CN205573323U - 一种pvc装饰膜和pvdc包装膜涂布用网纹辊 - Google Patents
一种pvc装饰膜和pvdc包装膜涂布用网纹辊 Download PDFInfo
- Publication number
- CN205573323U CN205573323U CN201620380909.9U CN201620380909U CN205573323U CN 205573323 U CN205573323 U CN 205573323U CN 201620380909 U CN201620380909 U CN 201620380909U CN 205573323 U CN205573323 U CN 205573323U
- Authority
- CN
- China
- Prior art keywords
- film
- packaging film
- pvdc
- coating
- pvdc packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本实用新型公开了一种PVC装饰膜和PVDC包装膜涂布用网纹辊，其包括金属辊坯体、喷涂在金属辊坯体表面上的陶瓷面层、喷涂在陶瓷面层表面上的封孔剂层。本实用新型的网纹辊取消了镍铬层这个过渡层，而在陶瓷面层上增加了封孔剂层，使得耐盐酸腐蚀性能大大增加，用于PVC装饰膜和PVDC包装膜这些有HCl分子析出的涂布环境时，产品的使用寿命较长。而且，由于产品的使用寿命较长而不需要频繁更换网纹辊，增加了PVC装饰膜和PVDC包装膜的产品稳定性。
Description
技术领域
本实用新型涉网纹辊技术领域，具体涉及一种PVC装饰膜和PVDC包装膜涂布用网纹辊。
背景技术
PVC装饰膜是以PVC(聚氯乙烯)为原料，添加各种助剂，经压延、复合、木纹印刷而制得的一种装饰材料，可与木材、塑料板、铝板、铁板等基材复合制成多用途装饰材料，广泛应用于家具、电器、音响表面装饰、室内装饰、飞机、轮船、火车的内装饰。PVC木纹装饰膜有广泛的市场，并有逐年上升的趋势。
PVC材料的热稳定性和耐光性较差，压延、印刷及涂布过程中会分解出氯化氢，随着增塑剂含量的多少发生不良反应。另外，颜料对PVC的影响，体现在颜料是否与PVC及组成PVC制品的其它组分发生反应以及颜料本身耐迁移性、耐热性。着色剂中的某些成份会促使树脂降解。如铁离子和锌离子是PVC树脂降解反应的催化剂。因此，使用氧化铁(红、黄、棕和黑)颜料或氧化锌、硫化锌和立德粉类白色颜料会降低PVC树脂的稳定性。
PVDC(聚偏二氯乙烯)包装膜广泛应用在食品、奶制品、化妆品、药品等需要防潮的产品包装，PVDC胶乳的涂布存在涂层展布和加热干燥过程。涂层2-3μm厚，但PVDC在紫外光的照射下极易分解出HCl气体。生产涂布环境中，不可避免会有部分紫外光的照射，分解出的HCl气体会同水分、氧气等通过薄膜基材与辊面的接触吸附渗透到网纹辊底层以及基体，同样造成基体和底层的腐蚀，从而引起表面陶瓷层的鼓泡、脱落；
PVC装饰膜涂布表面处理剂、上底色、涂胶及PVDC包装膜进行PVDC溶胶层的涂布过程都要用到网纹辊，并且网纹辊在此过程中作为核心部件要求性能非常稳定。
传统陶瓷网纹辊的加工一般采用无缝钢管做基材，经过除锈、毛化后采用热喷涂镍铬合金(Ni80Cr20)作为过渡层，之后再采用热喷涂三氧化二铬陶瓷层作为工作层。由于热喷涂涂层孔隙率的存在，外界介质极易通过孔隙渗透到过渡层及基体，逸出的HCl首先吸附在基材的表面，通过与辊面的接触逐步转移、累积并和水分、空气一起通过孔隙渗透到网纹辊过渡层和Ni80Cr20反应，并进一步使基体发生锈蚀。腐蚀产物的不断堆积必然造成表面陶瓷层的鼓泡、脱落。
以上两类涂布的使用环境下，都有HCl分子的析出，介质中由于Cl—离子的存在，会发生晶间腐蚀，镍铬合金作为过渡层时由于会参与腐蚀反应会严重影响到陶瓷层的寿命。
实用新型内容
针对上述技术问题，本实用新型提供了一种PVC装饰膜和PVDC包装膜涂布用网纹辊，用于PVC装饰膜涂布表面处理剂、上底色、涂胶及PVDC包装膜进行PVDC溶胶层的涂布时，该网纹辊的耐酸腐蚀性能较强，长期使用不会出现陶瓷层鼓泡、脱落的现象，产品使用寿命长。
为了达到上述目的，本实用新型所采用的技术方案如下：
一种PVC装饰膜和PVDC包装膜涂布用网纹辊，其包括金属辊坯体、喷涂在金属辊坯体表面上的陶瓷面层、喷涂在陶瓷面层表面上的封孔剂层。
进一步的，所述封孔剂层为改性环氧树脂层。
进一步的，所述陶瓷面层的厚度为0.8～1.5cm。
进一步的，所述封孔剂层的厚度为0.01～0.05cm。
与现有技术相比，本实用新型的有益效果是：
本实用新型的网纹辊取消了镍铬层这个过渡层，而在陶瓷面层上增加了封孔剂层，使得耐盐酸腐蚀性能大大增加，用于PVC装饰膜和PVDC包装膜这些有HCl分子析出的涂布环境时，产品的使用寿命较长。而且，由于产品的使用寿命较长而不需要频繁更换网纹辊，增加了PVC装饰膜和PVDC包装膜的产品稳定性。最后，由于取消了镍铬层这个过渡层，降低了网纹辊生产成本，提高生产效率。
附图说明
图1为本实用新型的结构示意图。
具体实施方式
下面，结合附图以及具体实施方式，对本实用新型做进一步描述。
如图1所示，一种PVC装饰膜和PVDC包装膜涂布用网纹辊，其包括金属辊坯体1、喷涂在金属辊坯体1表面上的陶瓷面层2、喷涂在陶瓷面层2表面上的封孔剂层3。具体地，所述封孔剂层3为改性环氧树脂层。所述改性环氧树脂层按质量百分数计由85％的环氧树脂、5％的环氧基丙基三甲氧基硅烷、10％的聚酰胺组成。
作为本实用新型进一步改进的方案，所述陶瓷面层2的厚度为0.8～1.5cm，所述封孔剂层3的厚度为0.01～0.05cm。
对于本领域的技术人员来说，可根据以上描述的技术方案以及构思，做出其它各种相应的改变以及变形，而所有的这些改变以及变形都应该属于本实用新型权利要求的保护范围之内。
Claims (4)
1.一种PVC装饰膜和PVDC包装膜涂布用网纹辊，其特征在于：包括金属辊坯体、喷涂在金属辊坯体表面上的陶瓷面层、喷涂在陶瓷面层表面上的封孔剂层。
2.如权利要求1所述的PVC装饰膜和PVDC包装膜涂布用网纹辊，其特征在于：所述封孔剂层为改性环氧树脂层。
3.如权利要求2所述的PVC装饰膜和PVDC包装膜涂布用网纹辊，其特征在于：所述陶瓷面层的厚度为0.8～1.5cm。
4.如权利要求1所述的PVC装饰膜和PVDC包装膜涂布用网纹辊，其特征在于：所述封孔剂层的厚度为0.01～0.05cm。