CN1686636A - 具有除硫磷功能的钢、铁水聚渣保温覆盖剂 - Google Patents

具有除硫磷功能的钢、铁水聚渣保温覆盖剂 Download PDF

Info

Publication number
CN1686636A
CN1686636A CN 200510018713 CN200510018713A CN1686636A CN 1686636 A CN1686636 A CN 1686636A CN 200510018713 CN200510018713 CN 200510018713 CN 200510018713 A CN200510018713 A CN 200510018713A CN 1686636 A CN1686636 A CN 1686636A
Authority
CN
China
Prior art keywords
steel
heat insulating
molten iron
insulating covering
covering agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510018713
Other languages
English (en)
Other versions
CN1311937C (zh
Inventor
高申明
汪光银
高俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005100187131A priority Critical patent/CN1311937C/zh
Publication of CN1686636A publication Critical patent/CN1686636A/zh
Application granted granted Critical
Publication of CN1311937C publication Critical patent/CN1311937C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种具有除硫磷功能的钢、铁水聚渣保温覆盖剂，属于冶金用辅助材料。本发明由M2S砂粉、炉渣、珍珠岩、电厂灰、沸石、石墨、桂林一号粉等组成。本覆盖剂能够在钢水包中迅速覆盖，壳层不粘包、挂包，随降性好；在造渣过程中，能够吸收钢水中的硫磷杂质，所形成的壳层可整体挑出，使钢水清亮；覆盖剂形成的壳层遮光性好，可防光热辐射，包中的钢水温降远低于传统珍珠岩覆盖剂；不污染钢水，不会对钢包产生损坏。

Description

具有除硫磷功能的钢、铁水聚渣保温覆盖剂
技术领域
本发明涉及一种钢、铁水聚渣、保温的覆盖剂，特别是一种具有除硫磷功能的钢、铁水聚渣保温覆盖剂。
背景技术
覆盖剂在冶金铸造行业如各种灰铸铁、球墨铸铁及各种铸钢液体生产过程中有着广泛地应用，传统覆盖剂使用的是草灰和珍珠岩、石英石等，这些覆盖剂在使用过程中的加入量大，聚渣能力不强，保温性能差，对钢水有一定的污染。撒在铁水表面，能放出大量的热能，反应生成良好的保温层，同时有很好的集渣、脱硫等作用。使用该覆盖剂是消除铸件气孔、夹渣、防止球铁球化衰退的有效措施。本品无毒、无味、无粉尘，使用非常方便。。
发明内容
本发明的目的是提供一种覆盖效果好，聚渣性能强，能够吸收钢水中的硫磷等杂质，保温性能好，不污染钢水的具有除硫磷功能的钢、铁水聚渣保温覆盖剂。
本发明的目的是这样实现的：一种具有除硫磷功能的钢、铁水聚渣保温覆盖剂，其组分的重量比为：M2S砂粉10-28％；炉渣20-26％；珍珠岩20-30％；电厂灰10-28％；沸石5-10％；石墨3-10％；桂林一号粉6-8％。本发明的优选组份的重量比为：M2S砂粉18％；炉渣23％；珍珠岩27％；电厂灰20％；沸石7％；石墨6％；桂林一号粉7％。本发明的制备方法是：将M2S砂粉、炉渣、电厂灰、沸石、石墨按上述比例混合后加入物料重量的3-10％的水搅拌1-5分钟，再加入珍珠岩和桂林一号粉混合后搅拌5-10分钟；搅拌好的混合料通过双层筛机制粒，收集颗粒集中度80％的颗粒进烘炉滚筒烘干，待物料冷却后得到本产品。M2S砂粉是由M2S破碎加工成100-150目得到。炉渣是将M2S煅烧时产生的含煤渣的M2S碎颗粒砂废料加工成大于50目的砂粉得到。电厂灰为火力发电厂除尘器下的粉煤灰尾料。双层筛机为20/100目双层制筛机。沸石加工成≥40目的砂粉。
本发明的提供的具有除硫磷功能的钢、铁水聚渣保温覆盖剂，覆盖性能好，能够在钢水包中迅速覆盖，壳层不粘包、挂包，随降性好；在造渣过程中，能够吸收钢水中的硫磷杂质，所形成的壳层可整体挑出，使钢水清亮；覆盖剂形成的壳层遮光性好，可防光热辐射，包中的钢水温降远低于传统珍珠岩覆盖剂；不污染钢水，不会对钢包产生损坏。
具体实施方式
本发明中的M2S为镁橄榄石，可选用宜昌出厂的镁橄榄石。
实施例配方：以Kg为单位
           实施例一  实施例二   实施例三   实施例  实施例五
M2S砂粉   100       150        180        250     280
炉渣       200       220        230        240     260
电厂灰     100       180        200        260     280
沸石       50        60         70         75      100
石墨       30        50         60         80      100
水         14.4      33         37         72.4    102
桂林一号粉 60        65         70         75      80
珍珠岩     200       220        270        260     300
本发明的制备方法是：将M2S砂粉、炉渣、电厂灰、沸石、石墨按上述比例混合后加入水搅拌1-5分钟，再加入珍珠岩和桂林一号粉混合后搅拌5-10分钟；搅拌好的混合料通过双层筛机制粒，收集颗粒集中度80％的颗粒进烘炉滚筒烘干，待物料冷却后得到本产品。
M2S即Mg2SiO4，为镁橄榄石的简写化学结构式。M2S砂粉是由M2S破碎加工成100-150目得到。炉渣是将M2S煅烧时产生的含煤渣的M2S碎颗粒砂废料加工成大于50目的砂粉得到，煅烧温度为1000-1200℃，时间一般为50-60分钟。珍珠岩可选用河南产40目珍珠岩产品。沸石可选用湖北鄂州产丝光、斜发沸石矿，加工成≥40目的砂粉。桂林一号粉为一种天然树脂剂。电厂灰为火力发电厂除尘器下的粉煤灰尾料。双层筛机为20/100目双层制筛机。

Claims (8)

1、一种具有除硫磷功能的钢、铁水聚渣保温覆盖剂，其特征在于：其组分的重量比为：M2S砂粉10-28％；炉渣20-26％；珍珠岩20-30％；电厂灰10-28％；沸石5-10％；石墨3-10％；桂林一号粉6-8％。
2、根据权利要求1所述的具有除硫磷功能的钢、铁水聚渣保温覆盖剂，其特征在于：其组分的重量比为：M2S砂粉18％；炉渣23％；珍珠岩27％；电厂灰20％；沸石7％；石墨6％；桂林一号粉7％。
3、一种制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：将M2S砂粉、炉渣、电厂灰、沸石、石墨按上述比例混合后加入物料重量的3-10％的水搅拌1-5分钟，再加入珍珠岩和桂林一号粉混合后搅拌5-10分钟；搅拌好的混合料通过双层筛机制粒，收集颗粒集中度80％的颗粒进烘炉滚筒烘干，待物料冷却后得到本产品。
4、根据权利要求3所述的制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：M2S砂粉是由M2S破碎加工成100-150目得到。
5、根据权利要求3所述的制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：炉渣是将M2S煅烧时产生的含煤渣的M2S碎颗粒砂废料加工成大于50目的砂粉得到。
6、根据权利要求3所述的制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：电厂灰为火力发电厂除尘器下的粉煤灰尾料。
7、根据权利要求3所述的制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：双层筛机为20/100目双层制筛机。
8、根据权利要求3所述的制备具有除硫磷功能的钢、铁水聚渣保温覆盖剂的方法，其特征在于：沸石加工成≥40目的砂粉。
CNB2005100187131A 2005-05-16 2005-05-16 具有除硫磷功能的钢、铁水聚渣保温覆盖剂 Expired - Fee Related CN1311937C (zh)