CN1600823A - 多功能隔热防水漆及生产工艺 - Google Patents

多功能隔热防水漆及生产工艺 Download PDF

Info

Publication number
CN1600823A
CN1600823A CN 03157556 CN03157556A CN1600823A CN 1600823 A CN1600823 A CN 1600823A CN 03157556 CN03157556 CN 03157556 CN 03157556 A CN03157556 A CN 03157556A CN 1600823 A CN1600823 A CN 1600823A
Authority
CN
China
Prior art keywords
water
resistant paint
multifunctional thermal
powder
insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 03157556
Other languages
English (en)
Inventor
颜振颖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 03157556 priority Critical patent/CN1600823A/zh
Publication of CN1600823A publication Critical patent/CN1600823A/zh
Pending legal-status Critical Current

Abstract

本发明是一种用于建筑方面的隔热防水涂料及生产工艺，特别是一种多功能隔热防水漆及生产工艺。其成分包括热水、聚乙烯醇、水玻璃(泡化碱)、盐酸、甲醛、丙烯酸乳液、消泡剂(磷酸三丁酯)、分散剂(磷酸三钠)、增稠剂(聚丙烯酰胺)、烧碱水、体质颜料。其生产工艺如下：将聚乙烯醇溶于热水。然后加入水玻璃(泡化碱)、盐酸和甲醛，经低温反应即为基料，于基料中加入体质颜料及消泡剂(磷酸三丁酯)、分散剂(磷酸三钠)，经高速搅拌混合，然后再加入增稠剂(聚丙烯酰胺)均匀调和，在调和料中加入烧碱水，使调和料呈碱性，将上述呈碱性的调和料，用60－80目的细筛过滤即得到本发明所述的多功能隔热防水漆。

Description

多功能隔热防水漆及生产工艺
技术领域
本发明是一种用于建筑方面的隔热防水涂料及生产工艺，特别是一种多功能隔热防水漆及生产工艺
背景技术
现有技术中的防水漆，它们有如下缺陷：对太阳光线反射能力较差，因此不能阻止热量的传导；涂层容易脱落，不耐老化；防水性能较差，不能很好地适应户外气候。
发明内容
本发明是为了克服上述公知技术的缺点而发明一种耐水性、耐碱性、耐热性、耐洗刷性均能达到国家标准，且涂层外观平滑的多功能隔热防水漆及生产工艺。
本发明所述的多功能隔热防水漆是由以下成分和比例所组成：(单位Kg)：
热水                                        90-110
聚乙烯醇                                    10-13
水玻璃(泡化碱)                              4-5
盐酸                                        1.3-1.5
甲醛                                        0.4-0.5
丙烯酸乳液                                  11-13
消泡剂(磷酸三丁酯)                          0.04-0.05
分散剂(磷酸三钠)                            0.10-0.11
增稠剂(聚丙烯酰胺)                          0.18-0.22
烧碱水                                      1-1.5
隔热粉                                       65-70
滑石粉                                       14-17
轻质碳酸钙粉                                 20-22
本发明所述的多功能隔热防水漆是由以下较佳的成分和比例所组成：
(单位Kg)
热水                                         95-100
聚乙烯醇                                     12-13
水玻璃(泡化碱)                               4-4.5
盐酸                                         1.4-1.5
甲醛                                         0.45-0.5
丙烯酸乳液                                   11.5-12.5
消泡剂(磷酸三丁酯)                           0.045-0.05
分散剂(磷酸三钠)                             0.095-0.105
增稠剂(聚丙烯酰胺)                           0.19-0.21
烧碱水                                       1-1.5
隔热粉                                       65-70
滑石粉                                       14-15
轻质碳酸钙粉                                 20-21
本发明所述多功能隔热防水漆的生产工艺是按如下的方式来实现的：
一.聚乙烯醇溶于热水(热水温度为90℃-95℃)中，然后加入水玻璃(泡化碱)、盐酸、甲醛和丙烯酸乳液，经0.9-1.1小时的低温(所述低温为
70℃-75℃)反应，即为基料。
二.于上述基料中加入体质颜料及消泡剂(磷酸三丁酯)、分散剂(磷酸三钠)，经高速搅拌混合，然后再加入增稠剂(聚丙烯酰胺)均匀调和。
三.在上述调和料中加入烧碱水，使调和料呈碱性，PH值为11-13。
四.将上述呈微碱性的调和料，用60-80目的细筛过滤即得到本发明所述的多功能隔热防水漆。
本发明具有以下积极效果：
本发明所述的多功能隔热防水漆，是一种水溶性涂料，只需薄薄的一层，就能将太阳的光线(包括红外线、紫外线)反射，阻止热量的传导，从而起到隔热的作用；该涂层干后非常坚固，不易脱落，耐老化，无毒，无放射性；隔热防水漆中的成份具有防水性，特高的户外耐气候性。
具体实施方式
本发明所述的多功能隔热防水漆是按如下具体实施方式来实现的：
多功能隔热防水漆是由以下成分和比例所组成(单位Kg)：
热水                                         100
聚乙烯醇                                     12
水玻璃(泡化碱)                               4
盐酸                                         1.5
甲醛                                         0.5
丙烯酸乳液                                   12
消泡剂(磷酸三丁酯)                           0.05
分散剂(磷酸三钠)                             0.1
增稠剂(聚丙烯酰胺)                           0.2
烧碱水                                       1.2
隔热粉                                       70
滑石粉                                       15
轻质碳酸钙粉                                 20
多功能隔热防水漆的生产工艺是按如下方式来实现的：
一.聚乙烯醇溶于热水(热水温度为90℃-95℃)中，然后加入水玻璃(泡化碱)、盐酸、甲醛和丙烯酸乳液，经0.9-1.1小时的低温(所述低温为
70℃-75℃)反应，即为基料。
二.于上述基料中加入体质颜料及消泡剂(磷酸三丁酯)、分散剂(磷酸三钠)，经高速搅拌混合，然后再加入增稠剂(聚丙烯酰胺)均匀调和。
三.在上述调和料中加入烧碱水，使调和料呈碱性，PH值为12
四.上述呈碱性的调和料，用60-80目的细筛过滤即得到本发明所述的多功能隔热防水漆。

Claims (4)

1.一种多功能隔热防水漆，其特征在于：所述多功能隔热防水漆是由以下成分和比例所组成：(单位Kg)：
热水                          90-110
聚乙烯醇                      10-13
水玻璃(泡化碱)                4-5
盐酸                          1.3-1.5
甲醛                          0.4-0.5
丙烯酸乳液                    11-13
消泡剂(磷酸三丁酯)            0.04-0.05
分散剂(磷酸三钠)              0.10-0.11
增稠剂(聚丙烯酰胺)            0.18-0.22
烧碱水                        1-1.5
隔热粉                        65-70
滑石粉                        14-17
轻质碳酸钙粉                  20-22
2.根据权利要求1所述的多功能隔热防水漆，其特征在于：所述的多功能隔热防水漆是由以下较佳的成分和比例所组成(单位Kg)：
热水                          95-100
聚乙烯醇                      12-13
水玻璃(泡化碱)                4-4.5
盐酸                          1.4-1.5
甲醛                          0.45-0.5
丙烯酸乳液                    11.5-12.5
消泡剂(磷酸三丁酯)            0.045-0.05
分散剂(磷酸三钠)              0.095-0.105
增稠剂(聚丙烯酰胺)         0.19-0.21
烧碱水                     1-1.5
隔热粉                     65-70
滑石粉                     14-15
轻质碳酸钙粉               20-21
3.根据权利要求1、2所述的多功能隔热防水漆，其特征在于：所述的多功能隔热防水漆是由以下较佳的成分和比例所组成(单位Kg)：
热水                       100
聚乙烯醇                   12
水玻璃(泡化碱)             4
盐酸                       1.5
甲醛                       0.5
丙烯酸乳液                 12
消泡剂(磷酸三丁酯)         0.05
分散剂(磷酸三钠)           0.1
增稠剂(聚丙烯酰胺)         0.2
烧碱水                     1.2
隔热粉                     70
滑石粉                     15
轻质碳酸钙粉               20
4.根据权利要求1、2、3所述的多功能隔热防水漆的生产工艺，其特征在于：
一.聚乙烯醇溶于热水(热水温度为90℃-95℃)中，然后加入水玻璃(泡化碱)、盐酸、甲醛和丙烯酸乳液，经0.9-1.1小时的低温(所述低温为70℃-75℃)反应，即为基料。
二.于上述基料中加入隔热粉、滑石粉、轻质碳酸钙粉及消泡剂(磷酸三丁酯)、分散剂(磷酸三钠)，经高速搅拌混合，然后再加入增稠剂(聚丙烯酰胺)均匀调和。
三.在上述调和料中加入烧碱水，使调和料呈碱性，PH值为11-13，最佳值为12。
四.将上述呈微碱性的调和料，用60-80目的细筛过滤即得到本发明所述的多功能隔热防水漆。
CN 03157556 2003-09-24 2003-09-24 多功能隔热防水漆及生产工艺 Pending CN1600823A (zh)