CN1947982A - Process for producing natural stone composite plate - Google Patents
Process for producing natural stone composite plate Download PDFInfo
- Publication number
- CN1947982A CN1947982A CN 200610118034 CN200610118034A CN1947982A CN 1947982 A CN1947982 A CN 1947982A CN 200610118034 CN200610118034 CN 200610118034 CN 200610118034 A CN200610118034 A CN 200610118034A CN 1947982 A CN1947982 A CN 1947982A
- Authority
- CN
- China
- Prior art keywords
- composite plate
- layer
- natural stone
- lithotome
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A combined slab is made up of natural stone through sizing ceramic tile, sizing marble tile, baking, combining, baking, cutting by needed sizes, sizing, baking, supplementing adhesive, baking, polishing, removing edges, chamferring, trimming and packing.
Description
Technical field
The present invention relates to a kind of natural stone composite board, relate in particular to a kind of processing technology of natural stone composite board.
Background technology
Stone material is as non-renewable resources, for a long time, numerous ore deposit masters, developer on quarrying stone inadequately rationally, science, ecological environment is caused in varying degrees destruction, and the product of listing also lacks market survey and prepares.And marble, granite class lithotome, because the high weight of price is big, be subjected to certain restriction in the use, some enterprise profit spaces constantly dwindle, when the road is walked narrower and narrower, part enterprise begins to pay attention to the location of self product, no longer manage single kind, the producer that has begins multi-channel management, and the enterprise that has turns to Products Development and productions such as artificial microlite, synthetic stone, but the complex manufacturing of products such as most of artificial microlite, synthetic stone is with high costs.
Summary of the invention
Purpose of the present invention is exactly to provide a kind of cost low for the defective that overcomes above-mentioned prior art existence, the processing technology of the simple natural stone composite board of technology.
Purpose of the present invention can be achieved through the following technical solutions:
A kind of processing technology of natural stone composite board is characterized in that, this technology may further comprise the steps:
(1) lithotome is cut into piece by certain specification, polishing is fixed thick and smooth, removes impurity such as surface dirt, sandstone, greasy dirt, the dry moisture of removing;
(2) be stained with ceramic tile in the lithotome upper and lower surface of handling with glue and be combined into elementary composite plate, leave standstill curing, adopt anchor clamps pressurization or jack evenly to pressurize, elementary composite plate pressurization is evenly distributed, and pressure is controlled at 4700kg/m
2When normal temperature cure 12 hours, winter temperature are low, elementary composite plate can be placed 120 ℃ drying room evenly to heat 3 hours, naturally cool to room temperature;
(3) with butt-splitting machine elementary composite plate is cut apart from middle marble layer, made elementary composite plate become two identical composite plates, this composite plate has two-layer, and one deck is the lithotome layer, and another layer is the ceramic tile layer;
(4) with above-mentioned composite plate by fixed thick, the oven dry back of certain specification and mend glue, fill up slit, the hole of lithotome surface layer, dry then, polish, side cut, chamfering, repair at last and promptly get product.
Described lithotome comprises marble, granite.
Described ceramic tile comprises artificial hard board such as clay brick, china clay brick, honeycomb aluminium sheet, cement plate, and its thickness is 5mm～30mm.
The consumption of described glue is 400～600g/m
2
Described composite plate thickness is 8mm～33mm, and specification is 300mm * 300mm～1200mm * 900mm.
Compared with prior art, the present invention is combined into composite plate with the gluing cheap ceramic tile of expensive lithotome upper and lower surface, and cutting into two halves from middle lithotome layer then becomes two composite plates.With ceramic tile instead of part lithotome, greatly reduce cost, and on the more coarse ceramic tile face gluing on than smooth lithotome such as marble surface gluing more helping install.
Description of drawings
Fig. 1 is a process chart of the present invention.
The specific embodiment
The invention will be further described below in conjunction with accompanying drawing.
Embodiment 1
As shown in Figure 1, a kind of processing technology of natural marble composite board, this technology may further comprise the steps:
(1) natural marble is slit into 603 * 603 specifications, polishing is fixed thick to be 20mm, and smooth, removes impurity such as surface dirt, sandstone, greasy dirt, the dry moisture of removing;
(2) in the natural marble upper and lower surface of handling with each sticking lastblock of glue and these marble length and width ceramic tile of uniform thickness 8mm (this ceramic tile adopt material such as ordinary cement manually synthetic) mutually, be combined into elementary composite plate, leave standstill curing, adopt anchor clamps pressurization or jack evenly to pressurize, elementary composite plate pressurization is evenly distributed, and pressure is controlled at 4700kg/m
2Again elementary composite plate is placed 120 ℃ drying room evenly to heat 3 hours, naturally cool to room temperature;
(3) with butt-splitting machine elementary composite plate is cut apart from middle marble layer, made elementary composite plate become two identical composite plates, this composite plate has two-layer, and one deck is the natural marble layer, and another layer is the ceramic tile layer;
(4) above-mentioned composite plate being pressed certain specification decides thick, the thickness of every composite plate is approximately 12mm, oven dry back and mends glue, fills up the slit of natural marble layer and ceramic tile interlayer, hole, dry then, polish, side cut, chamfering, repair at last and promptly get 600 * 600 product.
The consumption of glue is about 400～600g/m
2
Embodiment 2
A kind of processing technology of granite composite plate, this technology may further comprise the steps:
(1) natural granite is cut into 603 * 603 specifications, polishing is fixed thick to be 20mm, and smooth, removes impurity such as surface dirt, sandstone, greasy dirt, the dry moisture of removing;
(2) the natural granite upper and lower surface of handling with each sticking lastblock of glue and these granite length and width mutually the ceramic tile of uniform thickness 8mm be combined into elementary composite plate, leave standstill curing, adopt anchor clamps pressurization or jack evenly to pressurize, elementary composite plate pressurization is evenly distributed, and pressure is controlled at 4700k/m
2Normal temperature cure 12 hours;
(3) with butt-splitting machine elementary composite plate is cut apart from middle granite layer, made elementary composite plate become two identical composite plates, this composite plate has two-layer, and one deck is the natural granite layer, and another layer is the ceramic tile layer;
(4) above-mentioned composite plate being pressed certain specification decides thick, the thickness of every composite plate is approximately 12mm, oven dry back and mends glue, fills up the slit of natural granite layer and ceramic tile interlayer, hole, dry then, polish, side cut, chamfering, repair at last and promptly get 600 * 600 product.
The consumption of glue is about 400～600g/m
2
Claims (5)
1, a kind of processing technology of natural stone composite board is characterized in that, this technology may further comprise the steps:
(1) lithotome is cut into piece by certain specification, polishing is fixed thick and smooth, removes impurity such as surface dirt, sandstone, greasy dirt, the dry moisture of removing;
(2) be stained with ceramic tile in the lithotome upper and lower surface of handling with glue and be combined into elementary composite plate, leave standstill curing, adopt anchor clamps pressurization or jack evenly to pressurize, elementary composite plate pressurization is evenly distributed, and pressure is controlled at 4700kg/m
2When normal temperature cure 12 hours, winter temperature are low, elementary composite plate can be placed 120 ℃ drying room evenly to heat 3 hours, naturally cool to room temperature;
(3) with butt-splitting machine elementary composite plate is cut apart from middle marble layer, made elementary composite plate become two identical composite plates, this composite plate has two-layer, and one deck is the lithotome layer, and another layer is the ceramic tile layer;
(4) with above-mentioned composite plate by fixed thick, the oven dry back of certain specification and mend glue, fill up slit, the hole of lithotome surface layer, dry then, polish, side cut, chamfering, repair at last and promptly get product.
2, the processing technology of a kind of natural stone composite board according to claim 1 is characterized in that, described lithotome comprises marble, granite.
3, the processing technology of a kind of natural stone composite board according to claim 1 is characterized in that, described ceramic tile comprises artificial hard board such as clay brick, china clay brick, honeycomb aluminium sheet, cement plate, and its thickness is 5mm～30mm.
4, the processing technology of a kind of natural stone composite board according to claim 1 is characterized in that, the consumption of described glue is 400～600g/m
2
5, the processing technology of a kind of natural stone composite board according to claim 1 is characterized in that, described composite plate thickness is 8mm～33mm, and specification is 300mm * 300mm～1200mm * 900mm.