CN1474237A - 一种显影剂及其制备方法 - Google Patents

一种显影剂及其制备方法 Download PDF

Info

Publication number
CN1474237A
CN1474237A CNA03131855XA CN03131855A CN1474237A CN 1474237 A CN1474237 A CN 1474237A CN A03131855X A CNA03131855X A CN A03131855XA CN 03131855 A CN03131855 A CN 03131855A CN 1474237 A CN1474237 A CN 1474237A
Authority
CN
China
Prior art keywords
parts
developer
portions
resin
particle diameter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA03131855XA
Other languages
English (en)
Other versions
CN100340926C (zh
Inventor
周学良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB03131855XA priority Critical patent/CN100340926C/zh
Publication of CN1474237A publication Critical patent/CN1474237A/zh
Application granted granted Critical
Publication of CN100340926C publication Critical patent/CN100340926C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开一种显影剂及其制备方法。具体说，是静电复印机、传真机用显影剂及其制备方法。它是用75～90份的碳黑、50～55份的树脂、10～20份的聚丙烯腊、6～8份的荷电、1～1.5份的二氧化硅、0.5～1份的酞青蓝、0.5～1份的偶氮染料和5～12份的硬酯酸锌，经混炼、挤塑、粉碎和过筛等步骤而制成。这种显影剂，流动性好、带电量高，用其复印出的文稿或图像，不仅黑度高、清晰，而且无底灰。

Description

一种显影剂及其制备方法
(一)技术领域
本发明涉及一碳粉及其制备方法。具体说，是静电复印机、传真机用显影剂及其制备方法。
(二)背景技术
目前，复印机、传真机所用的显影剂主要由碳黑、树脂、聚丙烯腊、荷电和二氧化硅制成。而且，二氧化硅的用量较大。这种显影剂。流动性差、带电量低，使得复印出的文稿或图像，不仅黑度低、不清晰，而且有底灰。
(三)发明内容
本发明的目的在于提供一种显影剂。这种显影剂，流动性好、带电量高，用其复印出的文稿或图像，不仅黑度高、清晰，而且无底灰。
本发明的另一个目的是提供一种制备上述显影剂的方法。
本发明的上述目的由以下技术解决方案实现：
本发明的显影剂，由以下重量份数的原料组成：
碳黑75～90份；树脂50～55份；聚丙烯腊10～20份；荷电6～8份；二氧化硅1～1.5份；酞青蓝0.5～1份；偶氮染料0.5～1份；硬酯酸锌5～12份。其中的树脂是按丙乙烯∶丙烯酸丁酯＝4∶1的比例反应而成的二元共聚树脂。
制备本发明的显影剂的方法，依次包括以下步骤：
(1)先将碳黑、树脂、聚丙烯腊、酞青蓝、偶氮染料和荷电倒入混炼机中，均匀混合，制成混合料；
(2)再将上述混合料投入挤塑机中，在90～150℃的温度下将混合料挤成碎片；
(3)之后，用粉碎机将上述碎片粉碎成粒径为40～50μm的碎粉；
(4)之后，用压力为6～7kg/m2的空气进行气流粉碎，并用4500～5200转/分钟的分级机进行分级，用捕集器除去粒径大于或小于9～10μm的碎粉，得到粒径为9～10μm的碎粉半成品；
(5)再之后，加入二氧化硅和硬酯酸锌，用900转/分钟的搅拌机混合3～4分钟，使其流动性大于20％；
(5)最后，用100目筛网过筛，制成本发明的显影剂。
采用以上方案，具有以下优点：
本发明与目前复印机、传真机所用的显影剂相比，减少了二氧化硅的用量，增加了酞青蓝、偶氮染料和硬质酸锌等原料，提高了显影剂的流动性和带电量，使复印出的文稿不仅黑度高、清晰，而且无底灰。
(四)具体实施方式
第一个实施例
选取75份的碳黑、52份的树脂、20份的聚丙烯腊、7份的荷电、1份的二氧化硅、0.7份的酞青蓝、1份的偶氮染料和8份的硬酯酸锌，待用。其中的树脂是按丙乙烯∶丙烯酸丁酯＝4∶1的比例反应而成的二元共聚树脂。
先将碳黑、树脂、聚丙烯腊\酞青蓝、偶氮染料和荷电倒入混炼机中，均匀混合，制成混合料；
再将上述混合料投入挤塑机中，在95℃的温度下将混合料挤成碎片；
之后，用粉碎机将上述碎片粉碎成粒径为40μm的碎粉；
之后，用压力为6kg/m2的空气进行气流粉碎，并用4500转/分钟的分级机进行分级，用捕集器除去粒径大于或小于9～10μm的碎粉，得到粒径为9～10μm的碎粉半成品；
再之后，加入二氧化硅和硬酯酸锌，用900转/分钟的搅拌机混合3分钟，使其流动性大于20％；
最后，用100目筛网过筛，制成本发明的显影剂。
第二个实施例
选取81份的碳黑、55份的树脂、15份的聚丙烯腊、6份的荷电、1.3份的二氧化硅、1份的酞青蓝、0.7份的偶氮染料和6份的硬酯酸锌，待用。其中的树脂是按丙乙烯∶丙烯酸丁酯＝4∶1的比例反应而成的二元共聚树脂。
先将碳黑、树脂、聚丙烯腊\酞青蓝、偶氮染料和荷电倒入混炼机中，均匀混合，制成混合料；
再将上述混合料投入挤塑机中，在130℃的温度下将混合料挤成碎片；
之后，用粉碎机将上述碎片粉碎成粒径为45μm的碎粉；
之后，用压力为7kg/m2的空气进行气流粉碎，并用4900转/分钟的分级机进行分级，用捕集器除去粒径大于或小于9～10μm的碎粉，得到粒径为9～10μm的碎粉半成品；
再之后，加入二氧化硅和硬酯酸锌，用900转/分钟的搅拌机混合3分钟，使其流动性大于20％；
最后，用100目筛网过筛，制成本发明的显影剂。
第三个实施例
选取90份的碳黑、50份的树脂、11份的聚丙烯腊、8份的荷电、1.5份的二氧化硅、0.5份的酞青蓝、0.5份的偶氮染料和12份的硬酯酸锌，待用。其中的树脂是按丙乙烯∶丙烯酸丁酯＝4∶1的比例反应而成的二元共聚树脂。
先将碳黑、树脂、聚丙烯腊\酞青蓝、偶氮染料和荷电倒入混炼机中，均匀混合，制成混合料；
再将上述混合料投入挤塑机中，在150℃的温度下将混合料挤成碎片；
之后，用粉碎机将上述碎片粉碎成粒径为50μm的碎粉；
之后，用压力为6～7kg/m2的空气进行气流粉碎，并用5200转/分钟的分级机进行分级，用捕集器除去粒径大于或小于9～10μm的碎粉，得到粒径为9～10μm的碎粉半成品；
再之后，加入二氧化硅和硬酯酸锌，用900转/分钟的搅拌机混合4分钟，使其流动性大于20％；
最后，用100目筛网过筛，制成本发明的显影剂。

Claims (3)

1.一种显影剂，其特征在于由以下重量份数的原料组成：
碳黑75～90份；
树脂50～55份；
聚丙烯腊10～20份；
荷电6～8份；
二氧化硅1～1.5份；
酞青蓝0.5～1份；
偶氮染料0.5～1份；
硬酯酸锌5～12份。
2.根据权利要求1所述的显影剂，其特征在于所说的树脂是按丙乙烯∶丙烯酸丁酯＝4∶1的比例反应而成的二元共聚树脂。
3.制备上述显影剂的方法，其特征在于依次包括以下步骤：
(1)先将碳黑、树脂、聚丙烯腊、酞青蓝、偶氮染料和荷电倒入混炼机中，均匀混合，制成混合料；
(2)再将上述混合料投入挤塑机中，在90～150℃的温度下将混合料挤成碎片；
(3)之后，用粉碎机将上述碎片粉碎成粒径为40～50μm的碎粉；
(4)之后，用压力为6～7kg/m2的空气进行气流粉碎，并用4500～5200转/分钟的分级机进行分级，用捕集器除去粒径大于或小于9～10μm的碎粉，得到粒径为9～10μm的碎粉半成品；
(5)再之后，加入二氧化硅和硬酯酸锌，用900转/分钟的搅拌机混合3～4分钟，使其流动性大于20％；
(5)最后，用100目筛网过筛，制成本发明的显影剂。
CNB03131855XA 2003-06-12 2003-06-12 一种显影剂及其制备方法 Expired - Fee Related CN100340926C (zh)