CN102029644A - Process for producing wood grain antique brick - Google Patents
Process for producing wood grain antique brick Download PDFInfo
- Publication number
- CN102029644A CN102029644A CN 201010521240 CN201010521240A CN102029644A CN 102029644 A CN102029644 A CN 102029644A CN 201010521240 CN201010521240 CN 201010521240 CN 201010521240 A CN201010521240 A CN 201010521240A CN 102029644 A CN102029644 A CN 102029644A
- Authority
- CN
- China
- Prior art keywords
- brick
- glaze
- antique
- wood grain
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for producing a wood grain antique brick, which comprises the following steps of: (1) preparing a blank, a cover glaze and a fancy glaze; (2) forming a blank brick in a die brick by using the blank, wherein the die brick is provided with rugged grains, the depth of the rugged grains is in a range of 1.0 to 2.0 millimeters, and the forming pressure of the blank is 3,300 to 3,700MPa/cm<2>; (3) sintering and drying the formed blank brick, wherein the sintering temperature is 1,170 to 1,200 DEG C; (4) spraying the glaze on the dried blank, wherein the liquidity of the glaze slurry is 30 to 40 S/100M1, the fluctuation is 0 to 5S, the specific gravity of the glaze slurry is 170 to 190 g/cm<2> and the glaze quantity is 0.01 to 0.08 g/cm<2>; (5) printing with the fancy glaze through a silk screen, wherein the tension degree of the silk screen is 20 to 24MPa/cm<2>; (6) sintering in a kiln; and (7) edging. According to the process for producing the wood grain antique brick, the produced wood grain antique brick has more realistic visual effect of rugged wood scratching grains, clear grains and strong third dimension.
Description
Technical field
The present invention relates to the architectural pottery field, relate in particular to the production technology of a kind of wood grain brick modelled after an antique.
Background technology
At the ceramic building material produce market of competition that is growing more intense, brick modelled after an antique is liked by consumers in general more and more deeply with the pseudo-classic art and the natural style of its uniqueness.At present, the product of existing wood grain brick modelled after an antique exists fidelity not high, has only simple plane pattern or the simple concavo-convex or simple linear of point-like, does not have true rough wood grain hand to grab the visual effect of lines, and more stiff, third dimension is not strong.
Summary of the invention
Technical problem to be solved by this invention is the deficiency that remedies prior art, purpose is to provide the production technology of a kind of wood grain brick modelled after an antique, the wood grain brick of producing modelled after an antique has the visual effect that truer rough wood grain hand is grabbed lines, and lines is clear, and third dimension is stronger.
For solving above technical problem, technical scheme of the present invention is that the production technology of a kind of wood grain brick modelled after an antique comprises the steps:
(1) preparation blank, cover-coat enamel and fancy glaze;
(2) blank moulding in the mould brick forms the base brick, and the mould brick is provided with rough lines, and the degree of depth of rough lines is in the scope of 1.0mm-2.0mm, and the pressure of blank moulding is 3300Mpa/cm
2-3700Mpa/cm
2
(3) the base brick sintering drying after the moulding, sintering temperature is 1170 ℃-1200 ℃;
(4) dry body drenches glaze, and the flowability of glaze slip is 30S/100M1-40S/100M1, fluctuates to be that 0S-5S, glaze slip proportion are 170g/cm
2-190g/cm
2, the glaze amount is 0.01g/cm
2-0.08g/cm
2
(5) screen printing glaze, the tension degree of silk screen are 20Mpa/cm
2-24Mpa/cm
2
(6) go into klining;
(7) edging.
Preferably, the degree of depth of rough lines is in the scope of 1.2mm-1.8mm in the step (2), and the pressure of blank moulding is 3400Mpa/cm
2-3600Mpa/cm
2
Preferably, the hardness of mould brick surface glue is controlled at 97 degree-99 degree in the step (2).
Preferably, the size Control of mould brick is shunk 4.0%-5.5% at the base brick in the step (2).
Preferably, sintering temperature is 1180 ℃-1190 ℃ in the step (3).
Preferably, the flowability of glaze slip is 32S/100M1-38S/100M1 in the step (4), and fluctuating is that 0S-2S, glaze slip proportion are 180g/cm
2-185g/cm
2, the glaze amount is 0.02g/cm
2-0.06g/cm
2
Preferably, in the step (4), the base brick must drench by elder generation's water spray before drenching glaze, and injection flow rate is 0.005g/cm
2-0.01g/cm
2
Preferably, silk screen spray solidification agent mixed liquor before stamp in the step (5), the water of described curing agent mixed liquor: the volume ratio of curing agent is 100: 5-100: 20.
Preferably, the height of silk screen is 8mm-10mm in the step (5).
Compared with prior art, the production technology of wood grain provided by the invention brick modelled after an antique, the wood grain of production brick modelled after an antique has the visual effect that truer rough wood grain hand is grabbed lines, and lines is clear, and third dimension is stronger.
The specific embodiment
For those skilled in the art can understand technical scheme provided by the present invention better, set forth below in conjunction with specific embodiment.
The production technology of wood grain provided by the invention brick modelled after an antique comprises the steps:
(1) preparation blank, cover-coat enamel and fancy glaze.
(2) in common brick modelled after an antique, be to add stamp with the plane to reach and beautify effect mostly, and the mould brick of this patent is provided with rough lines, blank moulding in the mould brick forms the base brick, add that by base brick concave-convex surface effect printing ornament highlights stereoeffect, make product true to nature naturally, the surface pattern of this patent is to show the product natural stype with irregular concavo-convex lines effect.The degree of depth of rough lines is in the scope of 1.2mm-1.8mm, if lines is dark excessively, then drenches glaze and stamp is uncontrollable, if too shallow then can't manifest the effect of its concave convex texture.The hardness of mould brick surface glue is controlled at 97 degree-99 degree, and hardness is crossed low then surface and pitted skin occurred, and hardness is too high then can to produce the sticking to mould defective and product degradation roughly.The pressure of blank moulding is 3400Mpa/cm
2-3600Mpa/cm
2, hypotony then product strength is not enough, and hypertonia then semi-finished product can crack phenomenon.Because product is to give prominence to its characteristic with average piecemeal mould and concave-convex surface mould, and product size is subjected to effects of process parameters and change to some extent, so the size Control of mould brick is shunk 4.5%-5.0% at the base brick and is advisable, so then can guarantee back operation control, as stamp, edging etc., unaffected.
(3) the base brick sintering drying after the moulding.Sintering is the critical process of ceramic product, and product will be considered flatness, size, and a series of physical properties such as moisture content, thus sintering temperature be 1180 ℃-1190 ℃ and be advisable, could guarantee that so every index of product is unaffected.
(4) dry body drenches glaze.In this product type of ceramic antique bricks, the surface all will be executed the glazed glaze layer of one deck class and be come decorative product.And this patent is to drench glaze on product surface is uneven, and is then much more difficult than general planar products, and parameter control is bad then to produce defective such as pin hole, glaze bubble and make the product degradation.Therefore, the flowability of glaze slip is 32S/100M1-38S/100M1, fluctuates to be that 0S-2S, glaze slip proportion are 180g/cm
2-185g/cm
2, the glaze amount is 0.02g/cm
2-0.06g/cm
2The base brick must drench by elder generation's water spray before drenching glaze, and injection flow rate is 0.007g/cm
2
(5) screen printing glaze.Silk screen is spray solidification agent mixed liquor before stamp, the water of curing agent mixed liquor: the volume ratio of curing agent is 100: 10, solves the problem of the sticking net of stamp.The tension degree of silk screen is 22Mpa/cm
2In order to obtain definition and effect stamp preferably, the height of silk screen is 8mm-10mm.
(6) go into klining.
(7) edging.
Compared with prior art, the production technology of wood grain provided by the invention brick modelled after an antique, the wood grain of production brick modelled after an antique has the visual effect that truer rough wood grain hand is grabbed lines, and lines is clear, and third dimension is stronger.
To the above-mentioned explanation of the disclosed embodiments, make this area professional and technical personnel can realize or use the present invention.Multiple modification to these embodiment will be conspicuous concerning those skilled in the art, and defined herein General Principle can realize under the situation that does not break away from the spirit or scope of the present invention in other embodiments.Therefore, the present invention will can not be restricted to these embodiment shown in this article, but will meet and principle disclosed herein and features of novelty the wideest corresponding to scope.
Claims (9)
1. the production technology of a wood grain brick modelled after an antique is characterized in that, comprises the steps:
(1) preparation blank, cover-coat enamel and fancy glaze;
(2) blank moulding in the mould brick forms the base brick, and the mould brick is provided with rough lines, and the degree of depth of rough lines is in the scope of 1.0mm-2.0mm, and the pressure of blank moulding is 3300Mpa/cm
2-3700Mpa/cm
2
(3) the base brick sintering drying after the moulding, sintering temperature is 1170 ℃-1200 ℃;
(4) dry body drenches glaze, and the flowability of glaze slip is 30S/100M1-40S/100M1, fluctuates to be that 0S-5S, glaze slip proportion are 170g/cm
2-190g/cm
2, the glaze amount is 0.01g/cm
2-0.08g/cm
2
(5) screen printing glaze, the tension degree of silk screen are 20Mpa/cm
2-24Mpa/cm
2
(6) go into klining;
(7) edging.
2. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, the degree of depth of rough lines is in the scope of 1.2mm-1.8mm in the step (2), and the pressure of blank moulding is 3400Mpa/cm
2-3600Mpa/cm
2
3. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, the hardness of mould brick surface glue is controlled at 97 degree-99 degree in the step (2).
4. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, the size Control of mould brick is shunk 4.0%-5.5% at the base brick in the step (2).
5. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, sintering temperature is 1180 ℃-1190 ℃ in the step (3).
6. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, the flowability of glaze slip is 32S/100M1-38S/100M1 in the step (4), and fluctuating is that 0S-2S, glaze slip proportion are 180g/cm
2-185g/cm
2, the glaze amount is 0.02g/cm
2-0.06g/cm
2
7. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, in the step (4), the base brick must drench by elder generation's water spray before drenching glaze, and injection flow rate is 0.005g/cm
2-0.01g/cm
2
8. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, silk screen spray solidification agent mixed liquor before stamp in the step (5), and the water of described curing agent mixed liquor: the volume ratio of curing agent is 100: 5-100: 20.
9. the production technology of wood grain according to claim 1 brick modelled after an antique is characterized in that, the height of silk screen is 8mm-10mm in the step (5).