process for producing a wood-based panel according to one or more of claims 1 to 3 from glued chips, which are used in a spreading device ( 7 ) and to a multilayered molded article ( 3 ) on a circulating forming belt ( 6 ) and in a pressing device ( 5 ) are pressed, characterized in that silicate-containing material ( 2 ) with a transverse to the transport direction of the forming belt ( 6 ) arranged vibrating screen ( 4 ) before pressing on the molding ( 3 ) is sprinkled. Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass die Regelung der Auftragsmenge des silikathaltigen Materials (2) durch die Steuerung der Geschwindigkeit des Formbandes (6) und der Pressvorrichtung (5) erreicht wird.A method according to claim 5, characterized in that the regulation of the application amount of the silicate-containing material ( 2 ) by controlling the speed of the forming belt ( 6 ) and the pressing device ( 5 ) is achieved. Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass die Regelung der Auftragsmenge des silikathaltigen Materials (2) durch die Steuerung der Frequenz des Rüttelsiebes (4) erfolgt.A method according to claim 5, characterized in that the regulation of the application amount of the silicate-containing material ( 2 ) by controlling the frequency of the vibrating screen ( 4 ) he follows.
DE200410048427 2004-10-05 2004-10-05 Wooden material panel for wall coverings, has upper surface and lower surface of cover layer made of chippings and binders whereby filterable, silicate containing material is bound by binders to upper surface of wooden material panel Expired - Fee Related DE102004048427B3 (en)