CN1884455A - Domestic honeycomb charcoal produced from straw carbon and its preparation method - Google Patents
Domestic honeycomb charcoal produced from straw carbon and its preparation method Download PDFInfo
- Publication number
- CN1884455A CN1884455A CNA2006100859364A CN200610085936A CN1884455A CN 1884455 A CN1884455 A CN 1884455A CN A2006100859364 A CNA2006100859364 A CN A2006100859364A CN 200610085936 A CN200610085936 A CN 200610085936A CN 1884455 A CN1884455 A CN 1884455A
- Authority
- CN
- China
- Prior art keywords
- water
- charcoal
- carbon
- straw carbon
- making
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates the domestic fuel, especially the honeycomb charcoal made by straw charcoal. The fuel comprises the quartz flour, soluble glass or boracic acid, straw charcoal and water, and the mass ratio of them is 35- 40: 1.75-2.0: 50-70. The method comprises the following steps: squashing, stirring, squeezing, forming, drying, and getting the product. The honeycomb charcoal can be made to honey-comb coal.
Description
Technical field
The present invention relates to a kind of domestic fuel, particularly domestic honeycomb charcoal of making of the stalk charcoal and preparation method thereof.
Background technology
The fuel of making after charing with agriculture and forestry organic waste material has environmental protection, low cost and saves the advantage of Nonrenewable resources, particularly makes domestic fuel as heating or cook and be popular in northern China, uses extensively.But existing with agriculture and forestry organic waste material particularly the civilian charcoal fuel made of stalk a common shortcoming is arranged is can become ashes after the moulding burning, cave in while burning, all can not keep original shape, just can't use this energy as honeycomb briquette stove, and honeycomb briquette stove is a kind of very popular stove and accessory, and resident and refreshment bar are all in a large amount of uses, as not being applicable to honeycomb briquette stove, these energy are with regard to incompatibility resident's use technology requirement like this, and then its popularization will be very restricted.Ashes after the burning stop up ventilation duct easily and cause incomplete combustion in addition, need add blast apparatus and strengthen fully burning of oxygen-supplying amount assurance, otherwise can produce obnoxious flavour.
Summary of the invention
The objective of the invention is to provides the domestic honeycomb charcoal of making of the stalk charcoal that still can keep original shape after a kind of burning for overcoming the deficiencies in the prior art.
Further purpose of the present invention provides a kind of above-mentioned method of using the domestic honeycomb charcoal of stalk charcoal making of making.
To achieve these goals, the invention provides a kind of domestic honeycomb charcoal of making of the stalk charcoal, it is characterized in that its food ingredient is silica powder, water glass or boric acid, the broken end of stalk charcoal and an amount of water, described silica powder: water glass or boric acid: stalk charcoal powdered carbon is 35～40: 1.75～2.0 by mass ratio: 50～70, and described an amount of water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials.The method of the domestic honeycomb charcoal that the stalk charcoal is made is at first stalk charcoal powdered carbon to be crushed to below 70 orders, adds silica powder and water glass or boric acid and water again and evenly stirs, and extrusion molding then, last natural air drying or oven dry get final product.
Owing in this civilian charcoal of making of straw carbon, added silica powder, thereby silica powder can keep original shape with other material sintering together behind high temperature sintering, therefore can make the stalk charcoal product of various the same shapes with honeycomb briquette and technical requirements.
Embodiment
Concrete enforcement 1: prepare material silica powder 720KG, water glass 38KG, straw carbon 1000KG, with straw carbon pour into be crushed to below 70 orders in the beater grinder after, put in the stirrer, again silica powder and water glass and water are added and stirred 60 minutes, water can not be excessive, water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials, mixture after being mixed is put into the honeycomb briquet forming machine extrusion molding, and natural air drying or oven dry get final product.
Concrete enforcement 2: prepare material silica powder 700KG, water glass 35KG, straw carbon 1265KG, with straw carbon pour into be crushed to below 70 orders in the beater grinder after, put in the stirrer, again silica powder and water glass and water are added and stirred 60 minutes, water can not be excessive, water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials, mixture after being mixed is put into the honeycomb briquet forming machine extrusion molding, and natural air drying or oven dry get final product.
Concrete enforcement 3: prepare material silica powder 800KG, boric acid 40KG, straw carbon 1350KG, with straw carbon pour into be crushed to below 70 orders in the beater grinder after, put in the stirrer, again silica powder and water glass and water are added and stirred 60 minutes, water can not be excessive, water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials, mixture after being mixed is put into the honeycomb briquet forming machine extrusion molding, and natural air drying or oven dry get final product.
Concrete enforcement 4: prepare material silica powder 780KG, boric acid 36KG, straw carbon 1400KG, with straw carbon pour into be crushed to below 70 orders in the beater grinder after, put in the stirrer, again silica powder and water glass and water are added and stirred 60 minutes, water can not be excessive, water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials, mixture after being mixed is put into the honeycomb briquet forming machine extrusion molding, and natural air drying or oven dry get final product.
Claims (3)
1, a kind of domestic honeycomb charcoal of making of straw carbon, it is characterized in that its food ingredient is English powder, water glass or boric acid, the broken end of straw carbon and an amount of water, described silica powder: water glass or boric acid: the straw carbon powdered carbon is 35～40: 1.75～2.0 by mass ratio: 50～70, and described an amount of water is pinched agglomerating diffusing being as the criterion after making above-mentioned mixing of materials.
2, the domestic honeycomb charcoal of making of straw carbon according to claim 1, it is characterized in that described silica powder: water glass or boric acid: the straw carbon powdered carbon is 35: 1.75: 63.25.
3, a kind of method of making the described domestic honeycomb charcoal of claim 1 is characterized in that method may further comprise the steps:
A, the straw carbon powdered carbon is crushed to below 70 orders;
B, adding silica powder and water glass or boric acid and water evenly stir;
C, extrusion molding;
D, natural air drying or oven dry get final product.