CN1962516B - 环保型高温玻璃棉粘接剂 - Google Patents

环保型高温玻璃棉粘接剂 Download PDF

Info

Publication number
CN1962516B
CN1962516B CN2005101102412A CN200510110241A CN1962516B CN 1962516 B CN1962516 B CN 1962516B CN 2005101102412 A CN2005101102412 A CN 2005101102412A CN 200510110241 A CN200510110241 A CN 200510110241A CN 1962516 B CN1962516 B CN 1962516B
Authority
CN
China
Prior art keywords
groups
glass wool
xylose alcohol
methyl
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2005101102412A
Other languages
English (en)
Other versions
CN1962516A (zh
Inventor
王恕
郝玉凤
王潇俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Pengye Chemical Materials Co ltd
Original Assignee
Shanghai Pengye Chemical Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Pengye Chemical Materials Co ltd filed Critical Shanghai Pengye Chemical Materials Co ltd
Priority to CN2005101102412A priority Critical patent/CN1962516B/zh
Publication of CN1962516A publication Critical patent/CN1962516A/zh
Application granted granted Critical
Publication of CN1962516B publication Critical patent/CN1962516B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于粘接剂的制备与合成，特别是采用无味、有机类原料取代尿素而合成的一种环保型高温玻璃棉粘接剂，它是以甲基木糖醇等多糖类原料取代原来的尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～130组；甲基木糖醇2～25组；烷基苯磺酸0～10组；硫酸铵5～50组；硅烷0～5组；本发明主要所解决目前玻璃棉粘接剂因使用酚醛树脂以及尿素为原料而产生刺激性气味，减少对人体的危害，达到环保的要求。

Description

环保型高温玻璃棉粘接剂
技术领域：
本发明属于粘接剂的制备与合成，特别是采用无味、有机类原料取代尿素而合成玻璃棉用的粘接剂。
背景技术：
目前市场上传统的玻璃棉粘接剂主要是由酚醛树脂及尿素等为主要原料，具有优良的粘接性，适应性强，不需加压即可固化，且固化收缩率低等优点，在许多领域得到广泛应用，但其玻璃棉粘接剂在生产过程中使用了酚醛树脂，含有大量的游离甲醛，尿素带有强烈的刺激性气味，影响产品的使用性能，同时其气味对人体存在严重危害，消除其气味，减少游离甲醛是玻璃棉生产企业急于解决的问题。
发明内容：
本发明的目的是提供一种玻璃棉粘接剂，主要解决现有高温玻璃棉粘接剂因含有大量的游离甲醛以及有刺激性气味，减少对人体的危害，以达到环保的要求；
为解决上述技术问题，本发明是这样实现的：
以甲基木糖醇等多糖类原料取代尿素，与其它有效助剂复配而成，其重量组份为：酚醛树脂40～130组；甲基木糖醇2～25组；烷基苯磺酸0～10组；硫酸铵5～50组；硅烷0～5组；
本发明环保型高温玻璃棉所解决的问题：
目前市场上的玻璃棉粘接剂采用酚醛树脂以及尿素为原料会产生刺激性气味，并含有大量的游离甲醛；
本发明的设计思想：
采用甲基木糖醇等多糖类原料取代尿素，将原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，使产品消除了味道，降低了游离甲醛的含量；
具体实施方式：
以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～130组；甲基木糖醇2～25组；烷基苯磺酸0～10组；硫酸铵5～50组；硅烷0～5组；以下是四个具体实施例：
实施例一
以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂80～120组；甲基木糖醇10～25组；烷基苯磺酸5～10组；硫酸铵20～40组；硅烷0.5～1组；
实施例二
以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～65组；甲基木糖醇5～15组；烷基苯磺酸1～10组；硫酸铵5～25组；硅烷0.5～1组；
实施例三
以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～80组；甲基木糖醇5～15组；烷基苯磺酸2～6组；硫酸铵20～25组；硅烷1～3组；
实施例四
以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂60～100组；甲基木糖醇10～15组；烷基苯磺酸4～6组；硫酸铵25～40组；硅烷2～2.8组；
经过若干次试验，我们提出以上四组分析数据，并在试验室做试验，比较后实施例一试验结果最理想：环保型高温玻璃粘接剂在使用过程中，无甲醛以及无刺激性气味，达到环保的要求。

Claims (5)

1.一种玻璃棉粘接剂，其特征在于：以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～130组；甲基木糖醇2～25组；烷基苯磺酸0～10组；硫酸铵5～50组；硅烷0～5组。
2.根据权利要求1所述的玻璃棉粘接剂，其特征在于：以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂80～120组；甲基木糖醇10～25组；烷基苯磺酸5～10组；硫酸铵20～40组；硅烷0.5～1组。
3.根据权利要求1所述的玻璃棉粘接剂，其特征在于：以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～65组；甲基木糖醇5～15组；烷基苯磺酸1～10组；硫酸铵5～25组；硅烷0.5～1组。
4.根据权利要求1所述的玻璃棉粘接剂，其特征在于：以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂40～80组；甲基木糖醇5～15组；烷基苯磺酸2～6组；硫酸铵20～25组；硅烷1～3组。
5.根据权利要求1所述的环玻璃棉粘接剂，其特征在于：以甲基木糖醇等多糖类原料取代尿素，将下列原料配制成水溶液，加热至50～100℃，进行反应，反应时间为3～5小时，与其它有效助剂复配而成其重量组份为：酚醛树脂60～100组；甲基木糖醇10～15组；烷基苯磺酸4～6组；硫酸铵25～40组；硅烷2～2.8组。
CN2005101102412A 2005-11-10 2005-11-10 环保型高温玻璃棉粘接剂 Expired - Fee Related CN1962516B (zh)