CN1390879A - 无碱布增强玻璃钢固化全透成型材料 - Google Patents

无碱布增强玻璃钢固化全透成型材料 Download PDF

Info

Publication number
CN1390879A
CN1390879A CN 02132502 CN02132502A CN1390879A CN 1390879 A CN1390879 A CN 1390879A CN 02132502 CN02132502 CN 02132502 CN 02132502 A CN02132502 A CN 02132502A CN 1390879 A CN1390879 A CN 1390879A
Authority
CN
China
Prior art keywords
transparency
full
reinforced plastics
aniseed
solidifying material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 02132502
Other languages
English (en)
Other versions
CN1162469C (zh
Inventor
康艳红
张耀宇
陈玉璞
刘昱东
孙广岩
Original Assignee
康艳红
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 康艳红 filed Critical 康艳红
Priority to CNB021325022A priority Critical patent/CN1162469C/zh
Publication of CN1390879A publication Critical patent/CN1390879A/zh
Application granted granted Critical
Publication of CN1162469C publication Critical patent/CN1162469C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

无碱布增强玻璃钢固化全透成型材料，它主要由大料、稀释剂、小料按重量组成。大料：苯酐115－130g、顺酐85－113g、乙二醇50g、丙二醇52－70g、二甘醇12.5g；稀释剂：苯乙烯90－100g、甲基丙烯酸甲酯60－70g；小料：UV－9 0.616－0.685g、TBC 0.0121－0.0135g、环烷酸铜0.0126－0.014g、HQ0.045－0.05g、石蜡0.098－0.105g亚磷酸三苯酯0.12g。本发明的特点在于配方合理，制作方法简单。用其制作的无碱布增强玻璃钢，强度高，透光率好，用肉眼看不到玻璃丝内的网格。可广泛用于制作透光率要求较高的建筑、温室、大棚或建筑物的屋顶。

Description

无碱布增强玻璃钢固化全透成型材料
技术领域：本发明涉及一种无碱布增强玻璃钢固化全透成型材料，属于化工产品热固性树脂领域。
背景技术：现有技术中的无碱布增强玻璃钢成型材料，虽然无碱布与树脂二者均属透明材质，但由于二者的折光率不同，因此使得它的整个透光度下降，用肉眼能够看到无碱玻璃丝布的整个结构外形。用该产品制作温室顶棚透光率差，还不美观。
发明内容：本发明的目的是克服现有技术的不足，而向人们提供一种强度高、透光率好、用肉眼看不到无碱玻璃丝布条纹或方格的无碱布增强玻璃钢固化全透成型材料。为实现上述目的，本发明采用下述技术方案：无碱布增强玻璃钢固化全透成型材料，主要由大料、稀释剂、小料按重量组成。
大料：
      苯酐                           115-130g
      顺酐                            85-113g
      乙二醇                              50g
      丙二醇                           52-70g
      二甘醇                            12.5g
稀释剂：
      苯乙烯                          90-100g
      甲基丙烯酸甲酯                   60-70g
小料：(促固剂)
      UV-9                       0.616-0.685g
      TBC                      0.0121-0.0135g
      环烷酸铜                      0.0126-0.014g
      HQ                              0.045-0.05g
      石蜡                           0.098-0.105g
      亚磷酸三苯酯                          0.12g
具体的制作方法按下述方法步骤进行：
(1)将上述五种大料按上述配比置于反应釜内，搅拌混匀并抽真空；
(2)温度至210--220℃时，物料开始出水，当出水达到最大值时，开始水冷降温；
(3)温度降至180℃时按上述顺序加入小料后继续降温至135℃时，加入苯乙烯；
(4)温度降至100℃时再加入甲基丙烯酸甲酯后成型。
本发明的特点在于配方合理，制作方法简单。用其制作的无碱布增强玻璃钢，强度高，透光率好，用肉眼看不到玻璃丝内的网格。可广泛用于制作透光率要求较高的建筑、温室、大棚或建筑物的屋顶。
具体实施例：
实施例1
无碱布增强玻璃钢固化全透成型材料，主要由大料、稀释剂、小料按重量组成。
大料：
    苯酐                             115g
    顺酐                              85g
    乙二醇                            50g
    丙二醇                            52g
    二甘醇                          12.5g
稀释剂：
    苯乙烯                             90g
    甲基丙烯酸甲酯                     60g
小料：(促固剂)
    UV-9                            0.616g
    TBC                            0.0121g
    环烷酸铜                       0.0126g
    HQ                              0.045g
    石蜡                            0.098g
    亚磷酸三苯酯                     0.12g
具体的制作方法按下述方法步骤进行：
(1)将上述五种大料按上述配比置于反应釜内，搅拌混匀并抽真空；
(2)温度至210--220℃时，物料开始出水，当出水达到最大值时，开始水冷降温；
(3)当温度降至180℃时按上述顺序加入小料后继续降温至135℃时，加入苯乙烯；
(4)当温度降至100℃时再加入甲基丙烯酸甲酯后成型。
实施例2
无碱布增强玻璃钢固化全透成型材料，主要由大料、稀释剂、小料按重量组成。
大料：
    苯酐                            130g
    顺酐                            113g
    乙二醇                           50g
    丙二醇                             70g
    二甘醇                           12.5g
稀释剂：
    苯乙烯                            100g
    甲基丙烯酸甲酯                     75g
小料：(促固剂)
    UV-9                            0.685g
    TBC                            0.0135g
    环烷酸铜                        0.014g
    HQ                               0.05g
    石蜡                            0.105g
    亚磷酸三苯酯                     0.12g
具体的制作方法和步骤与实施例1相同。
实施例3
无碱布增强玻璃钢固化全透成型材料，主要由大料、稀释剂、小料按重量组成。
大料：
    苯酐                                  122g
    顺酐                                   89g
    乙二醇                                 50g
    丙二醇                               64.5g
    二甘醇                               12.5g
稀释剂：
    苯乙烯                                 99g
    甲基丙烯酸甲酯                         66g小料：(促固剂)
    UV-9                            0.647g
    TBC                            0.0127g
    环烷酸铜                       0.0127g
    HQ                              0.047g
    石蜡                           0.099克
    亚磷酸三苯酯                     0.12g具体的制作方法和步骤与实施例1相同。

Claims (5)

1、无碱布增强玻璃钢固化全透成型材料，其特征在于它主要由大料、稀释剂、小料按重量组成，
大料：
      苯酐                        115-130g
      顺酐                         85-113g
      乙二醇                           50g
      丙二醇                        52-70g
      二甘醇                         12.5g
稀释剂：
      苯乙烯                       90-100g
      甲基丙烯酸甲酯                60-70g
小料：(促固剂)
      UV-9                   0.616-0.685g
      TBC                  0.0121-0.0135g
      环烷酸铜               0.0126-0.014g
      HQ                      0.045-0.05g
      石蜡                   0.098-0.105g
      亚磷酸三苯酯                   0.12g
2、根据权利要求1所述的无碱布增强玻璃钢固化全透成型材料，其特征在于各组份的用量，
大料：
      苯酐                           115g
      顺酐                            85g
      乙二醇                          50g
      丙二醇                                 52g
      二甘醇                               12.5g
稀释剂：
      苯乙烯                                 90g
      甲基丙烯酸甲酯                         60g
小料：(促固剂)
      UV-9                               0.616g
      TBC                               0.0121g
      环烷酸铜                           0.0126g
      HQ                                 0.045g
      石蜡                               0.098g
      亚磷酸三苯酯                         0.12g
3、根据权利要求1所述的无碱布增强玻璃钢固化全透成型材料，其特征在于各组份的用量，
大料：
      苯酐                                 130g
      顺酐                                 113g
      乙二醇                                50g
      丙二醇                                70g
      二甘醇                              12.5g
稀释剂：
      苯乙烯                               100g
      甲基丙烯酸甲酯                        75g
小料：(促固剂)
      UV-9                              0.685g
      TBC                            0.0135g
      环烷酸铜                         0.014g
      HQ                               0.05g
      石蜡                            0.105g
      亚磷酸三苯酯                      0.12g
4、根据权利要求1所述的无碱布增强玻璃钢固化全透成型材料，其特征在于各组份的用量，
大料：
      苯酐                              122g
      顺酐                               89g
      乙二醇                             50g
      丙二醇                           64.5g
      二甘醇                           12.5g
稀释剂：
      苯乙烯                             99g
      甲基丙烯酸甲酯                     66g
小料：(促固剂)
      UV-9                           0.647g
      TBC                           0.0127g
      环烷酸铜                       0.0127g
      HQ                             0.047g
      石蜡                           0.099克
      亚磷酸三苯酯                     0.12g
5、制作如权利要求1--4所述无碱布增强玻璃钢固化全透成型材料的方法，其特征在于它是按照下述方法步骤进行：
(1)将上述五种大料按上述配比置于反应釜内，搅拌混匀并抽真空；
(2)温度至210--220℃时，物料开始出水，当出水达到最大值时，开始水冷降温；
(3)当温度降至180℃时按上述顺序加入小料后继续降温至135℃时，加入苯乙烯；
(4)当温度降至100℃时再加入甲基丙烯酸甲酯后成型。
CNB021325022A 2002-07-01 2002-07-01 用于无碱布增强玻璃钢的全透成型材料 Expired - Fee Related CN1162469C (zh)