CN1460696A - 一种水性裂纹涂料 - Google Patents
一种水性裂纹涂料 Download PDFInfo
- Publication number
- CN1460696A CN1460696A CN 03126521 CN03126521A CN1460696A CN 1460696 A CN1460696 A CN 1460696A CN 03126521 CN03126521 CN 03126521 CN 03126521 A CN03126521 A CN 03126521A CN 1460696 A CN1460696 A CN 1460696A
- Authority
- CN
- China
- Prior art keywords
- water
- substitute
- polyvinyl alcohol
- weight percent
- alcohol resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种水性裂纹涂料,组分及其重量百分比是:部份碱化型聚乙烯醇树脂4.39~21.31%,溶解树脂用水28.87~62.19%,自交联型醋丙乳液4.21~15.29%,消泡剂0.08~0.50%,杀菌剂0.16~0.66%,乳胶漆色浆0.00~11.70%,稀释用水19.25~49.75%和氨水0.08~0.33%。本发明对照现有油性裂纹涂料的有益效果是,组分新颖,配料科学,制备简单,施工容易,不会伤害施工人员的健康。以水作溶剂,无毒无害无污染,无火灾隐患。对多孔底材如陶瓷的渗透时间长,附着力好,产生裂纹的时间短,与底材和面层的接着强度高,可控制裂纹的大小,使制品的施工效果更美观。且制品的柔韧性明显优于油性裂纹涂料产品,耐久性更好。本发明的水性裂纹涂料是油性裂纹涂料的更新换代产品,可以在家居装修及中高档工艺产品上广泛使用,具有广阔的市场发展前景。
Description
技术领域 本发明涉及以其物理性质或所产生的起皱、裂纹状、桔皮状或类似装饰效果为特征的涂料组合物,尤其涉及一种水性裂纹涂料。
背景技术 属于美术类漆的裂纹漆,以其美观的花纹、高雅的装饰性被广泛应用在家居装修与陶瓷、木器等底材的中高档工艺品装饰上。但是,现有的裂纹漆都属于油性制品,制备时要采用很多有机溶剂,使用时要使用含有苯类、醇类、酯类或酮类的大量有机溶剂来稀释,对环境的污染及人体的健康危害都很大,而且由于是易燃易爆产品,生产及施工场所有火险隐患。此外,油性裂纹漆使用时要先用普通硝基漆做底漆,其施工原理是利用裂纹漆中的有机溶剂溶解施工在下面的硝基底漆,由于硝基底漆在干燥的过程中收缩性大于裂纹面漆从而将漆面拉裂而形成裂纹。因此温度对施工效果的影响很大,如果气温较高时施工,溶剂挥发会变得很快而不易产生裂纹。还有,使用挥发性、溶解性不同的稀释剂施工,裂纹效果也不一致,所以油性裂纹漆的施工难度较大,施工效果难以把握。
发明内容 为弥补现有技术的缺陷,本发明提出一种水性裂纹涂料,采用的技术方案分别如下:
这种水性裂纹涂料,其特征是组分及其重量百分比是:部份碱化型聚乙烯醇树脂 4.39~21.31%:溶解树脂用水 28.87~62.19%;自交联型醋丙乳液 4.21~15.29%;消泡剂 0.08~0.50%;杀菌剂 0.16~0.66%;乳胶漆色浆 0.00~11.70%;稀释用水 19.25~49.75%;氨水 0.08~0.33%。
上述部份碱化型聚乙烯醇树脂是成膜物,提供收缩力和附着力。
上述自交联型醋丙乳液也是成膜物,提供附着力,调节耐水性。
上述消泡剂是助剂,具有消泡的作用。
上述杀菌剂是助剂,具有杀菌防腐的作用。
上述乳胶漆色浆是辅料,具有调色的作用。
上述氨水也是助剂,调节酸碱度,具有稳定体系的作用。
这种水性裂纹涂料的进一步特征是:
上述部份碱化型聚乙烯醇树脂,可以用部份醇解型聚乙烯醇树脂替代,也可以用完全醇解型聚乙烯醇树脂替代,但相应重量百分比要进行调整。
上述自交联型醋丙乳液,可以用聚醋酸乙烯乳液替代,可以用醋丙乳液替代,也可以用苯丙乳液替代,还可以用纯丙乳液替代,但相应重量百分比要进行调整。
上述消泡剂,可以是矿物油表面活性剂。
上述杀菌剂,可以是异噻唑啉酮。
上述氨水,可以用有机胺类替代,但相应重量百分比要进行调整。
这种水性裂纹涂料的制备方法,其特征是依次有以下工序:先按照设定的重量百分比,将部份碱化型聚乙烯醇树脂和水投入搅拌容器,加热至温度80~100℃,充分搅拌至部份碱化型聚乙烯醇树脂完全溶解于水中,再按照设定的重量百分比,将自交联型醋丙乳液、消泡剂、杀菌剂、乳胶漆色浆和水投入搅拌容器,搅拌均匀后,仍按照设定的重量百分比,将氨水投入搅拌容器,调节混合物的酸碱度至8~9,即是制品。
本发明精选各种材料复合组配,采用多因素实验设计方法,正交试验设计法确定组分及其重量百分比。对照现有油性裂纹涂料的有益效果是,组分新颖,配料科学,制备简单,施工容易,不会伤害施工人员的健康。这种水性裂纹涂料以水作溶剂,无毒无害无污染,无火灾隐患。由于水的挥发性较慢,对多孔底材如陶瓷的渗透时间长,附着力好,部份碱化型聚乙烯醇树脂易溶于水,常温下易成膜,遇水又易收缩,制品产生裂纹的时间短。而采用自交联型醋丙乳液,制品的附着力优良,与底材和面层的接着强度高,同时可调节部份碱化型聚乙烯醇树脂的耐水性,从而控制裂纹的大小,使制品的施工效果更美观。由于所用成膜物的两种原料都具有优良的柔韧性,所以制品的柔韧性明显优于油性裂纹涂料产品,耐久性更好。本发明的水性裂纹涂料是油性裂纹涂料的更新换代产品,可以在家居装修及中高档工艺产品上广泛使用,具有广阔的市场发展前景。
具体实施方式 一种水性裂纹涂料
这种水性裂纹涂料,组分及其重量百分比是:部份碱化型聚乙烯醇树脂 15.0%;溶解树脂用水 40.0%;自交联型醋丙乳液 5.0%;矿物油表面活性剂 0.2%;异噻唑啉酮 0.2%;乳胶漆色浆 5.5%;稀释用水 34.0%;氨水 0.1%。先按照设定的重量百分比,将部份碱化型聚乙烯醇树脂和溶解树脂用水投入搅拌容器,加热至温度90℃,充分搅拌至部份碱化型聚乙烯醇树脂完全溶解于水中,再按照设定的重量百分比,将自交联型醋丙乳液、矿物油表面活性剂、异噻唑啉酮、乳胶漆色浆和稀释用水投入搅拌容器,搅拌均匀后,仍按照设定的重量百分比,将氨水投入搅拌容器,调节混合物的酸碱度至8.5,即是制品。在陶瓷、木器、室内砖墙等底材上使用时,先将本制品刷涂一遍,涂布方式也可以是滚涂或喷涂,在常温下间隔时间至少是0.5小时后,即可涂覆配套的水性面漆,也可以涂布颜料体积浓度大于60%的普通乳胶漆作为面层。
Claims (6)
1、一种水性裂纹涂料,其特征是组分及其重量百分比是:部份碱化型聚乙烯醇树脂 4.39~21.31%:溶解树脂用水 28.87~62.19%;自交联型醋丙乳液 4.21~15.29%;消泡剂 0.08~0.50%;杀菌剂 0.16~0.66%;乳胶漆色浆 0.00~11.70%;稀释用水 19.25~49.75%;氨水 0.08~0.33%。
2、如权利要求1所述的水性裂纹涂料,其特征是:
上述部份碱化型聚乙烯醇树脂,可以用部份醇解型聚乙烯醇树脂替代,也可以用完全醇解型聚乙烯醇树脂替代,但相应的重量百分比要进行调整。
3、如权利要求1所述的水性裂纹涂料,其特征是:
上述自交联型醋丙乳液,可以用聚醋酸乙烯乳液替代,可以用醋丙乳液替代,也可以用苯丙乳液替代,还可以用纯丙乳液替代,但相应的重量百分比要进行调整。
4、如权利要求1所述的水性裂纹涂料,其特征是:
上述消泡剂,可以是矿物油表面活性剂。
5、如权利要求1所述的水性裂纹涂料,其特征是:
上述杀菌剂,可以是异噻唑啉酮。
6、如权利要求1所述的水性裂纹涂料,其特征是:
上述氨水,可以用有机胺类替代,但相应的重量百分比要进行调整。