CS274117B1 - Glass with high manganese content suitable especially for recalibration standards production - Google Patents
Glass with high manganese content suitable especially for recalibration standards production Download PDFInfo
- Publication number
- CS274117B1 CS274117B1 CS415089A CS415089A CS274117B1 CS 274117 B1 CS274117 B1 CS 274117B1 CS 415089 A CS415089 A CS 415089A CS 415089 A CS415089 A CS 415089A CS 274117 B1 CS274117 B1 CS 274117B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- oxide
- glass
- weight
- recalibration
- iron
- Prior art date
Description
zejména k výrobě rekalibračnich standardů (57) sklo vykazuje dostatečnou chemickou stálost a homogenitu, výrazně vyšěi výtěžnost než jiná skla s vysokým obsahem manganu, dobrou tavitelnost. Obsahuje v procentech hmotnosti 30 až 40 oxidu manganatého MnO, 1 až 8 oxidu draselného KgO, 1 až 8 oxidu hořečnatého MgO, 1 až 10 oxidu zinečnatého ZnO/ 1 až 8 oxidu boritého, B20g, až 16 oxidu hlinitého Al203 a 30 až 40 oxidu křemičitého Si02« Dále může sklo β výhodou obsahovat v procentech hmotnosti nejméně jeden oxid prvku ze skupiny zahrnující lithium Li 0,1 až 5/ sodík Na 0,1 až 10, vápnik Ca 0,1 až 10/ stroncium Sr 0,1 až 10, baryum Ba 0,1 až 10, yttrium Y 0,1 až 10, lanthan La a lanthanoidy 0,1 až 10/ cér Ce 0/1 až 5/ cín Sn 0/1 až 5, olovo Pb 0,1 až 10/ foafor P 0,1 až 10, arsen As 0,1 až 5/ antimon Sb 0/1 až 5, bizmut Bi 0/1 až 5, chrom Cr 0/1 až 3, molybden Mo 0,1 až 5, wolfram W 0/1 až 5, železo Fe 0,1 až 10, kobalt Co 0/1 až 10/ nikl Ni Oyl až 10, thorium Th 0,1 až 5/ uran U 0,1 až 5, měí Cu 0,1 až 5/ stříbro Ag 0/1 až 3, kadmium Cd 0,1 až 5, titan Ti 0,1 až 10, zirkonium Zr 0,1 až 5,' vanad V 0,1 až 5, přičemž celkový obsah uvedených oxidů čini 0,1 až 15* Dále může sklo β výhodou obsahovat v procentech hmotnoeti 0,1 až 4 fluoridu draselného KF,
| (13) | Bl | 5 |
| (51) | Int.. C 03 C 03 | Cl. C 3/066 C 4/00 |
CS 274117 Bl
Vynólez se týká složeni skla š vyáókým obsahem manganu, které Je vhodné zejména k výrobě rekalibráěnich standardů používaných k rekalibraci a seřizováni rentgenových emlsnich a fluorescenčních spektrometrů.
Použiti skleněných standardů k rekalibraci rentgenových spektrometrů Je známo z čsl· autorského osvědčeni č* 231 390, které rovněž uvádí příkladná složeni skel vhodných pro použiti jako rekalibračni standardy. Mezi příkladnými skly ss uvádí i sklo s vysokým obsahem manganu, a to 45 % hmot·, které se používá jako rekalibračni standard při analýze s vysokým obsahem manganu, např. rud a slitin· 3ak věak bylo zjištěno, výroba uvedeného skla a vysokým obsahem manganu činí značné technologické obtíže, neboť během taviciho procesu dochází k silnému pěněni, obtížnému čeření a značné korozi žórovzdorných materiálů v tavícím agregátu. Důsledkem těchto jevů je velmi nízká výtěžnost, asi %, při výrobě kvalitních destiček z tohoto skla pro daný účel.
Z uvedeného důvodu došlo k Četným pokusům modifikovat známé složení skla s vysokým obsahem manganu, za účelem odstraněni nežádoucích jevů při současném zachováni potřebných vlastností skla, mezi něž patři obsah manganu nejméně 30 % hmot., dostatečná chemická stálost a homogenita.
Uvedeným účelům vyhovuje sklo s vysokým obsahem manganu Mn, vhodné zejména k výrobě rekalibračních standardů, podle vynálezu, jehož podstata spočivá v tom, že sklo obsahuje v procentech hmotnosti 30 až 40 oxidu manganatého MnO, 1 až 8 oxidu draselného K^O, 1 až 8 oxidů hořečnatého MgO, 1 až 10 oxidu zinečnatého ZnO, 1 až 8 oxidu boritého BgOg, 6 až oxidu hlinitého Al203 a 30 až 40 oxidu křemičitého SiOg,
Za účelem použiti skla jako rakalibračniho standardu pro další analytické rozbory, např. ostatních složek ve slitinách, může sklo dále s výhodou obsahovat v procentech hmotnosti nejméně jeden oxid ze skupiny zahrnující oxid lithný LigO 0,1 až 5, oxid sodný Na£0 0,1 až 10, oxid vápenatý CaO 0,1 až 10, oxid strontnatý SrO 0,1 až 10, oxid barnatý BaO
0,1 až 10, oxid yttritý Y2°3 ^·0· oxid lanthanitý La203 a/nebo oxidy lanthanoidů
0,1 až 10, oxid ceričitý Ca02 0,1 až 5, oxid cinatý SnO 0,1 až 5, oxid olovnatý PbO 0,1 až 10, oxid fosforečný P20g 0,1 až 10, oxid arsenitý As203 0,1 až 5, oxid antimonitý Sb203 0,1 až 5, oxid bismutitý BlgOg °»1 5» oxid chromitý Cr2O3 a/nebo oxid chromový
CrO3 0,1 až 3, oxid molybdenový Mo03 0,1 až 5, oxid wolframový W03 0,1 až 5, oxid železnatý FeO a/nebo oxid železitý Fe203 °,1 ež 10, oxid kobalnatý CoO 0,1 až 10, oxid nikelnatý NiO 0,1,až 10, oxid thoričitý Th02 0,1 až 5, oxid uranový U03 0,1 až 5, oxid měčfný Cu20 a/nebo oxid měčfnatý CuO 0,1 až 5, oxid stříbrný Ag20 0,1 až 3, oxid kademnatý CdO 0,1 až 5, oxid titaničitý Ti02 0,1 až 10, oxid zirkoničitý Zr02 0,1 až 5, oxid vanadičný V20g 0,1 až 5, přičemž celkový obsah uvedených oxidů čini 0,1 až 15 % hmotnosti skla.
Pro rozšířeni možnosti použiti skla ke stanoveni fluoru v analyzovaných surovinách může sklo g výhodou dále obsahovat v procentech hmotnosti 0,1 až 4 fluoridu draselného KF, který snižuje viskozitu, a tim přispívá k lepší tvarovatelnosti skla a současně slouži Jako čeřivo.
Sklo podle vynálezu vykazuje dostatečnou chemickou stálost a homogenitu, technologické výhody spočívající v lepší tavitelnosti a výrazně vyšší výtěžnosti vzhledem k velmi nízkému obsahu bublin. Rozšířením základního složeni ss zvětšuji možnosti uplatnění tohoto rekalibračniho standardu při rekalibraci přístroje pro řadu dalších analytických rozborů bez nutnosti použití samostatných standardů. Rekalibrace pro dalši analýzy, například ostatních složek ve slitinách, respektive jiné obecné analýzy, proběhne tak v jednom cyklu.
Příprava skel probíhá klasickými sklářskými postupy z kmene, do kterého jsou Jednotlivé požadované oxidy vnášeny jako takové nebo v podobě vhodných soli, uhličitanů, dusičnanů apod.
Podstata vynálezu je bliže objasněna příklady složeni skel podle vynálezu, uvedenými v tabulce, kde:
Sklo č. 1 je základním sklem bez dalších přídavků, vhodné k rekalibraci analytických postupů na stanoveni manganu Mn v jeho sloučeninách nebo jednodušších rudách a slitinách. Oeho výhodou je vysoká výtěžnost, až 90 %, daná příznivými technologickými vlastnostmi při tavení.
CS 274117 Bl
Claims (3)
1« Sklo s vysokým obsahem manganu, vhodné zejména k výrobě rekalibračnich standardů, vyznačující se tím,1 že obsahuje v procentech hmotnosti 30 až 40 oxidu manganatého, 1 až 8 oxidu draselného, 1 až 8 oxidu hořečnatého, 1 až 10 oxidu zinečnatého,' 1 až 8 oxidu boritého,' 6 až 16 oxidu hlinitého a 30 až 40 oxidu křemičitého.
2. Sklo podle bodu 1, vyznačující se tím, že obsahuje v procentech hmotnosti nejméně jeden oxid ze skupiny zahrnujici oxid lithný 0,1 až 5, oxid sodný 0,1 až 10, oxid vápenatý 0,1 až 10, oxid strontnatý 0,1 až 10, oxid barnatý 0,1 až 10, oxid yttritý 0,1 až 10, oxid lanthanitý a/nebo oxidy lanthanoidů 0,1 až 10, oxid ceričitý 0,1 až 5, oxid cinatý 0,1 až 5, oxid olovnatý 0,1 až 10, oxid fosforečný 0,1 až 10, oxid arsenitý 0,1 až 5, oxid antimonitý 0,1 až 5, oxid bismutitý 0,1 až 5, oxid chromitý a/nebo oxid chromový 0,1 až 3,' oxid molybdenový 0,1 až 5, oxid wolframový 0,1 až 5, oxid železnatý a/nebo oxid železitý 0,1 ež 10,< oxid kobeltnatý 0,1 až 10, oxid nikelnatý 0,1 až 10, oxid thoričitý 0,1 až 5, oxid uranový 0,1 až 5, oxid měčfný a/nebo oxid měffnatý 0,1 až 5, oxid stříbrný 0,1 až 3, oxid kademnatý 0,1 až 5, oxid titanlčitý 0,1 až 10, oxid zirkoničitý 0,1 až 5,· oxid vanadičný 0,1 až 5, přičemž celkový obsah uvedených oxidů čini 0,1 až
15 % hmotnosti skla.
3. Sklo podle bodů 1 a 2, vyznačující se tim, že obsahuje v procentech hmotnosti 0,1 až 4