CN1603447A - 耐延迟断裂和冷加工性能优良的高强度螺栓钢 - Google Patents
耐延迟断裂和冷加工性能优良的高强度螺栓钢 Download PDFInfo
- Publication number
- CN1603447A CN1603447A CN 200410074410 CN200410074410A CN1603447A CN 1603447 A CN1603447 A CN 1603447A CN 200410074410 CN200410074410 CN 200410074410 CN 200410074410 A CN200410074410 A CN 200410074410A CN 1603447 A CN1603447 A CN 1603447A
- Authority
- CN
- China
- Prior art keywords
- steel
- delayed fracture
- cold
- content
- high strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
炉号 | 钢种 | C | Si | Mn | P | S | Cr | Mo | B | Ti | RE | Al | N | Nb | Zr | Fe |
1 | 发明钢 | 0.37 | 0.09 | 0.51 | 0.006 | 0.004 | 0.26 | 0.15 | 0.0011 | 0.030 | 0.008 | 0.01 | 0.008 | - | - | 余 |
2 | 发明钢 | 0.31 | 0.08 | 0.80 | 0.009 | 0.003 | 0.31 | 0.21 | 0.0008 | 0.015 | 0.010 | 0.03 | 0.005 | - | 0.04 | 余 |
3 | 发明钢 | 0.28 | 0.09 | 1.23 | 0.006 | 0.007 | 0.16 | 0.33 | 0.0025 | 0.071 | 0.011 | 0.01 | 0.007 | 0.03 | - | 余 |
4 | 发明钢 | 0.30 | 0.07 | 0.75 | 0.004 | 0.003 | 0.41 | 0.20 | 0.0007 | 0.043 | 0.009 | 0.04 | 0.006 | - | - | 余 |
5 | 对比钢 | 0.35 | 0.08 | 0.62 | 0.010 | 0.007 | 0.35 | 0.29 | - | - | 0.012 | 0.01 | 0.006 | - | - | 余 |
6 | 对比钢 | 0.29 | 0.32 | 0.76 | 0.020 | 0.017 | 0.35 | 0.24 | 0.0007 | 0.011 | 0.015 | 0.02 | 0.007 | - | - | 余 |
7 | 对比钢 | 0.32 | 0.21 | 0.68 | 0.021 | 0.016 | 0.28 | 0.25 | - | - | - | 0.02 | 0.005 | - | - | 余 |
8 | 商业钢 | 0.39 | 0.30 | 0.80 | 0.025 | 0.019 | 1.08 | 0.22 | - | - | - | 0.02 | 0.008 | - | - | 余 |
炉号 | 抗拉强度MPa | 屈服强度MPa | 延伸率δ5% | 缺口拉伸临界应力σcMPa | 冷变形时的临界压缩变形量℃ | |
本发明钢 | 1 | 1410 | 1270 | 13.5 | 1500 | 77 |
2 | 1340 | 1210 | 14.0 | 1550 | 81 | |
3 | 1250 | 1130 | 16.0 | 1650 | 80 | |
4 | 1260 | 1110 | 15.5 | 1610 | 79 | |
1370 | 1230 | 14.0 | 1540 | |||
对比钢 | 5 | 1380 | 1240 | 13.5 | 1380 | 74 |
6 | 1320 | 1180 | 12.5 | 1450 | 75 | |
7 | 1230 | 1100 | 14.5 | 1350 | 71 | |
1380 | 1230 | 12.5 | 1040 | |||
8 | 1260 | 1140 | 12.0 | 1270 | 67 | |
1420 | 1280 | 11.0 | 990 |
Claims (2)