CN1889211B - 钛酸钡y5u电容材料配方 - Google Patents
钛酸钡y5u电容材料配方 Download PDFInfo
- Publication number
- CN1889211B CN1889211B CN2006100883842A CN200610088384A CN1889211B CN 1889211 B CN1889211 B CN 1889211B CN 2006100883842 A CN2006100883842 A CN 2006100883842A CN 200610088384 A CN200610088384 A CN 200610088384A CN 1889211 B CN1889211 B CN 1889211B
- Authority
- CN
- China
- Prior art keywords
- dielectric
- titanate
- prescription
- barium titanate
- catio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种高压电容的电介质配方，为解决目前的电介质在高压应用领域中存在的耐压值低、介电常数低、介质损耗大的缺点，本发明钛酸钡BaTiO 380％、钛酸钙CaTiO 38-10％、氧化锌ZnO 0.1-2％、二氧化锰MnO 20.1-1％、三氧化二镝Dy2O34-8％、钛酸镁MgTiO33-5％组成电介质，这样就可以将电容的交流耐压值提高到1.5kV/mm，介电常数ε≈6000，在100Hz-10kHz的交流工作电流中，介质损耗≤0.0006，适用于作旁路，耦合使用或用于在低频损耗和电容量高、稳定性都非重要的鉴频电路中。
Description
技术领域
本发明涉及一种电容材料配方，尤其是高压电容的电介质配方。
背景技术
目前的高压电容电介质多数是CT8B氧化锌等陶瓷，云母，玻璃，塑料，和各种金属氧化物，但目前的这些材料在高压应用领域存在耐压值不高、介电常数低、介质损耗大等缺点，这样就影响着高压领域安全和限制着应用。
发明内容
本发明提供一种耐压值高、介电常数高、介质损耗小的电容电介质配方。
本发明是采用钛酸钡BaTiO380％、钛酸钙CaTiO38-10％、二氧化锌ZnO 0.5-2％、二氧化锰MnO20.1-1％、三氧化二镝Dy2O34-8％、钛酸镁MgTiO33-5％组成电介质。由于BaTiO3作为介电材料和光电材料，可用于制造体积小、容量大的微型电容器，用于制作半导体陶瓷，有利于提高介电常数。
采用本配方，就可以将电容的交流耐压值提高到15KV/mm，介电常数ε≈6000，在100Hz-10KHz的交流工作电流中，介质损耗≤0.0006。
具体实施方式
具体实施时，我们将上述钛酸钡BaTiO3、钛酸钙CaTiO3、氧化锌ZnO、二氧化锰MnO2、三氧化二镝Dy2O3、钛酸镁MgTiO3按配方比例混合后加入聚乙烯醇压制成型，然后在1250到1400摄氏度范围内烧结得到陶瓷电容。
在配比时，我们首先将碳酸钡BaCO3和二氧化钛TiO2、碳酸钙CaCO3和二氧化钛TiO2按照一定配比，经过球磨混合，进行干燥，然后在1000到1200摄氏度合成得到钛酸钡BaTiO3、钛酸钙CaTiO3；在得到钛酸钡BaTiO3、钛酸钙CaTiO3后，再将ZnO、二氧化锰MnO2、三氧化二镝Dy2O3、钛酸镁MgTiO3等按照配比搅拌球磨混合，加入8％的聚乙烯醇进行喷雾造粒，就可以得到本配方的电介质。
Claims (4)
1.一种高压电容的电介质配方，其特征是钛酸钡BaTiO380％、钛酸钙CaTiO38-10％、氧化锌ZnO 0.5-2％、二氧化锰MnO20.1-1％、三氧化二镝Dy2O34-8％、钛酸镁MgTiO33-5％组成电介质。
2.如权利要求1所述的高压电容的电介质配方，其特征是将上述钛酸钡BaTiO3、钛酸钙CaTiO3、氧化锌ZnO、二氧化锰MnO2、三氧化二镝Dy2O3、钛酸镁MgTiO3按配方比例混合后加入聚乙烯醇压制成型，然后在1250到1400摄氏度范围内烧结得到陶瓷电容。
3.如权利要求1所述的高压电容的电介质配方，其特征是首先将碳酸钡BaCO3和二氧化钛TiO2、碳酸钙Ca CO3和二氧化钛TiO2按照一定配比，经过球磨混合，进行干燥，然后在1000到1200摄氏度合成得到钛酸钡BaTiO3、钛酸钙CaTiO3。
4.如权利要求1所述的高压电容的电介质配方，其特征是在得到钛酸钡BaTiO3、钛酸钙CaTiO3后，再将ZnO、二氧化锰MnO2、三氧化二镝Dy2O3、钛酸镁MgTiO3按照配比搅拌球磨混合，加入8％的聚乙烯醇进行喷雾造粒。