CN1884399A - Wall putty for inner and outer wall decoration - Google Patents
Wall putty for inner and outer wall decoration Download PDFInfo
- Publication number
- CN1884399A CN1884399A CN 200510027045 CN200510027045A CN1884399A CN 1884399 A CN1884399 A CN 1884399A CN 200510027045 CN200510027045 CN 200510027045 CN 200510027045 A CN200510027045 A CN 200510027045A CN 1884399 A CN1884399 A CN 1884399A
- Authority
- CN
- China
- Prior art keywords
- powder
- wall
- decoration
- wall putty
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates the wall putty, comprising 50-60wt% white marble powder, 8-10wt% tabular spar powder, 8-10wt% talcum powder, 8-10wt% white cement, 8-10wt% sierozem powder, 0.5-0.8wt% organic binding agent, 0.5-0.8wt% water-loss reducer, and 0.2-0.5wt% anticracking agent. The wall putty has the advantages of soapy handle, jade white, good decoration property, good binding power and crack resistance, innocuous, and environmental protection.
Description
Technical field:
The present invention relates to the technical field of wall body decoration, specifically a kind of environment friendly wall putty that is used for decorating inner and external walls.
Background technology:
Present wall putty often thicker, the many impurity of particle, cohesive force is poor, be coated with that decorate properties is poor on the wall, more coarse and with tiny crackle, for interior metope, need apply the decorative effect that the layer 2-3 emulsion paint just can reach pure white exquisiteness on the wall putty surface again, existing wall putty always has pungent smell simultaneously, and not environmental protection is detrimental to health.
Summary of the invention:
The object of the present invention is to provide a kind of improved wall putty that is used for decorating inner and external walls, it can overcome the prior art decorate properties low, have that sharp aroma, particle are thick, the some shortcomings of cohesive force difference.
To achieve these goals, technical scheme of the present invention is: a kind of wall putty that is used for inner wall decoration is characterized in that: the prescription of described wall putty is as follows: weight percent is the white marble powder of 50-60%, the wollastonite powder of 8-10%, the talcum powder of 8-10%, the white cement of 8-10%, the grey calcium powder of 8-10%, the organic binder bond of 0.5-0.8%, the water-holding agent of 0.5-0.8% and the anti-fissuring agent of 0.2-0.5%.
A kind of wall putty that is used for decoration of exterior wall is characterized in that: the prescription of described wall putty is as follows: weight percent is the white marble powder of 25-35%, the wollastonite powder of 16-20%, the talcum powder of 8-10%, the white cement of 24-30%, the grey calcium powder of 8-10%, the organic binder bond of 1.5-2%, the water-holding agent of 0.8-1% and the anti-fissuring agent of 0.5-0.8%.
Wall putty of the present invention is basic stopping composition with white marble powder during use, wollastonite powder and talcum powder are function row stopping composition, because white marble powder wetting capacity height, dispersibility is good, inclusion-free, soft and moist exquisiteness, so the wall putty feel exquisiteness made from it, pure white soft, decorate properties is high, on metope, do not cover with paint, lacquer, colour wash, etc. emulsion paint and can obtain the excellent decoration effect yet even batch scrape, the cohesive force and the resistance to cleavage of wollastonite powder energy strongthener, make the wall putty environment-protecting asepsis that makes, tasteless.
Embodiment:
The invention will be further described below in conjunction with embodiment.
A kind of wall putty that is used for inner wall decoration of the present invention, its difference with the prior art is: the prescription of described wall putty is as follows: weight percent is the white marble powder of 50-60%, the wollastonite powder of 8-10%, the talcum powder of 8-10%, the white cement of 8-10%, the grey calcium powder of 8-10%, the organic binder bond of 0.5-0.8%, the water-holding agent of 0.5-0.8% and the anti-fissuring agent of 0.2-0.5%.A kind of wall putty that is used for decoration of exterior wall is characterized in that: the prescription of described wall putty is as follows: weight percent is the white marble powder of 25-35%, the wollastonite powder of 16-20%, the talcum powder of 8-10%, the white cement of 24-30%, the grey calcium powder of 8-10%, the organic binder bond of 1.5-2%, the water-holding agent of 0.8-1% and the anti-fissuring agent of 0.5-0.8%.Wherein organic binder bond is the high molecular polymer latex powder, water-holding agent is a Mierocrystalline cellulose, but the water-retentivity of Mierocrystalline cellulose strongthener, prevent too fast drying of cement and sclerosis cracking phenomena, increase the plasticity-of material, improve construction operation, improve the adhesive property of material, make its better bonding substrates, sliding phenomenon appears in material in the time of can preventing to construct.Anti-fissuring agent is a wood fibre, wood fibre is water-fast natural fiber, have good snappiness, dispersiveness and unreactiveness, can improve the toughness of material, strengthen and make power effect and thickening power, improve thixotropy and sag resistance, improve stability, increase anti-the contraction and anti-cracking performance, prolong the operating time.The precision of white marble powder is 350 orders, and the precision of wollastonite powder, talcum powder and grey calcium powder is 325 orders, and the precision of high molecular polymer latex powder is 400 orders.Wherein white marble powder, wollastonite powder, talcum powder, white cement, grey calcium powder, high molecular polymer latex powder, Mierocrystalline cellulose and wood fibre are directly can buy on market.
More than during each form to divide, white marble is the double salt of lime carbonate and magnesiumcarbonate, mohs hardness 3.5-4, and the mohs hardness of common dicalcium powder is 3-3.5, because the hardness height, but strongthener intensity contains the magnesiumcarbonate composition and can improve material and criticize the slippery scraped and the surperficial feel slippery after the moulding, the white marble ctystallizing point is very little, and accessory mineral is few, so its purity height, whiteness is good, have fine and smooth pure white characteristics, its decorate properties is good, has surmounted other putty of producing with dicalcium powder.Needle-shaped wollastonite powder as functional stopping composition, can improve tensile strength, shock strength, flexural strength, linear stretch and the mould shrinking percentage of material with the raphioid fiber of its uniqueness, is used in the material to strengthen resistance to cleavage.The talcum powder major ingredient is silicon-dioxide, magnesium oxide, exists because of it has the magnesium composition, can improve criticizing of material and scrape the slippery grinability.White cement, grey calcium powder belong to inorganic coagulation material, and white cement can improve intensity and water tolerance, grey calcium powder problem high strength and plasticity-.
Latex powder wherein is a kind of dispersibility polymeric binder, for material provides cohesiveness, wear resistance and good snappiness, can improve the adhesive property and the force of cohesion of material, increase the elasticity and the flexural strength of material, improve the shock-resistance and the weathering resistance of material, reduced the water-absorbent of material and improved the water-retentivity of use.
Embodiment 1
Prepare a kind of wall putty that is used for inner wall decoration, earlier the anti-fissuring agent wood fibre of the white marble powder of weight percent 60%, 10% wollastonite powder, 10% talcum powder, 10% white cement, 10% grey calcium powder, 0.5% organic binder bond, 0.5% water-holding agent Mierocrystalline cellulose and 0.2% is dropped into the feed opening of lift respectively, by the screw-blade in the lift above-mentioned blended material is risen to the top, enter then in the stirrer cylindrical shell, above-mentioned material stirs in stirrer and reaches evenly the packing bag of packing at last after 5 minutes.During use, only needing will to go into weight percent and be the wall putty that 70% water promptly can be used as inner wall decoration in above-mentioned blended material uses, this putty feel exquisiteness, pure white soft, decorate properties is high, do not cover with paint, lacquer, colour wash, etc. emulsion paint on the wall and can obtain the excellent decoration effect yet even batch scrape.
Embodiment 2
Prepare a kind of wall putty that is used for decoration of exterior wall, with weight percent is to put into stirrer mixing stirring after the anti-fissuring agent wood fibre of 30% white marble powder, 20% wollastonite powder, 10% talcum powder, 30% white cement, 10% grey calcium powder, 1.5% organic binder bond, 1% water-holding agent Mierocrystalline cellulose and 0.5% mixes, after stirring, just pack in the packing bag, can use after the water of adding weight percent 50% stirs in above-mentioned blended powder during use.This wall putty is ornamental very strong, and hardness height, inclusion-free, and splitting resistance is good.
Claims (8)
1, a kind of wall putty that is used for inner wall decoration, it is characterized in that: the prescription of described wall putty is as follows: weight percent is the white marble powder of 50-60%, the wollastonite powder of 8-10%, the talcum powder of 8-10%, the white cement of 8-10%, the grey calcium powder of 8-10%, the organic binder bond of 0.5-0.8%, the water-holding agent of 0.5-0.8% and the anti-fissuring agent of 0.2-0.5%.
2, a kind of wall putty that is used for inner wall decoration according to claim 1, it is characterized in that: organic binder bond is the high molecular polymer latex powder, and water-holding agent is a Mierocrystalline cellulose, and anti-fissuring agent is a wood fibre.
3, a kind of wall putty that is used for inner wall decoration according to claim 1, it is characterized in that: the precision of white marble powder is 350 orders, the precision of wollastonite powder, talcum powder and grey calcium powder is 325 orders.
4, a kind of wall putty that is used for inner wall decoration according to claim 2, it is characterized in that: the precision of high molecular polymer latex powder is 400 orders.
5, a kind of wall putty that is used for decoration of exterior wall, it is characterized in that: the prescription of described wall putty is as follows: weight percent is the white marble powder of 25-35%, the wollastonite powder of 16-20%, the talcum powder of 8-10%, the white cement of 24-30%, the grey calcium powder of 8-10%, the organic binder bond of 1.5-2%, the water-holding agent of 0.8-1% and the anti-fissuring agent of 0.5-0.8%.
6, a kind of wall putty that is used for decoration of exterior wall according to claim 3, it is characterized in that: organic binder bond is the high molecular polymer latex powder, and water-holding agent is a Mierocrystalline cellulose, and anti-fissuring agent is a wood fibre.
7, a kind of wall putty that is used for decoration of exterior wall according to claim 3, it is characterized in that: the precision of white marble powder is 350 orders, the precision of wollastonite powder, talcum powder and grey calcium powder is 325 orders.
8, a kind of wall putty that is used for decoration of exterior wall according to claim 4, it is characterized in that: the precision of high molecular polymer latex powder is 400 orders.