CN1789205A - Ceramic glaze material and method for burning ceramic glaze - Google Patents
Ceramic glaze material and method for burning ceramic glaze Download PDFInfo
- Publication number
- CN1789205A CN1789205A CN 200510132394 CN200510132394A CN1789205A CN 1789205 A CN1789205 A CN 1789205A CN 200510132394 CN200510132394 CN 200510132394 CN 200510132394 A CN200510132394 A CN 200510132394A CN 1789205 A CN1789205 A CN 1789205A
- Authority
- CN
- China
- Prior art keywords
- glaze
- order
- weight part
- bristol
- weight parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ceramic color glaze, mixing the fine yellow mud of 100-150 order with 4-8 weight unit, calcite of 100-150 order with 2-4 weight unit, feldspar of 100-150 order with 1 weight unit and manganese powder with 1-6 weight unit, adding water, stirring homogenously to form mixture material of 50-60 degree. The invention also discloses a method for calcinating ceramic color glaze, comprising: preparing glaze, glazing, drying and calcinating, employing traditional wood earth kiln for calcinating for 7-8 hours, lasting 4 hours when temperature is 300 Deg C, two hours when temperature is 800 Deg C and 1-2 hours when temperature is 1200 Deg C, stopping heating, cooling naturally and getting out of kiln. The invention is characterized by the simple ceramic color glaze ingredient, low cost, simple calcinating method and abundant and bright color of the product, the color of the ceramic color glaze is deepened according to the increase of the manganese powder using amount, from jujube yellow to jujube red, jam-color and near black, which upgrades the ceramic product.
Description
Technical field
The present invention relates to the method for cooking of a kind of pottery glaze and bristol glaze, specifically, relate to the method for cooking of a kind of bristol glaze material and bristol glaze.
Background technology
Pottery is by clay or based on the mixture of clay, feldspar, quartz etc., through moulding, drying, fire the general name of the goods that form.Pottery has characteristics such as hoarsen, opaque, suction.Press the difference of clay ingredient, idiosome is white, blue or green, brown, brown isochrome.Come across the Neolithic Age the earliest, gray pottery, red pottery, white pottery, ancient painted pottery, black pottery etc. are arranged.Along with the development and the raising of ceramics, occurred again thereafter that plating is made pottery firmly, lead glaze pottery, three ancient painted potteries etc.The still emerging so far burning of pottery does not wane.
Ancient claim " stone kiln " of copper government porcelain kiln has another name called " Changsha kiln ".The copper government porcelain kiln is found in nineteen fifty-seven, and through repeatedly archaeological excavation, being regarded as substantially is exactly the source region of under glazed.
Copper government porcelain kiln pottery is to make the pottery that idiosome is made with copper official mud, generally is called the copper official and makes pottery.
Summary of the invention
Purpose of the present invention just is to provide the method for cooking of a kind of bristol glaze material and bristol glaze, and it is unique that it is filled a prescription, and the pottery product colour that burns out can be yellow to purplish red, dark reddish brown with near black by jujube, and rich color is colorful, has greatly enriched the glaze colours of pottery.
For addressing the above problem, the present invention adopts following technical scheme:
A kind of bristol glaze material of the present invention, it is that a kind of to add that water stirs to concentration after the thin yellow mud 4-8 of 100-150 order weight part, 100-150 order calcite 2-4 weight part, 100-150 order feldspar 1 weight part and manganese powder 1-6 weight part are mixed be the mixture of 50-60 degree.
Preferred glaze formula of the present invention is: add after thin yellow mud 6 weight parts of 100 orders, 100 order calcites, 3 weight parts, 100 order feldspars, 1 weight part and manganese powder 1.2 weight parts mix water stir to concentration be 55 degree.
In the above-mentioned prescription, when the manganese powder consumption was 1.2 weight parts, the bristol glaze that burns out was the jujube yellow.When the manganese powder consumption was the 1.6-2 weight part, the bristol glaze that burns out was a purplish red.When the manganese powder consumption was the 3-4 weight part, the bristol glaze that burns out was a dark reddish brown.When the manganese powder consumption was the 5-6 weight part, the bristol glaze that burns out was near black.
Bristol glaze material of the present invention is a kind of glaze that the copper official makes pottery that is suitable for.
The present invention also provides a kind of method for cooking of bristol glaze, and it comprises the following steps:
Preparation glaze: by the good glaze of above-mentioned formulated;
Glazing: at normal temperatures the pottery embryo who makes is immersed in the glaze pottery embryo is soaked glaze, reach pottery embryo surface and all soak glaze fully;
Dry: dry to the water evaporates of pottery surface glaze intact naturally;
Fire: adopt traditional firewood earth kiln to fire, fired 7-8 hour, process is 4 hours when being 300 ℃ of temperature, is 2 hours during 800 ℃ of middle temperature, is 1-2 hour during 1200 ℃ of high temperature, ceases fire, kiln discharge behind the naturally cooling.
Ingredients concentration of the present invention is defined as: under standard temperature 20 degree, heavily show to measure gained with mother-in-law Mei Shi, heavily show during use perpendicular to the mix level face, read that numerical value gets final product on the table till allowing it sink down into when no longer sinking automatically.
Bristol glaze batching of the present invention is simple, and with low cost, method for cooking is simple, the pottery product color that burns till is abundant, bright in colour, full, the color of bristol glaze is deepened with the increase of manganese powder consumption, and is yellow to purplish red, dark reddish brown with near black by jujube, improved the class of pottery.
Embodiment
Embodiment 1
1, preparation glaze: will be through 30 kilograms meticulous of yellow mud of 100 orders, through 14 kilograms meticulous in calcite of 100 orders, mix through 100 orders meticulous 5 kilograms of feldspars and manganese powder dry powder 6kg, add water and stir that to transfer to concentration be 55 degree, described concentration is under 20 ℃ of standard temperatures, measure gained with " the mother-in-law Mei Shi of qiyang,hunan overstatement instrucment and meter plant heavily shows ", heavily show during use perpendicular to the mix level face, read table till allowing it sink down into when no longer sinking automatically and go up numerical value and get final product.
2, glazing: at normal temperatures the pottery embryo of the clay work of copper official is immersed in the glaze pottery embryo is soaked glaze, reach pottery embryo surface and all soak glaze fully;
3, dry: dry to the water evaporates of pottery surface glaze intact naturally;
4, fire: adopt traditional firewood earth kiln to fire, fired 7-8 hour, process is 4 hours when being 300 ℃ of temperature, is 2 hours during 800 ℃ of middle temperature, is 1-2 hour during 1200 ℃ of high temperature, ceases fire, kiln discharge behind the naturally cooling, and the pottery glaze of being fired is the jujube yellow.
Embodiment 2
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the bristol glaze glaze is for mixing through 20 kilograms meticulous of yellow mud of 150 orders, through 10 kilograms meticulous in calcite of 150 orders, through 150 orders meticulous 5 kilograms of feldspars and manganese powder dry powder 8kg, add water and stir that to transfer to concentration be 50 degree, the bristol glaze color that burns out is a purplish red.
Embodiment 3
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the consumption of manganese powder is 10kg in the bristol glaze glaze, and other raw material consumption is with embodiment 1, and the bristol glaze color that burns out is a purplish red.
Embodiment 4
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the bristol glaze glaze is for mixing through 40 kilograms meticulous of yellow mud of 150 orders, through 20 kilograms meticulous in calcite of 150 orders, through 150 orders meticulous 5 kilograms of feldspars and manganese powder dry powder 15kg, add water and stir that to transfer to concentration be 60 degree, the bristol glaze color that burns out is a dark reddish brown.
Embodiment 5
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the consumption of manganese powder is 20kg in the bristol glaze glaze, and other raw material consumption is with embodiment 1, and the bristol glaze color that burns out is a dark reddish brown.
Embodiment 6
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the consumption of manganese powder is 25kg in the bristol glaze glaze, and other raw material consumption is with embodiment 1, and the bristol glaze color that burns out is near black.
Embodiment 7
By the described method preparation bristol glaze glaze of embodiment 1 and fire, wherein the consumption of manganese powder is 30kg in the bristol glaze glaze, and other raw material consumption is with embodiment 1, and the bristol glaze color that burns out is near black.
The present invention is not limited to above-mentioned preferred forms, and other any identical with the present invention or akin products that anyone draws under enlightenment of the present invention all drop within protection scope of the present invention.
Claims (7)
1, a kind of bristol glaze material is characterized in that it is that a kind of to add that water stirs to concentration after the thin yellow mud 4-8 of 100-150 order weight part, 100-150 order calcite 2-4 weight part, 100-150 order feldspar 1 weight part and manganese powder 1-6 weight part are mixed be the mixture of 50-60 degree.
2, bristol glaze material as claimed in claim 1, it is characterized in that it be add after thin yellow mud 6 weight parts of 100 orders, 100 order calcites, 3 weight parts, 100 order feldspars, 1 weight part and manganese powder 1.2 weight parts are mixed water stir to concentration be 55 degree.
3, bristol glaze material as claimed in claim 1, it is characterized in that it be add after thin yellow mud 6 weight parts of 100 orders, 100 order calcites, 3 weight parts, 100 order feldspars, 1 weight part and manganese powder 1.6-2 weight part are mixed water stir to concentration be 50 degree.
4, bristol glaze material as claimed in claim 1, it is characterized in that it be add after thin yellow mud 6 weight parts of 100 orders, 100 order calcites, 3 weight parts, 100 order feldspars, 1 weight part and manganese powder 3-4 weight part are mixed water stir to concentration be 55 degree.
5, bristol glaze material as claimed in claim 1, it is characterized in that it be add after thin yellow mud 6 weight parts of 100 orders, 100 order calcites, 3 weight parts, 100 order feldspars, 1 weight part and manganese powder 5-6 weight part are mixed water stir to concentration be 55 degree.
6,, it is characterized in that described bristol glaze material is for being suitable for copper official bristol glaze material as the arbitrary described bristol glaze material of claim 1-5.
7, a kind of method for cooking of bristol glaze, it is characterized in that: it comprises the following steps:
Preparation glaze: by the good glaze of arbitrary formulated of claim 1-6;
Glazing: at normal temperatures the pottery embryo is immersed in the glaze pottery embryo is soaked glaze, reach pottery embryo surface and all soak glaze fully;
Dry: dry to the water evaporates of pottery surface glaze intact naturally;
Fire: adopt traditional firewood earth kiln to fire, fired 7-8 hour, process is 4 hours when being 300 ℃ of temperature, is 2 hours during 800 ℃ of middle temperature, is 1-2 hour during 1200 ℃ of high temperature, ceases fire, kiln discharge behind the naturally cooling.