CN1855323B - 电感镇流器h级白色绝缘漆绝缘处理工艺 - Google Patents
电感镇流器h级白色绝缘漆绝缘处理工艺 Download PDFInfo
- Publication number
- CN1855323B CN1855323B CN200510025469A CN200510025469A CN1855323B CN 1855323 B CN1855323 B CN 1855323B CN 200510025469 A CN200510025469 A CN 200510025469A CN 200510025469 A CN200510025469 A CN 200510025469A CN 1855323 B CN1855323 B CN 1855323B
- Authority
- CN
- China
- Prior art keywords
- ballast
- lacquer
- minutes
- white insulating
- varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于电感镇流器H级白色绝缘漆绝缘处理技术领域。本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺具体步骤如下:将镇流器预烘,然后依次浸漆、滴漆、烘焙,浸漆和滴漆全部采用H级白色绝缘漆。本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺,在保证产品质量的前提下实现了一浸一烘技术,与现有技术相比在工序上减少了一半,使材料成本和制造成本大大降低,经济效益十分显著。
Description
技术领域
本发明属于电感镇流器H级白色绝缘漆绝缘处理技术领域。
背景技术
现有的电感镇流器作H级白色绝缘漆绝缘处理技术一般采用以下两种工艺:
1.两浸两烘工艺,工艺流程图见图1。
该工艺两次浸漆都采用H级白色绝缘漆,第一次浸漆时间长,作深度浸渍;第二次浸漆时间只有几秒,只作表面处理,其中两次浸漆中间要对产品表面进行除漆瘤处理。
2.一浸一烘再一涂一烘工艺,工艺流程图见图2。
该工艺第一遍浸漆采用H级清漆,然后对产品表面进行除漆瘤处理,第二遍采用白色绝缘漆进行喷涂处理。
以上工艺都必须采取两次浸渍两次烘焙工序才能满足产品要求,这样不仅油漆消耗量很大,而且产品制造成本很高。如采用一次浸渍一次烘焙后产品表面出现较多气泡,而且有的产品存在黄斑,严重影响产品外观质量。
发明内容
本发明的目的就是在不影响产品质量的前提下,简化现有生产工艺、降低生产成本,提供一种新的电感镇流器H级白色绝缘漆绝缘处理工艺。
为了达到上述目的,本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺采用一浸一烘工艺,不影响产品的质量,工艺流程图见图3。
本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺具体步骤如下:将镇流器预烘,然后依次浸漆、滴漆、烘焙,浸漆和滴漆全部采用H级白色绝缘漆。
本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺,镇流器的硅钢片选用S-808挥发油冲制,硅钢片浸漆前要求不生锈,产品没有乱片。
本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺,所用的H级白色绝缘漆可以是上海振立实业有限公司生产的HD-180-1H级白色绝缘漆。
本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺,预烘温度60℃~80℃,时间0.5~1小时;浸漆时间为8~10分钟;在产品出浸漆缸端设送漆喷淋头,对产品起除油斑和气泡作用,滴漆时间为30~40分钟;烘焙时,90℃~95℃烘40~60分钟,135℃~145℃烘120~150分钟;烘焙阶段完成后冷却即可下线。
本发明的有益效果:本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺,在保证产品质量的前提下实现了一浸一烘技术,与现有技术相比在工序上减少了一半,使材料成本和制造成本大大降低,经济效益十分显著。
附图说明
图1是现有电感镇流器绝缘漆绝缘处理两浸两烘工艺流程图。
图2是现有电感镇流器绝缘漆绝缘处理一浸一烘再一涂一烘工艺流程图。
图3是本发明所述的电感镇流器H级白色绝缘漆绝缘处理工艺流程图。
具体实施方式
实施例1
选用S-808挥发油冲制的硅钢片做镇流器,硅钢片浸漆前要求不生锈,产品没有乱片。将镇流器在60℃下预烘1小时,冷却后常压浸漆8分钟,采用上海振立实业有限公司生产的HD-180-1H级白色绝缘漆,浸漆后再滴漆40分钟,滴漆好后在90~95℃烘焙50分钟,135~145℃再烘120分钟,冷却,得到的电感镇流器符合相关要求。
实施例2
选用S-808挥发油冲制的硅钢片做镇流器,硅钢片浸漆前要求不生锈,产品没有乱片。将镇流器在80℃下预烘0.5小时,冷却后常压浸漆10分钟,采用H级白色绝缘漆,浸漆后再滴漆30分钟,滴漆好后在90~95℃烘焙45分钟,135~145℃烘145分钟,冷却,得到的电感镇流器符合相关要求。
实施例1~2中,在浸漆阶段将HD-180-1白色浸渍漆与专用的上海振立实业有限公司生产的HD180稀释剂混合调匀,用温度表测量浸漆的温度,然后用4号伏特杯测量工作漆液,并根据漆的温度对照表1要求调整浸漆漆液粘度。
表1
漆液温度T℃ | 粘度S |
T为10以下 | 80~90 |
10≤T<12 | 70~80 |
12≤T<15 | 62~70 |
15≤T<20 | 54~62 |
20≤T<25 | 53~54 |
25≤T≤30 | 50~53 |
T为30以上 | 45~50 |
*粘度测量仪器为4号伏特杯。
Claims (2)
1.电感镇流器H级白色绝缘漆绝缘处理工艺,该工艺具体步骤如下:先将镇流器预烘,然后依次浸漆、滴漆、烘焙;其中,所述预烘温度为60℃~80℃,时间为0.5~1小时;所述浸漆时间为8~10分钟;所述滴漆时间为30~40分钟;所述烘焙时,90~95℃烘40~60分钟,135~145℃烘120~150分钟;且浸漆和滴漆全部采用H级白色绝缘漆。
2.如权利要求1所述的电感镇流器H级白色绝缘漆绝缘处理工艺,其特征在于镇流器的硅钢片用S-808挥发油冲制,无锈且没有乱片。