CN1480546A - 超细硬质合金的制备方法 - Google Patents

超细硬质合金的制备方法 Download PDF

Info

Publication number
CN1480546A
CN1480546A CNA031246710A CN03124671A CN1480546A CN 1480546 A CN1480546 A CN 1480546A CN A031246710 A CNA031246710 A CN A031246710A CN 03124671 A CN03124671 A CN 03124671A CN 1480546 A CN1480546 A CN 1480546A
Authority
CN
China
Prior art keywords
powder
hard alloy
value
batching
tac
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031246710A
Other languages
English (en)
Other versions
CN1207417C (zh
Inventor
李来荣
刘知径
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Cemented Carbide Group Co Ltd
Original Assignee
Zhuzhou Cemented Carbide Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Cemented Carbide Group Co Ltd filed Critical Zhuzhou Cemented Carbide Group Co Ltd
Priority to CN 03124671 priority Critical patent/CN1207417C/zh
Publication of CN1480546A publication Critical patent/CN1480546A/zh
Application granted granted Critical
Publication of CN1207417C publication Critical patent/CN1207417C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(38～41)KA/m的WC粉和(7.8～8.2)wt％的Co粉，并加入(0.28～0.30)wt％的VC，(0.31～0.35)wt％的TaC，(0.31～0.35)wt％的Cr3C2，VC、TaC和Cr3C2的总量为(0.95～1.0)wt％，配料计算时，碳平衡值为(+0.26～+0.28)％。采用上述制备方法，可使制得的硬质合金中WC的平均晶粒度达(0.3～0.4)μm，硬质合金的硬度达HV3：1900～1980，并且可使用该种超细硬质合金制造的PCB微钻的钻径最小达0.3mm。

Description

超细硬质合金的制备方法
技术领域：
本发明涉及一种超细硬质合金的制备方法，特别是WC-Co超细硬质合金的制备方法。
背景技术：
硬质合金以其高硬度和高强度可用于制造PCB微钻。随着电子工业的飞速发展，需要钻径更小的PCB微钻。目前国内硬质合金材质一般只能制造0.8mm以上的PCB微钻，难以适应电子工业发展的要求。
发明内容：
本发明的目的是提供一种超细硬质合金的制备方法，使得用本方法制得的硬质合金可用于制造钻径0.8mm以下的微钻。
为达到上述目的，本发明的超细硬质合金的制备方法包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(38～41)KA/m的WC粉和(7.8～8.2)wt％的Co粉，并加入(0.28～0.30)wt％的VC，(0.31～0.35)wt％的TaC，(0.31～0.35)wt％的Cr3C2，VC、TaC和Cr3C2的总量为(0.95～1.0)wt％，配料计算时，碳平衡值为(+0.26～+0.28)％。
采用上述制备方法，可使制得的硬质合金中WC的平均晶粒度达(0.3～0.4)μm，硬质合金的硬度达HV3：1900～1980，并且可使用该种超细硬质合金制造的PCB微钻的钻径最小达0.3mm。
具体实施方式：
实施例1：配料时选用费氏粒度0.75μm的Co粉8.0wt％，1.2μmVC0.29wt％，1.2μmCr3C2 0.34wt％，1.2μmTaC0.34wt％，HCP值为39.3KA/m的余量WC粉，控制碳平衡值+0.27％，以酒精作研磨介质，液固比450ml/Kg，球料比5.45∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1950，抗弯强度4130N/mm2，WC平均晶粒度为0.35μm。
实施例2：配料时选用费氏粒度0.5μm的Co粉7.8wt％，1.2μmVC0.30wt％，1.2μmCr3C2 0.35wt％，1.2μmTaC0.35wt％，HCP值为41KA/m的余量WC粉，控制碳平衡值+0.28％，以酒精作研磨介质，液固比450ml/Kg，球料比5.45∶1，球磨80小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1980，抗弯强度3830N/mm2，WC平均晶粒度为0.30μm。
实施例3：配料时选用费氏粒度0.98μm的Co粉8.2wt％，1.2μmVC0.28wt％，1.2μmCr3C2 0.35wt％，1.2μmTaC0.32wt％，HCP值为38.0KA/m的余量WC粉，控制碳平衡值+0.26％，以酒精作研磨介质，液固比450ml/Kg，球料比5.45∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1910，抗弯强度4310N/mm2，WC平均晶粒度为0.4μm。
实施例4：配料时选用费氏粒度0.85μm的Co粉8.0wt％，1.2μmVC0.30wt％，1.2μmCr3C2 0.34wt％，1.2μmTaC0.34wt％，HCP值为40.3KA/m的余量WC粉，控制碳平衡值+0.28％，以酒精作研磨介质，液固比450ml/Kg，球料比5.45∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1960，抗弯强度4050N/mm2，WC平均晶粒度为0.35μm。
实施例5：配料时选用费氏粒度0.68μm的Co粉8.0wt％，1.2μmVC0.29wt％，1.2μmCr3C2 0.33wt％，1.2μmTaC0.35wt％，HCP值为38.8KA/m的余量WC粉，控制碳平衡值+0.27％，以酒精作研磨介质，液固比450ml/Kg，球料比5.45∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1940，抗弯强度3980N/mm2，WC平均晶粒度为0.35μm。

Claims (1)

1、一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，其特征在于：在配料时选用HCP值为(38～41)KA/m的WC粉和(7.8～8.2)wt％的Co粉，并加入(0.28～0.30)wt％的VC，(0.31～0.35)wt％的TaC，(0.31～0.35)wt％的Cr3C2，VC、TaC和Cr3C2的总量为(0.95～1.0)wt％，配料计算时，碳平衡值为(+0.26～+0.28)％。
CN 03124671 2003-07-22 2003-07-22 超细硬质合金的制备方法 Expired - Fee Related CN1207417C (zh)