CN1207416C - 超细硬质合金的制备方法 - Google Patents

超细硬质合金的制备方法 Download PDF

Info

Publication number
CN1207416C
CN1207416C CN 03124670 CN03124670A CN1207416C CN 1207416 C CN1207416 C CN 1207416C CN 03124670 CN03124670 CN 03124670 CN 03124670 A CN03124670 A CN 03124670A CN 1207416 C CN1207416 C CN 1207416C
Authority
CN
China
Prior art keywords
hard alloy
weight percent
powder
value
sintering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 03124670
Other languages
English (en)
Other versions
CN1480545A (zh
Inventor
何惧
言格夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Cemented Carbide Group Co Ltd
Original Assignee
Zhuzhou Cemented Carbide Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Cemented Carbide Group Co Ltd filed Critical Zhuzhou Cemented Carbide Group Co Ltd
Priority to CN 03124670 priority Critical patent/CN1207416C/zh
Publication of CN1480545A publication Critical patent/CN1480545A/zh
Application granted granted Critical
Publication of CN1207416C publication Critical patent/CN1207416C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结工序，在配料时选用HCP值为(38.5～41)KA/m的WC粉和重量百分比为11%～13%的Co粉，并加入重量百分比为0.3%～0.5%的VC、重量百分比为0.8%～1.0%的Cr3C2，配料计算时，碳平衡值为(+0.18～+0.21)%，硬质合金中WC的平均晶粒度达(0.30～0.35)μm。用本方法制得的硬质合金耐磨性增加，适用于制造有色金属切削刀片，特别是制造加工不锈钢的切削刀片。

Description

超细硬质合金的制备方法
技术领域：
本发明涉及一种超细硬质合金的制备方法。
背景技术：
硬质合金硬质合金以其高硬度和高强度有着广泛的用途。目前国内在制造有色金属切削刀片，特别是制造加工不锈钢的切削刀片时采用的材质一般为粒度为2.0μm的WC粉和重量百分比为11％的Co粉，并添加重量百分比为8％的(TaNb)C(80∶20)、8％的(WTi)C(50∶50)作为添加剂，经湿磨、干燥、压制成型和烧结等工序制得。用该方法制得的硬质合金硬度较低，HV30：1320～1460，耐磨性较差。
发明内容：
本发明的目的是提供一种超细硬质合金的制备方法，使得用本方法制得的硬质合金耐磨性增加。
为达到上述目的，本发明的超细硬质合金的制备方法包括：配料、湿磨、干燥、压制成型和烧结工序，在配料时选用HCP值为(38.5～41)KA/m的WC粉和重量百分比为11％～13％的Co粉，并加入重量百分比为0.3％～0.5％的VC、重量百分比为0.8％～1.0％的Cr3C，配料计算时，碳平衡值为(+0.18～+0.21)％，硬质合金中WC的平均晶粒度达(0.30～0.35)μm。
由于选用了细WC粉以及采用适量的VC和Cr3C2作晶粒抑制剂，可使得硬质合金中WC的平均晶粒度达(0.30～0.35)μm，在强度基本不变的情况下，可使得硬质合金的硬度达HV30：1750～1860，提高了其耐磨性。
具体实施方式：
实施例1：配料时选用Co粉重量百分比为11.0％，Cr3C2重量百分比为0.9％，VC重量百分比为0.3％，HCP值为39.6KA/m的余量WC粉，控制碳平衡+0.19％，以酒精作球磨介质，液固比500ml/Kg，球料比4.8∶1，球磨82小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后得φ3.25×38.5mm的棒材，其HV30：1830，抗弯强度4310N/mm2，WC平均晶粒度为0.30μm。
实施例2：配料时选用Co粉重量百分比为12.0％，Cr3C2重量百分比为0.8％，VC重量百分比为0.4％，HCP值为38.5KA/m的余量WC粉，控制碳平衡+0.21％，以酒精作球磨介质，液固比500ml/Kg，球料比4.8∶1，球磨87小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后得φ3.25×38.5mm的棒材，其HV30：1780，抗弯强度4260N/mm2，WC平均晶粒度为0.33μm。
实施例3：配料时选用Co粉重量百分比为12.0％，Cr3C2重量百分比为0.8％，VC重量百分比为0.5％，HCP值为40.5KA/m的余量WC粉，控制碳平衡+0.18％，以酒精作球磨介质，液固比500ml/Kg，球料比4.8∶1，球磨80小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后得φ3.25×38.5mm的棒材，其HV30：1860，抗弯强度4150N/mm2，WC平均晶粒度为0.30μm。
实施例4：配料时选用Co粉重量百分比为13.0％，Cr3C2重量百分比为1.0％，VC重量百分比为0.5％，HCP值为41KA/m的余量WC粉，控制碳平衡+0.21％，以酒精作球磨介质，液固比500ml/Kg，球料比4.8∶1，球磨90小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后得φ3.25×38.5mm的棒材，其HV30：1750，抗弯强度4530N/mm2，WC平均晶粒度为0.35μm。
实施例5：配料时选用Co粉重量百分比为11.0％，Cr3C2重量百分比为0.8％，VC重量百分比为0.3％，HCP值为38.5KA/m的余量WC粉，控制碳平衡+0.21％，以酒精作球磨介质，液固比500ml/Kg，球料比4.8∶1，球磨90小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后得φ3.25×38.5mm的棒材，其HV30：1860，抗弯强度4350N/mm2，WC平均晶粒度为0.30μm。

Claims (1)

1、一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结工序，其特征在于：在配料时选用HCP值为(38.5～41)KA/m的WC粉和重量百分比为11％～13％的Co粉，并加入重量百分比为0.3％～0.5％的VC、重量百分比为0.8％～1.0％的Cr3C2，配料计算时，碳平衡值为(+0.18～+0.21)％，硬质合金中WC的平均晶粒度达(0.30～0.35)μm。
CN 03124670 2003-07-22 2003-07-22 超细硬质合金的制备方法 Expired - Fee Related CN1207416C (zh)