CZ279262B6 - Bezolovnaté křišťálové sklo - Google Patents
Bezolovnaté křišťálové sklo Download PDFInfo
- Publication number
- CZ279262B6 CZ279262B6 CS901598A CS159890A CZ279262B6 CZ 279262 B6 CZ279262 B6 CZ 279262B6 CS 901598 A CS901598 A CS 901598A CS 159890 A CS159890 A CS 159890A CZ 279262 B6 CZ279262 B6 CZ 279262B6
- Authority
- CZ
- Czechia
- Prior art keywords
- oxide
- weight
- glass
- lead
- crystal glass
- Prior art date
Abstract
Bezolovnaté křišťálové sklo obsahuje v hmotnostních procentech 66 až 71 % oxidu křemičitého, 5 až 10 % oxidu sodného, 5 až 10 % oxidu draselného, 4 až 8 % oxidu vápenatého, 8 až 12 % oxidu barnatého, 0,2 až 1,5 % oxidu lithného, 0,1 až 0,7 % oxidu antimonitého a/nebo arsenitého, 0,2 až 0,7 % fluoridu nebo 0,1 až 0,4 % síranu, 0 až 4 % oxidu hořečnatého, 0 až 2 % oxidu hlinitého, 0 až 2 % oxidu boritého, 0 až 4 % oxidu zinečnatého.ŕ
Description
Řešení obsahuje 66 až 71 % hmot, oxidu křemičitého SIO2, 5 až 10 % hmot, oxidu sodného Na2O, 5 až 10 % hmot, oxidu draselného K2O, 4 až 8 % hmot, oxidu vápenatého CaO, 8 až 12 % hmot, oxidu barnatého BaO, 0,2 až 1,5 % hmot, oxidu lithného LI2O, 0,1 až 0,7 % hmot, oxidu antimonitého Sb2O3 a/nebo arsenitého AS2O3. a dále 0,2 až 0,7 % hmot, fluoridů F’ nebo 0,1 až 0,4 % hmot, síranů SO42'. S výhodou obsahuje Jednotlivě nebo v kombinaci 0,1 až 4 % hmot, oxidu hořečnatého MgO, 0,1 až 2 % hmot, oxidu hlinitého AI2O3. 0,1 až 2 % hmot, oxidu borltého B2O3 a 0,1 až 4 % hmot, oxidu zinečnatého ZnO.
Bezolovnaté křišťálové sklo
Dosavadní stav techniky
Vynález se týká bezolovnatého křišťálového skla s indexem lomu nD >1,52. Tento typ skla je vhodný především pro výrobu bižuterních polotovarů, lustrovaných ověsů, eventuálně užitkového skla.
Dosavadní stav techniky
Pro výrobu bižuterních polotovarů, lustrových ověsů, eventuálně užitkového skla se dosud používají dva základní druhy skel. Jsou to buď skla s vysokým indexem lomu nD vyšším než 1,52 obsahující více než 24 % hmot, oxidu olovnatého PbO, anebo skla s indexem lomu nD nižším než 1,52 obsahující oxid olovnatý PbO do množství 7 % hmot. Hodnota indexu lomu nD = 1,52 je hranice pro speciální křišťálová skla podle příslušných evropských norem.
Oba tyto typy skel obsahují poměrně značné množství oxidu olovnatého PbO, který je v současné době považován za zdravotně závadný, zejména při přípravě sklářského kmene a ekologicky závadný při tavení skloviny.
Podstata vynálezu
Uvedené nevýhody se odstraní nebo podstatně omezí u bezolovnatého křišťálového skla s indexem lomu nD > 1,52 podle tohoto vynálezu, jehož podstata spočívá v tom, že obsahuje 66 až 71 % hmot, oxidu křemičitého SiO2, 5 až 10 % hmot, oxidu sodného Na20, 5 až 10 % hmot, oxidu draselného K20, 4 až 8 % hmot, oxidu vápenatého CaO, 8 až 12 % hmot, oxidu barnatého BaO, 0,2 až 1,5 % hmot, oxidu lithnatého Li20, 0,1 až 0,7 % hmot, oxidu antimonitého Sb2O3 a/nebo arsenitého As2O3, a 0,2 až 0,7 % hmot, fluoridů F- nebo 0,1 až 0,4 % hmot, síranů SO4 2-.
S výhodou toto sklo obsahuje jednotlivě nebo v kombinaci 0,1 až 4 % hmot, oxidu hořečnatého MgO, 0,1 až 2 % hmot, oxidu hlinitého A12O3, 0,1 až 2 % hmot, oxidu boritého B2O3 a 0,1 až % hmot, oxidu zinečnatého ZnO.
Předností tohoto řešení je vytvoření skla bez přítomnosti zdravotně a ekologicky závadného oxidu olovnatého PbO, s indexem lomu nD >1,52, což je z hlediska brilance skla pro bižuterní výrobky, lustrové ověsy a užitkové sklo prvořadý požadavek. Dále je u tohoto typu skla minimalizována šlírovitost, která výrazně ovlivňuje vzhled a kvalitu výrobku. Odstraněním oxidu olovnatého PbO lze toto složení skla tavit na celoelektrických vanách bez použití pasivace molybdenových topných elektrod, takže dochází ke zlepšení hygienických podmínek v pracovním prostředí sklářských provozů. Velmi dobrých optických vlastností skla, t.j. indexu
-1CZ 279262 B6 lomu nD, disperze np - nD, Abbého čísla, také dobré odolnosti skla proti vodě, současně i výhodných tvarovacích podmínek skloviny, a zušlechťovacích vlastností vlastností skla, jako je obrusnost a leštitelnost, bylo dosaženo volbou optimální kombinace oxidů. Další výhodou tohoto typu skla je skutečnost, že teplota tavení se pohybuje v oblasti kolem 1 400°C, což je nižší hodnota než u dosud používaných typů křišťálových skel.
Příklady provedení vynálezu
Vynález bude blíže osvětlen na následujících příkladech provedení .
| Příklad č. | 1 | 2 | 3 |
| Složky skla | Obsah | v %. hmot. | |
| oxid křemičitý S1O2 | 69,05 | 70,56 1 | 67,30 |
| oxid sodný Na20 | 8,28 | 7,19 | 8,30 |
| oxid draselný K20 | 7,39 | 6,34 | 7,80 |
| oxid vápenatý CaO | 5,40 | 5,48 | 4,60 |
| oxid barnatý BaO | 8,56 | 9,41 | 8,10 |
| oxid lithný Li2O | 0,42 | 0,25 | 1,10 |
| oxid antimonitý Sb2O3 | 0,48 | 0,15 | |
| oxid arsenitý As20 | 0,30 | ||
| fluoridy F- | 0,42 | 0,62 | |
| sírany SO4 2- | 0,20 | ||
| oxid hořečnatý MgO | 1,70 | ||
| oxid hlinitý A12O3 | 0,30 | ||
| oxid boritý B2O3 | 0,10 | ||
| oxid zinečnatý ZnO | 0,20 | ||
| Hydrolytická odolnost | |||
| v ml (C=0,01 mol . I-1) HCL | 1,29 | 0,89 | 1,18 |
| index lomu | 1,522 | 1,521 | 1,521 |
| Hydrolytická odolnost | skla byla u | všech příkladů | měřena |
podle ČSN 700531 při spotřebě ml HCL, o koncentraci 0,01 mol.I”1, na 1 g drtě skla. Z utaveného skla podle příkladu 1 byly vytvarovány výlisky pro výrobu šatonu, které po vybroušení měly vynikající vizuální vlastnosti. Ze skla podle příkladu 2 byly lisovány bižuterní výrobky a lisofoukáním připraveny flakony, výborného vzhledu. Ze skla podle příkladu 3 byly vytvarovány polotovary pro užitkové broušené sklo.
Průmyslová využitelnost
Řešení je vhodné pro bižutérii, lustrové ověsy a užitkové sklo.
-2CZ 279262 B6
PATENTOVÉ
NÁROKY
Claims (2)
1. Bezolovnaté křišťálové sklo na bázi oxidu křemičitého SiO2, oxidu sodného Na2O, oxidu draselného K2O, oxidu vápenatého CaO, oxidu bamatého BaO, a oxidu lithného Li2O, vyznačující se tím, že obsahuje
2. Bezolovnaté křišťálové sklo podle nároku 1, vyznačuj íc í se tím, že obsahuje jednotlivě nebo v kombinaci
Konec dokumentu