CN1792963A - Imitating marble and mfg. process thereof - Google Patents
Imitating marble and mfg. process thereof Download PDFInfo
- Publication number
- CN1792963A CN1792963A CN 200510104619 CN200510104619A CN1792963A CN 1792963 A CN1792963 A CN 1792963A CN 200510104619 CN200510104619 CN 200510104619 CN 200510104619 A CN200510104619 A CN 200510104619A CN 1792963 A CN1792963 A CN 1792963A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- marble
- parian
- graphite
- butadiene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An artificial marble with fine quality, high hardness and no breaking of transverse vein is proportionally prepared from marble powder, emulsion of vinyl polyacetate, epoxy resin, urea-aldehyde resin, scotchweld and graphite through proportional mixing, baking in wooden mould at 200-300 deg.C, pressing in steel mould, and roasting at 60-80 deg.C and then at 110-200 deg.C.
Description
One, technical field: the present invention relates to artificial colored stone and preparation method thereof, especially a kind of texture exactly likes marmorean parian and preparation method thereof.
Two, prior art: the marble price is very high, does not generally dare to inquire.In addition, its resource is also extremely limited.The present inventor is through studying intensively for many years, and having invented a kind of is that main raw material adopts unique technology to produce the artificial marble that can look genuine with marble flour or white marble.
Three, summary of the invention: the object of the present invention is to provide a kind of texture to exactly like marble, the quality exquisiteness is hard, and band is easy fracture not, is not easy fragmentation, and is cheap, and shape is adjustable, parian simple for production and preparation method thereof.
Technical scheme: parian, form by following composition: marble flour or white marble powder, polyvinyl acetate emulsion, Resins, epoxy, urea formaldehyde resin adhesive, phenolic aldehyde butadiene-acrylonitrile rubber, graphite, pigment.Described component is:
Marble flour or white marble powder 60 ~ 70 weight parts
Polyvinyl acetate emulsion 15 ~ 20 weight parts
Resins, epoxy 25 ~ 30 weight parts
Urea formaldehyde resin adhesive 25 ~ 40 weight parts
Phenolic aldehyde butadiene-acrylonitrile rubber 30 ~ 35 weight parts
Graphite 5 ~ 15 weight parts
Pigment is an amount of
Make the parian method, be that each component is mixed in container, dry between 200 ~ 300 ℃ in wooden model, making water content is 5 ~ 15% weight, putting into punching block again pressurizes under 500 kg/cm, again at baking box in 60 ~ 80 ℃, subsequently at 110 ~ 200 ℃ of following parians of forming of baking.The marble or the white marble powder of aforementioned proportion are put into a plastic tank, adding Vinyl Acetate Copolymer, urea formaldehyde resin adhesive, phenolic aldehyde butadiene-acrylonitrile rubber and Graphite Powder 99 more in turn stirs at normal temperatures and uses each raw material to be mixed into soft material, pigment overlaps the pattern of the various textures of addition then, put into the wooden model of different size again, dry between 200 ~ 300 about half an hour ~ 4 hour.When treating that water content is 5 ~ 15% weight, from wooden model, take out fast and put into punching block, after compressing moulding in 3 ~ 5 minutes with the pressure of 500 kg/cm, putting into baking box baked 1 hour down in 60 ~ 80 ℃, improve then under temperature to 110 ~ 200 ℃ make roasting again half an hour the surface slightly the coking body become water insoluble or oily forming composition, promptly various parians.
Can regulate the amount and the drying time of phenolic aldehyde butadiene-acrylonitrile rubber by the requirement of different parians as for its hardness, the pressure size is regulated.Its hardness also can be adjusted between 4 ~ 8 degree.
Beneficial effect: the advantage of artificial parian of the present invention is advantages such as texture can be made into as marble, and the quality exquisiteness is hard, and horizontal hard line is easy fracture not, is not easy fragmentation, and is cheap, and shape is adjustable, and is simple for production.
Four, specific embodiment:
Embodiment: adding the marble flour granularity in one 0.5 liter plastic containers is (1000 order) 65 grams, add polyvinyl acetate emulsion (solid content is 40%) 17 grams more successively, Resins, epoxy 618 (production of Wuxi resin processing plant) 28 grams, general urea formaldehyde resin adhesive 30 grams, phenolic aldehyde butyronitrile agent fourth-01 (production of Zhejiang resin processing plant) 32 grams and Graphite Powder 99 10 restrain and stir into soft material under normal temperature, addition has texture to put into wooden model to soft material cover to go into to strengthen red advertisement look 5 grams then, under 125 ~ 160 ℃ temperature, dry, when treating that water content is the 10% weight left and right sides, take out to put in the rectangular punching block fast and under 500 kg/cm, pressurizeed 3 minutes with general pressing machine, take out module then and put into baking box in 60 ℃ of following baking 1 hour, temperature is brought up to 110 ℃ then, roasting again half an hour, take out with the polishing machine polishing.
Claims (3)
1, a kind of parian is characterized in that: be made up of following composition: marble flour or white marble powder, polyvinyl acetate emulsion, Resins, epoxy, urea formaldehyde resin adhesive, phenolic aldehyde butadiene-acrylonitrile rubber, graphite, pigment.
2, parian according to claim 1 is characterized in that: described component is:
Marble flour or white marble powder 60 ~ 70 weight parts
Polyvinyl acetate emulsion 15 ~ 20 weight parts
Resins, epoxy 25 ~ 30 weight parts
Urea formaldehyde resin adhesive 25 ~ 40 weight parts
Phenolic aldehyde butadiene-acrylonitrile rubber 30 ~ 35 weight parts
Graphite 5 ~ 15 weight parts
Pigment is an amount of
3, a kind of making method of parian, it is characterized in that: each component is mixed in container, dry between 200 ~ 300 ℃ in wooden model, making water content is 5 ~ 15% weight, putting into punching block again pressurizes under 500 kg/cm, again at baking box in 60 ~ 80 ℃, subsequently at 110 ~ 200 ℃ of following parians of forming of baking.