CN1125854A - 静电复印、绝缘型、磁性、干式、单组分、正电性显影剂 - Google Patents
静电复印、绝缘型、磁性、干式、单组分、正电性显影剂 Download PDFInfo
- Publication number
- CN1125854A CN1125854A CN 94119044 CN94119044A CN1125854A CN 1125854 A CN1125854 A CN 1125854A CN 94119044 CN94119044 CN 94119044 CN 94119044 A CN94119044 A CN 94119044A CN 1125854 A CN1125854 A CN 1125854A
- Authority
- CN
- China
- Prior art keywords
- magnetic
- positive
- charged
- xerox
- developer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种静电复印磁性显影剂,是用于静电复印机的墨粉。其组分有粘接树脂、磁性材料、荷电调节剂及内、外添加剂,其特征是粘接树脂选用苯乙烯-丙烯酸酯共聚物,其聚合比为70∶25∶5,
Description
本发明涉及一种静电复印、磁性显影剂,是用于静电复印机的墨粉。
现有的静电复印机显影剂制造技术中,生产出的磁性墨粉类别较细,大多只适用单一机型的静电复印机,而且该磁性墨粉的组成复杂,加工困难,成本较高。如日本专利“特许公开昭55—147638”中介绍,将磁性粉、粘接树脂、荷电调节剂等用球磨机、高速混合机等混合均匀后,再用挤压式混炼机或挤出式混炼机熔融混炼,使各组成成分充分分散混合,再用气流粉碎机粉碎,风力分级机分级最后制出所需磁性墨粉。在选取粘接树脂方面,一般多选用两种或两种以上不同标准的粘接树脂聚合而成,这样由于对墨粉带电性能、磁性能和粉体特性以及加工过程都有严格的要求和限制,因而使得制造工艺比较复杂并加大产品成本,同时墨粉使用适应范围窄,往往只能用于单一机型的复印机。
本发明的目的在于提供一种图象浓度高、分辨率高、底灰小且耐久性好、对多种正电性复印机适用性较强、加工简便、成本较低的静电复印、绝缘型、磁性、干式、单组分、正电性显影剂。
本发明的目的是这样实现的,该显影剂是由粘接树脂、磁性材料、荷电调节剂及内、外添加剂组成,其特征是粘接树脂选用苯乙烯—丙烯酸脂的共聚物,还可选取苯乙烯、O—甲基苯乙烯、N—甲基苯乙烯、P—甲基苯乙烯、P—氯化苯乙烯、3.4—二氯化苯乙烯、P—乙基苯乙烯、2.4—二甲基苯乙烯、P—n—J基苯乙烯、P—Pert—J基苯乙烯及各衍生物;乙烯、丙烯、丁烯、异丁烯等乙烯类不饱和单烃类、氯化乙烯、溴化乙烯、氟化乙烯、卤化乙烯等;醋酸乙烯、丙烯酸乙烯等含有不饱和烯烃的酸中两种或两种以上的共聚物。磁性材料选用四氧化三铁,也可选用其它铁氧体和氧化铁。荷电调节剂选用苯胺黑染料。内添加剂选用低分子聚丙烯。外添加剂选用疏水性二氧化硅。
显影剂组分构成重量配比为:
粘接树脂 40—80%
磁性材料 20—60%
荷电调节剂 1—5%
内添加剂 1—8%
外添加剂 0.1—0.8%
对于主要组分选材的具体要求:
粘接树脂选用苯乙烯—丙烯酸脂共聚物,其聚合比为70∶25∶5,Mn值控制在10—20万之间,MI值在1.5—5.5之间。
磁性材料选用四氧化三铁,其平均粒径为0.1—2.0μm,在10KOe的磁场下磁特性:饱和磁化强度为60—100emv/g,矫顽力为90—140Oe。
外添加剂选用疏水性二氧化硅,其疏水度为20—40。
显影剂的制作是将上述除外添加剂各组分按比例取量用高速混合机混合,再用挤压式混炼机熔融混炼,然后冷却、压片、粉碎,再用气流粉碎机粉碎并进行风力分级。最后按0.3%比例在分级品中加入外添加剂,即加入疏水性二氧化硅,充分混合即可。
本发明在选材和配比上都公开了一种新的方案,选材中既要求性能指标优良,又考虑简化加工工艺及降低成本。如粘结树脂选用苯乙烯—丙烯酸脂共聚物,既包容了两不同组分的有效成分,提高显影剂的性能指标,又简化了生产工艺降低了成本,同时增大适用范围,用于多种机型的静电复印机效果良好。荷电调节剂选用苯胺黑染料,一方面稳定显影剂的带电量,另一方面起到增色剂的作用。另外对疏水性二氧化硅的疏水度加以控制,以防显影剂吸潮结团影响复印效果。由于上述的改进,从而使获得的显影剂复印图象浓度高,分辨率高,底灰小。
实施例1:(重量比)
苯乙烯—丙烯酸丁脂共聚物(MI=3.0) 100份
四氧化三铁 60份
低分子聚丙烯 4份
苯胺黑染料 2份
将上述四种原料用高速混合机混合后,再用挤压式混炼机在150℃条件下熔融混炼,然后冷却、压片、粉碎,再用气流粉碎机粉碎,然后分级后得到如下粒度分布的分级品:
个数平均径: 6.43μm
5.04μm以下: 26.7%
体积平均径: 8.76μm
16.0μm以上: 0.00%
将0.6g疏水性二氧化硅加入上述分级品中,充分混合即获得所需的显影剂。将该显影剂用于NP—1215静电复印机,复印图象清晰,耐久性良好。
实施例2:(重量比)
苯乙烯—丙烯酸丁脂共聚物(MI=2.00) 100份
四氧化三铁 50份
低分子聚丙烯 4份
苯胺黑染料 2份
将上述四种原料按实施例1的方法加工后可获得如下粒度分布的分级品:
个数平均径: 5.71μm
5.04μm以下: 25.3%
体积平均径: 9.48μm
16.0μm以上: 3.4%
将0.6g疏水性二氧化硅加入上述分级品中,充分混合即获得所需的显影剂。将该显影剂用于NP—2020、NP—3020静电复印机,复印品图象指标全部达到国家标准,特别是分辨率、层次两项指标均高于国家3.6线/mm和连续四级的标准,分别可达5.0线/mm和连续五级的标准。
实施例3:(重量比)
苯乙烯—丙烯酸丁脂共聚物(MI=4.5) 100份
四氧化三铁 70份
低分子聚丙烯 4份
苯胺黑染料 2份
将上述四种原料按实施例1的方法加工后,再加入0.1—0.8%的疏水性二氧化硅,充分混合即可。用于其它类型静电复印机效果良好。
Claims (4)
1.静电复印、绝缘型、磁性、干式、单组分、正电性显影剂,是由粘接树脂、磁性材料、荷电调节剂及内、外添加剂组成,其特征是粘接树脂选用苯乙烯—丙烯酸脂共聚物,磁性材料选用四氧化三铁,荷电调节剂选用苯胺黑染料,内添加剂选用低分子聚丙烯,外添加剂选用疏水性二氧化硅,各组分构成重量配比为:
粘接树脂 40—80%
磁性材料 20—60%
荷电调节剂 1—5%
内添加剂 1—8%
外添加剂 0.1—0.8%
2.如权利要求1所述的静电复印、绝缘型、磁性、干式、单组分、正电性显影剂,其特征是粘接树脂选用苯乙烯—丙烯酸脂共聚物的聚合比为70∶25∶5,
Mn值控制在10—20万之间,MI值在1.5—5.5之间。
3.如权利要求1所述的静电复印、绝缘型、磁性、干式、单组分、正电性显影剂,其特征是磁性材料选用四氧化三铁,其平均粒径为0.1—2.0μm,在10KOe的磁场下的磁特性:饱和磁化强度为50—100emv/g,矫顽力为90—1400e。
4.如权利要求1所述的静电复印、绝缘型、磁性、干式、单组分、正电性显影剂,其特征是外添加剂选用的疏水性二氧化硅的疏水度为20—40。