CN1377859A - 一种抛光砖废泥陶粒及其制备方法 - Google Patents

一种抛光砖废泥陶粒及其制备方法 Download PDF

Info

Publication number
CN1377859A
CN1377859A CN01107686A CN01107686A CN1377859A CN 1377859 A CN1377859 A CN 1377859A CN 01107686 A CN01107686 A CN 01107686A CN 01107686 A CN01107686 A CN 01107686A CN 1377859 A CN1377859 A CN 1377859A
Authority
CN
China
Prior art keywords
mud
preparation
raw material
haydite
oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN01107686A
Other languages
English (en)
Other versions
CN1174935C (zh
Inventor
冯斌
万冬梅
彭刚
何锡伶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Jin Gang new materials Co., Ltd.
Original Assignee
CERAMIC INST FOTAO GROUP Co Ltd GUANGDONG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CERAMIC INST FOTAO GROUP Co Ltd GUANGDONG filed Critical CERAMIC INST FOTAO GROUP Co Ltd GUANGDONG
Priority to CNB011076860A priority Critical patent/CN1174935C/zh
Publication of CN1377859A publication Critical patent/CN1377859A/zh
Application granted granted Critical
Publication of CN1174935C publication Critical patent/CN1174935C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明是以陶瓷抛光砖生产线所产生陶瓷废泥为原料或主要原料,必要时加入生料废泥(球磨机和喷雾塔产生的废泥)及煤为外加剂,泥料的含水量控制在15～40,成型后,经预热和1100～1150℃高温烧结,冷却后即成为超轻或轻质高强陶粒。工艺简单可行,将陶瓷废料变废为宝,具有较好的经济效益和环保效益。

Description

一种抛光砖废泥陶粒及其制备方法
本发明涉及一种陶粒及其制备方法，尤其是一种以抛光砖废泥为原料或主要原料的陶粒及其制备方法。
从已公开发表的文献可知，制造陶粒的原料非常广泛，有粘土、页岩、膨胀珍珠岩等，这些材料制造的陶粒尤其是粘土陶粒成本较低、性能良好，但随着自然资源的日益减少，尤其是粘土陶粒的生产开始受到限制，国内外已经把目光转向利用废料或工业废渣如煤矸石、粉煤灰和垃圾等制造陶粒，然而目前废料陶粒普遍存在成本高、强度低以及含有影响混凝土强度的重金属元素等不利因素，因而限制了废料陶粒的发展。例如，中国专利申请《沸石岩陶粒的制造工艺》(85100118)，《超轻陶粒及其制备方法》(86106748)等多项专利申请公开了上述现有技术。
众所周知，我国是世界陶瓷生产大国，建筑陶瓷墙地砖的产量从1998年起位居世界第一。随着我国陶瓷产量的不断扩大，陶瓷废料的数量急剧增加，据不完全统计，仅广东省佛山地区陶瓷废料年排放量超过400万吨，其中抛光砖生产线产生的废泥料超过100万吨，我国一直以来对陶瓷废料的处理都是采用填埋方式，这种处理方式不仅侵占土地，还会造成空气和地下水资源的污染，随着陶瓷废料量的不断增加，填埋藏方式已经不能适应现代社会和环保的要求，如何变废料为再生资源是当今科学工作者迫在眉睫的任务。
本发明的目的是针对现有技术中的上述不足，以抛光砖废料为原料或主要原料生产陶粒，以使大量的陶瓷废料得以回收后再生利用，减少环境污染，节约土地资源。提供一种工艺简单、成本低又具环保作用的陶粒及其制备方法。
本发明是这样实现的：利用建筑陶瓷厂抛光砖生产线产生的废水，经沉淀、压滤后所得的废泥为原料或主要原料，经过堆放预处理，辅以陶瓷厂球磨机和喷雾塔产生的生料废泥，通过混练处理，利用对辊造粒工艺成型，采用回转窑烧结，经冷却得到陶粒成品。
一种轻质高强陶粒及其制备方法，其特征在于以陶瓷厂抛光砖生产线所产生的废水，经过沉淀或压滤后所得的陶瓷废泥为原料或主要原料，必要时加入适量生料废泥及煤为辅料，经均化处理、混料、造粒、烧成、筛分而成。
抛光砖废泥的含量不少于70％(重量百分比)，可以达到100％，即可全部用抛光砖废泥为原料生产轻细陶粒≤5mm)，可以不加入生料废泥或煤，抛光砖废泥的含水量控制在15～40％；。
生料废泥为由球磨机和喷雾塔产生的废泥。生产轻粗陶粒(＞5mm)骨料可加入不超过30％的生料废泥为辅料，或加入不超过30％的煤为辅料。还可加入不超过30％的生料废泥和煤的混合料作为辅料。
本发明中使用的主要原料是抛光砖废泥，其特点是混合有磨细的抛光砖粉和抛光磨料屑，根据大量统计，陶瓷厂抛光砖生产线产生的废泥其成份范围为氧化硅55～65％、氧化铝13～18％、氧化铁＜1％、氧化镁和氧化钙4～8％，氧化钾和氧化钠2～5％。在实施本发明的技术方案时，根据抛光砖废泥的塑性程度，可添加不同比例的生料废泥为辅料，以满足工艺生产的要求。
实施例1
制备密度等级为600的陶粒轻骨料，将90％的抛光砖废泥与10％的生料废泥混练预处理后，成型造粒，经1130℃高温发泡烧成，制备的抛光砖废泥陶粒其性能指标为堆积密度590kg/m3，筒压强度7Mpa，吸水率7.3％，产品达到或超过国家优等品级别。
实施例2
制备密度等级为400的陶粒轻骨料，将95％的抛光砖废泥与5％的煤粉混合，混练预处理后造粒成型，经过二次造粒处理，经1150℃高温发泡烧成，制备的抛光砖废泥陶粒其性能指标为堆积密度395kg/m3，筒压强度4Mpa，吸水率7.5％，产品达到或超过国家优等品级别。
利用抛光砖废泥生产陶粒，投资小、工艺简单、成本低，具有良好经济社会效益。而且由于抛光砖废泥主要成份为经高温烧结的粘土和各种研磨料，以此为原料经高温烧结后得到的陶粒性能十分稳定，不含任何对人体和混凝土强度有害的物质，制备的陶粒产品是一种符合现代消费要求的环保材料，既解决了抛光砖废泥的出路问题，同时又解决了制造陶粒的材料来源问题，具有良好的经济与环保效益。

Claims (8)

1、一种轻质高强陶粒及其制备方法，其特征在于以陶瓷厂抛光砖生产线所产生的废水，经过沉淀或压滤后所得的陶瓷废泥为原料或主要原料，必要时加入适量生料废泥及煤为辅料，经均化处理、混料、造粒、烧成、筛分而成。
2、根据权利要求1所述的陶粒及其制备方法，其特征在于抛光砖废泥的含量不少于70％(重量百分比)，抛光砖废泥的含水量控制在15～40％；
3、根据权利要求1所述的陶粒及其制备方法，其特征在于生产轻细陶粒(≤5mm)骨料，可以不加入生料废泥或煤，即全部原料均为抛光砖废泥组成；
4、根据权利要求1和3所述的陶粒及其制备方法，其特征在于该生料废泥为由球磨机和喷雾塔产生的废泥；
5、根据权利要求1所述的陶粒及其制备方法，其特征在于生产轻粗陶粒(＞5mm)骨料，可加入不超过30％的生料废泥为辅料。
6、根据权利要求1所述的陶粒及其制备方法，其特征在于生产轻粗陶粒(＞5mm)骨料，可加入不超过30％的煤为辅料。
7、根据权利要求1、5和6所述的陶粒及其制备方法，其特征在于生产轻粗陶粒(＞5mm)骨料，可加入不超过30％的生料废泥和煤的混合料作为辅料。
8、根据权利要求1所述的陶粒及其制备方法，其特征在于抛光砖生产线产生的废泥其成分含量范围为氧化硅55～65％、氧化铝、13～18％、氧化铁＜1％、氧化镁和氧化钙4～8％、氧化钾和氧化钠2～5％。
CNB011076860A 2001-03-30 2001-03-30 一种抛光砖废泥陶粒及其制备方法 Expired - Lifetime CN1174935C (zh)