CN1935919A - 水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法 - Google Patents

水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法 Download PDF

Info

Publication number
CN1935919A
CN1935919A CN 200610096037 CN200610096037A CN1935919A CN 1935919 A CN1935919 A CN 1935919A CN 200610096037 CN200610096037 CN 200610096037 CN 200610096037 A CN200610096037 A CN 200610096037A CN 1935919 A CN1935919 A CN 1935919A
Authority
CN
China
Prior art keywords
water
moisture
proof air
copllymerized
organofluorine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610096037
Other languages
English (en)
Other versions
CN100547044C (zh
Inventor
华明扬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Ruco Technology Co., Ltd.
Original Assignee
华明扬
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 华明扬 filed Critical 华明扬
Priority to CNB2006100960374A priority Critical patent/CN100547044C/zh
Publication of CN1935919A publication Critical patent/CN1935919A/zh
Application granted granted Critical
Publication of CN100547044C publication Critical patent/CN100547044C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法。该方法是用二异氰酸酯和二元醇化合物、烷羟基硅烷、羟基氟硅油、二羟甲基丙酸反应，生产端基为－NCO的预聚体，然后用1，4丁二醇扩链。最后用胺调节pH值至中性后，加入含有抗菌剂的去离子水高速搅拌，加水调节粘度后，即得到防水透气透湿抗菌涂层胶。涂布于织物的表面，不但防水透气透湿，还对常见的细菌，霉菌有很强的杀菌作用。

Description

水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌 涂层胶的制备方法
技术领域
本发明涉及一种聚氨酯防水透气透湿涂层胶，具体涉及一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法。属有机化工技术领域。
背景技术
聚氨酯防水透气透湿涂层胶在纺织、皮革领域广泛应用，可以赋予涂层防水，透湿的特殊功效。目前，聚氨酯的涂层胶还是以油性聚氨酯为主，在生产和涂布时放出大量有害的有机溶剂，极不环保。而新型的水性聚氨酯材料因使用无毒的水为分散介质，极有市场潜力。但水性涂层胶更易受到细菌的侵害。
发明内容
本发明的目的在于克服上述不足，提供一种不仅有极高的防水透气透湿性能，而且可以对大多数细菌有抗杀作用的水性聚氨酯与有机硅、有机氟共聚防水透气透湿涂层胶的制备方法。
本发明的目的是这样实现的：一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于它是用二异氰酸酯和二元醇化合物、烷羟基硅烷、羟基氟硅油、二羟甲基丙酸反应，生产端基为-NCO的预聚体；然后用1，4丁二醇扩链；最后用胺调节pH值至中性后，加入含有抗菌剂的去离子水高速搅拌，加水调节粘度后，即得到防水透气透湿抗菌涂层胶。
本发明的具体工艺为：在反应器内加入二元醇化合物、烷羟基硅烷和羟基氟硅油，100-120℃抽真空1.5～2.5小时，加入二羟甲基丙酸，溶解后，降温到70-80℃，加入二异氰酸酯与催化剂二月桂酸二丁基锡(DBTDL)，保温搅拌90-100min，降温至60-70℃，加入1，4丁二醇，保温搅拌40-50min，降温至15-25℃，加入胺中和，加含有抗菌剂的去离子水，高速搅拌，加水调节粘度后，即得到防水透气透湿抗菌涂层胶。
本发明各物料是按照以下配比进行反应：
-NCO∶-OH＝3-4∶1，其中-NCO表示异氰酸酯基；
烷羟基硅烷、羟基氟硅油与二元醇化合物的摩尔比为：烷羟基硅烷∶羟基氟硅油∶二元醇化合物＝1∶0.4～0.6∶10～12；
二羟甲基丙酸与二元醇化合物的摩尔比为：二羟甲基丙酸∶二元醇化合物＝1∶12～15；
1，4丁二醇与二元醇化合物的摩尔比为：1，4丁二醇∶二元醇化合物1∶12～15。
本发明所述二元醇化合物为聚乙二醇或聚丙二醇；
本发明所述烷羟基硅烷为二羟乙基硅烷或二羟甲基硅烷；
本发明所述胺为乙二胺或己二胺；
本发明所述二异氰酸酯为IPDI、HDI、TDI或改性二亚胺MDI；
本发明所述聚乙二醇分子量为800-1200；聚丙二醇分子量为800-1200；防水透气透湿抗菌涂层胶的数据分子量为10000-20000，粘度为800-1000cps；
本发明所述抗菌剂为无机载银抗菌剂，平均粒径为5um以下。
抗菌剂的重量浓度为1-2％。
本发明不仅有极高的防水透气透湿性能，而且可以对大多数细菌有抗杀作用。本发明涂布于织物的表面，不但防水透气透湿，还对常见的细菌，霉菌有很强的杀菌作用。
具体实施方式
实施例1：
在烧瓶内加入120g聚乙二醇(分子量：1000)，8g二羟甲基硅烷，4g羟基氟硅油，100℃抽真空2小时，加入8g二羟甲基丙酸，溶解后，降温到72℃，加入28gHDI与6滴催化剂DBTDL，保温搅拌90min，降温至63℃，加入7.6g1，4丁二醇，保温搅拌40min，降温至25℃，加入乙二胺10g，将分散有6g无机载银氧化硅的水228g快速加入，高速搅拌1小时，得产品。经涂布后检测抗菌性能(按JIS Z2801：2000标准)，其抗菌活性值大于4.0。
实施例2：
在烧瓶内加入120g聚丙二醇(分子量：1000)，10g二羟乙基硅烷，5g羟基氟硅油，100℃抽真空2小时，加入7.8g二羟甲基丙酸，溶解后，降温到75℃，加入30gIPDI与6滴催化剂DBTDL，保温搅拌90min。降温至60℃，加入7.5g1，4丁二醇，保温搅拌40min，降温至20℃，加入乙二胺9g，将分散有6g无机载银氧化钛的水230克快速加入，高速搅拌1小时，得产品。经涂布后检测抗菌性能(按JIS Z2801：2000标准)，其抗菌活性值大于4.0。
实施例3：
在烧瓶内加入120g聚乙二醇(分子量：800)，9g二羟甲基硅烷，4.5g羟基氟硅油，100℃抽真空2小时，加入9g二羟甲基丙酸，溶解后，降温到72℃，加入28gHDI与6滴催化剂DBTDL，保温搅拌90min。降温至65℃，加入8.0g1，4丁二醇，保温搅拌40min，降温至20℃，加入己二胺10g，将分散有8g无机载银氧化硅的水230g快速加入，高速搅拌1小时，得产品。经涂布后检测抗菌性能(按JIS Z2801：2000标准)，其抗菌活性值大于4.7。

Claims (10)

1、一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于它是用二异氰酸酯和二元醇化合物、烷羟基硅烷、羟基氟硅油、二羟甲基丙酸反应，生产端基为—NCO的预聚体；然后用1，4丁二醇扩链；最后用胺调节pH值至中性后，加入含有抗菌剂的去离子水高速搅拌，加水调节粘度后，即得到防水透气透湿抗菌涂层胶。
2、根据权利要求1所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于具体工艺为：在反应器内加入二元醇化合物、烷羟基硅烷和羟基氟硅油，100-120℃抽真空1.5～2.5小时，加入二羟甲基丙酸，溶解后，降温到70-80℃，加入二异氰酸酯与催化剂DBTDL，保温搅拌90-100min，降温至60-70℃，加入1，4丁二醇，保温搅拌40-50min，降温至15-25℃，加入胺中和，加含有抗菌剂的去离子水，高速搅拌，加水调节粘度后，即得到防水透气透湿抗菌涂层胶。
3、根据权利要求2所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于各物料是按照以下配比进行反应：
-NCO∶-OH＝3-4∶1，其中-NCO表示异氰酸酯基；
烷羟基硅烷、羟基氟硅油与二元醇化合物的摩尔比为：烷羟基硅烷∶羟基氟硅油∶二元醇化合物＝1∶0.4～0.6∶10～12；
二羟甲基丙酸与二元醇化合物的摩尔比为：二羟甲基丙酸∶二元醇化合物＝1∶12～15；
1，4丁二醇与多元醇化合物的摩尔比为：1，4丁二醇∶多元醇化合物1∶12～15。
4、根据权利要求3所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述二元醇化合物为聚乙二醇或聚丙二醇。
5、根据权利要求3所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述烷羟基硅烷为二羟乙基硅烷或二羟甲基硅烷。
6、根据权利要求3所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述胺为乙二胺或己二胺。
7、根据权利要求3所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述二异氰酸酯为IPDI、HDI、TDI或改性二亚胺MDI。
8、根据权利要求4所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述聚乙二醇分子量为800-1200；聚丙二醇分子量为800-1200；防水透气透湿抗菌涂层胶的数据分子量为10000-20000，粘度为800-1000cps。
9、根据权利要求3所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述抗菌剂为无机载银抗菌剂，平均粒径为5um以下。
10、根据权利要求9所述的一种水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法，其特征在于所述抗菌剂的重量浓度为1-2％。
CNB2006100960374A 2006-09-14 2006-09-14 水性聚氨酯与有机硅、有机氟共聚防水透气透湿抗菌涂层胶的制备方法 Expired - Fee Related CN100547044C (zh)