CN205100480U - 一种辐射固化彩色印刷装饰板 - Google Patents
一种辐射固化彩色印刷装饰板 Download PDFInfo
- Publication number
- CN205100480U CN205100480U CN201520882358.1U CN201520882358U CN205100480U CN 205100480 U CN205100480 U CN 205100480U CN 201520882358 U CN201520882358 U CN 201520882358U CN 205100480 U CN205100480 U CN 205100480U
- Authority
- CN
- China
- Prior art keywords
- radiation curing
- thickness
- decorative panel
- board
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本实用新型提供一种辐射固化彩色印刷装饰板，包括基板和从下到上依次附着在所述基板表面上的辐射固化附着底涂层、辐射固化彩色底涂层、油墨图案层和透明辐射固化保护涂层。本实用新型的一种辐射固化彩色印刷装饰板，具有强度高、抗折好、耐候性好、环保性好、图案丰富、漆膜丰满、硬度高、抗划伤、易清洁、用途广泛等特点，可替代现行的石材、木材、瓷砖、水泥纤维板、硅酸钙板、玻镁板、铝塑板、铝单板、金属板等。
Description
技术领域
本实用新型涉及建筑材料领域，特别涉及一种辐射固化彩色印刷装饰板。
背景技术
目前，国内各种建筑装饰材料相继出现，主要有纤维增强水泥板、纤维增强硅酸钙板、纤维增强氧化镁板、轻质氯镁水泥板、菱镁板、石膏装饰板等作为内墙等的装饰基板。目前的普遍施工工艺较为复杂，且由于基板本身的原因造成了该装饰板在部分场合不能使用，如在高湿等环境，因此该装饰板的使用受到了一定的限制；另外有于其基板本身的原因在安装和使用过程中无法解决安装面的阴角、阳角、收口等问题。
并且，目前较为流行的是通过转印的方式对基材板进行表面的图案、色彩的装饰，但相对成本比较高。
实用新型内容
本实用新型旨在解决上面描述的问题。本实用新型的目的是提供一种辐射固化彩色印刷装饰板。
一种辐射固化彩色印刷装饰板，包括基板和从下到上依次附着在基板表面上的辐射固化附着底涂层、辐射固化彩色底涂层、油墨图案层和透明辐射固化保护涂层。
其中，透明辐射固化保护涂层上还设置有聚丙烯或聚乙烯保护薄膜。
其中，油墨图案层为彩色油墨图案层。
其中，辐射固化彩色底涂层的厚度为2～100μm，油墨图案层的厚度为2～50μm，透明辐射固化保护涂层的厚度为2～400μm，辐射固化附着底涂层的厚度为2～100μm。
其中，辐射固化彩色底涂层的厚度为50μm，油墨图案层的厚度为25μm，透明辐射固化保护涂层的厚度为100μm，辐射固化附着底涂层的厚度为50μm。
其中，基板的厚度为1mm～1000mm。
其中，基板的厚度为10mm。
其中，基板包括钙塑板、木塑板、PVC板、高分子板、石塑板。
本实用新型的一种彩色印刷装饰板，具有强度高、抗折好、耐候性好、环保性好、图案丰富、漆膜丰满、硬度高、抗划伤、易清洁、用途广泛等特点，可替代现行的石材、木材、瓷砖、水泥纤维板、硅酸钙板、玻镁板、铝塑板、铝单板、金属板等。
参照附图来阅读对于示例性实施例的以下描述，本实用新型的其他特性特征和优点将变得清晰。
附图说明
并入到说明书中并且构成说明书的一部分的附图示出了本实用新型的实施例，并且与描述一起用于解释本实用新型的原理。在这些附图中，类似的附图标记用于表示类似的要素。下面描述中的附图是本实用新型的一些实施例，而不是全部实施例。对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，可以根据这些附图获得其他的附图。
图1示例性地示出了根据本实用新型的彩色印刷装饰板的结构示意图。
具体实施方式
为使本实用新型实施例的目的、技术方案和优点更加清楚，下面将结合本实用新型实施例中的附图，对本实用新型实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本实用新型一部分实施例，而不是全部的实施例。基于本实用新型中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本实用新型保护的范围。需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互任意组合。
本实用新型提供了一种辐射固化彩色印刷装饰板1，通过选用基板10作为基材，并在基板10上设置辐射固化彩色底涂层和彩色油墨图案层，形成一种图案多样，应用广泛的辐射固化彩色印刷装饰板。
一种辐射固化彩色印刷装饰板1，包括基板10和从下到上依次附着在基板10上的辐射固化附着底涂层20、辐射固化彩色底涂层30、油墨图案层40和透明辐射固化保护涂层50。
其中辐射固化附着底涂层30包括辐射固化附着底漆层或辐射固化附着底涂料层，透明辐射固化保护涂层50包括透明辐射固化保护漆层或透明辐射固化保护涂料层。
透明辐射固化保护涂层50上还设置有聚丙烯或聚乙烯保护薄膜，用于保护基板上的涂层，避免出现滑伤和擦伤。
油墨图案层40为彩色油墨图案层，起到进一步丰富彩色印刷装饰板的表面色彩的作用。
通常情况下，辐射固化彩色底涂层30的厚度为2～100μm，油墨图案层40的厚度为2～50μm，透明辐射固化保护涂层50的厚度为2～400μm，辐射固化附着底涂层20的厚度为2～100μm。
在本实用新型的一个实施例中，辐射固化彩色底涂层30的厚度为50μm，油墨图案层40的厚度为25μm，透明辐射固化保护涂层50的厚度为100μm，辐射固化附着底涂层20的厚度为50μm。基板的厚度为1mm～1000mm，一个常见的实施例中基板的厚度为10mm。另外，本实用新型中的基板包括钙塑板、木塑板、PVC板、高分子板、石塑板，并且本实用新型中所有辐射固化各种涂层均包括紫外光辐射固化层和电子光束固化层两种形式。
此外，本实用新型的辐射固化彩色印刷装饰板通过以下方法制得：
1基板表面的处理：砂磨，除尘；
2在基板上涂装辐射固化附着底；厚度为2～100μm；
3辐射固化；
4在辐射固化附着底涂层上涂装辐射固化彩色底层；
5辐射固化；
6在辐射固化彩色底层上印刷彩色油墨；
7辐射固化；
8在彩色油墨图案层上涂装辐射固化透明保护层；
9辐射固化；
10检验；
11贴保护膜；
12包装。
下面通过实施例的方式具体说明本实用新型的辐射固化彩色印刷装饰板。
实施例一木塑基辐射固化印刷胡桃木纹装饰板
将基板进行砂光、除尘处理；在12mm的木塑基材板上喷涂辐射固化附着底漆层，底漆层的厚度为40μm，然后进入装有4支9.6kw的高压汞灯，速度20米/分钟的固化机中进行固化，固化后，砂光、除尘、再在其表面喷涂辐射固化红咖啡色底漆层，红咖啡底漆层的厚度为20μm，然后进入装有4支11.2kw镓灯、镓灯、铁灯、汞灯，速度20米/分钟的固化机中进行固化，固化后，再在其表使用凹印的方法在辐射固化红咖啡色底层上印刷黑色油墨，黑色色油墨图案层的厚度为5μm，进入速度为20米、2支9.6KW镓灯的固化机进行半固化；然后同样方式印刷浅咖啡色油墨并固化，然后对其表面喷涂透明50度光泽保护涂层(60度光泽度仪)，然后进入装有4支11.2kw镓灯、镓灯、铁灯、汞灯，速度20米/分钟的固化机中进行固化，固化后，进行检验，在合格的木塑基辐射固化印刷胡桃木纹装饰板表面贴聚丙烯或聚乙烯等用于保护物体表面，避免划伤，擦伤的薄膜，对表面的涂层加以保护。然后对产品进行包装。
辐射固化附着底的重量百分比组成为：环氧丙烯酸酯20％，聚氨酯丙烯酸酯15％，NPGDA11％，DPGDA20％，滑石粉30％，2-羟基-2-甲基-1-苯基-1-丙酮3.8％，EFKA40100.2％。
辐射固化红咖啡色油墨的重量百分比组成为：聚氨酯丙烯酸酯20％，聚酯丙烯酸酯20％，丙烯酸酯共聚物10％，TMPTA10％，NPGDA10％，铁黄色粉7％，铁红色粉12％，碳黑1％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦3％，1-羟基环已基苯基甲酮3％，EFKA40101％，
辐射固化黑色油墨的重量百分比组成为：聚酯丙烯酸酯20％，改性环氧丙烯酸酯30％，TMPTA20％，DPGDA10％，碳黑8％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，1-羟基环已基苯基甲酮3％，EFKA40102％，
辐射固化浅咖啡色油墨的重量百分比组成为：环氧丙烯酸酯20％，聚酯丙烯酸酯20％，丙烯酸酯共聚物10％，TMPTA10％，NPGDA12％，铁黄色粉12％，铁红色粉5％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，1-羟基环已基苯基甲酮3％，EFKA40101％，
辐射固化50度光泽面漆的重量百分比组成为：环氧丙烯酸酯10％，聚氨酯丙烯酸酯40％，TPGDA14％，TMPTA20％，消光浆10％，1-羟基环已基苯基甲酮4％，Ciba50502％。
实施例二石塑基辐射固化印刷黑白花大理石装饰板
将石塑基板进行砂光、除尘处理；在15mm的石塑基材板上辊涂辐射固化附着底漆层，底漆层的厚度为50μm，然后进入装有5支7.6kw的高压汞灯，速度32米/分钟的固化机中进行固化，固化后，砂光、除尘、再在其表面辊涂辐射固化白色底漆层，白色底漆层的厚度为25μm，然后进入装有4支11.2kw镓灯，速度32米/分钟的固化机中进行固化，固化后，再在其表使用凹印的方式在辐射固化白色底漆层上印刷黑色油墨，黑色色油墨图案层的厚度为15μm，进入速度为32米、5支11.2KW镓灯的固化机进行半固化；然后对其表面辊涂透明30度光泽保护涂层(60度光泽度仪)，然后进入装有4支16.8kw镓灯、镓灯、铁灯、汞灯，速度32米/分钟的固化机中进行固化，固化后，进行检验，在合格的石塑基辐射固化印刷黑白花大理石装饰板表面贴聚丙烯或聚乙烯等用于保护物体表面，避免划伤，擦伤的薄膜，对表面的涂层加以保护。然后对产品进行包装。
辐射固化附着底的重量百分比组成为：环氧丙烯酸酯20％，聚氨酯丙烯酸酯15％，TMPTA20％，HDDA10％，滑石粉31％，2-羟基-2-甲基-1-苯基-1-丙酮3.8％，EFKA40100.2％。
辐射固化白色油墨的重量百分比组成为：聚氨酯丙烯酸酯25％，环氧丙烯酸酯15％，丙烯酸酯共聚物10％，TMPTA10％，NPGDA10％，钛白粉31％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮4％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，EFKA40101％，
辐射固化黑色油墨的重量百分比组成为：聚氨酯丙烯酸酯20％，改性环氧丙烯酸酯30％，NPGDA20％，DPGDA11％，碳黑8％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，1-羟基环已基苯基甲酮3％，EFKA40101％，
辐射固化30度光泽面漆的重量百分比组成为：含氟环氧丙烯酸酯20％，含氟聚氨酯丙烯酸酯30％，TPGDA14％，TMPTA14％，消光浆10％，消光粉5％，EFKA40101％，1-羟基环已基苯基甲酮4％，Ciba50502％。
实施例三钙塑基辐射固化印刷英国棕大理石耐磨装饰板
将钙塑基板进行砂光、除尘处理；在15mm的钙塑基材板上辊涂辐射固化附着底漆层，底漆层的厚度为50μm，然后进入装有5支7.6kw的高压汞灯，速度32米/分钟的固化机中进行固化，固化后，砂光、除尘、再在其表面辊涂辐射固化红褐色油墨层，红褐色油墨层的厚度为20μm，然后进入装有4支11.2kw镓灯，速度32米/分钟的固化机中进行固化，半固化后，再在其表使用凹印的方式在辐射固化红褐色油墨层上印刷咖啡色色油墨，咖啡色油墨图案层的厚度为5μm，进入速度为32米、5支11.2KW镓灯的固化机进行半固化；半固化后，再在其表使用凹印的方式在辐射固化咖啡色层上印刷蓝色色油墨，蓝色油墨图案层的厚度为3μm，进入速度为32米、6支9.6KW镓灯的固化机进行半固化；半固化后，再在其表使用凹印的方式在辐射固化蓝色层上印刷黑色色油墨，黑色油墨图案层的厚度为8μm，进入速度为32米、6支16.8KW镓灯的固化机进行半固化；然后对其表面辊涂透明70度光泽耐磨保护涂层(60度光泽度仪)，然后进入装有4支16.8kw镓灯、镓灯、铁灯、汞灯，速度32米/分钟的固化机中进行固化，固化后，进行检验，在合格的钙塑基辐射固化印刷英国棕大理石耐磨装饰板表面贴聚丙烯或聚乙烯等用于保护物体表面，避免划伤，擦伤的薄膜，对表面的涂层加以保护。然后对产品进行包装。
辐射固化附着底的重量百分比组成为：丙烯酸酯共聚物20％，聚氨酯丙烯酸酯20％，TMPTA10％，DPGDA10％，滑石粉35％，2-羟基-2-甲基-1-苯基-1-丙酮4％，EFKA40101％。
辐射固化红褐色油墨的重量百分比组成为：聚酯丙烯酸酯20％，氨基丙烯酸酯20％，丙烯酸酯共聚物10％，DPGDA15％，NPGDA10％，铁红粉15％，铁黄5％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮2％，2,4,6-三甲基苯甲酰基二苯基氧化膦2.5％，EFKA40100.5％.
辐射固化咖啡色油墨的重量百分比组成为：聚氨酯丙烯酸酯20％，氨基丙烯酸酯20％，TPGDA15％，NPGDA10％，铁红粉2％，铁黄23％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮4％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，EFKA40102％.
辐射固化蓝色油墨的重量百分比组成为：聚酯丙烯酸酯20％，环氧丙烯酸酯20％，TPGDA20％，NPGDA10％，酞青蓝20％，碳黑2％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，EFKA40101％.
辐射固化黑色油墨的重量百分比组成为：聚酯丙烯酸酯25％，改性环氧丙烯酸酯25％，NPGDA20％，TMPTA10％，碳黑8％，2-苄基-2-二甲基氨基-1-(4-吗啉基苯基)-1-丁酮3％，2,4,6-三甲基苯甲酰基二苯基氧化膦4％，1-羟基环已基苯基甲酮3％，EFKA40101％，
辐射固化70度光泽面漆的重量百分比组成为：含氟环氧丙烯酸酯10％，含丙烯酸酯共聚物35％，DPGDA10％，NPGDA5％,TMPTA20％，消光浆13％，EFKA40101％，1-羟基环已基苯基甲酮4％，Ciba50502％。
综上所述，本实用新型的一种辐射固化彩色印刷装饰板，具有强度高、抗折好、耐候性好、环保性好、图案丰富、漆膜丰满、硬度高、抗划伤、易清洁、用途广泛等特点，可替代现行的石材、木材、瓷砖、水泥纤维板、硅酸钙板、玻镁板、铝塑板、铝单板、金属板等。
最后应说明的是：以上实施例仅用以说明本实用新型的技术方案，而非对其限制。尽管参照前述实施例对本实用新型进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本实用新型各实施例技术方案的精神和范围。
Claims (8)
1.一种辐射固化彩色印刷装饰板(1)，其特征在于，包括基板(10)和从下到上依次附着在所述基板(10)表面上的辐射固化附着底涂层(20)、辐射固化彩色底涂层(30)、油墨图案层(40)和透明辐射固化保护涂层(50)。
2.如权利要求1所述的装饰板，其特征在于，
所述透明辐射固化保护涂层(50)上还设置有聚丙烯或聚乙烯保护薄膜。
3.如权利要求1所述的装饰板，其特征在于，
所述油墨图案层(40)为彩色油墨图案层。
4.如权利要求1所述的装饰板，其特征在于，
所述辐射固化彩色底涂层(30)的厚度为2～100μm，所述油墨图案层(40)的厚度为2～50μm，所述透明辐射固化保护涂层(50)的厚度为2～400μm，所述辐射固化附着底涂层(20)的厚度为2～100μm。
5.如权利要求4所述的装饰板，其特征在于，
所述辐射固化彩色底涂层(30)的厚度为50μm，所述油墨图案层(40)的厚度为25μm，所述透明辐射固化保护涂层(50)的厚度为100μm，所述辐射固化附着底涂层(20)的厚度为50μm。
6.如权利要求1所述的装饰板，其特征在于，
所述基板的厚度为1mm～1000mm。
7.如权利要求6所述的装饰板，其特征在于，
所述基板的厚度为10mm。
8.如权利要求1所述的装饰板，其特征在于，
所述基板包括钙塑板、木塑板、PVC板、高分子板、石塑板。