CN1831060A - Two-component epoxy type termide-proof and insect-proof putty and its application - Google Patents
Two-component epoxy type termide-proof and insect-proof putty and its application Download PDFInfo
- Publication number
- CN1831060A CN1831060A CN 200510024239 CN200510024239A CN1831060A CN 1831060 A CN1831060 A CN 1831060A CN 200510024239 CN200510024239 CN 200510024239 CN 200510024239 A CN200510024239 A CN 200510024239A CN 1831060 A CN1831060 A CN 1831060A
- Authority
- CN
- China
- Prior art keywords
- proof
- insect
- termide
- parts
- component epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses a two-component epoxy termite-proof and bug-proof putty and its application. The filming matter(liquid epoxy resin), special bug proof agent(such as insect control chrysanthemum ester style or other bug proof agent), coating auxiliary agent, quartz powder, talcum powder, disintagrated chalk, curing agent in the receipt are used in painting dressing process of furniture and plank floor to form termite and bug proof putty film to prevent termite and other bristletail to erode carpentry. Its efficiency is high, decorating effect is good, and execution is convenient, it can be used to carpentry processing of modern wood furniture painting and home decoration.
Description
Technical field
The present invention relates to a kind of coating, relate in particular to a kind of two component epoxy termide-proof and insect-proof putty.
Background technology
At present, the timber termide-proof and insect-proof is handled mainly based on infusion method and squeegee process, is about to timber and is immersed in the solution that contains medicine, and the solution brushing that maybe will contain medicine is on wood surface.As a kind of epoxide modified putty of Chinese patent, 02139822.4; And document (1) MA transparent woodenware priming paint of series and putty (" New Building Materials ", 2002,2); (2) the disclosed technology of the development of aqueous transparent woodenware putty (" medium-sized and small enterprises science and technology ", 2001,12) does not all have the termide-proof and insect-proof ability, and simultaneously, its shortcoming is that medicine easily runs off, and duration of efficacy is short; Medicine is harmful, environmental pollution; Behind the solution of wood surface brushing medicine, influenced lacquer decorations effect to wood surface.Therefore, the termide-proof and insect-proof pesticide application technology of present timber or plank can not be applicable to the application and the decoration design for residence of modern wooden furniture.
Summary of the invention
The technical issues that need to address of the present invention are to disclose a kind of two component epoxy termide-proof and insect-proof putty and application thereof, to overcome above-mentioned the deficiencies in the prior art.
Two component epoxy termide-proof and insect-proof putty of the present invention is made up of host and solidifying agent, and the weight ratio of host and solidifying agent is 10: 1～3;
The component and the parts by weight of said host comprise:
15～25 parts of liquid epoxiess
1～5 part of propyl carbinol
2～10 parts of dimethylbenzene
0.2～1.2 part of dispersion agent
0.1～4 part of insect-proof agent
40～60 parts of water-ground limestones
10～20 parts of talcum powder
1～10 part of anatase thpe white powder
2～10 parts of aerosils.
Said dispersion agent is selected from urethane, can adopt the commercially available prod, and the trade mark of producing as the chemical company limited of German Bi Ke is the polyurethane-type dispersion agent of BYK163, and it mainly acts on is to disperse various materials;
Said insect-proof agent is selected from the white spirit of pyrethroid, stuck gram missible oil or silicon (chemical name is 4-phenelyl [3-(4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane) or other insect-proof agent or its mixture, can adopt the product of Guangdong Province Insects Research Institute, Britain Shell Co. Ltd or Japan Pyrethrum Co., Ltd;
Preferred 600～1000 purpose products of said water-ground limestone;
Preferred 800～1200 purpose products of talcum powder;
The main effect of water-ground limestone is that coating is filled, and talcous main effect is that coating is filled, and the main effect of anatase thpe white powder is to improve the coating opacifying power, and the main effect of silicon-dioxide is to prevent sedimentation;
The component of said solidifying agent and parts by weight are:
Organic amine 90～98
DMP-30 (three (dimethylamino methyl) phenol) 2～4
Said organic amine is selected modified aromatic amine for use;
Said three (dimethylamino methyl) phenol can adopt the commercially available prod, as the product of Shanghai gold fringe phyllody worker company limited.
Two component epoxy termide-proof and insect-proof putty of the present invention can adopt the method preparation of conventional physical mixed, and host is mixed respectively with each component of solidifying agent, gets final product.Stir and to construct host and solidifying agent are mixed according to the above ratio during use.
Two component epoxy termide-proof and insect-proof putty of the present invention can be used for the application of woodworks such as timber floor, and constructional method is identical with conventional method.
The present invention mainly utilizes filmogen (Resins, epoxy) in the prescription, insect-proof agent, coatings additive(s), solvent, titanium dioxide, talcum powder, water-ground limestone, solidifying agent etc., in the coating process of woodworks such as furniture, timber floor, form the termide-proof and insect-proof putty membrane, thereby stop termite and of the moth erosion of other moth woodenware.Have advantages such as termide-proof and insect-proof efficient height, decorative effect are good, easy construction, can be used for the woodenware pre-treatment of modern wooden furniture application and the woodenware pre-treatment of decoration design for residence.After testing, termide-proof and insect-proof efficient is 1 grade.
Embodiment
Embodiment 1
Prescription:
Host (pulvis):
| Sequence number | Title | Weight, kilogram |
| 1 | Liquid epoxies | 20 |
| 2 | Propyl carbinol | 3 |
| 3 | Dimethylbenzene | 7 |
| 4 | Dispersion agent (urethane) | 0.6 |
| 5 | Pyrethroid (tetrabromo Cyano chrysanthemate) | 0.4 |
| 6 | 800 order water-ground limestones | 46 |
| 7 | 1000 order talcum powder | 11 |
| 8 | Anatase thpe white powder | 5 |
| 9 | Aerosil | 7 |
| Add up to | 100 | |
Solidifying agent
| Sequence number | Title | Weight, kilogram |
| 1 | Organic amine (113, modified aromatic amine) | 97 |
| 2 | DMP-30 (three (dimethylamino methyl) phenol) | 3 |
| Add up to | 100 | |
Each component of host and solidifying agent is mixed respectively, obtain two-pack, host is mixed according to 10: 1 weight ratio with solidifying agent, coated is in timber floor, detection method according to GB/T 18260-2000 " wood preservative is to termite toxic effect test method " regulation, after testing, quality and technical index is as follows:
| Sequence number | Interventions Requested | Assay | The method of inspection | |
| 1 | Outward appearance | There is not mechanical impurity, no skinning | ||
| 2 | Appearance of film | Surfacing, smooth | Range estimation | |
| 3 | The host denseness | 8～14cm | GB/T1749 | |
| 4 | Time of drying (25 ℃) | Surface drying | ≤4h | GB/T1728-89 (second method) |
| Do solid work | ≤10h | GB/T1728-89 (first method) | ||
| 5 | Bonding strength | ≥2.0MPa | JG/T3049-1998(N) | |
| 6 | Water tolerance | 168h passes through | GB/T1733-1993 | |
| 7 | Anti-gasoline | 96h passes through | GB/T1734-1993 | |
| 8 | The termide-proof and insect-proof ability, level | ≤ 1 grade | GB/T18260-2000 | |
Annotate: 0 grade of expression performance is best, and 1 grade is taken second place, and 5 grades the poorest.
Embodiment 2
Host (pulvis):
| Sequence number | Title | Weight, kilogram |
| 1 | Liquid epoxies | 24 |
| 2 | Propyl carbinol | 2 |
| 3 | Dimethylbenzene | 9 |
| 4 | Dispersion agent (urethane) | 0.8 |
| 5 | 1: 1 mixture (weight) of the white spirit of stuck gram missible oil and silicon | 3.2 |
| 6 | 800 order water-ground limestones | 42 |
| 7 | 1000 order talcum powder | 8 |
| 8 | Anatase thpe white powder | 8 |
| 9 | Aerosil | 4 |
| Add up to | 100 | |
B component (solidifying agent)
| Sequence number | Title | Weight, kilogram |
| 1 | Organic amine (modified aromatic amine) | 96 |
| 2 | Three (dimethylamino methyl) phenol | 4 |
| Add up to | 100 | |
Other are identical with embodiment 1.
Detected result is as follows:
| Sequence number | Interventions Requested | Assay | The method of inspection | |
| 1 | Outward appearance | There is not mechanical impurity, no skinning | ||
| 2 | Appearance of film | Surfacing, smooth | Range estimation | |
| 3 | The host denseness | 8～14cm | GB/T1749 | |
| 4 | Time of drying (25 ℃) | Surface drying | ≤4h | GB/T1728-89 (second method) |
| Do solid work | ≤10h | GB/T1728-89 (first method) | ||
| 5 | Bonding strength | ≥2.0MPa | JG/T3049-1998(N) |
| 6 | Water tolerance | 168h passes through | GB/T1733-1993 |
| 7 | Anti-gasoline | 96h passes through | GB/T1734-1993 |
| 8 | The termide-proof and insect-proof ability, level | ≤ 1 grade | GB/T18260-2000 |
Annotate: 0 grade of expression performance is best, and 1 grade is taken second place, and 5 grades the poorest.
Claims (8)
1. a two component epoxy termide-proof and insect-proof putty is characterized in that, is made up of host and solidifying agent, and the weight ratio of host and solidifying agent is 10: 1～3;
The component and the parts by weight of said host comprise:
15～25 parts of liquid epoxiess
1～5 part of propyl carbinol
2～10 parts of dimethylbenzene
0.2～1.2 part of dispersion agent
0.1～4 part of insect-proof agent
40～60 parts of water-ground limestones
10～20 parts of talcum powder
1～10 part of anatase thpe white powder
2～10 parts of aerosils.
The component of said solidifying agent and parts by weight are:
90～98 parts of organic amines
2～4 parts of three (dimethylamino methyl) phenol.
2. two component epoxy termide-proof and insect-proof putty according to claim 1 is characterized in that said dispersion agent is selected from BYK163, urethane.
3. two component epoxy termide-proof and insect-proof putty according to claim 1 is characterized in that, said insect-proof agent is selected from a kind of or its mixture of pyrethroid, stuck gram missible oil or silicon Bai Lingzhong.
4. two component epoxy termide-proof and insect-proof putty according to claim 3 is characterized in that, pyrethroid is Deltamethrin, effective cypermethrin or tetrabromo Cyano chrysanthemate.
5. two component epoxy termide-proof and insect-proof putty according to claim 1 is characterized in that said organic amine is selected modified aromatic amine for use.
6. two component epoxy termide-proof and insect-proof putty according to claim 1 is characterized in that, said water-ground limestone is 600～1000 purpose products.
7. two component epoxy termide-proof and insect-proof putty according to claim 1 is characterized in that, talcum powder is 800～1200 purpose products.
8. according to the application of each described two component epoxy termide-proof and insect-proof putty of claim 1～7, it is characterized in that, be used for the woodenware pre-treatment of wooden furniture application and the woodenware pre-treatment of decoration design for residence.