Plastic screw cleaning agent and system thereof are joined and using method
Technical field the present invention relates to detergent compositions, particularly is used for the clean-out system that the screw plastic processing machinery uses.
Background technology is in order to satisfy client's demand, in the course of processing, adopt different colours to make up, produce multicoloured plastic prod, be very general, this just requires often to add different pigment in the course of processing, and require can not have between the shades of colour and obscure, how to discolor in the course of processing proposed very high requirement.And in plastic working, adopt screw apparatus (single, double screw rod) extremely general, this equipment is when the needs colour changing, normally with in a large amount of raw material insertion apparatus, constantly, the residue that will remain in repeatedly in screw rod and the barrel penetrates or extrudes, so not only waste a large amount of raw materials, but also wasted a large amount of time.The way of selecting cleaning material for use is also arranged, and still, this way can only be carried out at some specific materials, and certain limitation is arranged.
It is that tensio-active agent, organosilicon and solvent carry out composite technology that summary of the invention the present invention adopts main component, solve in the prior art waste raw material, technical problem that time and raw material variety are restricted.
Technical scheme of the present invention is as follows: a kind of plastic screw cleaning agent comprises aliphatic alcohol polyethenoxy mystery sodium sulfate, Sodium dodecylbenzene sulfonate, lauric acid amide of ethanol, dimethyl siloxane, Virahol, emulsifying agent and deionized water.
Described aliphatic alcohol polyethenoxy mystery sodium sulfate is 5~10%; Sodium dodecylbenzene sulfonate 5~10%; Lauric acid amide of ethanol 0.5~0.8%; Dimethyl siloxane 2~5%; Virahol 15~35%; Emulsifying agent 3~5%, all the other are ionized water.
The method for formulating of this clean-out system may further comprise the steps:
A. with aliphatic alcohol polyethenoxy mystery sodium sulfate, Sodium dodecylbenzene sulfonate, lauric acid amide of ethanol, Virahol and deionized water on request mixed make mixed solution;
B. dimethyl siloxane and emulsifying agent are carried out mixing and emulsifying and make emulsion;
C. slight the stirring will be added in the mixed solution that steps A is made through the emulsion that step B makes.
The using method of this clean-out system may further comprise the steps:
I. a small amount of raw material is soaked into clean-out system;
The raw material that II. will be cleaned after agent is soaked into is poured in the screw rod of plastic processing machinery;
III. start this machinery, raw material is all extruded.
Adopt the above-mentioned made clean-out system of technical scheme, very strong perviousness and activation are arranged, the pigment in the residual raw material is dissolved rapidly, and it is effective to discolor, have that materials are few, the time is short, remove clean and the wide characteristics of use range.
Description of drawings
Fig. 1 is the present invention's synoptic diagram in use.
Introduce specific embodiments of the invention below the embodiment in detail.
A kind of plastic screw cleaning agent comprises aliphatic alcohol polyethenoxy mystery sodium sulfate, Sodium dodecylbenzene sulfonate, lauric acid amide of ethanol, dimethyl siloxane, Virahol, emulsifying agent and deionized water.
Emulsifying agent can adopt the polyoxyethylene nonylphenol ether series product, for example TX-10 type emulsifying agent.
This clean-out system can be adjusted proportioning according to the shade of raw material, generally should be that aliphatic alcohol polyethenoxy mystery sodium sulfate is 5~10%; Sodium dodecylbenzene sulfonate 5~10%; Lauric acid amide of ethanol 0.5~0.8%; Dimethyl siloxane 2~5%; Virahol 15~35%; Emulsifying agent 3~5%, all the other are ionized water.
The method for formulating of this clean-out system may further comprise the steps:
A. with aliphatic alcohol polyethenoxy mystery sodium sulfate, Sodium dodecylbenzene sulfonate, lauric acid amide of ethanol, Virahol and deionized water on request mixed make mixed solution;
B. dimethyl siloxane and emulsifying agent are carried out mixing and emulsifying and make emulsion;
C. will add through the emulsion that step B makes in the mixed solution that steps A is made, the slight stirring, bottling is used just passable then.
The using method of this clean-out system may further comprise the steps:
I. a small amount of raw material is soaked into clean-out system;
The raw material that II. will be cleaned after agent is soaked into is poured in the screw rod of plastic processing machinery;
III. start machinery, the new raw material that injects contacts with residual raw material, and rapid osmotic fades it in residual raw material, then raw material is all extruded (as shown in fig. 1).