CN1422668A - 医用微孔壳聚糖不对称膜及其制备方法 - Google Patents

医用微孔壳聚糖不对称膜及其制备方法 Download PDF

Info

Publication number
CN1422668A
CN1422668A CN 01139017 CN01139017A CN1422668A CN 1422668 A CN1422668 A CN 1422668A CN 01139017 CN01139017 CN 01139017 CN 01139017 A CN01139017 A CN 01139017A CN 1422668 A CN1422668 A CN 1422668A
Authority
CN
China
Prior art keywords
chitosan
film
chitoglycan
concentration
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 01139017
Other languages
English (en)
Inventor
胡巧玲
赵瑛
方征平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING BAILIKANG BIOCHEM Co Ltd
Zhejiang University ZJU
Original Assignee
BEIJING BAILIKANG BIOCHEM Co Ltd
Zhejiang University ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING BAILIKANG BIOCHEM Co Ltd, Zhejiang University ZJU filed Critical BEIJING BAILIKANG BIOCHEM Co Ltd
Priority to CN 01139017 priority Critical patent/CN1422668A/zh
Publication of CN1422668A publication Critical patent/CN1422668A/zh
Pending legal-status Critical Current

Abstract

本发明的医用微孔壳聚糖不对称膜是具有微孔的膜,微孔穿透膜层,呈锥状在膜的两表面的孔径不相同,该膜含有(按重量)壳聚糖为85～95%、甘油为5～15%。制备该膜的方法,包括:1)先将壳聚糖溶解在2%乙酸溶液中配制成浓度为1～2%的壳聚糖乙酸溶液,加入甘油,过滤,静置脱泡,注入模具；2)将无水乙醇、5%浓度的甘油、8%浓度的氢氧化钠按体积比1000∶50～100∶10～20配成凝固液,然后将模具放入凝固液中凝固,取出得到一白色凝胶；3)将凝胶放入50～70℃烘箱中干燥,即得本发明的膜。本发明的医用微孔壳聚糖不对称膜,因具有微孔结构,它透水,透气性好,能有效防止术后粘连,满足临床需要,且其制备采用溶液相转变法,可使制备膜的时间大大缩短。

Description

医用微孔壳聚糖不对称膜及其制备方法
                          技术领域
本发明涉及医用微孔壳聚糖不对称膜及其制备方法。
                          背景技术
壳聚糖是由甲壳素脱乙酰基而得，而甲壳素是从虾、蟹、蝇等动物壳中提取，在自然界中广泛存在，是仅次于纤维素的第二大类天然高分子。我国海岸线长，海洋资源丰富，有利于对壳聚糖进行研究和开发。由于壳聚糖具有良好的成膜性、生物相容性和降解性，在生物医用领域的应用前景十分广阔。
目前，在施行外科手术后，手术性粘连是普遍存在的问题，它有时候甚至使一个成功的手术归于失败。因此，防术后粘连是一个急待解决的问题。目前国际上正在研究应用“短期屏障”方法解决这个问题，即把聚合物制成薄膜或网状物，在手术时放在术后有可能粘连的组织之间。早期的聚合物采用聚四氟乙烯，但由于其不降解，需要二次手术，使患者难以接受。目前美国采用再生氧化纤维制成网状物，用于妇科盆骨手术。与氧化再生纤维相比，壳聚糖不仅具有良好的生物相容性和降解性，而且它还能促进伤口的愈合，抗溃疡及杀菌等多种生物活性，更加适于作为防术后粘连膜材料。
目前用于防术后粘连的壳聚糖，均采用直接干燥法，制备的膜均为致密膜，易积液、降解慢、力学性能差等缺点。而且制备过程长，花费时间久。
                          发明内容
本发明的目的是要提供一种防术后粘连的透水、透气性好的医用微孔壳聚糖不对称膜及其制备方法。
发明的医用微孔壳聚糖不对称膜是具有微孔的膜，微孔穿透膜层，呈锥状在膜的两表面的孔径不相同，该膜含有(按重量)
壳聚糖      85～95％
甘油        5～15％。
制备本发明医用微孔壳聚糖不对称膜的方法，包括以下步骤：
1)按所含成分的量，先将壳聚糖溶解在2％乙酸溶液中配制成浓度为1～2％的壳聚糖乙酸溶液，加入甘油，过滤，静置脱泡，注入模具；
2)将无水乙醇、5％浓度的甘油、8％浓度的氢氧化钠按体积比1000∶50～100∶10～20配成凝固液，然后将模具放入凝固液中凝固，取出得到一白色凝胶；其凝固时间与温度有关，可以在常温下进行，为缩短凝固时间，也可加温。
3)将步骤2)的凝胶放入50～70℃烘箱中干燥，得到无色透明柔软的本发明的膜。
本发明的医用微孔壳聚糖不对称膜，因具有微孔结构，它透水，透气性好，能有效防止术后粘连，满足临床需要，且其制备采用溶液相转变法，可使制备膜的时间大大缩短。
                          附图说明
附图是本发明医用微孔壳聚糖不对称膜的结构示意图。
                        具体实施方式
发明的医用微孔壳聚糖不对称膜，参见图1，它是具有微孔1的膜，微孔穿透膜层，呈锥状在膜的两表面的孔径不相同，该膜含有(按重量)
壳聚糖       85～95％
甘油         5～15％。
制备本发明膜的实施例：
本例壳聚糖和甘油的含量(按重量)分别是壳聚糖95％、甘油5％。
1)将壳聚糖溶解在2％乙酸溶液中配制成浓度为1～2％的壳聚糖乙酸溶液，加入甘油，过滤，静置脱泡，注入模具。
2)将无水乙醇、5％浓度的甘油、8％浓度的氢氧化钠按体积比1000∶80∶14配成凝固液，然后将模具放入凝固液中，在50～70℃凝固1～3小时，取出得到一白色凝胶。
3)将上述白色凝胶放入50～70℃烘箱中干燥，得到无色透明柔软的膜。
本发明的膜平均孔径为50～150μm，抗张强度为15～35Mpa，吸水率为18～170％，断裂伸长率为10～20％，含水率为5～12％。
试验表明，将本发明膜植入40天后，膜重量减少50％，成纤细胞受到抑制，观察到中性粒细胞，但无巨噬细胞，该膜防术后粘连效果明显。

Claims (3)

1.医用微孔壳聚糖不对称膜，其特征在于它是具有微孔[1]的膜，微孔穿透膜层，呈锥状在膜的两表面的孔径不相同，该膜含有(按重量)
壳聚糖        85～95％
甘油          5～15％。
2.按权利要求1所述的医用微孔壳聚糖不对称膜的制备方法，该方法包括以下步骤：
1)按所含成分的量，先将壳聚糖溶解在2％乙酸溶液中配制成浓度为1～2％的壳聚糖乙酸溶液，加入甘油，过滤，静置脱泡，注入模具；
2)将无水乙醇、5％浓度的甘油、8％浓度的氢氧化钠按体积比1000∶50～100∶10～20配成凝固液，然后将模具放入凝固液中凝固，取出得到一白色凝胶；
3)将步骤2)的凝胶放入50～70℃烘箱中干燥，得到无色透明柔软的本发明的膜。
3.按权利要求2所述的医用微孔壳聚糖不对称膜的制备方法，其特征是无水乙醇、5％浓度的甘油、8％浓度的氢氧化钠按体积比1000∶80∶14配成凝固液。
CN 01139017 2001-11-29 2001-11-29 医用微孔壳聚糖不对称膜及其制备方法 Pending CN1422668A (zh)