CN87215394U - 一种镀金属的预涂层织物 - Google Patents
一种镀金属的预涂层织物 Download PDFInfo
- Publication number
- CN87215394U CN87215394U CN 87215394 CN87215394U CN87215394U CN 87215394 U CN87215394 U CN 87215394U CN 87215394 CN87215394 CN 87215394 CN 87215394 U CN87215394 U CN 87215394U CN 87215394 U CN87215394 U CN 87215394U
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating
- plating
- metal
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本实用新型是一种镀金属的预涂层织物。其主要特征是靠织物上的预涂层结构阻塞织物组织孔隙,使其表面光洁平滑,因而通过真空镀等方法就可以在织物上形成光亮的金属膜。镀金属的预涂层织物外观华美,手感柔软,透气性好,可以广泛应用于服装及装饰品。另外有些镀金属的预涂层织物还可以制成各种防辐射用品及各种防水用品。镀金属的预涂层织物还可以广泛用于包装业。
Description
本实用新型是一种镀金属的预涂层织物。
与本实用新型接近的已有技术是镀铝膜-涤纶长丝织物。镀铝膜-涤纶长丝织物是在涤纶长丝上直接镀铝制成的。由于大部份织物纤维及织物组织都有许多孔隙,并且表面粗糙不平,而产生光亮的金属镀膜对表面光洁度要求很高,因此在织物上直接镀膜使表面呈灰色或黑灰色,只有表面光洁度较高的涤纶长丝等可以直接镀膜。
本实用新型的目的是研究一种织物-预涂层-金属镀膜-保护涂层结构的镀金属织物。这种结构的镀金属织物,其织物坯绸(布)可以是化纤织物、棉织品、化纤-棉交织品、真丝织物、真丝-化纤交织品及玻璃丝布。镀金属预涂层织物具有闪亮的金属光泽,外观华美、手感柔软、透气性好,可以广泛应用于服装和装饰产品。镀金属预涂层织物可以通过调整涂层的配方、厚度以及镀膜采用的金属材料、镀膜厚度,使其具有良好的反射辐射能的功能,这种镀金属织物可以用于制做防电磁辐射服装、遮阳产品、高温防护服等。采用拒水剂做涂层的防水镀金属织物还有很好的防水作用,用它制做的潜水衣防水性能好,穿着柔软,另外还有保暖作用。镀金属预涂层织物还可以用于其它防辐射产品及防水产品。
本实用新型是一种镀金属的预涂层织物。它是靠织物上的涂层结构阻塞织物纤维和织物组织孔隙,使其表面光洁平滑,因而通过真空镀等方法就可以在织物上形成光亮的金属膜,金属膜上还可以有保护涂层,其结构如图1。镀金属予涂层织物的制造工艺如下:
1、涂料处理
在镀金属前先对织物进行涂料处理,涂料可以选用丙烯酸类树脂、聚氨酯树脂、有机硅涂料或防水处理剂等。选择涂料的原则应注意涂料对织物的粘着性好、镀膜对涂层的附着度好、成膜手感柔软,同时要考虑到尽量选择毒性小的涂料,以减少涂料的人身损害。涂料处理可以采用喷涂、滚涂或刮涂等方法进行。涂层厚度可根据要求而定,涂层厚需要加热烘干。涂层时要注意配方成份的控制、环境的清洁、尤其应该注意涂层的均匀及厚度的控制,否则会引起镀膜光泽暗淡,甚至出现灰色、黑灰色。对于化纤织物的涂料处理可以选用醋酸乙酯、甲苯、三氯乙烯等溶剂进行。织物经过涂料处理后还要进行轧光处理,才能使表面光洁平滑。对于已经进行过涂料处理的涂层织物如尼龙丝、涤纶丝或绵纶丝油绸、防雨绸,可直接进行轧光处理。对于要求透气性好或孔洞较大的织物,也可以将涂料处理放在织物前进行,织布后仍需进行轧光处理,这种镀金属予涂层织物结构如图2。涂料处理还可以采用轧挤或挤塑工艺将热塑性橡胶或乙烯类塑料、橡塑材料涂布在织物表面。
2、轧光处理。
一般情况下用普通电热轧光机进行热压轧光即可满足要求。轧光温度、压力、速度根据要求而定。轧光处理后织物表面应平整光滑,并具有较好的光泽。
3、镀金属
镀金属可以采用真空蒸镀、磁控溅射等方法。金属材料可以是铝、铜、铬、铅、金、银等金属。由于铝资源丰富,价格便宜,因此大量使用的是铝。镀金属膜厚度可根据要求而定,镀膜应该注意温度的控制,镀膜一般应选用连续镀膜设备。
镀金属后可以在金属膜上印图案或染色,印刷或染色用的涂料应该与金属膜有较好的附着度。
4、涂保护膜
最后一道工艺是涂保护膜。保护膜使用的涂料可根据需要选择聚氨酯树脂、丙烯酸类涂料、有机硅涂料等。选择原则应为手感柔软、透明度高、有较好的耐磨性、耐洗性,与金属膜有较好的附着度。对于做防水用的镀金属予涂层织物可选用附着度较好的防水剂做保护膜。对于高温防护用的镀金属预涂层织物,应选用耐热有机硅涂料、防火涂料进行涂层处理或做保护膜。
涂料配方举例:
1、丙烯酸树脂:
克利斯夸脱 P1120 (Criscot P1120) 100
克利斯分 NX(Crsvon NX) 1.5
醋酸乙酯 适量
烘干温度80-85℃
2、聚氨酯树脂
102聚氨酯树脂 100
交链剂 4-5
醋酸乙酯 25
烘干温度80-100℃
3、有机硅涂料
贝特利SI-SW 25-40
贝特利VK15-20
醋酸铵 3-4
醋酸98% 3-3.5
涂料PH值应在5-5.5
预烘温度:85-90℃
定型温度:170-180℃ 时间20-30秒
4、含氟拒水剂
齐康帕GA 20-25
醋酸98% 2
涂料PH值应在5-5.5
预烘温度:90-100℃
定型温度 170-180℃
5、防火处理剂
四羟甲基氯化磷和尿素予缩液 147.5kg
40%NaOH 3L
12%三羟甲基聚氰胺 60.7kg
醋酸钠 1.86kg
渗透剂JFC 0.5kg
涂料PH值6
预烘温度:80-100℃
定型温度150℃,时间5分钟
实施举例:
镀铝锦纶丝织物
选择坯绸要结疵少,表面平整、清洁度高、表面无活性剂、污渍、油渍、酸碱等杂质。涂料处理选用有机硅涂料,用浮刀法进行涂层处理。浮刀法涂层机组造价低,适于薄涂。也可以采用回转滚筒法,其优点是设备精度高,涂层厚度可根据需要调整,但设备造价昂贵。涂料处理烘干温度应低于定型温度。轧光处理用热压法进行,热压温度为175+2℃。压力39.2KN,车速18-20m/min。镀铝在卧式连续真空镀膜机内进行,镀膜时注意温度控制及卷轴速度。镀铝后的织物可以印刷图案,印刷涂料用聚氨酯树脂涂料,这种涂料透明度高,并且与镀铝膜附着度好。保护膜选用丙烯酸类涂料,涂层工艺与涂料处理相同。
镀铝棉纶丝织物可用来制造窗帘、服装及包袋。由于涂料处理选用的有机硅涂料有拒水作用,因此加厚涂层可用来制造雨衣、蓬伞等防水用品。镀铝锦纶丝织物做潜水衣时要注意选择密度较高的坯绸,除涂层需加厚外,保护膜采用含氟防水剂。为了保温还可以两面镀铝。
附图说明:
图1、普通镀金属的预涂层织物结构
1-1保护涂层
1-2金属层
1-3预涂层
1-4织物
图2、涂料处理在织布前的镀金属预涂层织物结构
2-1保护膜
2-2金属层
2-5涂料织物
Claims (4)
1、一种镀金属的预涂层织物,其主要特征是:织物上或织物纤维上有一层用以阻塞织物纤维孔隙或织物组织孔隙,使其表面光洁平滑的涂料,在预涂层上镀有一层金属膜。
2、按权利要求1所述的镀金属预涂层织物,其特征是织物坯绸(布) 是化纤织物、棉织品、化纤-棉交织品、真丝织物、真丝-化纤交织品及玻璃丝布。
3、按权力要求1所述的镀金属预涂层织物,其特征是镀金属材料可以是铝、铜、铬、铅、金、银 金属。
4、按权利要求1所述的镀金属预涂层织物,其特征是光亮的金属表面 有一层起保护作用的涂料层。