CN1483779A - 一种防火涂料及其制备方法 - Google Patents
一种防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN1483779A CN1483779A CNA031262759A CN03126275A CN1483779A CN 1483779 A CN1483779 A CN 1483779A CN A031262759 A CNA031262759 A CN A031262759A CN 03126275 A CN03126275 A CN 03126275A CN 1483779 A CN1483779 A CN 1483779A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight part
- mixture
- mineral filler
- retardant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防火涂料及其制备方法，是由下述物质按重量份组合而成：甲基或苯基或乙烯基120－2型硅橡胶或者它们的混合物20－40份；交联固化剂过氧化物系列苯甲酰或双二四3－6份；补强剂白碳黑纳米级13－25份；无机填料40－60份。本发明的优点在于选用上述配料，并按照所述制备方法生产的防火涂料涂覆在PAN基氧化纤维布防火布上，用酒精灯外焰垂直燃烧5－10分钟，其限氧指数高于日本标准。经测试，其收缩率≤3％、热收缩率≤5％、烧焦长度≤4英寸、阴燃时间≤1.5秒钟。不仅大大地提高了PAN基氧化纤维布防火布的防火性能，同时又保持了PAN基氧化纤维布原有的物理性能。
Description
技术领域：
本发明涉及一种防火涂料，本发明还涉及该涂料的制备方法。
背景技术：
防火布广泛用于消防、炼钢、航天及军事等领域。如用于消防战士的战斗服，或作为炼钢人员的工作服等。目前所使用的防火布主要有PAN基氧化纤维布和石棉防火布。石棉防火布毒性大，属淘汰产品；PAN基氧化纤维防火布目前我国多从日本进口，国内现也有厂家生产，但其防火效果较比日本生产的防火布较差。目前国内还没有防火布的技术标准，日本对防火布的测试标准主要有氧指数垂直法，标准号为：JISK7201、JISD1201、JISA1323-1995，标准要求收缩率≤5％、热收缩率≤7％、烧焦长度≤6英寸、阴燃时间≤2秒钟。怎样进一步提高PAN基氧化纤维布的防火性能，是人们一直研究的课题。
在PAN基氧化纤维布上涂覆防火涂层不失为一种提高PAN基氧化纤维布防火性能的办法，但PAN基氧化纤维布防火布具有柔韧性，既要提高其防火性能又要保持其所具有的物理性能，这样的防火涂料目前还没有。
发明内容：
本发明之目的在于提供一种防火涂料，将它涂覆在PAN基氧化纤维布防火上不仅可以大大提高PAN基氧化纤维布的防火性能，同时不会改变PAN基氧化纤维布原有的物理性能。
本发明另一目的在于提供该防火涂料的制备方法。
为达到上述目的，本发明可通过下述技术方案实现：
本发明所述的防火涂料，是由下述物质按重量份组合而成：甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物20-40份；交联固化剂过氧化物系列苯甲酰或双二四3-6份；补强剂白碳黑纳米级13-25份；无机填料40-60份。
所述无机填料为滑石粉或水高岭、重质碳酸钙、水高岭土、灰硅石粉。
所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为20份；交联固化剂过氧化物系列苯甲酰或双二四为6份；无机填料重量份为40份；补强剂白碳黑纳米级13份。
所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为30份；交联固化剂过氧化物系列苯甲酰或双二四为5份；无机填料重量份为50份；补强剂白碳黑纳米级15份。
所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为40份；交联固化剂过氧化物系列苯甲酰或双二四为3份；无机填料重量份为60份；补强剂白碳黑纳米级25份。
本发明所述涂料的制备方法为：
第一步：按重量份取甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物，交联固化剂过氧化物系列苯甲酰或双二四，补强剂白碳黑纳米级；
第二步：按重量份取无机填料，在100-150℃下进行真空烘干处理；
第三步：取合成级石油甲苯，与第一步的混合物按2∶1的重量份充分混合；
第四步：将第三步所得物按3∶1的重量份与第二步的无机填料进行球磨胶体混合，第一次高速分散转速为1000-1200转/分，然后进行1200-1400目筛滤；进行第二次高速分散，转速为1350-1450转/分；
第五步：将第四步所得物进行各色指标测试后灌装。
所述第四步中的第一次高速分散转速为1000转/分，然后进行1300目筛滤；第二次高速分散，转速为1400转/分。
本发明的优点在于通过选用甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物20-40份，交联固化剂过氧化物系列苯甲酰或双二四3-6份，交联固化剂过氧化物系列苯甲酰或双二四3-6份，并按照所述制备方法生产的防火涂料涂覆在PAN基氧化纤维布防火布上，用酒精灯外焰垂直燃烧5-10分钟，其限氧指数高于日本标准。经测试，其收缩率≤3％、热收缩率≤5％、烧焦长度≤4英寸、阴燃时间≤1.5秒钟。不仅大大地提高了PAN基氧化纤维布防火布的防火性能，同时又保持了PAN基氧化纤维布原有的物理性能。
具体实施方式：
实施例1：
第一步，按重量份取甲基120-2型硅橡胶20份；交联固化剂过氧化物系列苯甲酰6份；补强剂白碳黑纳米级13份。
第二步：取滑石粉40份在100℃下进行真空烘干处理；
第三步：取合成级石油甲苯作溶剂，与第一的混合物按2∶1的重量份充分混合；
第四步：将第三步所得物按3∶1的重量份与第二步的滑石粉进行球磨胶体混合，第一次高速分散转速为1000转/分，然后进行1300目筛滤；进行第二次高速分散，转速为1400转/分；
第五步：将第四步所得物进行各色指标测试后灌装。
所述无机填料为或水高岭、重质碳酸钙、水高岭土、灰硅石粉。
实施例2：
第一步，按重量份取苯基120-2型硅橡胶30份；交联固化剂过氧化物系列双二四为5份；补强剂白碳黑纳米级15份。
第二步：取水高岭土50份在120℃下进行真空烘干处理；
第三步：取合成级石油甲苯作溶剂，与第一的混合物按2∶1的重量份充分混合；
第四步：将第三步所得物按3∶1的重量份与第二步的水高岭土进行球磨胶体混合，第一次高速分散转速为1100转/分，然后进行1200目筛滤；进行第二次高速分散，转速为1350转/分；
第五步：将第四步所得物进行各色指标测试后灌装。
实施例3：
第一步，按重量份取乙烯基120-2型硅橡胶40份；交联固化剂过氧化物系列苯甲酰3份；补强剂白碳黑纳米级25份。
第二步：取灰硅石粉60份在150℃下进行真空烘干处理；
第三步：取合成级石油甲苯作溶剂，与第一的混合物按2∶1的重量份充分混合；
第四步：将第三步所得物按3∶1的重量份与第二步的灰硅石粉进行球磨胶体混合，第一次高速分散转速为1200转/分，然后进行1150目筛滤；进行第二次高速分散，转速为1450转/分；
Claims (7)
1、一种防火涂料，其特征在于：它是由下述物质按重量份组合而成：甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物20-40份；交联固化剂过氧化物系列苯甲酰或双二四3-6份；补强剂白碳黑纳米级13-25份；无机填料40-60份。
2、根据权利要求1所述的防火涂料，其特征在于：所述无机填料为滑石粉或水高岭、重质碳酸钙、水高岭土、灰硅石粉。
3、根据权利要求1所述的防火涂料，其特征在于：所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为20份；交联固化剂过氧化物系列苯甲酰或双二四为6份；无机填料重量份为40份；补强剂白碳黑纳米级13份。
4、根据权利要求1所述的防火涂料，其特征在于：所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为30份；交联固化剂过氧化物系列苯甲酰或双二四为5份；无机填料重量份为50份；补强剂白碳黑纳米级15份。
5、根据权利要求1所述的防火涂料，其特征在于：所述甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物的重量份为40份；交联固化剂过氧化物系列苯甲酰或双二四为3份；无机填料重量份为60份；补强剂白碳黑纳米级25份。
6、如权利要求1所述防火涂料的制备方法，其特征在于：它是按照下述步骤制备：
第一步：按重量份取甲基或苯基或乙烯基120-2型硅橡胶或者它们的混合物，交联固化剂过氧化物系列苯甲酰或双二四，补强剂白碳黑纳米级；
第二步：按重量份取无机填料，在100-150℃下进行真空烘干处理；
第三步：取合成级石油甲苯，与第一步的混合物按2∶1的重量份充分混合；
第四步：将第三步所得物按3∶1的重量份与第二步的无机填料进行球磨胶体混合，第一次高速分散转速为1000-1200转/分，然后进行1200-1400目筛滤；进行第二次高速分散，转速为1350-1450转/分；
第五步：将第四步所得物进行各色指标测试后灌装。
7、根据权利要求6所述的制备方法，其特征在于：所述第四步中的第一次高速分散转速为1000转/分，然后进行1300目筛滤；第二次高速分散，转速为1400转/分。