CN1064028C - 垃圾粉煤灰轻质免烧砖 - Google Patents

垃圾粉煤灰轻质免烧砖 Download PDF

Info

Publication number
CN1064028C
CN1064028C CN98125624A CN98125624A CN1064028C CN 1064028 C CN1064028 C CN 1064028C CN 98125624 A CN98125624 A CN 98125624A CN 98125624 A CN98125624 A CN 98125624A CN 1064028 C CN1064028 C CN 1064028C
Authority
CN
China
Prior art keywords
parts
grog
brick
flyash
calcium oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN98125624A
Other languages
English (en)
Other versions
CN1226528A (zh
Inventor
李桓宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Li Huanyu
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN98125624A priority Critical patent/CN1064028C/zh
Publication of CN1226528A publication Critical patent/CN1226528A/zh
Application granted granted Critical
Publication of CN1064028C publication Critical patent/CN1064028C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种垃圾粉煤灰轻质免烧砖，它采用生活垃圾经焚烧后的熟料、粉煤灰、炉渣或砂石、水泥、氧化钙、硫酸钙、硫酸钠、硅酸钠、氟硅酸钠为原料，经成型机压制成砖或砌块。该产品符合国家建筑材料标准，其方法简单、成本低、效益好，解决了生活垃圾、粉煤灰的利用问题，也改善了生活环境，为国家创造了财富，是利国利民的大事。

Description

垃圾粉煤灰轻质免烧砖
本发明涉及一种生活垃圾煤灰轻质免烧砖，具体地说是用生活垃圾粉煤灰为主要原料制作的免烧砖。
生活垃圾多数是由国家投资采用填埋场进行填埋处理，以减少环境污染，但是随着城市生活垃圾的累积增多，不仅占用大量土地，又会造成二次污染，而其中的有用成份也被浪费；而粉煤灰是一种工业废渣，每年以2亿吨的速度增加，用来生产制作免烧砖成本高，强度低、耐水性差，抗冻性能不好，且砖体重。
本发明的目的是为了解决上述存在的问题，而提供一种以生活垃圾和粉煤灰为原料制作成垃圾粉煤灰轻质免烧砖，从而解决了生活垃圾处理和粉煤灰的合理利用，并有机的结合制作成符合国家建材标准的轻质免烧砖，落实国家66号文件“关于大力发展节能，节地、利废、保温、隔热的墙体新型材料”的精神。
本发明的目的是通过下列技术方案实现的：
垃圾粉煤灰轻质免烧砖，其特征在于它由下述重量配比的原料组成：
生活垃圾焚烧熟料      30-35份
粉煤灰                20-25份
炉渣或砂石骨料        20-25份
水泥                    6-8份
氧化钙                10-13份
硫酸钙                  3-5份
硫酸钠                1-1.5份
硅酸钠                0.5-1份
氟硅酸钠          0.01-0.02份
水                     8-15份
垃圾粉煤灰轻质免烧砖的原料最佳配比为：
生活垃圾焚烧熟料         30份
粉煤灰                   25份
炉渣或砂石骨料           21份
水泥                      8份
氧化钙          13份
硫酸钙           3份
硫酸钠           1份
硅酸钠         0.5份
氟硅酸钠      0.01份
水              12份
本发明所述的生活垃圾焚烧熟料，为生活垃圾除出废金属后进行焚烧经粉碎的熟料，其粉碎粒径为-10mm的块料，炉渣、氧化钙粉碎粒径为-10mm，砂石粒径为-15mm。
本发明采用生活垃圾为原料，是利用生活垃圾经焚烧后可得到的熟料中含有大量的二氧化硅、三氧化二铝等成分均是制砖的好材料，而粉煤灰经过活化处理，充分发挥粉煤灰的潜在活性，使之生成大量的水化硅酸钙，水化铝酸钙和水化硫铝酸钙等一系列稳定的水化产物，与生活垃圾焚烧熟料混合制成轻体砖，从而解决生活垃圾的问题也解决了现有粉煤灰免烧砖的成本高、强度低、砖体重等问题，是一举多得、利国、利民的百年大计。
本发明的免烧砖制作方法是先将生活垃圾除去废金属后进行焚烧，粉碎至粒径为-10mm的块料，然后再加入粉煤灰和粉碎至-10mm的炉渣或者粒径为-15mm的砂石骨料，加水泥和粒径为-0.20mm的氧化钙和硫酸钙，加硫酸钠、硅酸钠、氟硅酸钠，再加入水混合呈潮湿状的物料，用免烧砖成型机，在20-25Mpa压制成型免烧砖，再用喷水法在常温下，自然干燥养护四周，经检验合格出厂。本发明的原料也可制作空心砌块，用砌块成型机压制成型。
按着本发明技术生产的免烧砖，经国家规定的建筑材料质量检测部门检测，各项指标均达到国家规定的粘土实心砖标准和砌块的有关标准：
由深圳市建筑科学研究所建材质量检验站检测结果如下：
免烧砖检测：
1、抗压强度：依据JC239-91标准。
单块强度：取10块样测定，最大强度16Mpa，最小强度8.9Mpa，平均12.8Mpa，检验结论为抗压强度评为10级。
2、抗折强度：取10块料测定，单块抗折强度，最大为3.0Mpa，最小为1.9Mpa，平均2.4Mpa，检验结论为7.5级。
3、砌块物理性能检验结果，检验依据为GBT4111-1997及GB15229-94，规格为390×190×140(mm)，单块抗压强度最大5.8Mpa，最小2.2Mpa，平均3.3Mpa，结果评定为Mu2.5。
由于采取上述技术方案本发明技术与已有技术相比具有如下优点及效果：
a)本发明的轻质免烧砖，由于生活垃圾熟料，粉煤灰的相对密度比粘土小，每块免烧砖比粘土实心砖轻0.5kg左右，而制成砌块，比水泥沙子砌块要轻50％以上，因此减轻建筑物的自重和延长高层建筑楼房的使用寿命；
b)生产工艺简单，投资少、见效快，成本低、效益好，适用各级办厂；
c)利用生活垃圾和煤粉灰工业废渣制砖，代替传统粘土砖，为绿色建材，是我国21世纪的重点发展项目；
d)为生活垃圾处理和工业废渣的利用提供一条经济效益可观的技术，为解决环境污染，减少土地占用提供了条件。
实施例1
将城市生活垃圾分选除去废金属后进行焚烧成熟料粉碎，其粉碎粒径为-10mm的块料为生活垃圾焚烧熟料取30kg，再加入粉煤灰25kg，炉渣粉碎-10mm取21kg作骨料，水泥8kg，粉碎粒径-0.20mm的氧化钙13kg和硫酸钙3kg，硫酸钠1kg，硅酸钠0.5kg，氟硅酸钠0.01kg，再加水12kg进行充分混合呈潮湿状，用免烧砖机在20Mpa压力下压制成型，再在常温下自然干燥养护四周，经检测其单块强度为13.5Mpa，抗折强度为2.6Mpa，为合格产品。
实施例2
取实施例1的生活垃圾焚烧熟料35kg，粉煤灰20kg，粒径为-15mm的砂石20kg作骨料，水泥6kg，粉碎粒径-0.20mm的氧化钙10kg和硫酸钙5kg，硫酸钠1.5kg，硅酸钠1.0kg、氟硅酸钠0.02kg，再加水8kg，进行充分混合呈潮湿状，用免烧砖机在25Mpa，压力下压制成型，再在常温下自然干燥养护四周，经检测单块强度11.6Mpa，抗折强度为3.0Mpa，为合格产品。
实施例3
取实施例1的生活垃圾焚烧熟料32kg、炉渣25kg和氧化钙12kg，粉煤灰22kg，水泥7kg，硫酸钙4kg，硫酸钠1.2kg，硅酸钠0.8kg，氟硅酸钠0.015kg，水15kg，进行混合呈潮湿状，用砌块成型机在20Mpa的压力压制成型390×190×140(mm)砌块强度为5.8Mpa，为合格产品。

Claims (4)

1．垃圾粉煤灰轻质免烧砖，其特征在于它由下述重量配比的原料组成：
生活垃圾焚烧熟料  30-35份
粉煤灰            20-25份
炉渣或砂石骨料    20-25份
水泥                6-8份
氧化钙            10-13份
硫酸钙              3-5份
硫酸钠            1-1.5份
硅酸钠            0.5-1份
氟硅酸钠      0.01-0.02份
水                 8-15份
2．根据权利要求1所述的免烧砖，其特征在于所述原料的最佳配比为：
生活垃圾焚烧熟料     30份
粉煤灰               25份
炉渣或砂石骨料       21份
水泥                  8份
氧化钙               13份
硫酸钙                3份
硫酸钠                1份
硅酸钠              0.5份
氟硅酸钠           0.01份
水                   12份
3．根据权利要求1或2所述的免烧砖，其特征在于所述的生活垃圾焚烧熟料，为生活垃圾除去废金属后进行焚烧经粉碎的熟料，其粉碎粒径为-10mm的块料。
4．根据权利要求1或2所述的免烧砖，其特征在于所述的炉渣、氧化钙粉碎粒径为-10mm，砂石粒径为-15mm。
CN98125624A 1998-12-21 1998-12-21 垃圾粉煤灰轻质免烧砖 Expired - Fee Related CN1064028C (zh)