CN1628902A - 除污用载金属配位体棉纤维吸附剂的合成方法 - Google Patents
除污用载金属配位体棉纤维吸附剂的合成方法 Download PDFInfo
- Publication number
- CN1628902A CN1628902A CN 200310107562 CN200310107562A CN1628902A CN 1628902 A CN1628902 A CN 1628902A CN 200310107562 CN200310107562 CN 200310107562 CN 200310107562 A CN200310107562 A CN 200310107562A CN 1628902 A CN1628902 A CN 1628902A
- Authority
- CN
- China
- Prior art keywords
- ball
- gossypin
- cellulose
- balls
- cellulose balls
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于它是由以下四个步骤构成：①金属属性的选择；②棉纤维素球珠的制备；③纤维素球的交联和活化与异化；④棉纤维素球珠的功能基化。本发明的优越性在于：1.交换速度快，而且极易洗脱；2.交换能力非常强。
Description
(一)所属领域
本发明属于一种吸附剂的制备方法，特别涉及一种除污用载金属配位体棉纤维吸附剂的合成方法。
(二)背景技术
在生产实践和科学实验当中特别是去除地下水中砷的实践中，普通吸附剂虽然具有离子交换的性能，但存在诸多缺点，比如①成本偏高；②交换能力低；③交换速度慢且不易洗脱。
(三)发明内容
本发明的目的是制备一种高选择性的载铁配位体交换棉纤维吸附剂，使得上述缺点得以克服，同时能很好地去除地下水中的三价砷。
本发明的技术方案为：一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于它是由以下四个步骤构成：①金属属性的选择；②棉纤维素球珠的制备；③纤维素球的交联和活化与异化；④棉纤维素球珠的功能基化。
上述所说的棉纤维素球珠的制备由以下步骤完成：①碱棉花的制备；②碱棉花的老化；③碱棉花的酯化；④棉纤维素球的制备；⑤棉纤维素球致孔。
上述所说的棉纤维素球的制备如下：在500毫升的三口瓶中，加入50-100毫升的粘胶液，过250目筛的2-7克碳酸钙，搅拌均匀，然后加入100-200分散介质，分散15-30分钟后以2℃/min缓慢升温之80-100℃，保持2小时。反应完冷却之室温，先用热水冲洗纤维素球之白色，即得棉纤维素球。
上述所说的纤维素球的交联和活化由下述步骤构成：①纤维素球的交联；②纤维素球的活化。
上述所说的纤维素球的交联过程为：取一定量的致孔后的纤维素湿求球，加入其体积的1-3倍的1mol/LNaOH溶液，在水浴中搅拌20-30分钟，加入一定量的环氧氯丙烷，仍在水浴中搅拌20-30分钟，然后加热到60-79℃反应20-40分钟，反应结束后用水洗净纤维素球。
上述所说的纤维素球的活化方法为：取10-20毫升交联后的纤维素湿球，分别加入浓度为1-3mol/LnaOH溶液10-20毫升，和3-4毫升环氧氯丙烷，在室温下震荡24小时，反应结束后细净纤维素球。
本发明的工作原理为：该制备包括三个过程，顺序为：①棉纤维素球珠的制备；②纤维素球的交联和活化；③棉纤维素球珠的功能基化。
本发明的优越性在于：1、交换速度快，而且极易洗脱；2、交换能力非常强。
(四)具体实施方式
一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于它是由以下三个步骤构成：
第一步：棉纤维素球珠的制备；所说的棉纤维素球珠的制备由以下步骤完成：①碱棉花的制备；②碱棉花的老化；③碱棉花的酯化；④棉纤维素球的制备；所说的棉纤维素球的制备如下：在500毫升的三口瓶中，加入50毫升的粘胶液，过250目筛的2克碳酸钙，搅拌均匀，然后加入100分散介质，分散15分钟后以2℃/min缓慢升温之80℃，保持2小时。反应完冷却之室温，先用热水冲洗纤维素球之白色，即得棉纤维素球。⑤棉纤维素球致孔。
第二步：纤维素球的交联和活化；所说的纤维素球的交联和活化由下述步骤构成：①纤维素球的交联；所说的纤维素球的交联过程为：取一定量的致孔后的纤维素湿求球，加入其体积的3倍的1mol/LNaOH溶液，在水浴中搅拌20分钟，加入一定量的环氧氯丙烷，仍在水浴中搅拌20分钟，然后加热到60℃反应40分钟，反应结束后用水洗净纤维素球。②纤维素球的活化，所说的纤维素球的活化方法为：取10毫升交联后的纤维素湿球，分别加入浓度为1mol/LnaOH溶液10毫升，和3毫升环氧氯丙烷，在室温下震荡24小时，反应结束后细净纤维素球；
第三步：棉纤维素球珠的功能基化。
Claims (6)
1、一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于它是由以下四个步骤构成：①金属属性的选择；②棉纤维素球珠的制备；③纤维素球的交联和活化与异化；④棉纤维素球珠的功能基化。
2、根据权利要求1所说一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于棉纤维素球珠的制备由以下步骤完成：①碱棉花的制备；②碱棉花的老化；③碱棉花的酯化；④棉纤维素球的制备；⑤棉纤维素球致孔。
3、根据权利要求2所说一种除污用载金属配位体棉纤维吸附剂的合成方法，其特征在于所说的棉纤维素球的制备如下：在500毫升的三口瓶中，加入50-100毫升的粘胶液，过250目筛的2-7克碳酸钙，搅拌均匀，然后加入100-200分散介质，分散15-30分钟后以2℃/min缓慢升温之80-100℃，保持2小时。反应完冷却之室温，先用热水冲洗纤维素球之白色，即得棉纤维素球。
4、根据权利要求1所说的纤维素球的交联和活化由下述步骤构成：①纤维素球的交联；②纤维素球的活化。
5、根据权利要求4所说的纤维素球的交联过程为：取一定量的致孔后的纤维素湿求球，加入其体积的1-3倍的1mol/LNaOH溶液，在水浴中搅拌20-30分钟，加入一定量的环氧氯丙烷，仍在水浴中搅拌20-30分钟，然后加热到60-79℃反应20-40分钟，反应结束后用水洗净纤维素球。
6、根据权利要求4所说的纤维素球的活化方法为：取10-20毫升交联后的纤维素湿球，分别加入浓度为1-3mol/LnaOH溶液10-20毫升，和3-4毫升环氧氯丙烷，在室温下震荡24小时，反应结束后细净纤维素球。