CN1554584A - 一种制备线状硅灰石纳米材料的方法 - Google Patents

一种制备线状硅灰石纳米材料的方法 Download PDF

Info

Publication number
CN1554584A
CN1554584A CNA2003101224726A CN200310122472A CN1554584A CN 1554584 A CN1554584 A CN 1554584A CN A2003101224726 A CNA2003101224726 A CN A2003101224726A CN 200310122472 A CN200310122472 A CN 200310122472A CN 1554584 A CN1554584 A CN 1554584A
Authority
CN
China
Prior art keywords
nano
wollastonite
wire
quality
acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2003101224726A
Other languages
English (en)
Other versions
CN1237004C (zh
Inventor
林 曹
曹林
韩志华
潘德安
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Science and Technology Beijing USTB
Original Assignee
University of Science and Technology Beijing USTB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Science and Technology Beijing USTB filed Critical University of Science and Technology Beijing USTB
Priority to CN 200310122472 priority Critical patent/CN1237004C/zh
Publication of CN1554584A publication Critical patent/CN1554584A/zh
Application granted granted Critical
Publication of CN1237004C publication Critical patent/CN1237004C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供了一种制备线状硅灰石纳米材料的方法，其特征在于：利用微乳液法使乙酸和硅灰石反应的同时，加入柠檬酸作为活性剂使纳米颗粒自组装成为纳米线。具体方法为：在水中加入原料硅灰石和乙酸，浓度为硅灰石1～3质量％，乙酸5～8质量％，回流2.5～3.5小时，回流温度摄氏50～60℃；加柠檬酸2～5质量％，继续回流7～8小时，成乳液状；在摄氏450～700℃进行热处理，成线状纳米线。本发明的优点在于：具有方法简单、易于控制、材料稳定、不易在反应中分解为纳米二氧化硅和氧化钙的特点。同时，由于纳米线是由纳米颗粒排列组成，由其制作的其它材料会具有三维介孔结构。

Description

一种制备线状硅灰石纳米材料的方法
技术领域
本发明属于无机化工工艺技术领域，特别是提供了一种制备线状硅灰石纳米材料的方法，采用天然硅灰石制备自组装线状硅灰石纳米材料，
背景技术
硅灰石是制作精瓷的上佳原料，也是荧光材料的基质材料，同时又可作为补强剂和添加剂用于塑料、橡胶、涂料等领域。硅灰石纳米线可用于制作生物活性陶瓷、介孔陶瓷、自清洁陶瓷及具有可切削等特殊物理性能的特种陶瓷，也可用于前述其它领域。经中国科学院文献情报中心3003年5月19日关于“非金属矿物硅灰石纳米材料的应用研究”的科技查新报告显示，根据国际联机检索(使用了美国DIALOG系统)和国内联机检索，查找了29个有关数据库，从其存储的国内外文献中得到密切相关文献12篇，如在中国学位论文库中，发现“短纤维增强聚酰亚胺树脂基复合材料”(裴清钢，天津大学，管藏号Y283785，1998。1)一文，提出了以硅灰石改善短纤维的强复合材料力学性能和工艺性能的方法，发明者在这些文献中未见硅灰石纳米线制备方法的报道。发明者于近日在中国BAIDU及GOOGLE等检索网页和国际上有关检索网页上也未发现相关报道。
发明内容
利用微乳液法使乙酸和硅灰石反应的同时，加入柠檬酸作为活性剂使纳米颗粒自组装成为纳米线。具体方法如下：
1、在水中加入原料硅灰石和乙酸，浓度为硅灰石1～3质量％，乙酸5～8质量％，回流2.5～3.5小时，回流温度慑氏50～60℃。
2、加柠檬酸2～5质量％，继续回流7～8小时，成乳液状。
3、在慑氏450～700℃进行热处理，成线状纳米线。
本发明的优点在于：具有方法简单、易于控制、材料稳定、不易在反应中分解为纳米二氧化硅和氧化钙的特点。同时，由于纳米线是由纳米颗粒排列组成，由其制作的其它材料会具有三维介孔结构。
附图说明
图1是本发明硅灰石纳米线的电子显微镜照片，照片中可看到小于100纳米的纳米线是由10到几十纳米的纳米颗粒排列组成。
具体实施方式
实施例1：
1、在水中加入原料硅灰石和乙酸，浓度为硅灰石2质量％，乙酸6质量％，回流3小时，回流温度慑氏50℃。
2、加柠檬酸3质量％，继续回流7小时，成乳液状。
3、在慑氏600℃热处理2小时，成线状纳米线。
实施例2
1、在水中加入原料硅灰石和乙酸，浓度为硅灰石3质量％，乙酸7质量％，回流3小时，回流温度慑氏50℃。
2、加柠檬酸4质量％，继续回流7小时，成乳液状。
3、在慑氏480℃热处理2小时，成线状纳米线。

Claims (1)

1、一种制备线状硅灰石纳米材料的方法，其特征在于：利用微乳液法使乙酸和硅灰石反应的同时，加入柠檬酸作为活性剂使纳米颗粒自组装成为纳米线；具体方法如下：
a、在水中加入原料硅灰石和乙酸，浓度为硅灰石1～3质量％，乙酸5～8质量％，回流2.5～3.5小时，回流温度慑氏50～60℃；
b、加柠檬酸2～5质量％，继续回流7～8小时，成乳液状；
c、在慑氏450～700℃进行热处理，成线状纳米线。
CN 200310122472 2003-12-25 2003-12-25 一种制备线状硅灰石纳米材料的方法 Expired - Fee Related CN1237004C (zh)