CN1527036A - 电子秤用通电发热玻璃面板及其生产工艺 - Google Patents
电子秤用通电发热玻璃面板及其生产工艺 Download PDFInfo
- Publication number
- CN1527036A CN1527036A CNA031582710A CN03158271A CN1527036A CN 1527036 A CN1527036 A CN 1527036A CN A031582710 A CNA031582710 A CN A031582710A CN 03158271 A CN03158271 A CN 03158271A CN 1527036 A CN1527036 A CN 1527036A
- Authority
- CN
- China
- Prior art keywords
- lines
- face glass
- conducting film
- heating power
- conductive film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种电子秤用通电发热玻璃面板及其生产工艺,它包括钢化玻璃面板基体1以及间隔镀覆在玻璃面板基体上表面的导电膜层2,镀覆导电膜层后在玻璃面板基体上表面形成许多未镀覆导电膜层的纹路3,由此构成一个完整的通电发热电路。其生产工艺为:一、配制导电膜保护油墨以氧化铈粉末为主料,配以调粘剂、固化剂、挥发剂,采用油墨轧制机轧制调和均匀;二、丝网印刷纹路制作丝网网板,取配制好的导电膜保护油墨采用丝网印刷至玻璃面板基体上表面,烘干;三、镀导电膜层在上述丝印好的玻璃基体上表面镀导电膜;四、清除油墨残留形成纹路。通电后玻璃面板表面会发热产生热量。人赤足站立在玻璃电子秤面板上觉得比较暖和。
Description
技术领域:
本发明涉及一种电子秤面板。特别是涉及一种电子秤用通电发热玻璃面板及其生产工艺。
背景技术:
目前普通的电子秤面板,一般采用金属材料或普通钢化玻璃等材料制作而成。其表面不会产生热量。特别是在冬天,环境温度较低,人赤足站立在电子秤面板在会觉得较凉。经常使用会影响身体健康。
发明内容:
本发明的目的在于克服上述不足,提供一种表面能产生热量的电子秤用通电发热玻璃面板及其生产工艺。
本发明的目的是这样实现的:一种电子秤用通电发热玻璃面板,它包括钢化玻璃面板基体以及间隔镀覆在玻璃面板基体上表面的导电膜层,镀覆导电膜层后在玻璃面板基体上表面形成许多未镀覆导电膜层的纹路,由此构成一个完整的通电发热电路。
上述纹路分布于玻璃面板基体上表面四角,在每一角呈半圆弧状布置,其位于同侧的最外周的两圆弧纹路两两相连,置于面板四边靠近中间的圆弧纹路端部断开,其余纹路则导通。
通电后玻璃面板表面会发热产生热量。特别是在冬天,环境温度较低,人赤足站立在玻璃电子秤面板上觉得比较暖和。
本发明的目的还可以是这样实现的:一种电子秤用通电发热玻璃面板的生产工艺,其工艺步骤为:
一、配制导电膜保护油墨 以氧化铈粉末为主料,配以调粘剂、固化剂、挥发剂,采用油墨轧制机轧制调和均匀,其中氧化铈粉末在原料中所占的重量百分比为50-80%。
二、丝网印刷纹路 将上述纹路采用电脑制板,制作丝网网板,取配制好的导电膜保护油墨采用丝网印刷至玻璃面板基体上表面,烘干。
三、镀导电膜层 在上述丝印好的玻璃基体上表面镀导电膜。
四、清除油墨残留形成纹路。
附图说明:
图1为本发明的表面结构示意图。
图2为图1的侧视图。
具体实施方式:
如图1-2,本发明为一种电子秤用通电发热玻璃面板,它包括钢化玻璃面板基体1以及间隔镀覆在玻璃面板基体1上表面的ITO导电膜层2,镀覆导电膜层2后在玻璃面板基体1上表面形成许多未镀覆导电膜层的纹路3,由此构成一个完整的通电发热电路。纹路3分布于玻璃面板基体1上表面四角,在每一角呈半圆弧状布置,其位于同侧的最外周的两圆弧纹路3-1-1与3-2-1和3-3-1与3-4-1两两相连,置于面板四边靠近中间的圆弧纹路3-1-1、3-1-2、3-2-1、3-2-2、3-3-1、3-3-2、3-4-1、3-4-2端部断开,其余纹路则导通。
本发明的生产工艺步骤为:
一、配制导电膜保护油墨 以氧化铈粉末为主料,配以调粘剂、固化剂、挥发剂,采用油墨轧制机轧制调和均匀,其中氧化铈粉末在原料中所占的重量百分比为50-80%。
二、丝网印刷纹路 将上述纹路采用电脑制板,制作丝网网板,取配制好的导电膜保护油墨采用丝网印刷至玻璃面板基体上表面,烘干。
三、镀导电膜层 在上述丝印好的玻璃基体上表面镀导电膜。
四、清除油墨残留形成纹路。
Claims (3)
1、一种电子秤用通电发热玻璃面板,其特征在于它包括钢化玻璃面板基体(1)以及间隔镀覆在玻璃面板基体(1)上表面的导电膜层(2),镀覆导电膜层(2)后在玻璃面板基体(1)上表面形成许多未镀覆导电膜层的纹路(3),由此构成一个完整的通电发热电路。
2、根据权利要求1所述的一种电子秤用通电发热玻璃面板,其特征在于纹路(3)分布于玻璃面板基体(1)上表面四角,在每一角呈半圆弧状布置,其位于同侧的最外周的两圆弧纹路(3-1-1)与(3-2-1)和(3-3-1)与(3-4-1)两两相连,置于面板四边靠近中间的圆弧纹路(3-1-1、3-1-2、3-2-1、3-2-2、3-3-1、3-3-2、3-4-1、3-4-2)端部断开,其余纹路则导通。
3、根据权利要求1或2所述的一种电子秤用通电发热玻璃面板,其特征在于导电膜层(2)采用ITO导电膜。
4、根据权利要求1所述的一种电子秤用通电发热玻璃面板的生产工艺,其特征在于其工艺步骤为:
一、配制导电膜保护油墨 以氧化铈粉末为主料,配以调粘剂、固化剂、挥发剂,采用油墨轧制机轧制调和均匀,其中氧化铈粉末在原料中所占的重量百分比为50-80%;
二、丝网印刷纹路 将上述纹路采用电脑制板,制作丝网网板,取配制好的导电膜保护油墨采用丝网印刷至玻璃面板基体上表面,烘干;
三、镀导电膜层在上述丝印好的玻璃基体上表面镀导电膜;
四、清除油墨残留形成纹路。