CN1827723A - Chloroprene rubber type flame-retardant spray adhesive and process for preparing same - Google Patents
Chloroprene rubber type flame-retardant spray adhesive and process for preparing same Download PDFInfo
- Publication number
- CN1827723A CN1827723A CN 200610034765 CN200610034765A CN1827723A CN 1827723 A CN1827723 A CN 1827723A CN 200610034765 CN200610034765 CN 200610034765 CN 200610034765 A CN200610034765 A CN 200610034765A CN 1827723 A CN1827723 A CN 1827723A
- Authority
- CN
- China
- Prior art keywords
- chloroprene rubber
- parts
- retardant spray
- spray adhesive
- type flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a neoprene fire retardant spray-glue and its process for preparing, which is characterized in that it consists of dichloromethane, number six solvent naphtha, toluene, abietyl, terpene resin, triphenyl phosphate, chlorcosane and chloroprene rubber. Adding abietyl, terpene resin, triphenyl and phosphate chlorcosane into mixed solvent of dichloromethane, number six solvent naphtha and toluene till completely dissolving and forming uniform and pellucid solution, at last, adding chloroprene rubber and stirring at the normal temperature until the chloroprene rubber is completely dissolved, then the fire retardant spray-glue of this invention is obtained. The obtained fire retardant spray-glue is of outstanding fire-retardancy, good adhesion and product stability.
Description
Technical field
The present invention relates to a kind of tackiness agent, relate to a kind of chloroprene rubber type flame-retardant spray adhesive and preparation method thereof specifically.
Background technology
Spray glue is a kind of infant industry tackiness agent that development in recent years is come out.It has suitable viscosity, bonding force and suitable time of drying, can utilize spray gun to be sprayed on the adherend surface, forms uniform adhesive linkage.Spray glue through suitably dry, by sticking face pressing, has just been finished adhesion process after spraying.Compare with technique for sticking such as roll-in, brushings, consumption glue amount is little, and applying glue is even, uses more and more widely.
Spray glue is mainly used in the bonding of materials such as sponge, leather, leatheroid and timber.These materials are generally organism, easily burning.And their goods as furniture, case and bag, indoor decoration etc., often have harsh requirement to flame retardant properties.The flame retardant properties of spray glue has very big relation to the flame retardant resistance of goods.As raw materials for production, More and more factories, especially some export enterprises have proposed fire-retardant requirement to spray glue.
Spray glue product mainly contains two big classes at present.One class is a SBS type spray glue, is main raw material with the SBS Thermoplastic Elastomer, and cost is low, and tack is good.Another kind of is neoprene type spray glue, is main raw material with the chloroprene rubber, the bonding strength height, and temperature tolerance is good.Document [Chen Hui, the research of no triphen solvent-borne type neoprene spray glue, Fujian chemical industry, 2001,3:16-18] has been described the method for preparing neoprene spray glue.Yet because chloroprene rubber is easy to burning, oxygen index is lower, and after spray glue was applied to by bonding object, solvent evaporates finished, and the residual chloroprene rubber component that plays main adhesive effect can not suppress combustion processes, can't play fire retardation.
Summary of the invention
The object of the present invention is to provide a kind of chloroprene rubber type flame-retardant spray adhesive; Another purpose provides the preparation method of this spray glue.
We adopt nonflammable polymer as main raw material, and add fire retardant triphenylphosphate and clorafin, and the spray glue that obtains spraying back flame retardant properties is outstanding, can reduce disaster hidden-trouble, helps security against fire, thereby realizes purpose of the present invention.
Chloroprene rubber type flame-retardant spray adhesive provided by the invention, form by following compositions according to the mass fraction:
6～14 parts of methylene dichloride
26～46 parts of No. 6 solvent oils
8～18 parts of toluene
Rosin 10～18
1～10 part of terpine resin
1～10 part of triphenylphosphate
1～13 part of clorafin
5～19 parts of chloroprene rubbers
The preparation method of chloroprene rubber type flame-retardant spray adhesive provided by the invention may further comprise the steps:
(1) proportionally prepare methylene dichloride, No. 6 solvent oils and toluene stir under the normal temperature;
(2) in step (1) prepared solvent, proportionally add rosin, terpine resin, triphenylphosphate and clorafin stir up to dissolving fully, form the solution of transparent and homogeneous;
(3) add chloroprene rubber in the solution that step (2) obtains, normal temperature constantly stirs down, dissolves fully up to chloroprene rubber, promptly obtains flame-retardant spray adhesive.
The churning time of step (2) was generally 0.5～2 hour; The churning time of step (3) was generally 2～5 hours.
The major advantage of flame-retardant spray adhesive of the present invention comprises the following aspects:
(1) flame retardant properties is outstanding: since added can with the compatible fire retardant of spray peptizing agent-rubbery system, flame retardant effect is obvious, oxygen index can reach 23～24, can reduce disaster hidden-trouble, helps security against fire;
(2) cementability is good: have higher bonding strength, can satisfy the requirement of spraying operation commonly used;
(3) product stability is good: owing to consider the consistency of fire retardant and solvent-rubbery system especially in its preparation, so not stratified, shelf-stability is good.
Embodiment
Following examples are to further specify of the present invention, are not limitations of the present invention.
Embodiment 1
With 10 parts of methylene dichloride (quality, down with), 36 parts of No. 6 solvent oils stir under 13 parts of normal temperature of toluene.In solvent, add 14 parts of rosin, 5 parts of terpine resins, 5 parts of triphenylphosphates, clorafin stirred 1 hour for 7 parts, up to dissolving fully, formed the solution of transparent and homogeneous.Add 10 parts of chloroprene rubbers in solution, normal temperature constantly stirred 3 hours down, dissolved fully up to chloroprene rubber.Promptly obtain chloroprene rubber type flame-retardant spray adhesive, recording oxygen index is 23.5.
Embodiment 2
With 7 parts of methylene dichloride, 36 parts of No. 6 solvent oils stir under 13 parts of normal temperature of toluene.In solvent, add 10 parts of rosin, 2 parts of terpine resins, 4 parts of triphenylphosphates, clorafin stirred 0.8 hour for 3 parts, up to dissolving fully, formed the solution of transparent and homogeneous.Add 8 parts of chloroprene rubbers in solution, normal temperature constantly stirred 2.5 hours down, dissolved fully up to chloroprene rubber.Promptly obtain chloroprene rubber type flame-retardant spray adhesive, recording oxygen index is 24.
Embodiment 3
With 12 parts of methylene dichloride, 40 parts of No. 6 solvent oils stir under 10 parts of normal temperature of toluene.In solvent, add 14 parts of rosin, 9 parts of terpine resins, 4 parts of triphenylphosphates, clorafin stirred 1.5 hours for 7 parts, up to dissolving fully, formed the solution of transparent and homogeneous.Add 18 parts of chloroprene rubbers in solution, normal temperature constantly stirred 4 hours down, dissolved fully up to chloroprene rubber.Promptly obtain chloroprene rubber type flame-retardant spray adhesive, recording oxygen index is 23.8.
Claims (3)
1. chloroprene rubber type flame-retardant spray adhesive, form by following compositions according to the mass fraction:
6～14 parts of methylene dichloride
26～46 parts of No. 6 solvent oils
8～18 parts of toluene
Rosin 10～18
1～10 part of terpine resin
1～10 part of triphenylphosphate
1～13 part of clorafin
5～19 parts of chloroprene rubbers
2. the preparation method of a chloroprene rubber type flame-retardant spray adhesive may further comprise the steps:
(1) proportionally prepare methylene dichloride, No. 6 solvent oils and toluene stir under the normal temperature;
(2) in step (1) prepared solvent, proportionally add rosin, terpine resin, triphenylphosphate and clorafin stir up to dissolving fully, form the solution of transparent and homogeneous;
(3) add chloroprene rubber in the solution that step (2) obtains, normal temperature constantly stirs down, dissolves fully up to chloroprene rubber, promptly obtains flame-retardant spray adhesive.
3. according to the preparation method of a kind of chloroprene rubber type flame-retardant spray adhesive of claim 2, wherein the churning time in the step (2) is 0.5～2 hour; The churning time of step (3) is 2～5 hours.