CN1600983A - Printing paste and preparation method - Google Patents
Printing paste and preparation method Download PDFInfo
- Publication number
- CN1600983A CN1600983A CN 03151285 CN03151285A CN1600983A CN 1600983 A CN1600983 A CN 1600983A CN 03151285 CN03151285 CN 03151285 CN 03151285 A CN03151285 A CN 03151285A CN 1600983 A CN1600983 A CN 1600983A
- Authority
- CN
- China
- Prior art keywords
- printing
- mineral oil
- percentage
- weight
- sodium alginate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A printing thickener has composition (by wt.%) as carboxy methylamylose of 20-74.5%, sodium alginate of 20-70% and mineral oil of 0.5-25%. Its preparing process includes selecting materials a sper preparation ratio; grinding raw materials to be 20-50 millimcron; placing them into mixer for agitating, blending and spraying light lube, agitating continuously till raw materials being totally uniformed for obtaining product of printing thickener.
Description
[technical field]
The invention belongs to the carrier that the fabric printing dyestuff is used, the thickener and the preparation technology thereof that use when specifically a kind of activity, dispersion or direct dyes stamp.
[background technology]
The sodium alginate slurry is with a long history as printing paste, in stamp is used is a kind of more satisfactory thickener, and its maximum characteristics are and the dyestuff Fails To Respond easily to make dyestuff transfer to fiber from thickener and get on, print off simultaneously that decorative pattern is clear, bright-coloured, tinctorial yield is high, good hand touch.Not only be suitable for the cotton red ink paste used for seals, also be applicable to the stamp of wool, silk, synthetic fiber.
Existing sodium alginate slurry is to be made by pure sodium alginate, and sodium alginate mainly extracts from sea-tangle, but in recent years along with the application of sodium alginate on food industry and medical industry, it is nervous that marine algae resource seems, cost obviously improves; In addition, it is too short that sodium alginate is starched in use stationary phase, and slurry is stored and had only 2 days under the normal temperature, needs the existing existing usefulness of beating under summer high temperature, and both inconvenience easily caused waste again.
[summary of the invention]
The purpose of this invention is to provide a kind of new printing gum and preparation method thereof, reduce the use amount of sodium alginate in the prescription of the present invention, make that raw material obtains easily, the preparation method is easy, product good stability is arranged and store permanent, easy to use.
Each component and the percentage by weight thereof of printing gum of the present invention are as follows: carboxymethyl forms sediment 20～74.5%; Sodium alginate 20～70%; Mineral oil 0.5～2%.And can add calgon 5～20% or preservative agent 2～8%.Its preparation method may further comprise the steps: get material by formula rate; Raw material (not comprising mineral oil) is crushed to 20～50 orders; Put into blender, stir at normal temperatures, mix, spray into vaporific mineral oil simultaneously; Continue to stir 0.5～1.0 hour, until even fully; Get the finished product printing gum.Adopt carboxymethyl starch (belonging to etherification starch) to be because its thickening property and water-soluble are good, raw material is easy to get, thereby can reduce the use amount of sodium alginate relatively largely, reduced cost of material; Spray into vaporific mineral oil and play the mediation effect, and can further improve thickener give colourity and vividness.
Described preservative agent is Sodium Benzoate or sodium sorbate; Mineral oil is light profit oil (or light wheel oil).
The beneficial effect that the present invention has is: 1) reducing under the sodium alginate use amount, tinctorial yield will be higher than the printing gum of being made by pure sodium alginate on the contrary, and has the outstanding piece face uniformity; 2) cold water-soluble is good, and direct available cold-water solution is easy to use; 3) good stability is convenient to permanent storage, and summer, slurry can be deposited about 15 days; 4) wide adaptability can be used for activity, dispersion or the direct dyes stamp of various fibers, various models; 5) thickener is low-consuming, has reduced the production use cost; 6) preparation method of printing gum is simple.
The invention will be further described below in conjunction with embodiment.
[specific embodiment]
Embodiment 1, by carboxymethyl starch 70% (percentage by weight), the ratio of sodium alginate 28% (percentage by weight) takes by weighing 210 kilograms of carboxymethyl starch (commercially available), 84 kilograms sodium alginate, through being crushed to the 20-50 order, above-mentioned powder is put into blender to be stirred at normal temperatures, mix, the light profit oil (commercially available) of getting 6 kilograms (2% percentage by weights) feeds in the blender by the air pump pressurization, light profit oil is vaporific, stir while spraying into, the oil spraying finishes the back and continues to stir, mix, mixing time adds up and gets printing gum after 1 hour, through discharging, packing gets final product.Finished product is the ecru powdered granule, pH value: 6.5-7.0.During concrete the use, add the thickener of 5% (weight ratio) in the cold water of 95% (weight ratio), and constantly stir, the viscosity of gained slurry is 40000-60000CPS, is used for dispersion, direct dyes printing thickener.
Embodiment 2, by carboxymethyl starch 72% (percentage by weight), sodium alginate 25% (percentage by weight), the ratio of Sodium Benzoate 2% (percentage by weight) takes by weighing 216 kilograms of carboxymethyl starch (commercially available), 75 kilograms sodium alginate, 6 kilograms of Sodium Benzoates, through being crushed to the 20-50 order, above-mentioned powder is put into blender to be stirred at normal temperatures, mix, the light oil of taking turns of getting 3 kilograms (1%) is vaporific by the air pump pressurization and sprays in the blender, through stirring, mix and amount to 50 minutes, get the printing thickener finished product, the product of this prescription has stability for storage, owing to added preservative agent, it is added water be mixed with pasty slurry, even can guarantee that in summer the two weeks performance is constant, having overcome because of bacterial reproduction causes pasty slurry thinning, rotten, the defective of easy to leak, simultaneously also saved thickener, be used for disperseing, the direct dyes printing thickener.Used preservative agent also can adopt sodium sorbate.
Embodiment 3, by carboxymethyl starch 35% (percentage by weight), sodium alginate 49% (percentage by weight), the ratio of calgon 15% (percentage by weight) takes by weighing 105 kg carboxymethyl starch (commercially available), 147 kilograms sodium alginate, 45 kilograms calgon, through being crushed to the 20-50 order, above-mentioned powder is put into blender to be stirred at normal temperatures, mix, the light profit oil of getting 3 kilograms (1%) sprays in the blender by the air pump pressurization, light profit oil is vaporific, stir while spraying into, the oil spraying finishes the back and continues to stir, mix, mixing time adds up and gets printing gum after 1 hour, through discharging, packing gets final product.The thickener of this prescription is suitable for active, direct dyes printing thickener.
Claims (5)
1, a kind of printing gum is characterized in that each component and the percentage by weight thereof of described thickener is as follows:
Carboxymethyl starch 20～74.5%;
Sodium alginate 20～70%;
Mineral oil 0.5～2%.
2, a kind of printing gum according to claim 1 is characterized in that also containing in the described thickener percentage by weight and is 5～20% calgon.
3, a kind of printing gum according to claim 1 is characterized in that also containing in the described thickener percentage by weight and is 2～8% preservative agent, and described preservative agent is Sodium Benzoate or sodium sorbate.
4,, it is characterized in that the mineral oil in the described thickener is light profit oil according to claim 1,2 or 3 described a kind of printing gums.
5, a kind of preparation method of printing gum is characterized in that may further comprise the steps:
1) gets material (not comprising mineral oil) by formula rate;
2) raw material pulverizing to 20～50 orders;
3) raw material after the pulverizing is put into the blender stirring, is mixed, and sprays into vaporific mineral oil simultaneously;
4) continue to stir 0.5～1.0 hour,, get the printing gum finished product until fully evenly.