CN1887810A - Press formed dry glaze for ceramic tile adobe and its prepn process - Google Patents
Press formed dry glaze for ceramic tile adobe and its prepn process Download PDFInfo
- Publication number
- CN1887810A CN1887810A CN 200610036550 CN200610036550A CN1887810A CN 1887810 A CN1887810 A CN 1887810A CN 200610036550 CN200610036550 CN 200610036550 CN 200610036550 A CN200610036550 A CN 200610036550A CN 1887810 A CN1887810 A CN 1887810A
- Authority
- CN
- China
- Prior art keywords
- glaze
- dry type
- weight portions
- weight part
- ceramic tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses one kind of dry glaze for once forming ceramic tile adobe and its preparation process. The dry glaze consists of type-I dry glaze and type-II dry glaze. The type-I dry glaze has the similar composition and sintered surface effect to that of ceramic tile adobe; and the type-II dry glaze consists of mineral materials and has the components including Li2O/Na2O/K2O 1.0-30 weight portions, CaO 1.0-25 weight portions, MgO 0-15 weight portions, ZnO 0-50 weight portions, BaO 0.5-20 weight portions, SiO2 40-80 weight portions, Al2O3 1.5-20 weight portions, ZrO2 0-30 weight portions, TiO2 0-35 weight portions, B2O3 0-30 weight portions, PbO 0-50 weight portions, P2O50-25 weight portions, and ceramic color or coloring oxide or other coloring compound 0-40 weight portions. The dry glaze may be used to obtain ceramic tile products with different surface decoration effects, high wear resistance, anti-fouling performance and other advantages.
Description
Technical field
The present invention relates to raw material of ceramic tile and preparation method thereof, more particularly relate to a kind of ceramic tile base glaze that is used for and once be pressed into dry type glaze of shape production and preparation method thereof.
Background technology
At present, the ceramic tile that the lithotome effect is arranged, its production method mainly contains: with the base earth material of adjusting in advance with various different colours, require to adopt different secondary material distributing modes according to pattern, have in the concavo-convex mould that the rigid material of natural-like stone lines makes in the surface, through press-molding, drying, burn till after, product surface has the irregular lithotome effect of similar surfaces.The shortcoming of this production method is: only use this a kind of material of base soil because of product 1., surface effect changes few, can only obtain texture and effect after base soil burns, can't obtain surface effects such as unglazed, the mute light, gloss as the glaze product, transparent, milky white or transmutation, if will obtain glossy surface, has only the use glossing; 2. simultaneously because brick body entire body is made for the base earth material, if does not polish on the surface, then be difficult to have concurrently anti-skidding and anti-pollution characteristic, if surface finish, then anti-skidding and anti-pollution characteristic all is difficult to reach service requirements.3. surface color and pattern effect are with low uncertainty, because all colours obtains by the toning of base earth material, so the color kind is less, add the restriction of distributing mode when producing, and can only go out some fixed patterns by cloth, and change in pattern is single.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, the glaze product of different-effect is made dry powder or dry granular shape, before adobe is shaped, comply with required pattern cloth in blank surface by specific apparatus for distributing, through press forming of base glaze is ceramic tile blank, after drying is burnt till, can obtain the surface and have tile product as effects such as unglazed, inferior light, light, milkiness, transmutation and lithotome pattern effect, it is good that such tile product also has wear resistance, pollution resistance and non-skid property simultaneously, and advantage such as "dead".The present invention just provides composition of this dry type glaze and preparation method thereof.
The technical solution that the present invention adopts in order to solve the problems of the technologies described above is as follows:
A kind of ceramic tile base glaze that is used for once is pressed into the dry type glaze that shape is produced, and it is constituted for the dry type glaze for dry type glaze and II by I, and wherein I generation and II are made up of following component respectively again for the dry type glaze;
I is for the dry type glaze, constitute by raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, aluminum oxide powder, triphane, Feldspar Powder and burning talcum powder etc. and ceramic pigment or coloring oxide or coloring compound, its component and proportioning are (weight part), Li
2O/Na
2O/K
2O 2～5, CaO 0～1, MgO 0.5～2.0, SiO
260～80, Al
2O
315～25, ceramic pigment or coloring oxide or coloring compound 0～40;
II is for the dry type glaze, constitute by flux frit and ceramic pigment or coloring oxide or coloring compound of raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, zinc oxide, calcium phosphate, wollastonite, barium carbonate, aluminum oxide powder, titanium dioxide, triphane, Feldspar Powder and burning talcum powder etc. and low temperature, set of dispense is than being (weight part), Li
2O/Na
2O/K
2O 1.0～30, CaO 1.0～25, MgO 0～15, ZnO 0～50, BaO 0.5～20, SiO
240～80, Al
2O
31.5～20, ZrO
20～30, TiO
20～35, B
2O
30～30, PbO 0～50, P
2O
50～25, ceramic pigment or coloring oxide or coloring compound 0～40.
I is similar for dry type glaze burning rear surface effect and ceramic tile blank surface effect, and specific surface is white mutually with general ceramic tile blank when adding coloring material, the shape that is translucent, and resistance to soiling is also good than general ceramic tile blank surface; Can add all kinds of coloring materials as required and obtain the distinct colors effect.
II is made up of the product of a plurality of different ingredients for the dry type glaze, burn the rear surface and can obtain various glaze effects, as effects such as unglazed, mute light, gloss, transparent, milky white or transmutation, and can be modulated into shades of colour and pattern as required, resistance to soiling is also the same with ordinary porcelain brick glaze face good.
A kind ofly adopt the above-mentioned preparation method that ceramic tile base glaze once is pressed into the dry type glaze that shape produces that is used for, this preparation method comprises the steps:
(1.1) raw material of said components got ready with water mixed, after mixing with 100: 25～45 weight parts, add ball milling 10～30h in the ball mill (hour), ball milling is that 10000-hole sieve only surpluss 5～0.05% to the material fineness;
(1.2) above-mentioned ball milling is good slurry is emitted from ball mill, after deironing, sieving, deposits in the pulp storage tank and stirs 1～3 day;
(1.3) above-mentioned slurry is sent in the spray-drying tower by slush pump, be dried to size range 10～200 purpose dry type materials, promptly can be used as finished product and use.
In described (1.1) step, also can increase the interpolation binding agent in the mixing process of raw material and water, the raw material of said components be got ready with water and binding agent mixed, with 100: 25～45: (0.1～1) weight part mixes,
Described binding agent is the compound that commercial water glass, glue, CMC etc. have the binding agent effect.
After described (1.3) step, also increasing has the 3.4th step, is about to this dry type material fire-resistant saggar of packing into, places calcination equipment to be calcined to into after particle can not twist into pieces with finger with optimal temperature, promptly can be used as finished product.
Because dry type glaze product of the present invention is used in compression moulding technology of ceramic tile base glaze,, require this product particle to possess certain size and shape in order to be fit to the compression moulding process requirements.Though can obtain satisfactory particle by the spraying drying mode, some product is subjected to the influence of external force or environment in transportation or storage process, and its shape and size can not continue to keep, and phenomenons such as particle deformation, reunion, fine-powdered may occur.Therefore, according to needs of production, can adopt add binding agent or under cold condition the incinerating preparation method reach required coating of particles and size.
Use above-mentioned raw materials and preparation method's dry type glaze, use about 1200 ℃ ± 20 ℃ of firing temperatures, the quick baking into porcelain wall of firing period 50～120min floor tile.
The effect that the present invention adopts technique scheme to reach is: adopt the tile product surface of product manufacturing of the present invention to have the lithotome effect, can glaze be reached as unglazed by adjusting this dry granular glaze composition or proportioning, inferior light, transparent, milkiness, various effects such as transmutation, and pattern can be changed by the difference of distributing mode, make and produce the natural stone texture that each tile all has slight change, whole structure is natural and tripping after the paving, noble elegant, improved in the existing technology effect that can't reach lithotome when laying, enriched the kind of natural-like stone ceramic tile because of the single in use whole amalgamation of product pattern.Simultaneously it has avoided non-environmental protection factor such as lithotome potential radioactivity problem and the not resistant that causes because of polishing, not anti-skidding problem fully, have advantages such as "dead", wear resistance, pollution resistance and non-skid property be good, become the favorable substitutes of lithotome in indoor use.
Embodiment
Embodiment 1:
Be used for ceramic tile base glaze and once be pressed into the dry type glaze that shape is produced, this technology is made up of for the dry type glaze for dry type glaze and II I with glaze;
Described I can constitute colourless glaze for the dry type glaze, and its set of dispense ratio is Li
2O/Na
2O/K
2O weight part 5, CaO weight part 1, MgO weight part 2.0, SiO
2Weight part 70, Al
2O
3Weight part 22;
Described II can constitute colour glaze for dry type glaze group, and its set of dispense ratio is Li
2O/Na
2O/K
2O weight part 4, CaO weight part 15, MgO weight part 2, ZnO weight part 2, BaO weight part 10, ZrO
2Weight part 15, TiO
2Weight part 10, SiO
2Weight part 42, Al
2O
3Weight part 15, B
2O
3Weight part 10, PbO weight part 20, P
2O
5Weight part 10, ceramic pigment or coloring oxide or coloring compound weight part 10;
The preparation method's step that adopts above-mentioned raw materials to make glaze is, one, the raw material of said components got ready with water mixes, after mixing with 100: 25 weight parts, add ball milling 20h in the ball mill, and ball milling is that 10000-hole sieve only surpluss 0.05% to the material fineness;
Two, above-mentioned ball milling is good slurry is emitted from ball mill, after deironing, sieving, deposits in the pulp storage tank and stirs 3 days;
Three, above-mentioned mud is sent in the spray-drying tower by slush pump, dry size range standard sieve 10～200 purpose dry type materials, dry type material can be directly as the finished product storage of putting in storage.
Four, this thousand formulas material fire-resistant saggar of also can packing into gets final product finished product after placing equipment to be calcined to a formula material.
Its size composition is decided according to actual service requirements and design picture effect.
Embodiment 2:
This technology is made up of for the dry type glaze for dry type glaze and II I with glaze;
Described I can constitute colour glaze for the dry type glaze, and its set of dispense ratio is Li
2O/Na
2O/K
2O weight part 3, CaO weight part 2.5, MgO weight part 1.5, SiO
2Weight part 60, Al
2O
3Weight part 15, ceramic pigment or coloring oxide or coloring compound weight part 20.5;
Described II can constitute colourless glaze for the dry type glaze, and the set of dispense ratio is Li
2O/Na
2O/K
2O weight part 6, CaO weight part 20, MgO weight part 5, ZnO weight part 3, BaO weight part 5, ZrO
2Weight part 10, TiO
2Weight part 15, SiO
2Weight part 50, Al
2O
3Weight part 17, B
2O
3Weight part 20, PbO weight part 15, P
2O
5Weight part 5;
The preparation method's step that adopts above-mentioned raw materials to make glaze is, one, the raw material of said components got ready with water and water glass mixes, after mixing with 100: 45: 0.3 weight parts, add ball milling 15h in the ball mill, and ball milling is that 10000-hole sieve only surpluss 5% to the material fineness;
Two, above-mentioned ball milling is good slurry is emitted from ball mill, after deironing, sieving, deposits in the pulp storage tank and stirs 1 day;
Three, above-mentioned mud is sent in the spray-drying tower by slush pump, dry size range standard sieve 10～200 purpose dry type materials, this dry type material can be directly as the finished product storage of putting in storage.
Size composition is decided according to actual service requirements and design picture effect.
Embodiment 3:
This technology is made up of for the dry type glaze for dry type glaze and II I with glaze;
Described I can constitute colour glaze for the dry type glaze, and its set of dispense ratio is Li
2O/Na
2O/K
2O weight part 5, CaO weight part 1, MgO weight part 1, SiO
2Weight part 65, Al
2O
3Weight part 20, ceramic pigment or coloring oxide or coloring compound weight part 8;
Described II can constitute colourless glaze for the dry type glaze, and the set of dispense ratio is Li
2O/Na
2O/K
2O weight part 2, CaO weight part 15, MgO weight part 1, ZnO weight part 5, BaO weight part 10, ZrO
2Weight part 12, TiO
2Weight part 13, SiO
2Weight part 57, Al
2O
3Weight part 15, B
2O
3Weight part 25, PbO weight part 30, P
2O
5Weight part 15;
Making method is with example 1.
Use above-mentioned raw materials and preparation method's dry type glaze; be used in about 1200 ℃ ± 20 ℃ of firing temperatures; the quick baking into porcelain wall of firing period 50～120min floor tile; during use; prior to the good above-mentioned dry type glaze of cloth in framed; or above-mentioned dry type glaze is distributed in first precompressed on press in the mould; then on good base-material of cloth or the base-material that presses in advance; use is such as pulley type; duck-beak type; silk screen printing; all kinds of dry granulars or dry powder distributing modes such as roller printing; the dry type glaze of dissimilar or color is arranged according to layout is required; and then be pressed into adobe with base-material; after drying or drying add coloured silk; under temperature required condition, burn till, obtain the ceramic tile finished product through post-processed such as edging chamferings then.
This product is used in brand-new ceramic tile base glaze and once is pressed into the shape production technique, the gained tile product, and good product quality, decorative effect is good, and the substitute that can be used as lithotome is used.
Claims (5)
1, a kind of ceramic tile base glaze that is used for once is pressed into the dry type glaze that shape is produced, and it is characterized in that it is constituted for the dry type glaze for dry type glaze and II by I, and wherein I generation and II are made up of following component respectively again for the dry type glaze:
I is for the dry type glaze, constitute by raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, aluminum oxide powder, triphane, Feldspar Powder and burning talcum powder etc. and ceramic pigment or coloring oxide or coloring compound, its component and proportioning are (weight part), Li
2O/Na
2O/K
2O 2～5, CaO 0～1, MgO 0.5～2.0, SiO
260～80, Al
2O
315～25, ceramic pigment or coloring oxide or coloring compound 0～40;
II is for the dry type glaze, constitute by flux frit and ceramic pigment or coloring oxide or coloring compound of raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, zinc oxide, calcium phosphate, wollastonite, barium carbonate, aluminum oxide powder, titanium dioxide, triphane, Feldspar Powder and burning talcum powder etc. and low temperature, set of dispense is than being (weight part), Li
2O/Na
2O/K
2O 1.0～30, CaO 1.0～25, MgO 0～15, ZnO 0～50, BaO 0.5～20, SiO
240～80, Al
2O
31.5～20, ZrO
20～30, TiO
20～35, B
2O
30～30, PbO 0～50, P
2O
50～25, ceramic pigment or coloring oxide or coloring compound 0～40.
2, a kind of claim 1 is described is used for the preparation method that ceramic tile base glaze once is pressed into the dry type glaze that shape produces, and it is characterized in that this preparation method comprises the steps:
(1.1) raw material of said components got ready with water mixed, after mixing with 100: 25～45 weight parts, add ball milling 10～30h in the ball mill (hour), ball milling is that 10000-hole sieve only surpluss 5～0.05% to the material fineness;
(1.2) above-mentioned ball milling is good slurry is emitted from ball mill, after deironing, sieving, deposits in the pulp storage tank and stirs 1～3 day;
(1.3) above-mentioned slurry is sent in the spray-drying tower by slush pump, be dried to size range 10～200 purpose dry type materials, promptly can be used as finished product and use.
3, according to claim 2ly be used for the preparation method that ceramic tile base glaze once is pressed into the dry type glaze that shape produces, it is characterized in that, in described (1.1) step, also can increase the interpolation binding agent in the mixing process of raw material and water, the raw material of said components got ready with water and binding agent mix, with 100: 25～45: (0.1～1) weight part mixes.
4, according to claim 3ly be used for the preparation method that ceramic tile base glaze once is pressed into the dry type glaze that shape produces, it is characterized in that, described binding agent is the compound that commercial water glass, glue, CMC have the binding agent effect.
5, according to claim 2ly be used for the preparation method that ceramic tile base glaze once is pressed into the dry type glaze that shape produces, it is characterized in that, after described (1.3) step, also increase the 3.4th step is arranged, be about to this dry type material fire-resistant saggar of packing into, place calcination equipment to be calcined to into after particle can not twist into pieces with finger, promptly can be used as finished product with optimal temperature.