CN1480544A - 硬质合金的制备方法 - Google Patents

硬质合金的制备方法 Download PDF

Info

Publication number
CN1480544A
CN1480544A CNA031246680A CN03124668A CN1480544A CN 1480544 A CN1480544 A CN 1480544A CN A031246680 A CNA031246680 A CN A031246680A CN 03124668 A CN03124668 A CN 03124668A CN 1480544 A CN1480544 A CN 1480544A
Authority
CN
China
Prior art keywords
powder
sintering
tanb
wimet
wti
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031246680A
Other languages
English (en)
Other versions
CN1207415C (zh
Inventor
惧 何
何惧
言格夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Cemented Carbide Group Co Ltd
Original Assignee
Zhuzhou Cemented Carbide Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Cemented Carbide Group Co Ltd filed Critical Zhuzhou Cemented Carbide Group Co Ltd
Priority to CN 03124668 priority Critical patent/CN1207415C/zh
Publication of CN1480544A publication Critical patent/CN1480544A/zh
Application granted granted Critical
Publication of CN1207415C publication Critical patent/CN1207415C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(9～10)KA/m的WC粉和(5.5～6.5)wt％的Co粉，并加入(0.35～0.45)wt％的(TaNb)C(60∶40)、(14～16)wt％的(WTi)C(60∶40)，配料计算时，碳平衡值为(+0.08～+0.10)％。使得用该方法制得的硬质合金在加工竹木产品时，能提高产品的光洁度。

Description

硬质合金的制备方法
技术领域：
本发明涉及一种硬质合金的制备方法。
背景技术：
硬质合金以其高硬度和高强度有着广泛的用途。目前国内在加工竹木方面采用的硬质合金一般是选用粒度为1.0μm的WC粉和重量百分比为6％的Co粉，并添加重量百分比为0.4％的(TaNb)C(60∶40)作为抑制剂，经湿磨、干燥压制成型和烧结等工序制得。由于在加工木材和竹器这类产品时，会产生很大的热量，而竹木本身的散热又很差，导致硬质合金刀片上聚集大量的热量，刀片不能稳定的加工，以至于用该种硬质合金加工的竹木产品的表面光洁度差。
发明内容：
本发明的目的是提供一种硬质合金的制备方法，使得用该方法制得的硬质合金在加工竹木产品时，能提高产品的光洁度。
为达到上述目的，本发明的硬质合金的制备方法包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(9～10)KA/m的WC粉和(5.5～6.5)wt％的Co粉，并加入(0.35～0.45)wt％的(TaNb)C(60∶40)、(14～16)wt％的(WTi)C(60∶40)，配料计算时，碳平衡值为(+0.08～+0.10)％。
由于本发明的制备方法添加了钨钛固溶体，提高了硬质合金的红硬性，在强度和硬度基本不变的情况下，可使其在高温下工作的稳定性增加，因此，被加工的竹木产品的表面光洁度得到了改善。
具体实施方式：
实施例1：配料时选用Co粉5.5wt％，(TaNb)C(60∶40)粉0.35wt％，(WTi)C(60∶40)粉15wt％，HCP值为9KA/m的余量WC粉，控制碳平衡+0.08％，以酒精作球磨介质，液固比350ml/Kg，球料比4.8∶1，球磨60小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，制得6.5×5.25×20(mm)的试样条，其HV30：1680，抗弯强度1850N/mm2，WC平均晶粒度为1.2μm。
实施例2：配料时选用Co粉6.0wt％，(TaNb)C(60∶40)粉0.45wt％，(WTi)C(60∶40)粉14wt％，HCP值为9.5KA/m的余量WC粉，控制碳平衡+0.09％，以酒精作球磨介质，液固比350ml/Kg，球料比4.8∶1，球磨63小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，制得6.5×5.25×20(mm)的试样条，其HV30：1650，抗弯强度1930N/mm2，WC平均晶粒度为1.2μm。
实施例3：配料时选用Co粉6.5wt％，(TaNb)C(60∶40)粉0.40wt％，(WTi)C(60∶40)粉16wt％，HCP值为10KA/m的余量WC粉，控制碳平衡+0.10％，以酒精作球磨介质，液固比350ml/Kg，球料比4.8∶1，球磨65小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，制得6.5×5.25×20(mm)的试样条，其HV30：1690，抗弯强度2020N/mm2，WC平均晶粒度为1.1μm。
实施例4：配料时选用Co粉6.5wt％，(TaNb)C(60∶40)粉0.45wt％，(WTi)C(60∶40)粉15wt％，HCP值为9.8KA/m的余量WC粉，控制碳平衡+0.10％，以酒精作球磨介质，液固比350ml/Kg，球料比4.8∶1，球磨68小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，制得6.5×5.25×20(mm)的试样条，其HV30：1700，抗弯强度2030N/mm2，WC平均晶粒度为1.1μm。
实施例5：配料时选用Co粉6.0wt％，(TaNb)C(60∶40)粉0.40wt％，(WTi)C(60∶40)粉16wt％，HCP值为9.3KA/m的余量WC粉，控制碳平衡+0.10％，以酒精作球磨介质，液固比350ml/Kg，球料比4.8∶1，球磨65小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，制得6.5×5.25×20(mm)的试样条，其HV30：1640，抗弯强度1890N/mm2，WC平均晶粒度为1.2μm。

Claims (1)

1.一种硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，其特征在于：在配料时选用HCP值为(9～10)KA/m的WC粉和(5.5～6.5)wt％的Co粉，并加入(0.35～0.45)wt％的(TaNb)C(60∶40)、(14～16)wt％的(WTi)C(60∶40)，配料计算时，碳平衡值为(+0.08～+0.10)％。
CN 03124668 2003-07-22 2003-07-22 硬质合金的制备方法 Expired - Fee Related CN1207415C (zh)