CN1958508A - Building bricks sintered from fly ash and red sandstone, and preparation technique - Google Patents
Building bricks sintered from fly ash and red sandstone, and preparation technique Download PDFInfo
- Publication number
- CN1958508A CN1958508A CNA2006101626910A CN200610162691A CN1958508A CN 1958508 A CN1958508 A CN 1958508A CN A2006101626910 A CNA2006101626910 A CN A2006101626910A CN 200610162691 A CN200610162691 A CN 200610162691A CN 1958508 A CN1958508 A CN 1958508A
- Authority
- CN
- China
- Prior art keywords
- red sandstone
- flyash
- softening agent
- fly ash
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses a method for preparing construction bricks by sintering fly ashes and red sandstone. The raw materials comprise: fly ashes, red sandstone, plasticizer (kaolin or bentonite), and water at a weight ratio of (50-60) :( 40-50) :( 1-5) :( 18-30). The fly ashes are the mass fly ashes from fluidized bed furnace and piled on the material field. The red sandstone is from waste roadbed materials or lost natural resources in mountain areas. The construction bricks can be used for bearing or non-bearing inner and outer walls. The method has such advantages as simple process, easy operation, high efficiency, low sintering temperature, low energy consumption, high performance and wide applications.
Description
Technical field
The invention belongs to building material technical field, particularly a kind of flyash and Red Sandstone utilized prepares building brick and preparation technology thereof.
Background technology
China is that flyash discharges the third-largest state in the world, and power industry flyash annual emissions surpasses 100,000,000 t, utilization ratio only about 38%.At present the main raw material of preparation coal ash sintering brick is flyash clay, flyash, shale, flyash coal gangue etc., and yet there are no report with brick utilizing Red Sandstone to prepare fly ash building.Red Sandstone is widely distributed in China, be a kind of be rich in the irony oxide compound and take on a red color, the deposition rocks such as mud stone, chiltern mud stone, shale packsand, shale or arenaceous rock of scarlet or brown.Red Sandstone exists in Mountainous Highway Construction in a large number, but the natural intensity of Red Sandstone is lower, it is softening to meet fragmentation of water easy disintegrating and intensity, easily cause diseases such as roadbed damaged or destroyed by flood, landslide, depression to take place, it is a kind of bad filling roadbed material, often be used as the side's of abandoning processing, and the Red Sandstone in the mountain area is quite big because of the difference Strength Changes of mineralogical composition and cementing material, under atmospheric environment or drying and watering cycle effect, sillar bursts apart and disintegrates, and particle is softening, intensity reduces, engineering properties is very poor, and easily water and soil runs off, and causes the wasting of resources.
Summary of the invention
The objective of the invention is to be that raw material burns the mass fly ashes that nature is stacked at the stock ground from fluidizing furnace, and to make full use of Red Sandstone be the natural resource that run off in the filling roadbed material passed into disuse in the road project and mountain area, adds a spot of softening agent and prepare heavy-load bearing brick and furring tile.The water-intake rate of its heavy-load bearing brick is little, intensity is higher; Furring tile has better thermal insulation performance, intensity can guarantee that also construction wall uses.
Technical scheme of the present invention is as follows:
The raw material of the building brick of sintered from fly ash and red sandstone is formed and weight part is: flyash: Red Sandstone: softening agent (kaolin or wilkinite): water=50～60: 40～50: 1～5: 18～30.
The building brick preparation technology concrete steps of sintered from fly ash and red sandstone are as follows:
1. Red Sandstone is ground, grain diameter tails over 5% for the 0.080mm square hole sieve, and again in 50～60: 40～50: 1～5 weight part ratio is got flyash, Red Sandstone and softening agent (kaolin or wilkinite), is placed in the stirrer, and siccative stirs;
2. get continuous the pouring in the siccative in land and water of 18～30 weight parts, carry out secondary with stirrer again and mix stirring;
3. the pug that stirs was carried out ageing 1～3 hour, make pug fully wetting, seasoning or be placed in the baking oven its excessive moisture of oven dry increases its plasticity;
4. with the needed brick shape of the molded or molded preparation of the pug hand after the ageing;
5. the adobe of making being placed on 80 ℃～120 ℃ baking ovens dries;
6. with dried adobe, 900 ℃～1200 ℃ sintering 1～2 hour.
The present invention has the following advantages:
1, China's flyash discharge capacity increases day by day, the effusive waste water in stockyard, polluted agricultural land; Permeate the ground polluted underground water; The dust of kicking up, polluted air, Red Sandstone also is bad roadbed filling simultaneously, easily cause pavement depression, often be used as and abandon the material processing, Red Sandstone is subjected to effect and destructions such as weathering, aqueous solution erosion, mankind's activity in addition, stability has been subjected to serious threat, the part location is easy to cause soil erosion because sand has been weathered in effects such as weathering, aqueous solution erosion, therefore with flyash and Red Sandstone be main raw material prepare building brick can utilization of waste material, be beneficial to environmental protection, the saving energy;
2, the thorough mixing of material makes hydration reaction more abundant, provides prerequisite for improving quality of item.Simultaneously later carry out ageing stirring, also strengthened mixed effect, between the material particles contact more even, hydration reaction is more abundant, makes the gelling better effects if of flyash.Baking load-bearing adobe after tested, the ultimate compression strength after the oven dry just can reach 2MPa, for the reduction of later stage sintering temperature is laid a good foundation, and then provides technical guarantee for low cost prepares the Red Sandstone flyash brick;
3, applicable surface of the present invention is wider, be not only applicable to heavy-load bearing brick, can also be applicable to the production of perforated brick goods, be applicable to inside and outside body of wall load-bearing and non-bearing building brick, not only have energy-conservation, joint soil, lowly pollute, be easy to advantage such as construction, and all be very helpful to producing the gathering materials on the spot of the manufacturing enterprise of solid clay brick of present preparation or flyash clay vitrified brick, in-situ reformation, transition etc., also be the needs of realizing the building materials industry structural adjustment, created very advantageous conditions for novel wall material develops rapidly simultaneously.
Description of drawings
Fig. 1 is a process flow sheet of the present invention.
Embodiment
Embodiment 1:
1. Red Sandstone is ground, grain diameter tails over 5% for the 0.080mm square hole sieve, gets flyash, Red Sandstone and wilkinite in 50: 45: 5 weight part ratio again, is placed in the stirrer, and siccative stirs;
2. get continuous the pouring in the siccative in land and water of 22 weight parts, carry out secondary with stirrer again and mix stirring;
3. the pug that stirs was carried out ageing 1.5 hours, make pug fully wetting, seasoning or be placed in the baking oven its excessive moisture of oven dry increases its plasticity;
With the pug hand after the ageing molded be the adobe of heavy-load bearing brick;
5. the adobe of making being placed on 100 ℃ of baking ovens dries;
6. with dried adobe, 1080 ℃ of sintering 1.5 hours.
The ultimate compression strength of obtained heavy-load bearing brick product is 17.58MPa, and water-intake rate is 10.23%, satisfies the national standard requirement of the MU15 of GB/T5101-1998 " fired common brick ".
Embodiment 2:
1. Red Sandstone is ground, grain diameter tails over 5% for the 0.080mm square hole sieve, gets flyash, Red Sandstone and kaolin in 55: 40: 5 weight part ratio again, is placed in the stirrer, and siccative stirs;
2. get continuous the pouring in the siccative in land and water of 18 weight parts, carry out secondary with stirrer again and mix stirring;
3. the pug that stirs was carried out ageing 2 hours, make pug fully wetting, seasoning or be placed in the baking oven its excessive moisture of oven dry increases its plasticity;
With the pug after the ageing molded be the adobe of perforated brick;
5. the adobe of making being placed on 90 ℃ of baking ovens dries;
6. with dried adobe, 1050 ℃ of sintering 1.5 hours.
Obtained furring tile product ultimate compression strength is 13.56MPa, and hole ratio is 26.25%, satisfies the national standard requirement of the MU10 of GB13544-2000 " sintered perforated brick ".
Claims (4)
1. the building brick of a sintered from fly ash and red sandstone is characterized in that using flyash and Red Sandstone to be main raw material, adds that an amount of softening agent and water makes; Parts by weight of raw materials is a flyash: Red Sandstone: softening agent: water=50～60: 40～50: 1～5: 18～30.
2. the building brick of sintered from fly ash and red sandstone as claimed in claim 1, it is characterized in that described flyash is to burn the mass fly ashes that nature is stacked at the stock ground with fluidizing furnace, Red Sandstone is the natural resource that run off in the filling roadbed material passed into disuse in the road project or mountain area; Softening agent is a kind of in kaolin, the wilkinite.
3. the preparation technology of the building brick of sintered from fly ash and red sandstone as claimed in claim 1 is characterized in that adopting following steps:
(1) Red Sandstone is ground, grain diameter tails over 5% for the 0.080mm square hole sieve, and again in 50～60: 40～50: 1～5 weight part ratio is got flyash, Red Sandstone and softening agent, is placed in the stirrer, and siccative stirs;
(2) get continuous the pouring in the siccative in land and water of 18～30 weight parts, carry out secondary with stirrer again and mix and stir;
(3) pug that stirs was carried out ageing 1～3 hour, make pug fully wetting, seasoning or be placed in the baking oven its excessive moisture of oven dry increases its plasticity;
(4) with the needed brick shape of the molded or molded preparation of the pug hand after the ageing;
(5) adobe of making being placed on 80 ℃～120 ℃ baking ovens dries;
(6) with dried adobe, 900 ℃～1200 ℃ sintering 1～2 hour.
4. preparation technology as claimed in claim 3, it is characterized in that described flyash is to burn the mass fly ashes that nature is stacked at the stock ground with fluidizing furnace, Red Sandstone is the natural resource that run off in the filling roadbed material passed into disuse in the road project or mountain area; Softening agent is a kind of in kaolin, the wilkinite.