CN85103888B - 一种环氧树脂的增韧剂的配制工艺 - Google Patents

一种环氧树脂的增韧剂的配制工艺 Download PDF

Info

Publication number
CN85103888B
CN85103888B CN85103888A CN85103888A CN85103888B CN 85103888 B CN85103888 B CN 85103888B CN 85103888 A CN85103888 A CN 85103888A CN 85103888 A CN85103888 A CN 85103888A CN 85103888 B CN85103888 B CN 85103888B
Authority
CN
China
Prior art keywords
epoxy resin
present
nitrile rubber
toughening agent
weight parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CN85103888A
Other languages
English (en)
Other versions
CN85103888A (zh
Inventor
尹寿琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUANAN POLYTECHNIC COLLEGE
Original Assignee
HUANAN POLYTECHNIC COLLEGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUANAN POLYTECHNIC COLLEGE filed Critical HUANAN POLYTECHNIC COLLEGE
Priority to CN85103888A priority Critical patent/CN85103888B/zh
Publication of CN85103888A publication Critical patent/CN85103888A/zh
Publication of CN85103888B publication Critical patent/CN85103888B/zh
Expired legal-status Critical Current

Abstract

一种环氧树脂的增韧剂的配制方法。本发明属于对有机化合物的改性工艺,其要点在于将丙烯腈含量为40%的固体丁腈橡胶与醋酸乙酯及邻苯二甲酸二丁酯混合,从而可得到可用做环氧树脂的增韧剂的改性丁腈橡胶。按本发明配制环氧树脂的增韧剂,所需设备少,合成工艺简单,成本低。用按本发明制得的改性丁腈橡胶做增韧剂,可使环氧树脂胶粘剂具有较高的粘结抗剪强度。

Description

一种环氧树脂的增韧剂的配制工艺
本发明属于对有机化合物的改性工艺。
在本发明做出之前,环氧树脂胶粘剂中最常用的增韧剂是端羧基液体丁腈(CTBN)和聚硫橡胶。采用端羧基液体丁腈作增韧剂配制的环氧树脂胶粘剂,具有较高的粘结强度。例如据1984年中国粘结年会文献介绍,将这种胶粘剂用于碳钢之间的粘结,其粘结抗剪强度可达280kg/cm2,用于铝之间的粘结,其粘结抗剪强度可达292kg/cm2。但是,合成这种增韧剂的原料来源少而且有毒,合成工艺复杂,生产效率低,因而价格高达每公斤340元。采用聚硫橡胶作增韧剂,虽然价格较低,每公斤24元,但用它作增韧剂配制的环氧树脂胶粘剂,其粘结抗剪强度仅有210kg/cm2
本发明的目的在于获得一种原料来源广、合成工艺简单,价格便宜而又可用之制得粘结抗剪强度高的环氧树脂胶粘剂的增韧剂。
本发明的要点在于,将丙烯腈含量为40%的固体丁腈橡胶与醋酸乙酯及邻苯二甲酸二丁酯混合,从而得到可用作做环氧树脂的增韧剂的改性丁腈橡胶。混合的工艺过程为:按重量份,每100份固体丁腈橡胶在15℃~40℃但最好是25℃的温度下与100份~200份但最好是100份醋酸乙酯混合,按常规连续搅拌8~12小时后再加入100份~400份但最好是300份的邻苯二甲酸二丁酯,同样在15℃~40℃但最好是25℃的温度下按常规连续搅拌48~60小时,即可得可用做环氧树脂的增韧剂的改性丁腈橡胶。
按本发明所制得的改性丁腈橡胶,用作环氧树脂的增韧剂,可使环氧树脂胶粘剂有较高的粘结抗剪强度。如用于铝合金之间的粘结,在60℃下固化,粘结强度可达264kg/cm2,用于铸铁间粘结,粘结抗剪强度为267kg/cm2。按本发明配制改性丁腈橡胶,所需设备少,原料来源广,合成工艺简单,并可在常温下进行,因此每公斤改性丁腈橡胶仅需成本费12元左右。而且经与美国的Dialog情报公司联机检索,1963年~1984年年底的世界专利文档中的世界专利索引(WPI)和世界专利最新索引(WPIL),尚未发现有用改性丁腈橡胶作环氧树脂的增韧剂的记载。

Claims (1)

1、一种环氧树脂的增韧剂的配制工艺,它是将含丙烯腈40%的固体丁腈橡胶、醋酸乙酯以及邻苯二甲酸二丁酯混合的过程,其特征在于首先将含丙烯腈40%的固体丁腈橡胶100重量份,醋酸乙酯100重量份~200重量份在10℃~40℃的温度下混合,按常规连续搅拌8~12小时,然后再加入邻苯二甲酸二丁酯100重量份~400重量份,并在10℃~40℃的温度下按常规连续搅拌48~60小时。
CN85103888A 1985-05-07 1985-05-07 一种环氧树脂的增韧剂的配制工艺 Expired CN85103888B (zh)